Simulating natural leaching process for cementitious materials is essential to perform long-term safety assessments of repositories for nuclear waste. However, the current test methods in literature are time consuming, limited to crushed material and often produce small size samples which are not suitable for further testing. This paper presents the results from the study of the physical (gas permeability as well as chloride diffusion coefficient) and mechanical properties (tensile and compressive strength and elastic modulus) of solid cementitious specimens which have been depleted in calcium by the use of a newly developed method for accelerated calcium leaching of solid specimens of flexible size. The results show that up to 4 times increase in capillary water absorption, 10 times higher gas permeability and at least 3 times higher chloride diffusion rate, is expected due to complete leaching of the Portlandite. This coincides with a 70 % decrease in mechanical strength and more than 40 % decrease in elastic modulus.
ASTM C39/C39M-14a, Standard Test Method for Compressive Strength of Cylindrical Concrete Specimens.
ASTM C496/C496M-11, Standard Test Method for Splitting Tensile Strength of Cylindrical Concrete Specimens.
Babaahmadi, A., Tang, L., Abbas, Z., Zack, T., & Mårtensson, P. (2015). Development of an electro-chemical accelerated ageing method for leaching of calcium from cementitious materials. Materials and Structures. doi: 10.1617/s11527-015-0531-8.
Carde, C., Escadeillas, G., & François, R. (1997). Use of ammonium nitrate solution to simulate and accelerate the leaching of cement pastes due to deionized water. Magazine of Concrete Research, 49, 295–301. CrossRef
Emborg, M., Jonasson, J. E., & Knutsson, S. (2007) Long-term stability due to freezing and thawing of concrete and bentonite at the disposal of low and intermediate level nuclear waste in SFR 1 ( in Swedish) vol. R-07-60. SKB Technical Report R-07-60, Swedish Nuclear and Waste Management Company
EN 933-1 Tests for geometrical properties of aggregates.
Faucon, P., Adenot, F., Jacquinot, J. F., Petit, J. C., Cabrillac, R., & Jorda, M. (1998). Long-term behaviour of cement pastes used for nuclear waste disposal: Review of physico-chemical mechanisms of water degradation. Cement and Concrete Research, 28, 847–857. doi: 10.1016/s0008-8846(98)00053-2. CrossRef
Gustafson, G., Hagström, M., & Abbas, Z. (2008). Beständighet av cementinjektering
Heukamp, F. H., Ulm, F. J., & Germaine, J. T. (2001). Mechanical properties of calcium-leached cement pastes: Triaxial stress states and the influence of the pore pressures. Cement and Concrete Research, 31, 767–774. CrossRef
Hinsenveld, M. (1992). A shrinkage core model as a fundamental representation of leaching mechanism in cement stabilized waste. Doctoral thesis, University of Cincinnati, Cincinnati, OH.
Höglund, L.-O. (2001). Project SAFE: Modeling of long-term concrete degradation processes in the Swedish SFR repository vol R-01-08. SKB Report, Svensk Kärnbränslehantering AB.
Lagerblad, B. (2001). Leaching performance of concrete based on studies of sample from old concrete constructions, TR-01-27. Stockholm, Sweden: Swedish Nuclear Fuel and Waste Management.
Langton, C., & Kosson, D. (2009). Review of mechanistic understanding and modeling and uncertainty analysis methods for predicting cementitious barriers performance. doi: 10.2172/974326
NT BUILD 492. (1999). Concrete, mortar and cement-based repair materials: Chloride migration coefficient from non-steady-state migration experiments.
Peyronnard, O., Benzaazoua, M., Blanc, D., & Moszkowicz, P. (2009). Study of mineralogy and leaching behavior of stabilized/solidified sludge using differential acid neutralization analysis: Part I: Experimental study. Cement and Concrete Research, 39, 600–609. doi: 10.1016/j.cemconres.2009.03.016. CrossRef
Tang, L. (1996). Electrically accelerated methods for determining chloride diffusivity in concrete—Current development. Magazine of Concrete Research, 48, 173–179. CrossRef
Trägårdh, J., & Lagerblad, B. (1998). Leaching of 90-year old concrete in contact with stagnant water, TR 98-11. Stockholm, Sweden: Swedish Nuclear fuel and Waste.
Torrent, R. (2007). Non-destructive evaluation of the penetrability and thickness of the concrete cover—State-of-the-Art Report of RILEM Technical Committee 189-NEC vol rep040.
Zhang, Q., & Ye, G. (2012). Dehydration kinetics of Portland cement paste at high temperature J Therm Anal Calorim, 110, 153–158. doi: 10.1007/s10973-012-2303-9.
- Physical and Mechanical Properties of Cementitious Specimens Exposed to an Electrochemically Derived Accelerated Leaching of Calcium
- Korea Concrete Institute
International Journal of Concrete Structures and Materials
Print ISSN: 1976-0485
Elektronische ISSN: 2234-1315