Phase composition and luminescent properties of strontium aluminate long persistence phosphor synthesized by combustion synthesis method with different Sr/Al ratios

verfasst von: Wen-Zhou Sun, Yu-Hong Chen, Lan-Er Wu, Yong Jiang

Erschienen in: Rare Metals | Ausgabe 4/2013

Einloggen

Aktivieren Sie unsere intelligente Suche um passende Fachinhalte oder Patente zu finden.

search-config
loading …

Abstract

Strontium aluminate long persistence phosphors are synthesized by combustion method. By controlling the raw material ratio (Sr/Al), the effects of phase composition on subsequent spectroscopic properties of phosphors are studied. Results show that the phase composition changes from strontium-rich phase to aluminum-rich phase with the decrease of Sr/Al: when the rate of Al/Sr changes from 3:1 to 1:1, the main crystal phase of samples is Sr3Al2O6, and it exhibits the characteristic fluorescence of Eu3+ in the lattice of Sr3Al2O6; when the rate of Al/Sr is between 1:2 and 2:7, phase composition is the mixture of SrAl2O4 and SrAl4O7, and it emits the characteristic fluorescence of Eu2+ in SrAl2O4 but not in SrAl4O7; when Al/Sr decreases to 1:4 or even 1:12, the main crystal phase of samples transform into SrAl12O19, and the characteristic emission peak is about 470 nm, which corresponds to the characteristic emission of Eu2+ in SrAl12O19. At the end of the article, the influence laws of two different synthesis methods on phase composition of samples between high-temperature solid method and combustion method are compared. Compared with the high-temperature solid method, the rule of influence is similar, but the mole ratio of Al/Sr in products is always higher than the initial ratio of the raw material, and compounds like Sr4Al14O25 are not obtained by combustion method.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Literatur
[1]
Zurück zum Zitat Qu YD, Li XJ, Chen T, Li RY. Development of long-lasting phosphorescent materials of aluminates hosts. Chin J Rare Met. 2006;30(1):100. Qu YD, Li XJ, Chen T, Li RY. Development of long-lasting phosphorescent materials of aluminates hosts. Chin J Rare Met. 2006;30(1):100.
[2]
Zurück zum Zitat Sun JB, Wang HR, An YQ, Cui CX, Han D. Progress on long persistence luminescent materials. Rare Metal Mat Eng. 2008;38(2):189. Sun JB, Wang HR, An YQ, Cui CX, Han D. Progress on long persistence luminescent materials. Rare Metal Mat Eng. 2008;38(2):189.
[3]
Zurück zum Zitat Li XB, Huang QS, Lei YF, Ding JH, Zhou SH, Zhang Z. Present situation of the domestic market demand and application of rare earth aluminate long afterglow materials. Mater Res App. 2008;38(2):189. Li XB, Huang QS, Lei YF, Ding JH, Zhou SH, Zhang Z. Present situation of the domestic market demand and application of rare earth aluminate long afterglow materials. Mater Res App. 2008;38(2):189.
[4]
Zurück zum Zitat Luan L, Guo CF, Huang DX. Effect of Al/Sr ratio on properties of strontium alum inate long lasting phosphor. J Inorg Mater. 2009;24(1):53.CrossRef Luan L, Guo CF, Huang DX. Effect of Al/Sr ratio on properties of strontium alum inate long lasting phosphor. J Inorg Mater. 2009;24(1):53.CrossRef
[5]
Zurück zum Zitat Cui CE, Wang S, Huang P. Effect of Dy on properties of red long-afterglow phosphor Sr3Al2O6:Eu2+, Dy3+. Chin Phys. Soc. 2009;58(5):3565. Cui CE, Wang S, Huang P. Effect of Dy on properties of red long-afterglow phosphor Sr3Al2O6:Eu2+, Dy3+. Chin Phys. Soc. 2009;58(5):3565.
[6]
Zurück zum Zitat Li JF. Combustion synthesis and luminescence properties of rare earth-doped aluminate luminescence materials. Chengdu: Chengdu University of Technology; 2005. 18. Li JF. Combustion synthesis and luminescence properties of rare earth-doped aluminate luminescence materials. Chengdu: Chengdu University of Technology; 2005. 18.
[7]
Zurück zum Zitat Zhang YF, Li L, Zhang XS, Wang DJ, Zhang SS. Preparation and photoluminescence of Tb3+doped SrAl2O4 phosphor by composite combustion method. J Rare Earths. 2008;26(5):656.CrossRef Zhang YF, Li L, Zhang XS, Wang DJ, Zhang SS. Preparation and photoluminescence of Tb3+doped SrAl2O4 phosphor by composite combustion method. J Rare Earths. 2008;26(5):656.CrossRef
[8]
Zurück zum Zitat Song HJ, Chen DH, Tang WJ, Peng YH. Synthesis of SrAl2O4:Eu, Dy, Gd phosphor by combustion method and its phosphorescence properties. Displays. 2008;29:41.CrossRef Song HJ, Chen DH, Tang WJ, Peng YH. Synthesis of SrAl2O4:Eu, Dy, Gd phosphor by combustion method and its phosphorescence properties. Displays. 2008;29:41.CrossRef
[9]
Zurück zum Zitat Sun WZ, Mamg JJ, Jiang L, Hang F, Wang B. Effects of Al/Sr ratio on SrAl2O4:Eu2+, Dy3+ long lasting phosphors prepared by microwave plasma synthesis method. J Mater Sci Eng. 2010;28(3):429. Sun WZ, Mamg JJ, Jiang L, Hang F, Wang B. Effects of Al/Sr ratio on SrAl2O4:Eu2+, Dy3+ long lasting phosphors prepared by microwave plasma synthesis method. J Mater Sci Eng. 2010;28(3):429.
[10]
Zurück zum Zitat Sun WZ, Chen YH, Han F, Jiang L. Study on phase composition of long persistence phosphors SrAl2O4:Eu2+, Dy3+ synthesized by combustion synthesis method. Adv Mater Res. 2011;2161:284.CrossRef Sun WZ, Chen YH, Han F, Jiang L. Study on phase composition of long persistence phosphors SrAl2O4:Eu2+, Dy3+ synthesized by combustion synthesis method. Adv Mater Res. 2011;2161:284.CrossRef
[11]
Zurück zum Zitat Li J. Study on preparation and properties of the red long afterglow phosphors of Eu ions in different valences as activator. Taiyuan: Taiyuan University of Technology; 2011. 05. Li J. Study on preparation and properties of the red long afterglow phosphors of Eu ions in different valences as activator. Taiyuan: Taiyuan University of Technology; 2011. 05.
[12]
Zurück zum Zitat Li J. Study on preparation and properties of the red long afterglow phosphors of Eu ions in different valences as activator. Taiyuan: Taiyuan University of Technology; 2011. 35. Li J. Study on preparation and properties of the red long afterglow phosphors of Eu ions in different valences as activator. Taiyuan: Taiyuan University of Technology; 2011. 35.
[13]
Zurück zum Zitat Zhang L, Jin Z, Li WZ, Ge MQ. Action mechanism of Eu2+ on mixed-based red long afterglow phosphor. J Chin Rare Earth Soc. 2010;28(3):293. Zhang L, Jin Z, Li WZ, Ge MQ. Action mechanism of Eu2+ on mixed-based red long afterglow phosphor. J Chin Rare Earth Soc. 2010;28(3):293.
[14]
Zurück zum Zitat Zhang YQ, Zheng ZG, Zhuang JM, Zhou ZM, Luo DH, Tang L. Light storing emitting material SrAl2O4:Eu2+, Dy3+ and its room temperature phosphorescent spectrum analysis. Chin J Inorg Chem. 2003;19(10):1129. Zhang YQ, Zheng ZG, Zhuang JM, Zhou ZM, Luo DH, Tang L. Light storing emitting material SrAl2O4:Eu2+, Dy3+ and its room temperature phosphorescent spectrum analysis. Chin J Inorg Chem. 2003;19(10):1129.
[15]
Zurück zum Zitat Lu XD, Shu WL. Formation and roles of point defects in SrAl2O4:Eu Dy phosphors. Chinese J Inorg Chem. 2006;22(5):808. Lu XD, Shu WL. Formation and roles of point defects in SrAl2O4:Eu Dy phosphors. Chinese J Inorg Chem. 2006;22(5):808.
[16]
Zurück zum Zitat Kuang JY, Liu YL, Zhang JX. Effects of RE3+ as a co-dopant in blue-emitting long-lasting phosphors, Sr3Al10SiO20:Eu2+. Mater Sci. 2006;41:5500.CrossRef Kuang JY, Liu YL, Zhang JX. Effects of RE3+ as a co-dopant in blue-emitting long-lasting phosphors, Sr3Al10SiO20:Eu2+. Mater Sci. 2006;41:5500.CrossRef
[17]
Zurück zum Zitat Jin ZQ, Preparation and token of long-after mica covering strontium aluminates: Eu, Dy, Wuhan: Wuhan University of Technology, 2007:43. Jin ZQ, Preparation and token of long-after mica covering strontium aluminates: Eu, Dy, Wuhan: Wuhan University of Technology, 2007:43.
[18]
Zurück zum Zitat Ryu H, Bartwal KS. Defect structure and its relevance to photoluminescence in SrAl2O4:Eu2+, Nd3+. Phys B. 2009;404:1714.CrossRef Ryu H, Bartwal KS. Defect structure and its relevance to photoluminescence in SrAl2O4:Eu2+, Nd3+. Phys B. 2009;404:1714.CrossRef
[19]
Zurück zum Zitat Holsa J, Laamanen T, Lastusaari M, Niittykoski J, Novák P. Electronic structure of the SrAl2O4:Eu2+persistent luminescence material. J Rare Earths. 2009;27(4):550.CrossRef Holsa J, Laamanen T, Lastusaari M, Niittykoski J, Novák P. Electronic structure of the SrAl2O4:Eu2+persistent luminescence material. J Rare Earths. 2009;27(4):550.CrossRef
[20]
Zurück zum Zitat Geng J, Wu Z. Synthesis of long afterglow SrAl2O4:Eu2+, Dy3+ phosphors through microwave route. J Mater Synth Process. 2002;10(5):245.CrossRef Geng J, Wu Z. Synthesis of long afterglow SrAl2O4:Eu2+, Dy3+ phosphors through microwave route. J Mater Synth Process. 2002;10(5):245.CrossRef
[21]
Zurück zum Zitat Shafia E, Aghaei A, Bodaghi M, Tahrir M. Combusion synthesis, structural and photo-physical characteristics of Eu2+and Dy3+ co-doped SrAl2O4 phosphor nanopowders. J Mater Sci. 2011;22:1136. Shafia E, Aghaei A, Bodaghi M, Tahrir M. Combusion synthesis, structural and photo-physical characteristics of Eu2+and Dy3+ co-doped SrAl2O4 phosphor nanopowders. J Mater Sci. 2011;22:1136.
Metadaten
Titel
Phase composition and luminescent properties of strontium aluminate long persistence phosphor synthesized by combustion synthesis method with different Sr/Al ratios
verfasst von
Wen-Zhou Sun
Yu-Hong Chen
Lan-Er Wu
Yong Jiang
Publikationsdatum
01.08.2013
Verlag
Springer Berlin Heidelberg
Erschienen in
Rare Metals / Ausgabe 4/2013
Print ISSN: 1001-0521
Elektronische ISSN: 1867-7185
DOI
https://doi.org/10.1007/s12598-013-0111-4

Weitere Artikel der Ausgabe 4/2013

Rare Metals 4/2013 Zur Ausgabe

    Marktübersichten

    Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen.