Luminescence properties of novel double perovskite Gd2MgTiO6:Eu3+ phosphors prepared by solid state method
Erschienen in: Journal of Materials Science: Materials in Electronics | Ausgabe 16/2017
EinloggenAktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.
Wählen Sie Textabschnitte aus um mit Künstlicher Intelligenz passenden Patente zu finden. powered by
Markieren Sie Textabschnitte, um KI-gestützt weitere passende Inhalte zu finden. powered by
Abstract
A novel red double perovskite phosphor Gd2MgTiO6 was successfully synthesized by the conventional solid state method. The effects of the synthesis conditions of ball-milling parameters and calcination temperature on the phase composition, microstructure and luminescent properties were systematically investigated. Gd2MgTiO6:Eu3+ phosphors with purity crystalline phase and particle size of 3–5 μm for LED package application had been synthesized at the calcination temperature of 1400 °C. Gd2MgTiO6:Eu3+ emitted an intense peak centered at 615 nm under 395 nm UV excitation and the excitation spectrum had a wide absorption band in the range of 250–350 nm, and prominentsharp peaks at 395 and 466 nm. The optimized ball-milling parameters of the rotation speed of 300 rpm and milling time of 6 h could obtain a better size distribution and higher luminescence intensity due to the better crystallinity and less impurities introduced by ball-milling process.