On Characterizing a Composite Microstructure in 316LN Stainless Steel Weld Metal and a New Damage Micromechanism During Creep

The austenitic stainless steel weld metal fabricated by multipass welding exhibits a composite microstructure. Microstructural characterization of the weld metal revealed that there are two distinct regions on either side of the weld-pass interface. The variations in dislocation substructure and delta ferrite morphology are the two microstructural attributes which delineate these regions. The generation of subsequent thermal cycles during the fabrication of multipass weld joint is the paramount factor influencing the formation of the composite microstructure. During creep exposure, the extent of creep cavitation and propagation varies substantially in these two regions due to differences in their microstructures. This results in preferential damage during creep exposure of austenitic stainless steel weld metal.