Microstructure transformation of X70 pipeline steel welding heat-affected zone

verfasst von: Hui Li, Jing-Long Liang, Yun-Li Feng, Dong-Xing Huo

Erschienen in: Rare Metals | Ausgabe 4/2014

Einloggen

Aktivieren Sie unsere intelligente Suche um passende Fachinhalte oder Patente zu finden.

search-config
loading …

Abstract

The continuous cooling transformation curve of heat-affected zone (HAZ) of X70 pipeline steel was measured by Gleeble-3500 thermal mechanical simulator, optical microscope (OM) and hardness analysis. The microstructure transformation rule at different cooling rates and solution behaviors of microalloy carbonitride during heating process of simulated specimens were investigated. When the cooling rate changes from 10 to 20 °C·s−1, microstructures at HAZ are identified as granular bainite, lathy bainite, and quasi-polygonal ferrite. This microstructure is featured with fine ferrite grains, martensite/austenite islands dispersed, high-density dislocations, and fine carbonitride particles, resulting in improving the strength and toughness of HAZ. With the cooling rate increasing to above 40 °C·s−1, the microstructure is predominantly coarse lathy bainite with clear primary austenite grain boundary. While the cooling rate decreases to below 1 °C·s−1, a fairly small amount of pearlite can be observed at the boundaries. The strength and toughness of HAZ are deteriorated because of coarse grains among these microstructures. Most of microalloy carbonitrides in HAZ could be dissolved in the matrix during heating process. A few of TiN particles existing as residues in the matrix can prevent austenite grain from growing, and then improve the strength and toughness of HAZ.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Literatur
[1]
Zurück zum Zitat Zheng L, Gao S. Research and development of X70 coils for large diameter pipes of west-east gas pipeline project. J Iron Steel Res Int. 2006;18(3):46. Zheng L, Gao S. Research and development of X70 coils for large diameter pipes of west-east gas pipeline project. J Iron Steel Res Int. 2006;18(3):46.
[2]
Zurück zum Zitat Chen QJ, Kang YL, Sun H, Yu H. Static-recrystallization behavior of hot deformation austenite in X70 pipeline steel. J Univ Sci Technol B. 2007;29(12):1212. Chen QJ, Kang YL, Sun H, Yu H. Static-recrystallization behavior of hot deformation austenite in X70 pipeline steel. J Univ Sci Technol B. 2007;29(12):1212.
[3]
Zurück zum Zitat Zhang HM, Wang HB, Liu ZY, Liu XH, Wang GD. Study on the grain refinement mechanism of low carbon microalloyed steels for pipeline alllicatios. Trans Mater Heat Treat. 2006;27(6):99. Zhang HM, Wang HB, Liu ZY, Liu XH, Wang GD. Study on the grain refinement mechanism of low carbon microalloyed steels for pipeline alllicatios. Trans Mater Heat Treat. 2006;27(6):99.
[4]
Zurück zum Zitat Chen YH, Wang Y. Effect of second thermal cycle on the microstructure of the coarse grain heat-affected zone of in-service welded pipeline steel. J Univ Sci Technol B. 2008;30(9):1002. Chen YH, Wang Y. Effect of second thermal cycle on the microstructure of the coarse grain heat-affected zone of in-service welded pipeline steel. J Univ Sci Technol B. 2008;30(9):1002.
[5]
Zurück zum Zitat Xue XH, Zhou Y, Qian BN, Li JL, Lou SN. Coarse grain heat affect zone microstructures and toughness of X80 pipeline steel. J Shanghai Jiaotong Univ. 2003;37(12):1854. Xue XH, Zhou Y, Qian BN, Li JL, Lou SN. Coarse grain heat affect zone microstructures and toughness of X80 pipeline steel. J Shanghai Jiaotong Univ. 2003;37(12):1854.
[6]
Zurück zum Zitat Chen XW, Tian P, Wen K, Li ZH, Xiao FR, Wang X, Liao B. Study on microstructure and toughness of heat-affected zone of X70 pipeline steel. Met Hotworking Technol. 2007;36(11):6. Chen XW, Tian P, Wen K, Li ZH, Xiao FR, Wang X, Liao B. Study on microstructure and toughness of heat-affected zone of X70 pipeline steel. Met Hotworking Technol. 2007;36(11):6.
[7]
Zurück zum Zitat Chen XW, Xiao FR, Liao B, Wang X, Wang JM. Microstructure and performance forecast and welding process optimization model of HAZ of X70 pipeline steel. Met Hotworking Technol. 2007;36(3):10. Chen XW, Xiao FR, Liao B, Wang X, Wang JM. Microstructure and performance forecast and welding process optimization model of HAZ of X70 pipeline steel. Met Hotworking Technol. 2007;36(3):10.
[8]
Zurück zum Zitat Jia KN, Wang HD, Wang H. Thermal simulating the microstructure in weld heat affected zone of calcium microalloyed C-Mn steel and its effect on toughness. Heat Treat Met. 2008;33(2):24. Jia KN, Wang HD, Wang H. Thermal simulating the microstructure in weld heat affected zone of calcium microalloyed C-Mn steel and its effect on toughness. Heat Treat Met. 2008;33(2):24.
[9]
Zurück zum Zitat Xu XL, Xin XX, Shi K, Zhou Y. Influence of welding thermal cycle on toughness and microstructure in grain-coarsening region of X80 pipeline steel. Trans China Weld Inst. 2005;26(8):69. Xu XL, Xin XX, Shi K, Zhou Y. Influence of welding thermal cycle on toughness and microstructure in grain-coarsening region of X80 pipeline steel. Trans China Weld Inst. 2005;26(8):69.
[10]
Zurück zum Zitat Moon J, Lee C. Behavior of (Ti, Nb)(C, N) complex particle during thermomechanical cycling in the weld CGHAZ of a microalloyed steel. Acta Mater. 2009;57(7):2311.CrossRef Moon J, Lee C. Behavior of (Ti, Nb)(C, N) complex particle during thermomechanical cycling in the weld CGHAZ of a microalloyed steel. Acta Mater. 2009;57(7):2311.CrossRef
[11]
Zurück zum Zitat Zhao MC, Yang K, Xiao FR, Shan YY. Continuous cooling transformation of undeformed and deformed low carbon pipeline steels. Mater Sci Eng. 2003;A355(1–2):126.CrossRef Zhao MC, Yang K, Xiao FR, Shan YY. Continuous cooling transformation of undeformed and deformed low carbon pipeline steels. Mater Sci Eng. 2003;A355(1–2):126.CrossRef
[12]
Zurück zum Zitat Wang Y, Han T, Liu M. Local brittleness of weld heat-affected zone of X70 pipeline steel. J Mater Eng. 1999;44(10):14. Wang Y, Han T, Liu M. Local brittleness of weld heat-affected zone of X70 pipeline steel. J Mater Eng. 1999;44(10):14.
[13]
Zurück zum Zitat Zhou X, Liu SH, Duan YW, Wang B. Effect of t 8/5 on the coarse grain zone of HAZ properties for X70 pipeline steel. Welded Pipe Tube. 2008;31(6):22. Zhou X, Liu SH, Duan YW, Wang B. Effect of t 8/5 on the coarse grain zone of HAZ properties for X70 pipeline steel. Welded Pipe Tube. 2008;31(6):22.
[14]
Zurück zum Zitat Cai XJ, Lin ZY, Meng XQ, Jiang JJ, Liu F, Feng SL. Experiment on the toughness of weld joint of X70 pipeline steel. Res Explor Lab. 2013;32(8):33. Cai XJ, Lin ZY, Meng XQ, Jiang JJ, Liu F, Feng SL. Experiment on the toughness of weld joint of X70 pipeline steel. Res Explor Lab. 2013;32(8):33.
[15]
Zurück zum Zitat Wang CM, Wu XF, Liu J, Xu NA. Precipitates in X70 pipeline steel. J Univ Sci Technol B. 2006;28(3):253. Wang CM, Wu XF, Liu J, Xu NA. Precipitates in X70 pipeline steel. J Univ Sci Technol B. 2006;28(3):253.
Metadaten
Titel
Microstructure transformation of X70 pipeline steel welding heat-affected zone
verfasst von
Hui Li
Jing-Long Liang
Yun-Li Feng
Dong-Xing Huo
Publikationsdatum
01.08.2014
Verlag
Nonferrous Metals Society of China
Erschienen in
Rare Metals / Ausgabe 4/2014
Print ISSN: 1001-0521
Elektronische ISSN: 1867-7185
DOI
https://doi.org/10.1007/s12598-014-0344-x

Weitere Artikel der Ausgabe 4/2014

Rare Metals 4/2014 Zur Ausgabe

    Marktübersichten

    Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen.