Optimization of Mold Flux for the Continuous Casting of Cr-Contained Steels

To compensate the negative effect caused by the absorption of chromium oxide inclusions during the casting process of Cr-contained steels, a new mold flux system has been designed and investigated. The melting temperature range of the newly designed mold flux system is from [1124 K to 1395 K (851 °C to 1122 °C)]. The viscosity at 1573 K (1300 °C) and the break temperature increase with the addition of MnO and Cr₂O₃ but decrease with the addition of B₂O₃. The crystalline fraction of mold flux decreases from 81 to 42.1 pct with the addition of MnO and Cr₂O₃, and then further decreases to 25.3 pct with the addition of B₂O₃; however, it improves from 54.4 to 81.5 pct when the basicity increases. Besides, the heat-transfer ability of mold flux is inverse to the crystallization ratio of the slag. The comprehensive study of the properties for the four designed mold fluxes suggests that the mold flux with 1.15 basicity-3.01 pct B₂O₃-1.10 pct MnO-2.10 pct Cr₂O₃ shows the best properties for the continuous casting of Cr-contained steels.