Erschienen in: Journal of Materials Science: Materials in Electronics 7/2016

07.03.2016

Optimization of CdSe layer on modified ZnO hierarchical spheres by spin-SILAR for efficient CdS/CdSe co-sensitized solar cells

verfasst von: Yibing Lin, Yu Lin, Jihuai Wu, Xiaolong Zhang, Biaopeng Fang

Erschienen in: Journal of Materials Science: Materials in Electronics | Ausgabe 7/2016

Einloggen, um Zugang zu erhalten
share
TEILEN

Abstract

In this study, after CdS quantum dots sensitized ZnO hierarchical spheres (ZnO HS), we used a simple process to deposit CdSe QDs on ZnO by spin-coating-based SILAR, and applied to photoanodes of quantum dots-sensitized solar cells. Before CdS and CdSe QDs deposition, the ZnO HS photoanodes were modified by Zn(CH3COO)2·2H2O methanol solution to further enhance the open-circuit voltage and power conversion efficiency (PCE). The program of modifying photoanodes and the number of CdSe spin-SILAR cycles are evaluated on the optical and electrochemical properties of the cells. As a result, a high energy conversion efficiency of 2.49 % was obtained by using modified ZnO HS/CdS photoanode under AM 1.5 illumination of 100 mW cm−2. And further decorated by the CdSe QDs, the ZnO HS/CdS/CdSe cell achieved a PCE of 5.36 % due to the modification of ZnO HS nanostructure, the enhanced absorption in the visible region, the lower recombination reaction and higher electron lifetime.

Sie möchten Zugang zu diesem Inhalt erhalten? Dann informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 69.000 Bücher
  • über 500 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Testen Sie jetzt 15 Tage kostenlos.

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 50.000 Bücher
  • über 380 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




Testen Sie jetzt 15 Tage kostenlos.

Springer Professional "Wirtschaft"

Online-Abonnement

Mit Springer Professional "Wirtschaft" erhalten Sie Zugriff auf:

  • über 58.000 Bücher
  • über 300 Zeitschriften

aus folgenden Fachgebieten:

  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Versicherung + Risiko




Testen Sie jetzt 15 Tage kostenlos.

Literatur
1.
Zurück zum Zitat A. Kongkanand, K. Tvrdy, K. Takechi, M. Kuno, P.V. Kamat, Quantum dot solar cells. J. Am. Chem. Soc. 130, 4007 (2008) CrossRef A. Kongkanand, K. Tvrdy, K. Takechi, M. Kuno, P.V. Kamat, Quantum dot solar cells. J. Am. Chem. Soc. 130, 4007 (2008) CrossRef
2.
Zurück zum Zitat J. Xu, X. Yang, H.K. Wang, X. Chen, C.Y. Luan, Z.X. Xu, Z.Z. Lu, V.A. Roy, W.J. Zhang, C.S. Lee, Nano Lett. 11, 4138 (2011) CrossRef J. Xu, X. Yang, H.K. Wang, X. Chen, C.Y. Luan, Z.X. Xu, Z.Z. Lu, V.A. Roy, W.J. Zhang, C.S. Lee, Nano Lett. 11, 4138 (2011) CrossRef
3.
Zurück zum Zitat B. O’Regan, M. Grätzel, Nature 353, 373 (1991) B. O’Regan, M. Grätzel, Nature 353, 373 (1991)
6.
Zurück zum Zitat S. Rühle, M. Shalom, A. Zaban, Chem. Phys. Chem. 11, 2290 (2010) S. Rühle, M. Shalom, A. Zaban, Chem. Phys. Chem. 11, 2290 (2010)
7.
Zurück zum Zitat V. Gonzalez-Pedro, X. Xu, I. Mora-Sero, J. Bisquert, ACS Nano 4, 5783 (2010) CrossRef V. Gonzalez-Pedro, X. Xu, I. Mora-Sero, J. Bisquert, ACS Nano 4, 5783 (2010) CrossRef
8.
9.
Zurück zum Zitat A. Ranjitha, N. Muthukumarasamy, M. Thambidurai, J. Mater. Sci. Mater. Electron. 24, 3014 (2013) CrossRef A. Ranjitha, N. Muthukumarasamy, M. Thambidurai, J. Mater. Sci. Mater. Electron. 24, 3014 (2013) CrossRef
10.
Zurück zum Zitat Y. Xiong, F. Deng, L. Wang, Y.S. Liu, J. Mater. Sci. Mater. Electron. 25, 3039 (2014) CrossRef Y. Xiong, F. Deng, L. Wang, Y.S. Liu, J. Mater. Sci. Mater. Electron. 25, 3039 (2014) CrossRef
11.
Zurück zum Zitat P. Yu, K. Zhu, A.G. Norman, S. Ferrere, A.J. Frank, A.J. Nozik, J. Phys. Chem. B 110, 25451 (2006) CrossRef P. Yu, K. Zhu, A.G. Norman, S. Ferrere, A.J. Frank, A.J. Nozik, J. Phys. Chem. B 110, 25451 (2006) CrossRef
12.
Zurück zum Zitat L. Meng, F. Zhao, J. Zhang, R. Luo, A. Chen, L. Sun, S. Bai, G. Tang, Y. Lin, J. Alloys Compd. 595, 51 (2014) CrossRef L. Meng, F. Zhao, J. Zhang, R. Luo, A. Chen, L. Sun, S. Bai, G. Tang, Y. Lin, J. Alloys Compd. 595, 51 (2014) CrossRef
13.
Zurück zum Zitat N. Guijarro, T. Lana-Villarreal, T. Lutz, S.A. Haque, R. Gómez, J. Phys. Chem. Lett. 3, 3367 (2012) CrossRef N. Guijarro, T. Lana-Villarreal, T. Lutz, S.A. Haque, R. Gómez, J. Phys. Chem. Lett. 3, 3367 (2012) CrossRef
14.
Zurück zum Zitat X. Hu, Q. Zhang, X. Huang, D. Li, Y. Luo, Q. Meng, J. Mater. Chem. 21, 15903 (2011) CrossRef X. Hu, Q. Zhang, X. Huang, D. Li, Y. Luo, Q. Meng, J. Mater. Chem. 21, 15903 (2011) CrossRef
15.
Zurück zum Zitat C. JustinRaj, S.N. Karthick, S. Park, K.V. Hemalatha, S.-K. Kim, K. Prabakar, H.J. Kim, J. Power Sources 248, 439 (2014) CrossRef C. JustinRaj, S.N. Karthick, S. Park, K.V. Hemalatha, S.-K. Kim, K. Prabakar, H.J. Kim, J. Power Sources 248, 439 (2014) CrossRef
16.
Zurück zum Zitat D. Panda, T.Y. Tseng, J. Mater. Sci. 20, 6849 (2003) D. Panda, T.Y. Tseng, J. Mater. Sci. 20, 6849 (2003)
17.
Zurück zum Zitat J. Chen, J. Wu, W. Lei, J.L. Song, W.Q. Deng, X.W. Sun, Appl. Surf. Sci. 256, 7438 (2010) CrossRef J. Chen, J. Wu, W. Lei, J.L. Song, W.Q. Deng, X.W. Sun, Appl. Surf. Sci. 256, 7438 (2010) CrossRef
18.
Zurück zum Zitat Z. Zhu, J. Qiu, K. Yan, S. Yang, ACS Appl. Mater. Interfaces 5, 4000 (2013) Z. Zhu, J. Qiu, K. Yan, S. Yang, ACS Appl. Mater. Interfaces 5, 4000 (2013)
19.
Zurück zum Zitat Y.B. Lin, Y. Lin, Y.M. Meng, Y.G. Tu, X.L. Zhang, Opt. Commun. 346, 64 (2015) CrossRef Y.B. Lin, Y. Lin, Y.M. Meng, Y.G. Tu, X.L. Zhang, Opt. Commun. 346, 64 (2015) CrossRef
20.
Zurück zum Zitat G. Zhu, L. Pan, T. Xu, Z. Sun, A.C.S. Appl, Mater. Interfaces. 3, 3146 (2011) CrossRef G. Zhu, L. Pan, T. Xu, Z. Sun, A.C.S. Appl, Mater. Interfaces. 3, 3146 (2011) CrossRef
21.
Zurück zum Zitat X.Y. Yu, J.Y. Liao, K.Q. Qiu, D.B. Kuang, C.Y. Su, ACS Nano 5, 9494 (2011) CrossRef X.Y. Yu, J.Y. Liao, K.Q. Qiu, D.B. Kuang, C.Y. Su, ACS Nano 5, 9494 (2011) CrossRef
22.
Zurück zum Zitat Q. Zhang, Y. Zhang, S. Huang, X. Huang, Y. Luo, Q. Meng, D. Li, Electrochem. Commun. 12, 327 (2010) CrossRef Q. Zhang, Y. Zhang, S. Huang, X. Huang, Y. Luo, Q. Meng, D. Li, Electrochem. Commun. 12, 327 (2010) CrossRef
23.
Zurück zum Zitat J.Y. Joo, D. Kim, D.J. Yun, H.C. Jun, S.W. Rhee, J.S. Lee, K.J. Yong, S.J. Kim, S.M. Jeon, Nanotechnology 21, 325604 (2010) CrossRef J.Y. Joo, D. Kim, D.J. Yun, H.C. Jun, S.W. Rhee, J.S. Lee, K.J. Yong, S.J. Kim, S.M. Jeon, Nanotechnology 21, 325604 (2010) CrossRef
24.
Zurück zum Zitat R. Zhang, Q.-P. Luo, H.-Y. Chen, X.-Y. Yu, D.-B. Kuang, C.-Y. Su, Chem. Phys. Chem. 13, 1435 (2012) R. Zhang, Q.-P. Luo, H.-Y. Chen, X.-Y. Yu, D.-B. Kuang, C.-Y. Su, Chem. Phys. Chem. 13, 1435 (2012)
25.
Zurück zum Zitat Y.B. Lin, Y. Lin, J.H. Wu, Y.G. Tu, X.L. Zhang, B.P. Fang, Ceram. Int. 41, 14501 (2015) CrossRef Y.B. Lin, Y. Lin, J.H. Wu, Y.G. Tu, X.L. Zhang, B.P. Fang, Ceram. Int. 41, 14501 (2015) CrossRef
26.
Zurück zum Zitat S. Hao, J. Wu, L. Fan, Y. Huang, J. Lin, Y. Wei, Sol. Energy 76, 745 (2004) CrossRef S. Hao, J. Wu, L. Fan, Y. Huang, J. Lin, Y. Wei, Sol. Energy 76, 745 (2004) CrossRef
27.
Zurück zum Zitat W.T. Jiang, C.T. Wu, Y.H. Sung, J.J. Wu, A.C.S. Apll, Mater. Interfaces 5, 911 (2013) CrossRef W.T. Jiang, C.T. Wu, Y.H. Sung, J.J. Wu, A.C.S. Apll, Mater. Interfaces 5, 911 (2013) CrossRef
28.
30.
Zurück zum Zitat R. Gao, Z. Liang, J. Tian, Q. Zhang, L. Wang, G. Cao, Nano Energy 2, 40 (2013) CrossRef R. Gao, Z. Liang, J. Tian, Q. Zhang, L. Wang, G. Cao, Nano Energy 2, 40 (2013) CrossRef
31.
Zurück zum Zitat G. Shang, J. Wu, S. Tang, L. Liu, X. Zhang, J. Phys. Chem. C 117, 4345 (2013) CrossRef G. Shang, J. Wu, S. Tang, L. Liu, X. Zhang, J. Phys. Chem. C 117, 4345 (2013) CrossRef
32.
33.
Zurück zum Zitat E.M. Kaidashev, M. Lorenz, H. Von Wenckstern, A. Rahm, H.C. Semmelhack, K.H. Han, G. Benndorf, C. Bundesmann, H. Hochmuth, M. Grundmann, Appl. Phys. Lett. 82, 3901 (2003) CrossRef E.M. Kaidashev, M. Lorenz, H. Von Wenckstern, A. Rahm, H.C. Semmelhack, K.H. Han, G. Benndorf, C. Bundesmann, H. Hochmuth, M. Grundmann, Appl. Phys. Lett. 82, 3901 (2003) CrossRef
Metadaten
Titel
Optimization of CdSe layer on modified ZnO hierarchical spheres by spin-SILAR for efficient CdS/CdSe co-sensitized solar cells
verfasst von
Yibing Lin
Yu Lin
Jihuai Wu
Xiaolong Zhang
Biaopeng Fang
Publikationsdatum
07.03.2016
Verlag
Springer US
Erschienen in
Journal of Materials Science: Materials in Electronics / Ausgabe 7/2016
Print ISSN: 0957-4522
Elektronische ISSN: 1573-482X
DOI
https://doi.org/10.1007/s10854-016-4612-4