One-pot synthesis of mixed-valence MoO_x on carbon nanotube as an anode material for lithium ion batteries

verfasst von: Jong-Pil Jegal, Hyun-Kyung Kim, Jeom-Soo Kim, Kwang-Bum Kim

Erschienen in: Journal of Electroceramics | Ausgabe 1-2/2013

Einloggen

Aktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.

search-config

KI-gestützte Suche

Aus

Abstract

A mixed-valence MoO_x/carbon nanotube nanocomposite was synthesized using a one-pot microwave-assisted hydrothermal reaction in which 5 nm MoO_x nanoparticles were coated on the surfaces of carbon nanotube. The MoO_x nanoparticles in the nanocomposite had mixed Mo⁴⁺ and Mo⁶⁺ valence states. Thus, the nanocomposite showed a discharge behavior corresponding to both MoO₂ and MoO₃. The nanocomposite had a reversible discharge capacity of 900 mAh g⁻¹ at a current density of 90 mA g⁻¹, and could deliver discharge capacities of 770, 700, and 570 mAh g⁻¹ at current densities of 450, 900, and 1800 mA g⁻¹, respectively.

Vorheriger Artikel Structure and electrochemical performance of LiFexNi1-xO2 (0.00 ≤ x ≤ 0.20) cathode materials for rechargeable lithium-ion batteries

Nächster Artikel Catalytic activity of carbon-sphere/Co3O4/RuO2 nanocomposite for Li-air batteries

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

über 102.000 Bücher
über 537 Zeitschriften

aus folgenden Fachgebieten:

Automobil + Motoren
Bauwesen + Immobilien
Business IT + Informatik
Elektrotechnik + Elektronik
Energie + Nachhaltigkeit
Finance + Banking
Management + Führung
Marketing + Vertrieb
Maschinenbau + Werkstoffe
Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Jetzt informieren

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

über 67.000 Bücher
über 390 Zeitschriften

aus folgenden Fachgebieten:

Automobil + Motoren
Bauwesen + Immobilien
Business IT + Informatik
Elektrotechnik + Elektronik
Energie + Nachhaltigkeit
Maschinenbau + Werkstoffe

Jetzt Wissensvorsprung sichern!

Jetzt informieren

J.-M. Tarascon, M. Armand, Nature 414, 359–367 (2001). doi:10.1038/35104644 CrossRef

A.A. Arie, W.Y. Chang, J.K. Lee, J. Electroceram. 24, 308–312 (2010). doi:10.1007/s10832-009-9573-z CrossRef

P. Poizot, S. Laruelle, S. Grugeon, L. Dupont, J.-M. Tarascon, Nature 407, 496–499 (2000). doi:10.1038/35035045 CrossRef

W.Y. Li, L.N. Xu, J. Chen, Adv. Funct. Mater. 15, 851–857 (2005). doi:10.1002/adfm.200400429 CrossRef

M.V. Reddy, T. Yu, C.H. Sow, Z.X. Shen, C.T. Lim, G.V.S. Rao, B.V.R. Chowdari, Adv. Funct. Mater. 17, 2792–2799 (2007). doi:10.1002/adfm.200601186 CrossRef

C.M. Ban, Z.C. Wu, D.T. Gillaspie, L. Chen, Y.F. Yan, J.L. Blackburn, A.C. Dillon, Adv. Mater. 22, E145–E149 (2010). doi:10.1002/adma.200904285 CrossRef

H.L. Wang, L.F. Cui, Y. Yang, H.S. Casalongue, J.T. Robinson, Y.Y. Liang, Y. Cui, H.J. Dai, J. Am, Chem. Soc. 132, 13978–13980 (2010). doi:10.1021/ja105296a CrossRef

S.H. Lee, Y.H. Kim, R. Deshpande, P.A. Parilla, E. Whitney, D.T. Gillaspie, K.M. Jones, A.H. Mahan, S.B. Zhang, A.C. Dillon, Adv. Mater. 20, 3627–3632 (2008). doi:10.1002/adma.200800999 CrossRef

L.A. Riley, S.H. Lee, L. Gedvilias, A.C. Dillon, J. Power Sources 195, 588–592 (2010). doi:10.1016/j.jpowsour.2009.08.013 CrossRef

10.

Y.S. Jung, S.K. Lee, D.J. Ahn, A.C. Dillon, S.H. Lee, J. Power Sources 188, 286–291 (2009). doi:10.1016/j.jpowsour.2008.11.125 CrossRef

11.

Y.F. Shi, B.K. Guo, S.A. Corr, Q.H. Shi, Y.S. Hu, K.R. Heier, L.Q. Chen, R. Seshadri, G.D. Stucky, Nano Lett. 9, 4215–4220 (2009). doi:10.1021/nl902423a CrossRef

12.

L.C. Yang, Q.S. Gao, Y. Tang, Y.P. Wua, R. Holze, J. Power Sources 179, 357–360 (2008). doi:10.1016/j.jpowsour.2007.12.099 CrossRef

13.

J.H. Ku, Y.S. Jung, K.T. Lee, C.H. Kim, S.M. Oh, J. Electrochem, Soc. 156, A688–A693 (2009). doi:10.1149/1.3141670

14.

L. Zhou, H.B. Wu, Z.Y. Wang, X.W. Lou, ACS Appl. Mater. Interfaces 3, 4853–4857 (2011). doi:10.1021/am201351z CrossRef

15.

S. Hu, X. Wang, J. Am, Chem. Soc. 130, 8126–8127 (2008). doi:10.1021/ja801448c CrossRef

16.

Z.Y. Wang, S. Madhavi, X.W. Lou, J. Phys, Chem. C 116, 12508–12513 (2012). doi:10.1021/jp304216z

17.

L.C. Yang, L.L. Liu, Y.S. Zhu, X.J. Wang, Y.P. Wu, J. Mater, Chem. 22, 13148–13152 (2012). doi:10.1039/c2jm31364b

18.

L.C. Yang, Q.S. Gao, Y.H. Zhang, Y. Tang, Y.P. Wu, Electrochem. Commun. 10, 118–122 (2008). doi:10.1016/j.elecom.2007.11.009 CrossRef

19.

Z.Y. Wang, D. Luan, S. Madhavi, Y. Hu, X.W. Lou, Energy Environ. Sci. 5, 5252–5256 (2012). doi:10.1039/c1ee02831f CrossRef

20.

Z.S. Wu, W.C. Ren, L. Wen, L.B. Gao, J.P. Zhao, Z.P. Chen, G.M. Zhou, F. Li, H.M. Cheng, ACS Nano 4, 3187–3194 (2010). doi:10.1021/nn100740x CrossRef

21.

G.M. Zhou, D.W. Wang, F. Li, L.L. Zhang, N. Li, Z.S. Wu, L. Wen, G.Q. Lu, H.M. Cheng, Chem. Mater. 22, 5306–5313 (2010). doi:10.1021/cm101532x CrossRef

22.

Y.M. Sun, X.L. Hu, W. Luo, Y.H. Huang, ACS Nano 5, 7100–7107 (2011). doi:10.1021/nn201802c CrossRef

23.

K.H. Seng, G.D. Du, L. Li, Z.X. Chen, H.K. Liu, Z.P. Guo, J. Mater, Chem. 22, 16072–16077 (2012). doi:10.1039/c2jm32822d

24.

S.B. Ma, K.W. Nam, W.S. Yoon, S.M. Bak, X.Q. Yang, B.W. Cho, K.B. Kim, Electrochem. Commun. 11, 1575–1578 (2009). doi:10.1016/j.elecom.2009.05.058 CrossRef

25.

B. Ellis, W.H. Kan, W.R.M. Makahnouk, L.F. Nazar, J. Mater, Chem. 17, 3248–3254 (2007). doi:10.1039/b705443m

26.

J.R. Dahn, W.R. McKinnon, Solid State Ionics 23, 1–7 (1987). doi:10.1016/0167-2738(87)90074-9 CrossRef

27.

B.K. Guo, X.P. Fang, B. Li, Y.F. Shi, C.Y. Ouying, Y.S. Hu, Z.X. Wang, G.D. Stucky, L.Q. Chen, Chem. Mater. 24, 457–463 (2012). doi:10.1021/cm202459r CrossRef

28.

S.H. Ng, J. Wang, Z.P. Guo, J. Chen, G.X. Wang, H.K. Liu, Electrochim. Acta 51, 23–28 (2005). doi:10.1016/j.electacta.2005.04.045 CrossRef

Titel: One-pot synthesis of mixed-valence MoO x on carbon nanotube as an anode material for lithium ion batteries
verfasst von: Jong-Pil Jegal
Hyun-Kyung Kim
Jeom-Soo Kim
Kwang-Bum Kim
Publikationsdatum: 01.10.2013
Verlag: Springer US
Erschienen in: Journal of Electroceramics / Ausgabe 1-2/2013
Print ISSN: 1385-3449
Elektronische ISSN: 1573-8663
DOI: https://doi.org/10.1007/s10832-013-9821-0

Neuer Inhalt

Bildnachweise

VDI-Icon, Profil Icon, inhalt2, Springer Professional Modul/© Springer Fachmedien Wiesbaden GmbH, Nachhaltigkeitsaward Key Visual/© Cometis AG/Global ESG Monitor | Daniel Rupp | Generiert mit KI, Search Icon, Banner Hanser, Frank Urbansky/© Peter Eichler / Leipzig, CO2-Fußabdruck/© Jenny Sturm / stock.adobe.com, Interview Entropie Bild 1/© Bernhard Weßling, Zeitschrift Wissensmanagement Cover, PatentFit-Logo/© Springer Fachmedien Wiesbaden GmbH, Sustainibility Finance/© Robert Kneschke / stock.adobe.com / Springer Fachmedien Wiesbaden GmbH, Zukunftswerkstatt Sales Excellence 2024/© AndreyPopov / Getty Images / iStock, 2023_Antrieb/© supervisuell

Springer Professional

Abstract

Bitte loggen Sie sich ein, um Zugang zu Ihrer Lizenz zu erhalten.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Springer Professional "Technik"

Weitere Artikel der Ausgabe 1-2/2013

Characteristics of silver powders synthesized from silver 2-ethylhexanoate and Di-n-octylamine

Application of GDC-YDB bilayer and LSM-YDB cathode for intermediate temperature solid oxide fuel cells

Sintering and varistor behaviour of SnO2-Zn2SnO4 composite ceramics

Effect of sintering temperature on microstructure and piezoelectric properties of Pb-free BiFeO3–BaTiO3 ceramics in the composition range of large BiFeO3 concentrations

Determination of optical band gap of ZnO:ZnAl2O4 composite semiconductor nanopowder materials by optical reflectance method

Fabrication and electrical characterization of solution-processed all-oxide transparent NiO/TiO2 p-n junction diode by sol–gel spin coating method

Neuer Inhalt

Bitte loggen Sie sich ein, um Zugang zu Ihrer Lizenz zu erhalten.

Bitte loggen Sie sich ein, um Zugang zu Ihrer Lizenz zu erhalten.