Next Article in Journal
Canady Cold Helios Plasma Reduces Soft Tissue Sarcoma Viability by Inhibiting Proliferation, Disrupting Cell Cycle, and Inducing Apoptosis: A Preliminary Report
Previous Article in Journal
Effect of Extraction Methods and In Vitro Bio-Accessibility of Microencapsulated Lemon Extract
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Molecules
Volume 27
Issue 13
10.3390/molecules27134167
molecules-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles thumb_up
...
Endorse textsms
...
Comment
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Article

Interpretation of Strengthening Mechanism of Densified Wood from Supramolecular Structures

by
Kunpeng Li
,
Lihong Zhao
*,
Junli Ren
and
Beihai He
State Key Laboratory of Pulp and Paper Engineering, South China University of Technology, Guangzhou 510640, China
*
Author to whom correspondence should be addressed.
Molecules 2022, 27(13), 4167; https://doi.org/10.3390/molecules27134167
Submission received: 17 April 2022 / Revised: 20 June 2022 / Accepted: 27 June 2022 / Published: 29 June 2022
(This article belongs to the Section Macromolecular Chemistry)
Browse Figures
Versions Notes

Abstract

:
In this study, densified wood was prepared by hot pressing after partial lignin and hemicellulose were removed through alkaline solution cooking. The tensile strength and elastic modulus of densified wood were improved up to 398.5 MPa and 22.5 GPa as compared with the original wood, and the characterization of its supramolecular structures showed that the crystal plane spacing of the densified wood decreased, the crystallite size increased, and the maximum crystallinity (CI) of cellulose increased by 15.05%; outstandingly, the content of O(6)H⋯O(3′) intermolecular H-bonds increased by approximately one-fold at most. It was found that the intermolecular H-bond content was significantly positively correlated with the tensile strength and elastic modulus, and accordingly, their Pearson correlation coefficients were 0.952 (p < 0.01) and 0.822 (p < 0.05), respectively. This work provides a supramolecular explanation for the enhancement of tensile strength of densified wood.

1. Introduction

With environmental degradation and resource depletion, wood has attracted considerable attention from researchers due to its biodegradable, carbon-neutral, and inherently sustainable properties. Researchers have recently utilized and modified the intrinsic hierarchical structure of the wood to develop wood-based materials with specific properties, such as transparency [1,2], thermal management [3,4], electrical conductivity [5,6], and magnetism [7]. Most of these emerging applications reflected the lightweight and high-strength characteristics of wood-based materials. Accordingly, in-depth knowledge of the structure–strength relationship is the key to designing of wood-based materials with certain mechanical properties.
The skeleton component of wood-based materials is cellulose. Cellulose has excellent mechanical strength, such as cellulose nanofibrils with tensile strength up to 1.6 to 3.0 GPa [8] and crystalline cellulose I with the axial elastic modulus up to 130 to 150 GPa [9,10]. Presently, it is generally accepted that wood-based materials with higher cellulose content produce higher mechanical strength [11]. Therefore, partial removal of the matrix, especially the lignin, from wood allowed the preparation of high-strength, densified wood [2,12,13,14,15,16,17]. Specifically, wood was treated with a delignification process derived from the classical pulp production method while maintaining the aligned structure of wood fibers; subsequently, the delignified wood was densified by hot pressing.
The arrangement and stacking state of the cellulose molecular chains, defined as the supramolecular structures, is critical to the mechanical properties of densified wood. For instance, Jakob et al. [18] found that the tensile strength and elastic modulus decreased with the increasing tensile misalignment angle relative to fiber orientation and leveled off at misalignment angles of ≥30°. Khakalo et al. [15] used ionic liquids to convert the cellulose I of densified wood into cellulose II. They found that the tensile strength of densified wood decreased with the polymorphic transformation and the decreasing crystallinity.
The hydrogen bond was considered as the critical force determining the mechanical properties of cellulosic materials and densified wood [16,19,20,21,22]. Researchers have done much work on the relationship between them by simulations. For cellulose-based paper, Zhu et al. [20] showed that easier formation and reorganization of hydrogen bonds was crucial to simultaneously improving the strength and toughness of cellulose nanopaper. Meng et al. [23] developed a multi-scale crack bridging model. It suggested that bridging and hydrogen bonding between cellulose nanofibrils played an essential role in the toughening of cellulose nanopaper. In densified wood, cellulose molecular chains were in a highly aligned orientation, which amplified the enhancement of hydrogen bonding with the collective synergistic effect of molecular interlocking [24]. Molecular simulations by Song et al. [16] showed that hydrogen bonds could increase the sliding resistance between two adjacent lignocellulosic fibers of densified wood about 10-fold. In addition, the researchers have indirectly demonstrated the influence of hydrogen bonding on mechanical properties of cellulose-based paper and densified wood through experiments [25,26]. In the preparation of densified wood, Han et al. [26] investigated the effects of different drying methods and moisture content of delignified wood on the mechanical properties of the material and found a close relationship between them. There has been a lack of actual experimental data on the relationship between the tensile strength and hydrogen bonds of densified wood and cellulose-based materials.
In this work, densified wood with partially removed lignin and hemicellulose was prepared. The variations of intermolecular hydrogen bond content, crystalline structure, and crystallinity with cooking time were investigated. Based on the analysis of the supramolecular structures of cellulose, especially the content of intermolecular H-bonds, and the relationship between physical strength and the supramolecular structure, a molecular-level explanation for the enhanced tensile strength of densified wood was provided.

2. Results and Discussion

2.1. Tensile Strength and Morphology of Densified Wood

To prepare densified wood, natural basswood (NW) was treated in boiled water or boiled NaOH and Na2SO3 aqueous solutions at different times following a hot-pressing process. There were two kinds of densified wood: densified wood treated with boiled water, named DW-W1, and densified wood treated with boiled alkali solutions for 1 h, 2 h, 3 h, 4 h, 8 h, and 12 h, named DW-A1, DW-A2, DW-A3, DW-A4, DW-A8, and DW-A12, respectively. As shown in Figure 1, Figure S1 and Table 1, the mechanical properties of densified wood were significantly improved compared with NW. The tensile strength and elastic modulus of DW-W1 increased to 168.9 MPa and 12.7 GPa, respectively. It was attributed to the densification that increased the stress-transfer capacity within fiber substrates. The tensile strength and elastic modulus of densified wood kept rising during the alkali cooking time of 1–3 h, and the maximum reached 398.5 MPa and 22.5 GPa for DW-A3, as seen in Table 1. They were a 4.8-fold increase in tensile strength and 2.8-fold in elastic modulus compared to NW. This phenomenon was generally considered as an increase in the intermolecular hydrogen bonding content due to the removal of lignin and hemicellulose [13,16]. With the further extension of alkali cooking time, the tensile strength declined, while in comparison with DW-A3, the tensile strength and elastic modulus for DW-A12 decreased by 102.3 MPa and 6.8 GPa, respectively.
As shown in Figure 2, compared with log NW in Figure 2a,c,e, the densified DW-A3 in Figure 2b,d,f had the following changes through alkali cooking and hot pressing. Compared to NW, the thickness of DW-A3 showed a reduction of approximately four times. Comparing Figure 2c,d, it can be seen that NW had many lumens with diameters around 10–20 μm, while the cell lumens and cell walls of DW-A3 collapsed and formed a tighter bond inside. Comparing Figure 2e,f, the gaps between fibers were diminished, the boundary between fibers was blurred, and the surface was denser and smoother.

2.2. Content of Intermolecular H-Bonds

Taking the second derivative of the hydroxyl band from 3700 to 3000 cm−1 will improve the resolution of various H-bonds. In the second derivative spectrum, 3580–3550 cm−1 is assigned for free OH(2) and OH(6), 3455–3410 cm−1 is for O(2)H⋯O(6) intramolecular H-bonds, 3375–3340 cm−1 is for O(3)H⋯O(5) intramolecular H-bonds, and 3310–3230 cm−1 is for O(6)H⋯O(3′) intermolecular H-bonds. According to the peak positions of H-bonds and free hydroxyl groups, the bands of 3700–3000 cm−1 were deconvoluted, as in Figure 3. The relative contents of different hydrogen bonds and free hydroxyl groups were calculated according to the percentage of the area they occupied. The calculated results are shown in Table 2.
As shown in Table 2 and Figure 4a, the content of O(6)H⋯O(3′) intermolecular H-bonds of DW-W1 cooked in water increased by 24.8%, from 10.8% to 13.5% compared to NW. Furthermore, the O(6)H⋯O(3′) H-bond content of each densified wood treated with alkali solutions was higher than DW-W1. This is because there is more lignin and hemicellulose removal by boiled alkali solution, allowing more intermolecular H-bond formation between the aligned fibers. Figure 4 illustrates the removal of lignin and hemicellulose and the formation of intermolecular H-bonds in densified wood treated with alkali solutions. O(6)H⋯O(3′) H-bond content within alkali cooking time ranging from 1 to 8 h was significantly higher than 12 h. The reduction of intermolecular H-bond content caused by the longer alkali cooking might be due to the destruction of H-bonds by OH− in alkali [27,28]. The maximum content of O(6)H⋯O(3′) H-bond was observed in DW-A2, which increased by 111% from 10.8% to 22.8% compared with NW.

2.3. Crystal Structure and Crystallinity

As shown in Figure 5, the positions of the 11(_)0, 110, 200, and 004 lattice planes remained almost consistent for all samples, which indicated that the cellulose polymorph lattice shape did not change. Table 3 shows that the CI for DW-W1 increased by 5.02% compared to NW, which was consistent with the rising crystallinities after hot pressing in the literature [29,30]. It could be explained by co-crystallization [31]. The CI for densified wood showed an overall trend of first increasing and then decreasing with the alkali cooking time. It increased in the alkali cooking phase of 1–4 h, and compared with NW and DW-W1, the CI of DW-A4 increased by 15.05% and 10.03%, respectively. The rise in CI could be attributed to two factors. One was the increase of cellulose proportion with the removal of amorphous lignin and hemicellulose. Another was the co-crystallization of free cellulose chains adjacent to the crystalline region after lignin and hemicellulose removal [32,33]. The CI of densified wood slightly decreased as cooking time over 4 h, probably due to the peeling effect of alkali on cellulose crystal [34].
The value of interplanar spacing is related to the number of paracrystalline layers. It had a minimum between 0.384 and 0.3866 nm for perfect cellulose microcrystals [35,36]. As shown in Table 3, the interplanar spacing of all densified wood samples was smaller than that of NW. In particular, the reduction in the interplanar spacing was more significant for the alkali-cooked densified wood than the water-cooked one. It was consistent with the literature [37] and associated with the more intense stacking of cellulose chains after the partial removal of lignin and hemicellulose.
The crystallite size of DW-W1 was slightly reduced by 0.1 nm compared to NW. However, it significantly increased for the densified wood treated with alkali. DW-A4 and DW-A8 had the maximum crystallite size, both increasing by 0.9 nm compared to NW, which could be explained by co-crystallization. Compared with DW-A8, the crystallite size for DW-A12 was slightly reduced by 0.2 nm. It might be caused by the peeling action of the alkali.

2.4. Correlation Analysis

Increasing the content of intermolecular H-bonds during cooking procedures resulted in a considerable increase in tensile strength and elastic modulus, as shown in Figure 6. The Pearson correlation coefficient between intermolecular H-bond content and tensile strength as well as between intermolecular H-bond content and elastic modulus was 0.952 (p < 0.01) and 0.822 (p < 0.05), respectively. It supports the molecular simulation results of Song et al. [16], which showed the pivotal contribution of intermolecular H-bonds to the enhanced strength of densified wood. Furthermore, the Pearson correlation coefficients between CI and tensile strength and between CI and elastic modulus were 0.945 (p < 0.01) and 0.904 (p < 0.01), respectively. The results illustrate the close relationships between the supramolecular structures of cellulose and the tensile properties of densified wood. Notably, some researchers considered that van der Waals forces also impacted the mechanical properties of cellulose materials [22,38,39]. Therefore, the correlation between tensile strength and density was also explored, and the Pearson correlation coefficient was 0.921 (p < 0.01), which was less than the 0.952 (p < 0.01) that was between tensile strength and intermolecular H-bond content. It might be due to the fact that H-bonds played a dominant role in the enhancing strength of densified wood, while van der Waals forces played a subordinate role.

3. Materials and Methods

3.1. Materials

Basswood, 30 × 30 × 1 mm; sodium hydroxide (AR, 96%); sodium sulfite (AR, 97%).

3.2. The Preparation of Densified Wood

As shown in Figure 7, natural basswood veneers were cooked in boiled water for 1 h or boiled 2.5 M NaOH and 0.4 M Na2SO3 aqueous solutions (the liquid ratio was 20:1) for 1 h, 2 h, 3 h, 4 h, 8 h, and 12 h. Residual chemicals were removed with deionized water. The treated wood samples in the water-saturated state were covered with polytetrafluoroethylene plates and pressed with a hydraulic press under pressure of 2.5 MPa at 100 °C for 4 h to obtain densified wood.

3.3. Chemical Composition Analysis

The chemical compositions of the samples were analyzed according to the NREL protocol, including cellulose (glucan), hemicellulose (xylan, arabinose, galactan), and lignin (Klason lignin and acid-soluble lignin) [40].

3.4. Scanning Electron Microscope (SEM) Analysis

The microstructure of samples was characterized by the SEM (Zeiss, Merlin, Germany) with an acceleration voltage of 10 kV.

3.5. Mechanical Properties

The mechanical properties were carried out on an Instron 5565 universal tester (Boston, MA, USA) using a 2 KN load cell. The dry specimens were balanced in a standard conditioned room (23 ± 1 °C, 50 ± 2% RH) for 24 h before the test.

3.6. XRD Analysis

The crystalline structure was determined by a Shimadzu XRD 7000S (Shimadzu, Kyoto, Japan) while using Cu-Ka radiation. The samples were scanned at 40 kV and 30 mA in a 2θ range of 4–40° at 1° min−1. Before analysis, the experimental data were nine points smoothed with Savitzky–Golay algorithm. The crystalline index (CI) values were obtained from the peak intensity method. The CI was calculated as Equation (1) [41].
CI = ( I 200   -   I m ) I 200   ×   100 %
where I200 is the maximum diffraction intensity value of the (200) lattice plane between the scattering angles of 2θ = 22° and 23°, and Iam is the minimum diffraction intensity of amorphous fraction between 2θ = 18° and 19°.
The crystallite size was calculated by the widely used Scherrer Equation (2) [42]:
L = k   ×   λ ( β   ×   cos θ )
where L is the size that is perpendicular to the lattice plane, k is a constant that depends on the crystal shape (0.89), λ is the wavelength of the incident beam in the diffraction experiment (0.154 nm), β is the full width at half maximum of the diffraction peak, and θ is the Bragg’s angle.

3.7. FT-IR Analysis

The FT-IR spectra were recorded on solid samples in KBr pellets by means of an FT-IR Bruker Vertex 70 spectrometer (Karlsruhe, Germany). The spectra were recorded by averaging 64 recordings and at a resolution of 4 cm−1 with transmission mode from 4000 cm−1 to 400 cm−1. The results were made on the average spectra (seen in Figure S2) obtained from three recordings. Nonlinear fitting of the FT-IR spectral region from 3000 cm−1 to 3700 cm−1 was carried out with the Gaussian function [42].

4. Conclusions

In this work, densified wood with the enhanced strength was successfully prepared by cooking with hot water and alkali followed by hot pressing, and the relationship between the strength properties of densified wood and the supramolecular structures of cellulose was discussed. From the experimental results, alkali solution removed lignin and hemicellulose in wood fibers more efficiently than hot water, creating conditions for the formation of hydrogen bonds between cellulose molecules and thus more significantly improving the strength of densified wood. Finally, it was concluded that there was a significantly positive correlation between the tensile strength of densified wood and the supramolecular structures of cellulose, such as crystallinity and the intermolecular hydrogen bond content.

Supplementary Materials

The following supporting information can be downloaded at: https://www.mdpi.com/article/10.3390/molecules27134167/s1, Figure S1: stress-strain curve of NW and densified wood with various cooking time; Figure S2: FT-IR of NW and densified wood.

Author Contributions

Conceptualization, K.L. and L.Z.; methodology, K.L.; software, K.L.; validation, K.L. and L.Z.; formal analysis, K.L.; investigation, K.L.; resources, L.Z., J.R. and B.H.; data curation, K.L.; writing—original draft preparation, K.L.; writing—review and editing, L.Z.; visualization, K.L.; supervision, L.Z.; project administration, L.Z., J.R. and B.H.; funding acquisition, L.Z., J.R. and B.H. All authors have read and agreed to the published version of the manuscript.

Funding

This research was supported by the Key Area R&D Program of Guangdong Province (2020B0101070001).

Institutional Review Board Statement

Not applicable.

Informed Consent Statement

Not applicable.

Data Availability Statement

Not applicable.

Conflicts of Interest

The authors declare no conflict of interest. The funders had no role in the design of the study; in the collection, analyses, or interpretation of data; in the writing of the manuscript, or in the decision to publish the results.

References

  1. Xia, Q.; Chen, C.; Li, T.; He, S.; Gao, J.; Wang, X.; Hu, L. Solar-assisted fabrication of large-scale, patternable transparent wood. Sci. Adv. 2021, 7, d7342. [Google Scholar] [CrossRef] [PubMed]
  2. Fu, Q.; Chen, Y.; Sorieul, M. Wood-based flexible electronics. ACS Nano 2020, 14, 3528–3538. [Google Scholar] [CrossRef] [PubMed]
  3. Li, T.; Zhai, Y.; He, S.; Gan, W.; Wei, Z.; Heidarinejad, M.; Dalgo, D.; Mi, R.; Zhao, X.; Song, J. A radiative cooling structural material. Science 2019, 364, 760–763. [Google Scholar] [CrossRef] [PubMed] [Green Version]
  4. Li, T.; Song, J.; Zhao, X.; Yang, Z.; Pastel, G.; Xu, S.; Jia, C.; Dai, J.; Chen, C.; Gong, A. Anisotropic, lightweight, strong, and super thermally insulating nanowood with naturally aligned nanocellulose. Sci. Adv. 2018, 4, r3724. [Google Scholar] [CrossRef] [Green Version]
  5. Zhang, J.; Shen, Q. Processing natural wood into bulk conducting materials. SN Appl. Sci. 2019, 1, 1–7. [Google Scholar] [CrossRef] [Green Version]
  6. Gan, W.; Chen, C.; Giroux, M.; Zhong, G.; Goyal, M.M.; Wang, Y.; Ping, W.; Song, J.; Xu, S.; He, S. Conductive wood for high-performance structural electromagnetic interference shielding. Chem. Mater. 2020, 32, 5280–5289. [Google Scholar] [CrossRef]
  7. Cheng, Z.; Wei, Y.; Liu, C.; Chen, Y.; Ma, Y.; Chen, H.; Liang, X.; Sun, N.X.; Zhu, H. Lightweight and construable magnetic wood for electromagnetic interference shielding. Adv. Eng. Mater. 2020, 22, 2000257. [Google Scholar] [CrossRef]
  8. Saito, T.; Kuramae, R.; Wohlert, J.; Berglund, L.A.; Isogai, A. An ultrastrong nanofibrillar biomaterial: The strength of single cellulose nanofibrils revealed via sonication-induced fragmentation. Biomacromolecules 2013, 14, 248–253. [Google Scholar] [CrossRef]
  9. Sakurada, I.; Nukushina, Y.; Ito, T. Experimental determination of the elastic modulus of crystalline regions in oriented polymers. J. Polym. Ence Part A Polym. Chem. 1962, 57, 651–660. [Google Scholar] [CrossRef]
  10. Shinichiro, I.; Weihua, K.; Akira, I.; Tadahisa, I. Elastic modulus of single cellulose microfibrils from tunicate measured by atomic force microscopy. Biomacromolecules 2009, 10, 2571–2576. [Google Scholar]
  11. Keplinger, T.; Wittel, F.K.; Rüggeberg, M.; Burgert, I. Wood derived cellulose scaffolds—processing and mechanics. Adv. Mater. 2020, 33, 2001375. [Google Scholar] [CrossRef] [PubMed]
  12. Khakalo, A.; Tanaka, A.; Korpela, A.; Hauru, L.K.; Orelma, H. All-wood composite material by partial fiber surface dissolution with an ionic liquid. ACS Sustain. Chem. Eng. 2019, 7, 3195–3202. [Google Scholar] [CrossRef]
  13. Fang, Z.; Li, B.; Liu, Y.; Zhu, J.; Li, G.; Hou, G.; Zhou, J.; Qiu, X. Critical role of degree of polymerization of cellulose in super-strong nanocellulose films. Matter 2020, 2, 1000–1014. [Google Scholar] [CrossRef]
  14. Frey, M.; Widner, D.; Segmehl, J.S.; Casdorff, K.; Keplinger, T.; Burgert, I. Delignified and densified cellulose bulk materials with excellent tensile properties for sustainable engineering. ACS Appl. Mater. Inter. 2018, 10, 5030–5037. [Google Scholar] [CrossRef] [PubMed]
  15. Khakalo, A.; Tanaka, A.; Korpela, A.; Orelma, H. Delignification and ionic liquid treatment of wood toward multifunctional high-performance structural materials. ACS Appl. Mater. Inter. 2020, 12, 23532–23542. [Google Scholar] [CrossRef] [PubMed]
  16. Song, J.; Chen, C.; Zhu, S.; Zhu, M.; Dai, J.; Ray, U.; Li, Y.; Kuang, Y.; Li, Y.; Quispe, N. Processing bulk natural wood into a high-performance structural material. Nature 2018, 554, 224–228. [Google Scholar] [CrossRef]
  17. Li, Z.; Chen, C.; Mi, R.; Gan, W.; Dai, J.; Jiao, M.; Xie, H.; Yao, Y.; Xiao, S.; Hu, L. A strong, tough, and scalable structural material from fast-growing bamboo. Adv. Mater. 2020, 32, 1906308. [Google Scholar] [CrossRef]
  18. Jakob, M.; Gaugeler, J.; Gindl-Altmutter, W. Effects of fiber angle on the tensile properties of partially delignified and densified wood. Materials 2020, 13, 5405. [Google Scholar] [CrossRef]
  19. Ray, U.; Zhu, S.; Pang, Z.; Li, T. Mechanics design in cellulose-enabled high-performance functional materials. Adv. Mater. 2021, 33, 2002504. [Google Scholar] [CrossRef]
  20. Zhu, H.; Zhu, S.; Jia, Z.; Parvinian, S.; Li, Y.; Vaaland, O.; Hu, L.; Li, T. Anomalous scaling law of strength and toughness of cellulose nanopaper. Proc. Natl. Acad. Sci. USA 2015, 112, 8971–8976. [Google Scholar] [CrossRef] [Green Version]
  21. Chen, C.; Kuang, Y.; Zhu, S.; Burgert, I.; Keplinger, T.; Gong, A.; Li, T.; Berglund, L.; Eichhorn, S.J.; Hu, L. Structure–property–function relationships of natural and engineered wood. Nat. Rev. Mater. 2020, 5, 642–666. [Google Scholar] [CrossRef]
  22. Wohlert, M.; Benselfelt, T.; Wågberg, L.; Furó, I.; Berglund, L.A.; Wohlert, J. Cellulose and the role of hydrogen bonds: Not in charge of everything. Cellulose 2021, 29, 1–23. [Google Scholar] [CrossRef]
  23. Meng, Q.; Li, B.; Li, T.; Feng, X. A multiscale crack-bridging model of cellulose nanopaper. J. Mech. Phys. Solids 2017, 103, 22–39. [Google Scholar] [CrossRef] [Green Version]
  24. Mittal, N.; Ansari, F.; Gowda, V.K.; Brouzet, C.; Chen, P.; Larsson, P.T.; Roth, S.V.; Lundell, F.; Wagberg, L.; Kotov, N.A. Multiscale control of nanocellulose assembly: Transferring remarkable nanoscale fibril mechanics to macroscale fibers. ACS Nano 2018, 12, 6378–6388. [Google Scholar] [CrossRef] [PubMed]
  25. Manrίquez, R.; López-Dellamary, F.A.; Frydel, J.; Emmler, T.; Breitzke, H.; Buntkowsky, G.; Limbach, H.; Shenderovich, I.G. Solid-state nmr studies of aminocarboxylic salt bridges in l-lysine modified cellulose. J. Phys. Chem. B 2009, 113, 934–940. [Google Scholar] [CrossRef]
  26. Han, X.; Ye, Y.; Lam, F.; Pu, J.; Jiang, F. Hydrogen-bonding-induced assembly of aligned cellulose nanofibers into ultrastrong and tough bulk materials. J. Mater. Chem. A 2019, 7, 27023–27031. [Google Scholar] [CrossRef]
  27. Xiong, B.; Zhao, P.; Cai, P.; Zhang, L.; Hu, K.; Cheng, G. Nmr spectroscopic studies on the mechanism of cellulose dissolution in alkali solutions. Cellulose 2013, 20, 613–621. [Google Scholar] [CrossRef]
  28. Xu, Y.; Xu, Y.; Yue, X. Changes of hydrogen bonding and aggregation structure of cellulose fiber due to microwave-assisted alkali treatment and its impacts on the application as fluff pulp. Cellulose 2017, 24, 967–976. [Google Scholar] [CrossRef]
  29. Ucuncu, T.; Durmaz, E.; Kaymakci, A. Characteristics of hot-compressed poplar wood boards. BioResources 2017, 12, 9038–9049. [Google Scholar]
  30. Wang, Q.; Xiao, S.; Shi, S.Q.; Cai, L. The effect of delignification on the properties of cellulosic fiber material. Holzforschung 2018, 72, 443–449. [Google Scholar] [CrossRef]
  31. Newman, R.H. Carbon-13 nmr evidence for cocrystallization of cellulose as a mechanism for hornification of bleached kraft pulp. Cellulose 2004, 11, 45–52. [Google Scholar] [CrossRef]
  32. Duchemin, B.; Thuault, A.; Vicente, A.; Rigaud, B.; Fernandez, C.; Eve, S. Ultrastructure of cellulose crystallites in flax textile fibres. Cellulose 2012, 19, 1837–1854. [Google Scholar] [CrossRef]
  33. Evans, R.; Newman, R.H.; Roick, U.C.; Suckling, I.D.; Wallis, A.F. Changes in cellulose crystallinity during kraft pulping. Comparison of infrared, x-ray diffraction and solid state nmr results. Holzforschung 1995, 49, 498–504. [Google Scholar] [CrossRef]
  34. Funahashi, R.; Okita, Y.; Hondo, H.; Zhao, M.; Saito, T.; Isogai, A. Different conformations of surface cellulose molecules in native cellulose microfibrils revealed by layer-by-layer peeling. Biomacromolecules 2017, 18, 3687–3694. [Google Scholar] [CrossRef] [PubMed]
  35. Nishiyama, Y.; Langan, P.; Chanzy, H. Crystal structure and hydrogen-bonding system in cellulose iβ from synchrotron x-ray and neutron fiber diffraction. J. Am. Chem. Soc. 2002, 124, 9074–9082. [Google Scholar] [CrossRef]
  36. Ioelovich, M.; Leykin, A.; Figovsky, O. Study of cellulose paracrystallinity. BioResources 2010, 5, 1393–1407. [Google Scholar]
  37. Thulluri, C.; Balasubramaniam, R.; Velankar, H.R. Generation of highly amenable cellulose-iβ via selective delignification of rice straw using a reusable cyclic ether-assisted deep eutectic solvent system. Sci. Rep. UK 2021, 11, 1–14. [Google Scholar] [CrossRef]
  38. Nishiyama, Y. Molecular interactions in nanocellulose assembly. Philos. Trans. R. Soc. A Math. Phys. Eng. Sci. 2018, 376, 20170047. [Google Scholar] [CrossRef]
  39. Chen, P.; Nishiyama, Y.; Wohlert, J. Quantifying the influence of dispersion interactions on the elastic properties of crystalline cellulose. Cellulose 2021, 28, 10777–10786. [Google Scholar] [CrossRef]
  40. Sluiter, A.; Hames, B.; Ruiz, R.; Scarlata, C.; Sluiter, J.; Templeton, D.; Crocker, D. Determination of structural carbohydrates and lignin in biomass. Lab. Anal. Proced. 2008, 1617, 1–16. [Google Scholar]
  41. Segal, L.; Creely, J.J.; Martin, A.E.; Conrad, C.M. An empirical method for estimating the degree of crystallinity of native cellulose using the x-ray diffractometer. Text. Res. J. 1959, 29, 786–794. [Google Scholar] [CrossRef]
  42. Li, K.; Zhao, L.; He, B. Probing effect of papirindustriens forskningsinstitut (pfi) refining on aggregation structure of cellulose: Crystal packing and hydrogen-bonding network. Polymers 2020, 12, 2912. [Google Scholar] [CrossRef] [PubMed]
Molecules 27 04167 g001 550
Figure 1. Tensile strength and elastic modulus of NW and densified wood.
Figure 1. Tensile strength and elastic modulus of NW and densified wood.
Molecules 27 04167 g001
Molecules 27 04167 g002 550
Figure 2. Photographs of (a) NW and (b) DW-A3 (densified wood from 3 h alkali cooking), cross-sections of (c) NW and (d) DW-A3, and longitudinal sections of (e) NW and (f) DW-A3.
Figure 2. Photographs of (a) NW and (b) DW-A3 (densified wood from 3 h alkali cooking), cross-sections of (c) NW and (d) DW-A3, and longitudinal sections of (e) NW and (f) DW-A3.
Molecules 27 04167 g002
Molecules 27 04167 g003 550
Figure 3. The deconvoluted FT-IR spectra of (a) NW and densified wood: (b) DW-W1, (c) DW-A1, (d) DW-A2, (e) DW-A3, (f) DW-A4, (g) DW-A8, and (h) DW-A12.
Figure 3. The deconvoluted FT-IR spectra of (a) NW and densified wood: (b) DW-W1, (c) DW-A1, (d) DW-A2, (e) DW-A3, (f) DW-A4, (g) DW-A8, and (h) DW-A12.
Molecules 27 04167 g003
Molecules 27 04167 g004 550
Figure 4. (a) The intermolecular H-bond content of NW and densified wood and (b) illustration of changes in cellulose interfibrillar components and the formation of intermolecular H-bonds in the wood through alkali cooking and densification.
Figure 4. (a) The intermolecular H-bond content of NW and densified wood and (b) illustration of changes in cellulose interfibrillar components and the formation of intermolecular H-bonds in the wood through alkali cooking and densification.
Molecules 27 04167 g004
Molecules 27 04167 g005 550
Figure 5. XRD diffractograms of the natural wood and densified wood.
Figure 5. XRD diffractograms of the natural wood and densified wood.
Molecules 27 04167 g005
Molecules 27 04167 g006 550
Figure 6. (a) Relationships between the content of intermolecular H-bonds and mechanical properties of natural and densified wood and (b) relationships between CI and mechanical properties of natural and densified wood.
Figure 6. (a) Relationships between the content of intermolecular H-bonds and mechanical properties of natural and densified wood and (b) relationships between CI and mechanical properties of natural and densified wood.
Molecules 27 04167 g006
Molecules 27 04167 g007 550
Figure 7. Schematic diagram of the preparation process of densified wood.
Figure 7. Schematic diagram of the preparation process of densified wood.
Molecules 27 04167 g007
Table
Table 1. Chemical components, density, and tensile properties of NW and densified wood.
Table 1. Chemical components, density, and tensile properties of NW and densified wood.
SamplesLignin Content (%)Cellulose Content (%)Hemicellulose Content (%)Density
(g cm−3)		Tensile Strength (MPa)Elastic Modulus (GPa)
NW24.7 (0.4)45.4 (0.5)19.2 (0.3)0.44(0.04)68.4 (20.4)5.9 (1.6)
DW-W124.7 (0.2)45.3 (0.7)19.5 (0.7)1.06(0.05)168.9 (22.6)12.7 (2.1)
DW-A120.4 (0.1)62.3 (1.2)8.9 (1.2)1.32(0.03)294.3 (46.8)13.7 (2.7)
DW-A220.2 (0.5)64.7 (1.1)9.3 (1.2)1.31(0.00)353.0 (25.0)17.8 (2.5)
DW-A319.3 (0.6)66.7 (0.9)8.5 (0.9)1.34(0.02)398.5 (36.7)22.5 (1.5)
DW-A418.4 (0.4)68.7 (0.6)9.7 (1.1)1.33(0.02)356.1 (31.2)21.3 (2.0)
DW-A818.4 (0.7)72.7 (0.8)8.7 (0.5)1.30(0.04)334.7 (41.5)17.1 (2.2)
DW-A1219.0 (0.5)74.3 (0.7)8.0 (0.7)1.26(0.02)296.2 (39.3)15.7 (1.2)
Table
Table 2. The relative content of three H-bonds and the free OH of NW and densified wood.
Table 2. The relative content of three H-bonds and the free OH of NW and densified wood.
SamplesO(6)H⋯O(3′)O(3)H⋯O(5)O(2)H⋯O(6)Free OH(2) and OH(6)R2
NW10.846.129.613.50.9988
DW-W113.545.426.514.60.9988
DW-A122.229.531.117.20.9976
DW-A222.826.034.616.60.9976
DW-A321.726.134.218.00.9979
DW-A422.327.435.814.50.9976
DW-A821.924.835.018.30.9979
DW-A1219.031.435.414.20.9984
R2 is the coefficient of determination.
Table
Table 3. Crystalline index, crystallite size, and interplanar spacing of natural wood and densified wood.
Table 3. Crystalline index, crystallite size, and interplanar spacing of natural wood and densified wood.
SampleCI (%)Crystallite Size (nm) aInterplanar Spacing (nm) b
NW60.823.30.398
DW-W165.843.20.396
DW-A169.543.80.393
DW-A273.753.80.392
DW-A373.863.80.391
DW-A475.874.20.393
DW-A874.754.20.393
DW-A1274.204.00.391
a The size perpendicular to 200 planes; b the interplanar spacing of 200 planes.
Publisher’s Note: MDPI stays neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Share and Cite

MDPI and ACS Style

Li, K.; Zhao, L.; Ren, J.; He, B. Interpretation of Strengthening Mechanism of Densified Wood from Supramolecular Structures. Molecules 2022, 27, 4167. https://doi.org/10.3390/molecules27134167

AMA Style

Li K, Zhao L, Ren J, He B. Interpretation of Strengthening Mechanism of Densified Wood from Supramolecular Structures. Molecules. 2022; 27(13):4167. https://doi.org/10.3390/molecules27134167

Chicago/Turabian Style

Li, Kunpeng, Lihong Zhao, Junli Ren, and Beihai He. 2022. "Interpretation of Strengthening Mechanism of Densified Wood from Supramolecular Structures" Molecules 27, no. 13: 4167. https://doi.org/10.3390/molecules27134167