Oxidation and SCC Initiation Studies of Type 304L SS in PWR Primary Water
Aktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.
Wählen Sie Textabschnitte aus um mit Künstlicher Intelligenz passenden Patente zu finden. powered by
Markieren Sie Textabschnitte, um KI-gestützt weitere passende Inhalte zu finden. powered by
Slow strain rate tensile (SSRT) tests Slow Strain Rate Test (SSRT)were conducted on conventional and tapered samples manufactured from forged Type 304L stainless steel304L Stainless steel to assess the stress corrosion cracking (SCC) Stress Corrosion Cracking (SCC) initiationbehaviour in simulated PWR primary water. Several testing and microstructural parameters were investigated in order to explore the conditions under which crack initiation might occur. Surface preparation appeared to play a very important role on SCC initiation whereby the machined surfaces were the least susceptible to SCC initiation whilst oxide polishing suspension (OPS) polished surfaces were more susceptible. On the machined surfaces the cracks were always transgranular (TG) in nature and associated with the machining marks. Conversely, on fine polished surfaces with oxide polishing suspension the crack morphology was mainly intergranular in nature, although minor transgranular cracking was observed. The regions in the proximity of the δ-ferrite/austenite interface were shown to be very susceptible to SCC initiation especially on the OPS polished surfaces and this was attributed to the strain localization upon dynamic deformation. Furthermore, intragranular inclusions appeared to dissolve and act as initiation sites for transgranular cracking to occur. The roles of strain rate, dynamic deformation and microstructure on the initiation of SCC are also discussed.