Manuscript submitted January 13, 2013.
Oxide inclusions in high-Mn steel welds were analyzed and almost all of which were found to belong to the MnO-Al2O3-SiO2 system. In this study, the inclusions were categorized based on MnS morphology into the following two types: (1) aluminosilicate with a MnS patch, or (2) aluminosilicate with a MnS shell. The most frequently detected was type 1, the formation mechanism of which was investigated using commercially available thermochemical computing software, FactSage™ (ver. 6.3). The thermodynamic calculations predicted that galaxite (MnAl2O4), tephroite (Mn2SiO4), and MnS could precipitate during solidification. However, because of the fast cooling rate in welding processes, galaxite and tephroite phases were unable to fully crystallize, but rather were supercooled as glassy phases. In order to confirm the validity of the thermodynamic calculations, the composition of the observed inclusions was compared with the MnO-SiO2-Al2O3 ternary phase diagram, resulting in remarkably good agreement. Furthermore, it was found that the type of the oxide inclusions was dependent on their location (i.e., MnS shell- and MnS patch-type oxides were detected at the dendritic core and interdendritic boundary, respectively). Both types of oxides were occasionally found in one oxide, near the interdendritic boundary. This indicates that the morphology variation originates from the redistribution of solute due to fast solidification.
Bitte loggen Sie sich ein, um Zugang zu diesem Inhalt zu erhalten
Sie möchten Zugang zu diesem Inhalt erhalten? Dann informieren Sie sich jetzt über unsere Produkte:
H. Idrissi, K. Renard, L. Ryelandt, D. Schryvers and P.J. Jacques: Acta Mater., 2010, vol. 58, pp.2464–76. CrossRef
S. W. Hwanga, J. H. Ji and K.T. Park: Mater. Sci. Eng. A, 2011, vol. 528, pp. 7267–75. CrossRef
A. Dumaya, J.P. Chateau, S. Allain, S. Migot and O. Bouaziz: Mater. Sci. Eng. A, 2008, vol. 483-484, pp. 184-187. CrossRef
G. Liu, S. Scudino, R. Li, U. Kühn, J. Sun and J. Eckert: Mech. Mater., 2011, vol. 43, pp. 556–566. CrossRef
K. Sato: Ph.D. Thesis, University of California, Berkeley, 2002.
J. H. Park, D.J. Kim, and D. J. Min: Metall. Mater. Trans., 2012, vol. 43A, pp. 2316-24. CrossRef
M. Wakoh, T. Sawai, and Mizoguchi: ISIJ Int., 1996, vol. 36, pp. 1014–21.
K. Oikawa, H. Ohtani, K. Ishida and T. Nishizawa: ISIJ Int., 1995, vol. 35, pp. 402-408. CrossRef
J.M. Dowling, J.M. Corbett, and H.W. Kerr: Metall. Trans. A, 1986, vol. 17A, pp. 1611-23. CrossRef
T. Furuhara, J. Yamaguchi, N. Sugita, G. Miyamoto and T. Maki: ISIJ Int., 2003, vol. 43, pp. 1630–39. CrossRef
T. Koseki and G. Thewlis: Mater. Sci. Tech., 2005, vol. 21, pp. 867-897. CrossRef
A. R. Mills, G. Thewlis, and J. A. Whiteman: Mater. Sci. Technol., 1987, vol. 3 pp. 1051–61. CrossRef
S. E. Kang, A. Tuling, J. R. Banerjee, W. D. Gunawardana and B. Mintz: Mater. Sci. Tech., 2011, vol. 27, pp. 95-100. CrossRef
C.W. Bale, P. Chartrand, S.A. Degterov, G. Eriksson, K. Hack, R. Ben Mahfoud, J. Melanqon, A.D. Pelton, and S. Petersen: CALPHAD, 2002, vol. 26, pp. 189–228. CrossRef
J.H. Park: CALPHAD, 2011, vol. 35, pp. 455-462. CrossRef
J.H. Park: CALPHAD, 2007, vol. 31, pp. 428-437. CrossRef
J.H. Park: CALPHAD, 2007, vol. 31, pp. 149-154. CrossRef
J.S. Park, C. Lee and J.H. Park: Metall. Mater. Trans., 2012, vol. 43B, pp. 1550-64. CrossRef
H. S. Kim, H. G. Lee and K. S. OH: Metal.Mater.Int., 2000, vol. 6, pp. 305-310.
M. Wakoh, T. Sawai, S. Mizoguchi: Tetsu- to- Hagané, 1992, vol. 78, pp. 1697-1704.
W. A. Tiller, K. A. Jackson, J. W. Rutter and B. Chalmerst: Acta Metall., 1953, vol. 1,pp. 428-437. CrossRef
K. Oikawa, K. Ishida, and T. Nishizawa: ISIJ Int., 1997, vol. 37, No. 4, pp. 332–38. CrossRef
H. S. Kim, H. G. Lee, and K. S. Oh: Metall. Mater. Trans., 2001, vol. 32A, pp. 1519-25. CrossRef
G. E. Totten, L. Xie and K. Funatani: Handbook of Mechanical Alloy Design, 2003, CRC Press, New York. CrossRef
- Oxide Formation Mechanisms in High Manganese Steel Welds
Joo Hyun Park
- Springer US
in-adhesives, MKVS, Hellmich GmbH/© Hellmich GmbH, Zühlke/© Zühlke