Nanoscale silica coating of porous stainless steel and its impact on water wettability

Zeitschrift:
Journal of Coatings Technology and Research
Autoren:
Chiemi Oka, Kimihide Odagiri, Hosei Nagano
Wichtige Hinweise

Electronic supplementary material

The online version of this article (https://​doi.​org/​10.​1007/​s11998-020-00417-1) contains supplementary material, which is available to authorized users.

Publisher's Note

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Abstract

The water wettability of porous stainless steel specimens was enhanced via a nanoscaled silica coating for application to passive two-phase heat transfer devices. A combination of porous stainless steel and water has attracted attention in the area of the heat transfer devices. However, the water wettability of stainless steel is poor, limiting the performance of the devices. In the present study, the silica coating of the specimens was conducted via a reaction of tetraethyl orthosilicate (TEOS) after pretreatment using NaOH aq. or HCl aq. Energy-dispersive X-ray spectrometry revealed that the amount of silica deposited on the surface was dependent on the pretreatment conditions and the composition of the silica-coating solutions. Measurement of porous properties indicated that the silica coating did not affect pore diameter and gas permeability since the coating was in nanoscale. Microscale contact angles were directly evaluated using an environmental SEM. The specimens showed excellent water wettability when they were covered with numerous tiny silica bumps. When the specimen was pretreated with 2 M NaOH aq. and coated in weak alkaline TEOS solution, the contact angle of the porous stainless steel decreased from 87° to 54° after silica coating. The excellent water wettability originated from the relatively smooth surface and a sufficient coverage ratio, which resulted from the moderate strength of chemical etching of the NaOH aq. and the mild silica-coating condition in the weak alkaline solution.

Bitte loggen Sie sich ein, um Zugang zu diesem Inhalt zu erhalten

Sie möchten Zugang zu diesem Inhalt erhalten? Dann informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 69.000 Bücher
  • über 500 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Umwelt
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Testen Sie jetzt 30 Tage kostenlos.

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 50.000 Bücher
  • über 380 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Umwelt
  • Maschinenbau + Werkstoffe




Testen Sie jetzt 30 Tage kostenlos.

Zusatzmaterial
Nur für berechtigte Nutzer zugänglich
Literatur
Über diesen Artikel

Premium Partner

    Marktübersichten

    Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen. 

    Bildnachweise