Oxidation Behavior of Molten Cu-Be Binary and Cu-Be-X (X = Ca or Zr) Ternary Alloys at 1423 K (1150 °C) Under Controlled Oxygen Partial Pressure

verfasst von: Mitsuru Tanahashi, Jutaro Miura, Takaharu Iwadachi, Keigo Nojiri, Toshiharu Fujisawa, Chikabumi Yamauchi

Erschienen in: Metallurgical and Materials Transactions B | Ausgabe 1/2017

Einloggen

Aktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.

search-config

KI-gestützte Suche

Aus

Abstract

The oxidation behavior of molten Cu-Be binary and Cu-Be-X (Ca or Zr) ternary alloys was investigated by exposing these molten alloy systems to various Ar-O₂ atmospheres to control the oxygen partial pressure from 10 to 10⁵ Pa at 1423 K (1150 °C). The experimental results clarified that the oxygen partial pressure in gas phase affects the morphology of the oxide formed on the surface of the alloy and the oxidation rate of beryllium. At lower oxygen partial pressure, a molten Cu-Be alloy is covered with a homogeneous and compact internal layer of BeO, which leads to a minimization of the beryllium oxidation rate. By adding a small amount of calcium or zirconium into the molten Cu-0.5 mass pct Be alloy, a protective BeO layer is formed even at higher oxygen partial pressure, resulting in achievement of a significant reduction in the beryllium oxidation rate.

Vorheriger Artikel Relationship Between Sulfide Capacity and Structure of MnO-SiO2-Al2O3-Ce2O3 System

Nächster Artikel Evolution of Inclusions in Fe-13Cr Treated by CaO-SiO2-Al2O3-Based Top Slag

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

über 102.000 Bücher
über 537 Zeitschriften

aus folgenden Fachgebieten:

Automobil + Motoren
Bauwesen + Immobilien
Business IT + Informatik
Elektrotechnik + Elektronik
Energie + Nachhaltigkeit
Finance + Banking
Management + Führung
Marketing + Vertrieb
Maschinenbau + Werkstoffe
Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Jetzt informieren

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

über 67.000 Bücher
über 390 Zeitschriften

aus folgenden Fachgebieten:

Automobil + Motoren
Bauwesen + Immobilien
Business IT + Informatik
Elektrotechnik + Elektronik
Energie + Nachhaltigkeit
Maschinenbau + Werkstoffe

Jetzt Wissensvorsprung sichern!

Jetzt informieren

In the case of pure beryllium oxidation at 1423 K (1150 °C), it can be estimated from its Ellingham line plotted in Figure 1 that beryllium is oxidized to form solid BeO at an oxygen partial pressure higher than 3.65 × 10⁻³⁰ Pa.

The normalized oxygen partial pressures, \( p_{{{\text{O}}_{2} }} \) and \( p^{\prime}_{{{\text{O}}_{2} }} \), are defined, respectively, as \( p_{{{\text{O}}_{2} }} \equiv P_{{{\text{O}}_{2} }} /P^{ \circ } \) and \( p^{\prime}_{{{\text{O}}_{2} }} \equiv P^{\prime}_{{{\text{O}}_{2} }} /P^{ \circ } \), where \( P^{ \circ } \) is the standard state pressure (SSP) defined to be 101325 Pa; \( P_{{{\text{O}}_{2} }} \) and \( P^{\prime}_{{{\text{O}}_{2} }} \) are, respectively, the oxygen partial pressures in the gas phase and at the interface between metal and M_1+δO-type oxide (in Pa).

Similarly to \( p_{{{\text{O}}_{2} }} \) and \( p^{\prime}_{{{\text{O}}_{2} }} \), \( p^{\prime\prime}_{{{\text{O}}_{2} }} \) is the normalized oxygen partial pressure defined as \( p^{\prime\prime}_{{{\text{O}}_{2} }} \equiv P^{\prime\prime}_{{{\text{O}}_{2} }} /P^{ \circ } \), where \( P^{\prime\prime}_{{{\text{O}}_{2} }} \) is the oxygen partial pressures at the interface between metal and M_1−δO-type oxide (in Pa).

1. I. Barin: Thermochemical Data of Pure Substances, 2nd ed., VCH Verlagsgesellschaft mbH., Weinheim, 1993.

2. M. Tanahashi, T. Inoue, J. Okamoto, G. R. Alvear, T. Iwadachi, T. Fujisawa, and C. Yamauchi: J. Min. Mater. Inst. Jpn., 2001, vol. 117, pp. 967-74.

3. D. P. Whittle and J. Stringer: Philos. Trans. R. Soc. London, Ser. A, 1980, vol. 295, pp. 309-29.CrossRef

4. K. Ishii, M. Kohno, S. Ishikawa, and S. Satoh: Mater. Trans. JIM, 1997, vol. 38, pp. 787-92.CrossRef

5. Y. Kawai and K. Mori: Tetsu-to-Hagané, 1970, vol. 56, pp. 695-707.

T.B. Massalski, H. Okamoto, P.R. Subramanian, L. Kacprzak, eds.: Binary Alloy Phase Diagrams, 2nd ed., ASM International, Materials Park, OH, 1990, p. 1448.

N. Birks and G.H. Meier: Introduction to the High Temperature Oxidation of Metals, Edward Arnold (Publishers) Ltd, London, 1983, pp. 105–07.

8. S. Mrowec and A. Stokłosa: Oxid. Met., 1971, vol. 3, pp. 291-311.CrossRef

9. S. Mrowec, A. Stokłosa, and K. Godlewski: Cryst. Latt. Def., 1974, vol. 5, pp. 239-55.

10.

10. D. Cubicciotti: J. Am. Chem. Soc., 1950, vol. 72, pp. 2084-6CrossRef

11.

C. Wagner: Z. Phys. Chem., Abt. B, 1933, vol. 21, pp. 25–41.

12.

12. N. Birks, G. H. Meier, and F. S. Pettit: Introduction to the High-Temperature Oxidation of Metals, 2nd ed., Cambridge University Press, Cambridge, 2006, pp. 50-51.CrossRef

13.

13. W. J. Moore: Z. Elektrochem., 1959, vol. 63, pp. 794-99.

14.

14. N. Birks, G. H. Meier, and F. S. Pettit: Introduction to the High-Temperature Oxidation of Metals, 2nd ed., Cambridge University Press, Cambridge, 2006, pp. 55-62.CrossRef

15.

15. K. Przybylski, A. J. Garratt-Reed, B. A. Pint, E. P. Katz, and G. J. Yurek: J. Electrochem. Soc., 1987, vol. 134, pp. 3207-8.CrossRef

Titel: Oxidation Behavior of Molten Cu-Be Binary and Cu-Be-X (X = Ca or Zr) Ternary Alloys at 1423 K (1150 °C) Under Controlled Oxygen Partial Pressure
verfasst von: Mitsuru Tanahashi
Jutaro Miura
Takaharu Iwadachi
Keigo Nojiri
Toshiharu Fujisawa
Chikabumi Yamauchi
Publikationsdatum: 03.11.2016
Verlag: Springer US
Erschienen in: Metallurgical and Materials Transactions B / Ausgabe 1/2017
Print ISSN: 1073-5615
Elektronische ISSN: 1543-1916
DOI: https://doi.org/10.1007/s11663-016-0849-9

Premium Partner

Marktübersichten

Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen.

Zur Marktübersicht

Springer Professional

Abstract

Bitte loggen Sie sich ein, um Zugang zu Ihrer Lizenz zu erhalten.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Springer Professional "Technik"

Weitere Artikel der Ausgabe 1/2017

Analysis of Operational Parameters Affecting the Sulfur Content in Hot Metal of the COREX Process

The Dissolution Kinetics of MgO into CaO-MgO-Fe2O3 Slag

Relationship Between Liquid Fluidity of Iron Ore and Generated Liquid Content During Sintering

Numerical Investigation of the Inner Profiles of Ironmaking Blast Furnaces: Effect of Throat-to-Belly Diameter Ratio

Thermodynamics of Palladium (Pd) and Tantalum (Ta) Relevant to Secondary Copper Smelting

Refractory–Slag–Metal–Inclusion Multiphase Reactions Modeling Using Computational Thermodynamics: Kinetic Model for Prediction of Inclusion Evolution in Molten Steel

Premium Partner

Marktübersichten