The c/a Ratio in Quenched Fe-C and Fe-N Steels - A Heuristic Story

Article Preview

Abstract:

The body-centered tetragonal (BCT) structure in quenched Fe-C steels is usually illustrated to show a linear change in the c and a axes with an increase in carbon content from 0 to 1.4%C. The work of Campbell and Fink, however, shows that this continuous linear relationship is not correct. Rather, it was shown that the body-centered-cubic (BCC) structure is the stable structure from 0 to 0.6 wt%C with the c/a ratio equal to unity. An abrupt change in the c/a ratio to 1.02 occurs at 0.6 wt%C. The BCT structure forms, and the c/a ratio increases with further increase in carbon content. An identical observation is noted in quenched Fe-N steels. This discontinuity is explained by a change in the transformation process. It is proposed that a two-step transformation process occurs in the low carbon region, with the FCC first transforming to HCP and then from HCP to BCC. In the high carbon region, the FCC structure transforms to the BCT structure. The results are explained with the Engel-Brewer theory of valence and crystal structure of the elements. An understanding of the strength of quenched iron-carbon steels plays a key role in the proposed explanation of the c/a anomaly based on interstitial solutes and precipitates.

You might also be interested in these eBooks

Info:

Periodical:

Materials Science Forum (Volumes 539-543)

Pages:

215-222

Citation:

Online since:

March 2007

Export:

Price:

[1] E.C. Bain and H.W. Paxton: Alloying Elements in Steel (ASM, Metals Park, Ohio, 1966).

Google Scholar

[2] W.L. Fink and E.D. Campbell: Trans. Am. Soc. Steel Treat, Vol. 9 (1926), pp.717-752.

Google Scholar

[3] K. Honda and Z. Nishiyama: Science Reports, Tohoku Imperial Univ. Vol. 21 (1932), p.299; Trans. Am. Soc. Metals Vol. 20 (1932), p.464.

Google Scholar

[4] M. Cohen: Phase Transformations in Solids (John Wiley & Sons, New York 1951), p.588.

Google Scholar

[5] W.S. Owen, E.A. Wilson and T. Bell: High Strength Materials (V.F. Zackay Ed., John Wiley & Sons, New York 1965), pp.167-212.

Google Scholar

[6] L. Brewer: ibid, p.12.

Google Scholar

[7] W. Hume-Rothery: Prog. Mater. Sci. Vol. 13 (1968), p.229.

Google Scholar

[8] O.D. Sherby and J. Wadsworth: LLNL reports, May 25, 1999 and Nov. 4, (1999).

Google Scholar

[9] J.R. Cahoon and O.D. Sherby: Metall. Mater. Trans. Vol. 23A (1992), p.2491.

Google Scholar

[10] O.D. Sherby and C.M. Young: Plastic Deformation of Materials (J.C.M. Li and A.K. Mukherjee, Eds. Am. Soc. Metals, Metals Park, Ohio 1975), Vol. 6, pp.487-541.

Google Scholar

[11] M. Cohen: Trans. Metall. Society of AIME Vol. 224 (1962). p.638.

Google Scholar

[12] B.A. Bilby and J.W. Christian: Jnl. Iron and Steel Inst. Vol. 197 (1961), p.122.

Google Scholar

[13] P.G. Winchell: The Structure and Mechanical Properties of Iron-Nickel-Carbon Martensites (Sc.D. Thesis, MIT 1958).

Google Scholar

[14] V. Seetharamen and R. Krishman: J. Mater. Sci. Vol. 16 (1981), p.523.

Google Scholar

[15] A.R. Marder and G. Krauss: Trans. ASM Vol. 60 (1967), p.651.

Google Scholar

[16] C. Zener: Trans. AIME Vol. 167 (1946), p.550.

Google Scholar

[17] A.H. Cottrell: An Introduction to Metallurgy (Edward Arnold Publishers, Ltd, London 1967).

Google Scholar

[18] E.C. Bain: Trans. AIME Vol. 70 (1924), p.25.

Google Scholar

[19] G.R. Speich: Trans. Met. Soc. AIME Vol. 245 (1969), p.2553.

Google Scholar

[20] H. Carpenter and J.M. Robertson: Metals (Oxford University Press, 1939).

Google Scholar

[21] A.B. Greninger and A.R. Troiano: Trans. ASM Vol. 28 (1940), p.537.

Google Scholar

[22] M.C. Zhao, Y. Hanamura, H. Qui, and K. Yang: Mater. Trans. JIM Vol. 46 (2005), p.784.

Google Scholar

[23] C.K. Syn, D.R. Lesuer and O.D. Sherby: Mater. Sci. Tech. Vol. 21 (2005), p.317.

Google Scholar

[24] D.R. Lesuer, C.K. Syn and O.D. Sherby: submitted to Mater. Trans. JIM (2006).

Google Scholar

[25] G.V. Kurdjumov: J. Iron and Steel Inst. Vol. 195 (1960), p.26.

Google Scholar