Mechanical and Thermal Characterization of Urea-Formaldehyde Impregnated Wood Polymer Nanocomposites (WPNCs)

verfasst von : M. R. Rahman

Erschienen in: Wood Polymer Nanocomposites

Verlag: Springer International Publishing

Einloggen

Aktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.

search-config

KI-gestützte Suche

Aus

Abstract

In this study, urea-formaldehyde resin wood polymer nanocomposites (WPNCs) were investigated. All the WPNCs undergo characterizations. The FT-IR spectra confirmed the impregnation of organic urea-formaldehyde into the raw wood. Besides, WPNCs were generally more thermally stable over temperature compared to the raw wood due to the introduction of urea-formaldehyde into the raw wood. From mechanical testing, WPNCs showed higher MOE and MOR for Eugenia spp. and Xylopia spp., respectively. Besides, WPNCs on Eugenia spp. showed higher Young’s modulus compared to raw wood and other WPNCs. From the X-ray diffraction patterns, the crystallinity of WPNCs increased with the introduction of urea-formaldehyde resin into raw wood. The SEM micrograph of WPNCs clearly proved that the void space was fully filled with urea-formaldehyde resins and most of the waxy substance was removed. Therefore, urea-formaldehyde-impregnated WPNCs showed significantly effective on Eugenia spp., continued by Xylopia spp. and Artocarpus elasticus wood species.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

über 102.000 Bücher
über 537 Zeitschriften

aus folgenden Fachgebieten:

Automobil + Motoren
Bauwesen + Immobilien
Business IT + Informatik
Elektrotechnik + Elektronik
Energie + Nachhaltigkeit
Finance + Banking
Management + Führung
Marketing + Vertrieb
Maschinenbau + Werkstoffe
Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Jetzt informieren

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

über 67.000 Bücher
über 390 Zeitschriften

aus folgenden Fachgebieten:

Automobil + Motoren
Bauwesen + Immobilien
Business IT + Informatik
Elektrotechnik + Elektronik
Energie + Nachhaltigkeit
Maschinenbau + Werkstoffe

Jetzt Wissensvorsprung sichern!

Jetzt informieren

Vorheriges Kapitel Characterization of N,N-Dimethylacetamide Impregnated Wood Polymer Nanocomposites (WPNCs)

Nächstes Kapitel Characterization of Epoxy/Nanoclay Wood Polymer Nanocomposites (WPNCs)

Adams DG, Choong ET Mcllhenny RC (1970) Bending strength of radiation-produced southern pine wood-plastic combinations. Forest Prod J 20(4):25–28

Akita K, Kase M (1967) Determination of kinetic parameters for pyrolysis of cellulose and cellulose treated with ammonium phosphate by differential thermal analysis and thermal gravimetric analysis. J Polym Sci 1(5):833–848CrossRef

Autio T, Miettinen JK (1970) Experiments in Finland on properties of wood-polymer combinations. Forest Prod J 20(3):36–42

Bourgois J, Bartholin MC, Guyonnet R (1989) Thermal Treatment of wood: analysis of the obtained product. Wood Sci Technol 23:303–310CrossRef

Hamdan S, Talib ZA, Rahman MR, Ahmed AS, Islam MS (2010) Dynamic Young’s modulus measurement of treated and post-treated tropical wood polymer composites (WPC). BioRes 5(1):324–342

Herrera-France P, Aguilar-Vega M (1997) Effect of fiber treatment on the mechanical properties of LDPE-henequen cellulosic fibre composites. J Appl Polym Sci 10:197–207

Owen NL, Thomas DW (1989) Infrared studies of hard and soft woods. Appl Spec 43:451–455

Peters R, Still R (1979) Some aspects of the degradation of polymers used in textile applications. In: Happey F (ed) Applied Fiber Science, 2nd edn. Academic Press, London, pp 321–420

Rahman MR, Hamdan S, Saleh AA, Islam MS (2010) Mechanical and biological performance of sodium mataperiodate impregnated plasticized wood (PW). BioRes 5(2):1022–1035

Sreekala M, Kumaran M, Thomas S (1997) Oil plam fibres: morphology, chemical composition, surface modification and mechanical properties. J Appl Polym Sci 66:821–835CrossRef

Stamm AJ (1964) Factors affecting the bulking and dimensional stabilization of wood with polyethylene glycols. Forest Prod J 14:403–408

Wielage B, Lampke Th, Mark G, Nestler K, Starke D (1999) Thermogravimetric and differential scanning calorimetric analysis of natural fibers and polypropylene. Thermochim Acta 337:169–177CrossRef

Yildiz CU, Yildiz S, Gezer DE (2005) Mechanical properties and decay resistance of wood polymer composites prepared from fast growing species in Turkey. Biores Technol 96:1003–1011CrossRef

Titel: Mechanical and Thermal Characterization of Urea-Formaldehyde Impregnated Wood Polymer Nanocomposites (WPNCs)
verfasst von: M. R. Rahman
Verlag: Springer International Publishing
Buch: Wood Polymer Nanocomposites
Print ISBN: 978-3-319-65734-9

Electronic ISBN: 978-3-319-65735-6

Copyright-Jahr: 2018
DOI: https://doi.org/10.1007/978-3-319-65735-6_6

Premium Partner

Marktübersichten

Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen.

Zur Marktübersicht