镀<span>Cr层对低碳钢/CFRP激光连接接头剪切强度及界面结合特征的影响</span>

doi:10.3724/SP.J.1037.2013.00045

金属学报

2013, Vol. 49

Issue (6): 751-756 DOI: 10.3724/SP.J.1037.2013.00045

论文

本期目录 | 过刊浏览

镀Cr层对低碳钢/CFRP激光连接接头剪切强度及界面结合特征的影响

谭向虎^1),单际国^1,2),任家烈¹⁾

1) 清华大学机械工程系,北京 100084
2) 清华大学先进成形制造教育部重点实验室, 北京100084

EFFECTS OF Cr PLATING LAYER ON SHEAR STRENGTH AND INTERFACE BONDING CHARACTERISTICS OF MILD STEEL/CFRP JOINT BY LASER HEATING

TAN Xianghu¹⁾,SHAN Jiguo^1,²⁾,REN Jialie¹⁾

1) Department of Mechanical Engineering, Tsinghua University, Beijing 100084
2) Key Laboratory for Advanced Materials Processing Technology, Ministry of Education, Tsinghua University, Beijing 100084

引用本文:

谭向虎,单际国,任家烈. 镀Cr层对低碳钢/CFRP激光连接接头剪切强度及界面结合特征的影响[J]. 金属学报, 2013, 49(6): 751-756.
TAN Xianghu, SHAN Jiguo, REN Jialie. EFFECTS OF Cr PLATING LAYER ON SHEAR STRENGTH AND INTERFACE BONDING CHARACTERISTICS OF MILD STEEL/CFRP JOINT BY LASER HEATING[J]. Acta Metall Sin, 2013, 49(6): 751-756.

全文: PDF(2437 KB)

摘要:

在低碳钢表面电镀一定厚度的Cr层,再利用光纤激光连接低碳钢与碳纤维增强树脂基复合材料(CFRP),研究镀Cr层对低碳钢/CFRP搭接接头剪切强度及界面结合特征的影响.结果表明, 低碳钢表面镀Cr层大大提高了接头的剪切力和剪切强度,剪切力由2237.37 N增加到6127.81 N, 剪切强度由9.32 MPa增加到22.14 MPa;未镀Cr的低碳钢/CFRP接头的剪切破坏主要发生在搭接接头的连接界面上,镀Cr后改善了界面结合质量,剪切破坏发生在靠近搭接接头连接界面的CFRP上,断裂位置与CFRP中的气孔区相吻合. 激光连接过程中,镀Cr层与CFRP在连接界面处发生反应, 形成了Cr-O-PA6T化学键合,是接头界面强度得以提高的重要原因.

关键词 ：低碳钢/CFRP异质结构, 镀Cr层, 激光连接, 界面反应, 剪切强度

Abstract：

The carbon fiber reinforced polymer (CFRP) has been widely used in aerospace and military fields, whereas it is still at its initial stage in the field of automobile manufacturing, wind power generation and so on. One of the main reasons to restrict its wide application is that the strength of metal/CFRP joint is very low and cannot meet the industrial requirements. In this study, an investigation of the laser joining between CFRP and mild steel with Cr electroplating was presented. The influence of Cr plating layer on shear strength of mild steel/CFRP lap joint was studied and the bonding characteristics of the joint interface were analyzed by SEM and XPS. The results show that Cr plating layer can greatly improve the shear force and shear strength of mild steel/CFRP joint. The shear force increases from 2237.37 N to 6127.81 N and the shear strength increases from 9.32 MPa to 22.14 MPa. For the mild steel/CFRP joint without Cr plating, the shear failure happens at the interface. However, for the mild steel/CFRP joint with Cr plating, the shear failure happens at the porosities zone in the CFRP. It means that the Cr plating can improve the interfacial bonding strength. The results of SEM observation and XPS analyses show that the mechanical bonding represented as the ``anchoring effect'' is achieved at the mild steel/CFRP interface both with and without Cr plating. But the chemical bonding is detected only at the mild steel/CFRP interface with Cr plating, which is considered as an important reason that the Cr plating can improve the bonding strength of the mild steel/CFRP joint.

Key words： mild steel/CFRP dissimilar joint Cr plating layer laser joining, interfacial reaction shear strength

收稿日期: 2013-01-24

基金资助:

国家自然科学基金资助项目51275271

作者简介: 谭向虎, 男, 1987年生, 博士生

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	谭向虎
	单际国
	任家烈
44.8K

链接本文:

https://www.ams.org.cn/CN/10.3724/SP.J.1037.2013.00045 或 https://www.ams.org.cn/CN/Y2013/V49/I6/751

[1]Williams G J,Trask R S, Bond I P. Composites, 2007; 38A: 1525
[2] Soutis C. Mater Sci Eng, 2005; A412: 171
[3] Vaidya U K, Chawla K K. Int Mater Rev, 2008; 53:185
[4] Duflou J R, De Moor J, Verpoest I, Dewulf W.CIRP Ann Manuf Technol, 2009; 58: 9
[5] Jaeschke P, Herzog D, Haferkamp H, Peters C, Herrmann AS. J Reinf Plast Compos, 2010; 29: 3083
[6] Amancio--Filho S T, Santos J F D. Polym Eng Sci,2009; 8: 1461
[7] Ageorges C, Ye L, Hou M. Composites, 2001; 32A:839
[8] Hino M, Mitooka Y, Murakami K, Kanadani T. In: Chandra T,Ionescu M, Mantovani D eds., Materials Science Forum,Quebec: Trans Tech Publications Ltd, 2012: 2956
[9] Katayama S, Jung K W, Kawahito Y. In: David A ed.,ICALEO 2010 Congress Proceedings, Orlando: Laser Instituteof America, 2010: 333
[10] Jung K W, Kawahito Y, Katayama S. Sci Technol Weld Join, 2011; 16: 676
[11] Katayama S, Kawahito Y. Scr Mater, 2008; 59:1247
[12] Wahba M, Kawahito Y, Katayama S. J Mater Process Technol, 2011; 211: 1166
[13] Kawahito Y, Tange A, Kubota S, Katayama S. In: Laser Institute of America ed., ICALEO 2006 Congress Proceedings, Orlando: Laser Institute of America, 2006: 376
[14] Roesner A, Scheik S, Olowinsky A, Gillner A, Poprawe R, Schleser M, Reisgen U. J Laser Appl, 2011; 23:032007-1
[15] Holtkamp J, Roesner A, Gillner A. Int J Adv Manuf Technol, 2010; 47: 923
[16] Lee H Y, Qu J M. J Adhes Sci Technol, 2003; 17:195
[17] Ho P S, Hahn P O, Bartha J W, Rubloff G W, Legoues F K, Silverman B D. J Vac Sci Technol, 1985; 3A: 739
[18] Chou N J, Tang C H. J Vac Sci Technol, 1984; 2A:751
[19] Bebin P, Prud'Homme R E. J Vac Sci Technol, 2002;20A: 1611
[20] Cantrell J H. J Appl Phys, 2004; 96: 3775
[21] McCafferty E. J Adhes Sci Technol, 2002; 16: 239
[22] Fortunato A, Cuccolini G, Ascari A, Orazi L, Campana G, Tani G. Int J Mater Form, 2010; 3(suppl 1): 1131
[23] Goldberg M J, Clabes J G, Kovac C A. J Vac Sci Technol, 1988; 6A: 991
[24] Friedrich J F, Koprinarov I, Giebler R, Lippitz A, Unger W E S. J Adhes, 1999; 71: 297
[25] Tang D Y, Guo Y D, Zhang X H, Liu J. Surf Interface Anal, 2009; 41: 974

[1]	沈莹莹, 张国兴, 贾清, 王玉敏, 崔玉友, 杨锐. SiC_f/TiAl复合材料界面反应及热稳定性[J]. 金属学报, 2022, 58(9): 1150-1158.
[2]	宋庆忠, 潜坤, 舒磊, 陈波, 马颖澈, 刘奎. 镍基高温合金K417G与氧化物耐火材料的界面反应[J]. 金属学报, 2022, 58(7): 868-882.
[3]	王超, 张旭, 王玉敏, 杨青, 杨丽娜, 张国兴, 吴颖, 孔旭, 杨锐. SiC_f/Ti65复合材料界面反应与基体相变机理[J]. 金属学报, 2020, 56(9): 1275-1285.
[4]	肖宏,许朋朋,祁梓宸,吴宗河,赵云鹏. 感应加热异温轧制制备钢/铝复合板[J]. 金属学报, 2020, 56(2): 231-239.
[5]	张志杰, 黄明亮. 原位研究Cu/Sn-37Pb/Cu微焊点液-固电迁移行为[J]. 金属学报, 2020, 56(10): 1386-1392.
[6]	吉华,邓运来,徐红勇,郭伟强,邓建峰,范世通. 焊接线能量对5182-O/HC260YD+Z异种材料CMT搭接接头组织与性能的影响[J]. 金属学报, 2019, 55(3): 376-388.
[7]	曹丽华, 陈胤伯, 史起源, 远杰, 刘志权. 合金元素对中温Sn-Ag-Cu焊料互连组织及剪切强度的影响[J]. 金属学报, 2019, 55(12): 1606-1614.
[8]	冯业飞,周晓明,邹金文,王超渊,田高峰,宋晓俊,曾维虎. 粉末高温合金中SiO₂夹杂物与基体的界面反应机理及对其变形行为的影响[J]. 金属学报, 2019, 55(11): 1437-1447.
[9]	邱丰, 佟昊天, 沈平, 丛晓霜, 王轶, 姜启川. 综述：SiC/Al界面反应与界面结构演变规律及机制[J]. 金属学报, 2019, 55(1): 87-100.
[10]	刘佳琳, 王玉敏, 张国兴, 张旭, 杨丽娜, 杨青, 杨锐. SiC单纤维增强TC17复合材料横向拉伸性能研究[J]. 金属学报, 2018, 54(12): 1809-1817.
[11]	赵宁,邓建峰,钟毅,殷录桥. 热迁移下Ni/Sn-xCu/Ni微焊点钎焊界面金属间化合物的演变[J]. 金属学报, 2017, 53(7): 861-868.
[12]	张志杰,黄明亮. Cu/Sn-52In/Cu微焊点液-固电迁移行为研究[J]. 金属学报, 2017, 53(5): 592-600.
[13]	靳鹏,隋然,李富祥,俞伟元,林巧力. 熔融6061/4043铝合金在TC4钛合金表面的反应润湿[J]. 金属学报, 2017, 53(4): 479-486.
[14]	刘积厚,赵洪运,李卓霖,宋晓国,董红杰,赵一璇,冯吉才. Cu/Sn/Cu超声-TLP接头的显微组织与力学性能[J]. 金属学报, 2017, 53(2): 227-232.
[15]	王玉敏, 张国兴, 张旭, 杨青, 杨丽娜, 杨锐. 连续SiC纤维增强钛基复合材料研究进展^*[J]. 金属学报, 2016, 52(10): 1153-1170.

Viewed

Full text

Abstract

Cited

Shared

Discussed