Properties of nano-thick BaSnO3/Cu/BaSnO3 multilayer thin films: the role of substrate temperature

verfasst von: Muying Wu, Shihui Yu, Lin He, Lei Yang

Erschienen in: Journal of Materials Science: Materials in Electronics | Ausgabe 12/2016

Einloggen

Aktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.

search-config
loading …

Abstract

The nano-thick BaSnO3/Cu/BaSnO3 multilayer thin films have been designed and fabricated on glass by magnetron sputtering. The thickness of BaSnO3, Cu, and BaSnO3 layer in the multilayer thin films was set at 50, 10, and 50 nm, respectively. The structural, electrical, and optical properties of multilayer thin films were investigated with respect to the variation of substrate temperature. The average optical transmittance in the visible range of wavelengths (400–800 nm) shows an increase for the multilayer thin films grown at a temperature below 250 °C. A low resistivity (<10−4 Ω cm) for the multilayer thin films is found to be retained until 200 °C, followed by a quickly increase as the substrate temperature further increases to 300 °C. In addition, a mechanism for the variation of electrical and optical properties with the substrate temperature was proposed.
Vorheriger Artikel A novel method for the deposition of polycrystalline Sb2S3 thin films
Nächster Artikel In situ synthesis of biocarbon coated Li3V2(PO4)3 cathode material using lotus leaf as carbon source

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Jetzt informieren

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Jetzt informieren

Springer Professional "Wirtschaft"

Online-Abonnement

Mit Springer Professional "Wirtschaft" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 340 Zeitschriften

aus folgenden Fachgebieten:

  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Versicherung + Risiko




Jetzt Wissensvorsprung sichern!

Jetzt informieren
Literatur
1.
2.
C. Tian, X. Chen, J. Ni, J. Liu, D. Zhang, Q. Huang, Y. Zhao, X. Zhang, Sol. Energy Mater. Sol. Cells 125, 59 (2014)CrossRef
3.
H. Hagendorfer, K. Lienau, S. Nishiwaki, C.M. Fella, L. Kranz, A.R. Uhl, D. Jaeger, L. Luo, C. Gretener, S. Buecheler, Y.E. Romanyuk, A.N. Tiwari, Adv. Mater. 26, 632 (2014)CrossRef
4.
Q. Lin, Y. Guo, T. Sun, C. Guo, D. Carnahan, M. Giersig, Y. Wang, J. Gao, Z. Ren, K. Kempa, Adv. Mater. 26, 873 (2014)CrossRef
5.
F.Q. Adurodija, H. Izumi, T. Ishihara, J. Mater. Sci. Mater. Electron. 12, 57 (2000)CrossRef
6.
O.J. Gregory, M. Amani, I.M. Tougas, A.J. Drehman, J. Am. Ceram. Soc. 95, 705 (2012)CrossRef
7.
8.
X. Luo, Y.S. Oh, A. Sirenko, P. Gao, T.A. Tyson, K. Char, S.W. Cheong, App. Phys. Lett. 100, 172112 (2012)CrossRef
9.
Q. Liu, J. Dai, Z. Liu, X. Zhang, G. Zhu, G. Ding, J. Phys. D Appl. Phys. 43, 455401 (2010)CrossRef
10.
H. Meixner, J. Gerblinger, U. Lampe, M. Fleischer, Sens. Actuators B Chem. 23, 119 (1995)CrossRef
11.
H.F. Wang, Q.Z. Liu, F. Chen, G.Y. Gao, W. Wu, X.H. Chen, J. Appl. Phys. 101, 106105 (2007)CrossRef
12.
S.H. Yu, C.H. Jia, H.W. Zheng, L.H. Ding, W.F. Zhang, Mater. Lett. 85, 68 (2012)CrossRef
13.
14.
C. Lee, R.P. Dwivedi, W. Lee, C. Hong, I.L. Wan, H.W. Kim, J. Mater. Sci. Mater. Electron. 19, 981 (2008)CrossRef
15.
16.
J. Cui, A. Wang, N.L. Edleman, J. Ni, P. Lee, N.R. Armstrong, T.J. Marks, Adv. Mater. 13, 1476 (2001)CrossRef
17.
18.
19.
T.W. Chiu, S.W. Tsai, Y.P. Wang, K.H. Hsu, Ceram. Int. 38, S673 (2012)CrossRef
20.
K. Miyamoto, M. Sano, H. Kato, T. Yao, J. Cryst. Growth 265, 34 (2004)CrossRef
21.
X.R. Deng, H. Deng, M. Wei, J.J. Chen, J. Mater. Sci. Mater. Electron. 23, 413 (2012)CrossRef
22.
S. Wu, Y. Li, J. Luo, J. Lin, Y. Fan, Z. Gan, X. Liu, Opt. Exp. 22, 4731 (2014)CrossRef
23.
N. Rashidi, V.L. Kuznetsov, J.R. Dilworth, M. Pepper, P.J. Dobson, P.P. Edwards, J. Mater. Chem. C 1, 6960 (2013)CrossRef
24.
K. Maejima, T. Koida, H. Sai, T. Matsui, K. Saito, M. Kondo, T. Takagawa, Thin Solid Films 559, 83 (2014)CrossRef
25.
N. Bouhssira, S. Abed, E. Tomasella, J. Cellier, A. Mosbah, M.S. Aida, M. Jacquet, Appl. Surf. Sci. 252, 5594 (2006)CrossRef
26.
M.D. Barankin, E. Gonzalez Ii, A.M. Ladwig, R.F. Hicks, Sol. Energy Mater. Sol. Cells 91, 924 (2007)CrossRef
27.
J. Zhang, H. Yang, Q.L. Zhang, S. Dong, J.K. Luo, Appl. Surf. Sci. 282, 390 (2013)CrossRef
28.
29.
W.S. Liu, W.K. Chen, S.Y. Wu, K.P. Hsueh, J. Am. Ceram. Soc. 97, 473 (2014)CrossRef
30.
S. Yu, L. Li, D. Xu, H. Dong, Y. Jin, Thin Solid Films 562, 501 (2014)CrossRef
31.
W.G. Driscoll, W. Vaughan, Handbook of Optics (McGraw-Hill, New York, 1978)
32.
R. Pandey, B. Angadi, S.K. Kim, J.W. Choi, D.K. Hwang, W.K. Choi, Opt. Mater. Exp. 4, 2078 (2014)CrossRef
33.
34.
S. Yu, L. Li, W. Zhang, H. Dong, D. Xu, Y. Jin, Vacuum 102, 43 (2014)CrossRef
35.
A. Kim, Y. Won, K. Woo, S. Jeong, J. Moon, Adv. Funct. Mater. 24, 2414 (2014)CrossRef
36.
K.H. Choi, J. Kim, Y.J. Noh, S.I. Na, H.K. Kim, Sol. Energy Mater. Sol. Cells 110, 147 (2013)CrossRef
37.
P. Atkins, J. de Paula, Atkins’ Physical Chemistry (Higher Education Press, Beijing, 2006), p. 1078
38.
39.
N. Serin, T. Serin, Ş. Horzum, Y. Celik, Semicond. Sci. Technol. 20, 398 (2005)CrossRef
40.
H. Takahashi, R. Okazaki, I. Terasaki, Y. Yasui, Phys. Rev. B 88(16), 3532 (2013)CrossRef
41.
Metadaten
Titel
Properties of nano-thick BaSnO3/Cu/BaSnO3 multilayer thin films: the role of substrate temperature
verfasst von
Muying Wu
Shihui Yu
Lin He
Lei Yang
Publikationsdatum
18.07.2016
Verlag
Springer US
Erschienen in
Journal of Materials Science: Materials in Electronics / Ausgabe 12/2016
Print ISSN: 0957-4522
Elektronische ISSN: 1573-482X
DOI
https://doi.org/10.1007/s10854-016-5392-6

Weitere Artikel der Ausgabe 12/2016

Identification and characteristics of core–shell ZnO/ZnO:Mg nanorods synthesized by hydrothermal method

Effect of multiple defects and substituted impurities on the band structure of graphene: a DFT study

Thermoelectric properties of directionally grown Bi2Ba2Co2Oδ/Ag composites: effect of annealing

Effect of SDS decoration of graphene on the rheological and electrical properties of graphene-filled epoxy/Ag composites

Dendritic α-Fe2O3 nanostructures: facile hydrothermal synthesis, characterization and microwave absorption

Characterization of titania thin films grown by dip-coating technique