Preparation and microwave absorbing properties of nickel-coated carbon fiber with polyaniline via in situ polymerization
Erschienen in: Journal of Materials Science: Materials in Electronics | Ausgabe 6/2016
EinloggenAktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.
Wählen Sie Textabschnitte aus um mit Künstlicher Intelligenz passenden Patente zu finden. powered by
Markieren Sie Textabschnitte, um KI-gestützt weitere passende Inhalte zu finden. powered by
Abstract
Electric conductive and microwave absorbing material PANI/Ni/CF was prepared by in situ polymerization of polyaniline on the surface of nickel-coated carbon fiber (Ni/CF). The morphologies and structures of CF, Ni/CF, PANI and PANI/Ni/CF were characterized by scanning electron microscope and X-ray diffraction. Results show that the CF was wrapped tightly around the nickel layer, and the Ni/CF was coated by PANI. Measurement of four probes resistance tester indicates that the electrical conductivity of PANI/Ni/CF was great improved compared with PANI and PANI/CF. Vibrating sample magnetometry shows that the magnetic saturation intensity of Ni/CF and PANI/Ni/CF was 13.8 and 2.3 emu/g, respectively. According to the vector network analyzer, the microwave absorbing properties of PANI/Ni/CF were better than those of PANI and PANI/CF, and its minimum loss value is −12.4 dB at 8.8 GHz.