Preparation of TiO2–(B) by microemulsion mediated hydrothermal method: effect of the precursor and its electrochemical performance

verfasst von: Nayely Pineda-Aguilar, Lorena Leticia Garza-Tovar, Eduardo M. Sánchez-Cervantes, Margarita Sánchez-Domínguez

Erschienen in: Journal of Materials Science: Materials in Electronics | Ausgabe 18/2018

Einloggen

Aktivieren Sie unsere intelligente Suche um passende Fachinhalte oder Patente zu finden.

search-config
loading …

Abstract

Synthesis of TiO2–(B) bronze was carried out by hydrothermal method using different precursors: (a) commercial anatase, (b) amorphous TiO2 prepared by O/W microemulsion method and (c) oil-in-water (O/W) microemulsion with freshly prepared amorphous TiO2. It is important to highlight this is the first report of the preparation of TiO2–(B) using an O/W microemulsion as a precursor. The effect of precursor type on the resulting TiO2 nanostructures, namely, their structural and morphological features were studied using X-ray diffraction, thermal analysis (TGA–DTA), Brunauer–Emmett–Teller, Raman spectroscopy and scanning electron microscopy (SEM–EDX). From commercial anatase powder, amorphous TiO2 ME and O/W microemulsion ME238 (NaOH/TiO2 molar ratio 238), biphasic nanoribbons were obtained: TiO2–(B) (88–92%) and anatase (8–12%). While from the O/W microemulsion ME30 (NaOH/TiO2 molar ratio 30) only anatase phase was obtained. The material with higher TiO2–(B) phase content, showed an increase in its reversible capacity, thus the crystalline nature of the precursor as well as the textural properties contribute to the electrode performance. Materials synthesized from commercial anatase and amorphous TiO2 ME exhibited similar charge retention (86–87%) despite the slight difference in reversible capacity, 210 and 180 mAh/g, respectively. It is noticed that TiO2–(B)–AME (prepared from amorphous TiO2 ME) exhibited the lowest capacity loss, e.g. the highest reversibility.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Springer Professional "Wirtschaft"

Online-Abonnement

Mit Springer Professional "Wirtschaft" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 340 Zeitschriften

aus folgenden Fachgebieten:

  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Versicherung + Risiko




Jetzt Wissensvorsprung sichern!

Literatur
1.
Zurück zum Zitat J.S. Chen, L.A. Archer, X. Wen Lou, J. Mater. Chem. 21, 9912–9924 (2011)CrossRef J.S. Chen, L.A. Archer, X. Wen Lou, J. Mater. Chem. 21, 9912–9924 (2011)CrossRef
2.
Zurück zum Zitat M.V. Reddy, G.V. Subba Rao, B.V.R. Chowdari, Chem. Rev. 113, 5364–5457 (2013)CrossRef M.V. Reddy, G.V. Subba Rao, B.V.R. Chowdari, Chem. Rev. 113, 5364–5457 (2013)CrossRef
3.
Zurück zum Zitat H.-Y. Wu, M.-H. Hon, C.-Y. Kuan, I.-C. Leu, J. Electron. Mater. 43, 1048–1054 (2014)CrossRef H.-Y. Wu, M.-H. Hon, C.-Y. Kuan, I.-C. Leu, J. Electron. Mater. 43, 1048–1054 (2014)CrossRef
4.
Zurück zum Zitat A.G. Dylla, G. Henkelman, K.J. Stevenson, Acc. Chem. Res. 46, 1104–1112 (2013)CrossRef A.G. Dylla, G. Henkelman, K.J. Stevenson, Acc. Chem. Res. 46, 1104–1112 (2013)CrossRef
5.
Zurück zum Zitat T. Kasuga, M. Hiramatsu, A. Hoson, T. Sekino, K. Niihara, Langmuir 14, 3160–3163 (1998)CrossRef T. Kasuga, M. Hiramatsu, A. Hoson, T. Sekino, K. Niihara, Langmuir 14, 3160–3163 (1998)CrossRef
6.
Zurück zum Zitat A.R. Armstrong, G. Armstrong, J. Canales, P.G. Bruce, Angew. Chem. Int. Ed. 43, 2286–2288 (2004)CrossRef A.R. Armstrong, G. Armstrong, J. Canales, P.G. Bruce, Angew. Chem. Int. Ed. 43, 2286–2288 (2004)CrossRef
7.
Zurück zum Zitat G. Armstrong, A.R. Armstrong, J. Canales, P.G. Bruce, Chem. Commun. 19, 2454 (2005)CrossRef G. Armstrong, A.R. Armstrong, J. Canales, P.G. Bruce, Chem. Commun. 19, 2454 (2005)CrossRef
8.
Zurück zum Zitat N. Liu, X. Chen, J. Zhang, J.W. Schwank, Catal. Today 225, 34–51 (2014)CrossRef N. Liu, X. Chen, J. Zhang, J.W. Schwank, Catal. Today 225, 34–51 (2014)CrossRef
9.
Zurück zum Zitat M. Sanchez-Dominguez, M. Boutonnet, C. Solans, J. Nanopart. Res. 11, 1823 (2009)CrossRef M. Sanchez-Dominguez, M. Boutonnet, C. Solans, J. Nanopart. Res. 11, 1823 (2009)CrossRef
10.
Zurück zum Zitat M. Sanchez-Dominguez, K. Pemartin, M. Boutonnet, Curr. Opin. Colloid Interface Sci. 17, 297–305 (2012)CrossRef M. Sanchez-Dominguez, K. Pemartin, M. Boutonnet, Curr. Opin. Colloid Interface Sci. 17, 297–305 (2012)CrossRef
11.
Zurück zum Zitat M. Boutonnet, J. Kizling, P. Stenius, G. Maire, Colloids Surf. 5, 209–225 (1982)CrossRef M. Boutonnet, J. Kizling, P. Stenius, G. Maire, Colloids Surf. 5, 209–225 (1982)CrossRef
12.
Zurück zum Zitat M. Sanchez-Dominguez, L.F. Liotta, G. Di Carlo, G. Pantaleo, A.M. Venezia, C. Solans, M. Boutonnet, Catal. Today 158, 35–43 (2010)CrossRef M. Sanchez-Dominguez, L.F. Liotta, G. Di Carlo, G. Pantaleo, A.M. Venezia, C. Solans, M. Boutonnet, Catal. Today 158, 35–43 (2010)CrossRef
13.
Zurück zum Zitat C. Tiseanu, V.I. Parvulescu, M. Boutonnet, B. Cojocaru, P.A. Primus, C.M. Teodorescu, C. Solans, M.S. Dominguez, Phys. Chem. Chem. Phys. 13, 17135–17145 (2011)CrossRef C. Tiseanu, V.I. Parvulescu, M. Boutonnet, B. Cojocaru, P.A. Primus, C.M. Teodorescu, C. Solans, M.S. Dominguez, Phys. Chem. Chem. Phys. 13, 17135–17145 (2011)CrossRef
14.
Zurück zum Zitat M. Sanchez-Dominguez, H. Koleilat, M. Boutonnet, C. Solans, J. Dispersion Sci. Technol. 32, 1765–1770 (2011)CrossRef M. Sanchez-Dominguez, H. Koleilat, M. Boutonnet, C. Solans, J. Dispersion Sci. Technol. 32, 1765–1770 (2011)CrossRef
15.
Zurück zum Zitat K. Pemartin, C. Solans, G. Vidal-Lopez, M. Sanchez-Dominguez, Chem. Lett. 41, 1032–1034 (2012)CrossRef K. Pemartin, C. Solans, G. Vidal-Lopez, M. Sanchez-Dominguez, Chem. Lett. 41, 1032–1034 (2012)CrossRef
16.
Zurück zum Zitat G. Di Carlo, M. Lualdi, A.M. Venezia, M. Boutonnet, M. Sanchez-Dominguez, Catalysts 5, 442–459 (2015)CrossRef G. Di Carlo, M. Lualdi, A.M. Venezia, M. Boutonnet, M. Sanchez-Dominguez, Catalysts 5, 442–459 (2015)CrossRef
17.
Zurück zum Zitat R. Yoshida, Y. Suzuki, S. Yoshikawa, J. Solid State Chem. 178, 2179–2185 (2005)CrossRef R. Yoshida, Y. Suzuki, S. Yoshikawa, J. Solid State Chem. 178, 2179–2185 (2005)CrossRef
18.
Zurück zum Zitat M. Sanchez-Dominguez, G. Morales-Mendoza, M.J. Rodriguez-Vargas, C.C. Ibarra-Malo, A.A. Rodriguez-Rodriguez, A.V. Vela-Gonzalez, S. Perez-Garcia, R. Gomez, J. Environ. Chemi. Eng. 3, 3037–3047 (2015)CrossRef M. Sanchez-Dominguez, G. Morales-Mendoza, M.J. Rodriguez-Vargas, C.C. Ibarra-Malo, A.A. Rodriguez-Rodriguez, A.V. Vela-Gonzalez, S. Perez-Garcia, R. Gomez, J. Environ. Chemi. Eng. 3, 3037–3047 (2015)CrossRef
19.
Zurück zum Zitat K. Pemartin-Biernath, A.V. Vela-González, M.B. Moreno-Trejo, C. Leyva-Porras, I.E. Castañeda-Reyna, I. Juárez-Ramírez, C. Solans, M. Sánchez-Domínguez, Materials 9, 480 (2016)CrossRef K. Pemartin-Biernath, A.V. Vela-González, M.B. Moreno-Trejo, C. Leyva-Porras, I.E. Castañeda-Reyna, I. Juárez-Ramírez, C. Solans, M. Sánchez-Domínguez, Materials 9, 480 (2016)CrossRef
20.
Zurück zum Zitat C. Okoli, M. Sanchez-Dominguez, M. Boutonnet, S. Järås, C.n. Civera, C. Solans, G.R. Kuttuva, Langmuir 28, 8479–8485 (2012)CrossRef C. Okoli, M. Sanchez-Dominguez, M. Boutonnet, S. Järås, C.n. Civera, C. Solans, G.R. Kuttuva, Langmuir 28, 8479–8485 (2012)CrossRef
21.
Zurück zum Zitat K. Pemartin, C. Solans, J. Alvarez-Quintana, M. Sanchez-Dominguez, Colloids Surf. A 451, 161–171 (2014)CrossRef K. Pemartin, C. Solans, J. Alvarez-Quintana, M. Sanchez-Dominguez, Colloids Surf. A 451, 161–171 (2014)CrossRef
22.
Zurück zum Zitat T. Beuvier, M. Richard-Plouet, L. Brohan, J Phys. Chem. C 113, 13703–13706 (2009)CrossRef T. Beuvier, M. Richard-Plouet, L. Brohan, J Phys. Chem. C 113, 13703–13706 (2009)CrossRef
23.
Zurück zum Zitat Z. Liu, Y.G. Andreev, A. Robert Armstrong, S. Brutti, Y. Ren, P.G. Bruce, Prog. Nat. Sci.: Mater. Int. 23, 235–244 (2013)CrossRef Z. Liu, Y.G. Andreev, A. Robert Armstrong, S. Brutti, Y. Ren, P.G. Bruce, Prog. Nat. Sci.: Mater. Int. 23, 235–244 (2013)CrossRef
24.
Zurück zum Zitat G.-N. Zhu, C.-X. Wang, Y.-Y. Xia, J. Power Sources 196, 2848–2853 (2011)CrossRef G.-N. Zhu, C.-X. Wang, Y.-Y. Xia, J. Power Sources 196, 2848–2853 (2011)CrossRef
25.
Zurück zum Zitat M. Fehse, F. Fischer, C. Tessier, L. Stievano, L. Monconduit, J. Power Sources 231, 23–28 (2013)CrossRef M. Fehse, F. Fischer, C. Tessier, L. Stievano, L. Monconduit, J. Power Sources 231, 23–28 (2013)CrossRef
26.
Zurück zum Zitat A.-L. Papa, N. Millot, L. Saviot, R. Chassagnon, O. Heintz, J. Phys. Chem. C 113, 12682–12689 (2009)CrossRef A.-L. Papa, N. Millot, L. Saviot, R. Chassagnon, O. Heintz, J. Phys. Chem. C 113, 12682–12689 (2009)CrossRef
27.
Zurück zum Zitat M. Sanchez-Dominguez, C.A.C. Solans, in Smart Nanoparticles Technology, ed. by A. Hashim (Intech, Rijeka, 2012), pp. 195–220 M. Sanchez-Dominguez, C.A.C. Solans, in Smart Nanoparticles Technology, ed. by A. Hashim (Intech, Rijeka, 2012), pp. 195–220
28.
Zurück zum Zitat V. Bellat, R. Chassagnon, O. Heintz, L. Saviot, D. Vandroux, N. Millot, Dalton Trans. 44, 1150–1160 (2015)CrossRef V. Bellat, R. Chassagnon, O. Heintz, L. Saviot, D. Vandroux, N. Millot, Dalton Trans. 44, 1150–1160 (2015)CrossRef
29.
Zurück zum Zitat D.L. Morgan, H.-W. Liu, R.L. Frost, E.R. Waclawik, J. Phys. Chem. C 114, 101–110 (2010)CrossRef D.L. Morgan, H.-W. Liu, R.L. Frost, E.R. Waclawik, J. Phys. Chem. C 114, 101–110 (2010)CrossRef
30.
Zurück zum Zitat B. Yao, Y.F. Chan, X. Zhang, W. Zhang, Z. Yang, N. Wang, Appl. Phys. Lett. 82, 281–283 (2003)CrossRef B. Yao, Y.F. Chan, X. Zhang, W. Zhang, Z. Yang, N. Wang, Appl. Phys. Lett. 82, 281–283 (2003)CrossRef
31.
Zurück zum Zitat J. Huang, Y. Cao, M. Wang, C. Huang, Z. Deng, H. Tong, Z. Liu, J. Phys. Chem. C 114, 14748–14754 (2010)CrossRef J. Huang, Y. Cao, M. Wang, C. Huang, Z. Deng, H. Tong, Z. Liu, J. Phys. Chem. C 114, 14748–14754 (2010)CrossRef
32.
Zurück zum Zitat D.L. Morgan, G. Triani, M.G. Blackford, N.A. Raftery, R.L. Frost, E.R. Waclawik, J. Mater. Sci. 46, 548–557 (2011)CrossRef D.L. Morgan, G. Triani, M.G. Blackford, N.A. Raftery, R.L. Frost, E.R. Waclawik, J. Mater. Sci. 46, 548–557 (2011)CrossRef
34.
Zurück zum Zitat D.V. Bavykin, M. Carravetta, A.N. Kulak, F.C. Walsh, Chem. Mater. 22, 2458–2465 (2010)CrossRef D.V. Bavykin, M. Carravetta, A.N. Kulak, F.C. Walsh, Chem. Mater. 22, 2458–2465 (2010)CrossRef
35.
Zurück zum Zitat D.V. Bavykin, V.N. Parmon, A.A. Lapkin, F.C. Walsh, J. Mater. Chem. 14, 3370–3377 (2004)CrossRef D.V. Bavykin, V.N. Parmon, A.A. Lapkin, F.C. Walsh, J. Mater. Chem. 14, 3370–3377 (2004)CrossRef
36.
Zurück zum Zitat A. Elsanousi, E.M. Elssfah, J. Zhang, J. Lin, H.S. Song, C. Tang, J. Phys. Chem. C 111, 14353–14357 (2007)CrossRef A. Elsanousi, E.M. Elssfah, J. Zhang, J. Lin, H.S. Song, C. Tang, J. Phys. Chem. C 111, 14353–14357 (2007)CrossRef
37.
Zurück zum Zitat J. Sheng, L. Hu, L.E. Mo, W. Li, H. Tian, S. Dai, Sci. China Chem. 55, 368–372 (2012)CrossRef J. Sheng, L. Hu, L.E. Mo, W. Li, H. Tian, S. Dai, Sci. China Chem. 55, 368–372 (2012)CrossRef
38.
Zurück zum Zitat M. Zukalová, M. Kalbáč, L. Kavan, I. Exnar, M. Graetzel, Chem. Mater. 17, 1248–1255 (2005)CrossRef M. Zukalová, M. Kalbáč, L. Kavan, I. Exnar, M. Graetzel, Chem. Mater. 17, 1248–1255 (2005)CrossRef
39.
40.
Zurück zum Zitat Z. Yang, G. Du, Q. Meng, Z. Guo, X. Yu, Z. Chen, T. Guo, R. Zeng, RSC Adv. 1, 1834–1840 (2011)CrossRef Z. Yang, G. Du, Q. Meng, Z. Guo, X. Yu, Z. Chen, T. Guo, R. Zeng, RSC Adv. 1, 1834–1840 (2011)CrossRef
41.
Zurück zum Zitat Y. Ren, Z. Liu, F. Pourpoint, A.R. Armstrong, C.P. Grey, P.G. Bruce, Angew. Chem. Int. Ed. 51, 2164–2167 (2012)CrossRef Y. Ren, Z. Liu, F. Pourpoint, A.R. Armstrong, C.P. Grey, P.G. Bruce, Angew. Chem. Int. Ed. 51, 2164–2167 (2012)CrossRef
42.
Zurück zum Zitat R. Grosjean, M. Fehse, S. Pigeot-Remy, L. Stievano, L. Monconduit, S. Cassaignon, J. Power Sources 278, 1–8 (2015)CrossRef R. Grosjean, M. Fehse, S. Pigeot-Remy, L. Stievano, L. Monconduit, S. Cassaignon, J. Power Sources 278, 1–8 (2015)CrossRef
43.
Zurück zum Zitat P. Zheng, T. Liu, Y. Su, L. Zhang, S. Guo, Sci. Rep. 6, 36580 (2016) P. Zheng, T. Liu, Y. Su, L. Zhang, S. Guo, Sci. Rep. 6, 36580 (2016)
Metadaten
Titel
Preparation of TiO2–(B) by microemulsion mediated hydrothermal method: effect of the precursor and its electrochemical performance
verfasst von
Nayely Pineda-Aguilar
Lorena Leticia Garza-Tovar
Eduardo M. Sánchez-Cervantes
Margarita Sánchez-Domínguez
Publikationsdatum
17.04.2018
Verlag
Springer US
Erschienen in
Journal of Materials Science: Materials in Electronics / Ausgabe 18/2018
Print ISSN: 0957-4522
Elektronische ISSN: 1573-482X
DOI
https://doi.org/10.1007/s10854-018-9085-1

Weitere Artikel der Ausgabe 18/2018

Journal of Materials Science: Materials in Electronics 18/2018 Zur Ausgabe

Guest Editorial

Editorial

Neuer Inhalt