Radiation-Induced Precipitates in a Self-ion Irradiated Cold-Worked 316 Austenitic Stainless Steel Used for PWR Baffle-Bolts

5 meV Ni++ and Fe++ ion irradiations were performed to investigate radiation-induced precipitates evolution in a cold-worked 316 austenitic stainless steel at high doses and temperatures. The irradiation conditions were 23 dpa at 380 °C, 130 dpa at 380 °C, 23 dpa at 500 °C, and 15 dpa at 600 °C. TEM selected electron diffraction (SAED), TEMTEM dark-field imaging and energy dispersive spectroscopy (EDS) Energy Dispersive Spectroscopy (EDS)mapping were used as complementary techniques to determine crystallography, morphology and chemical composition of radiation-induced precipitates. The precipitates were predominantly in form of the Ni–Si rich γ′ phase at all irradiation conditions. The EDS analysis further determined Ni–Si–Mo–P and Ni–Si–Mn rich precipitates after irradiation at 380 and 600 °C, respectively. The precipitates were found close to saturated state between 23 and 130 dpa at 380 °C irradiation conditions. A different effect of higher irradiation temperatures was found between 500 and 600 °C. In case of the irradiation to 23 dpa at 500 °C, the average size of precipitates was similar to irradiations at 380 °C, but the density was lower. However, the precipitates revealed large size and very low density following the irradiation to 15 dpa at 600 °C. The original dislocation network introduced by cold-working was found as dominant sink for intra-granular solute radiation-induced segregation (RIS) and possibly took place as primary nucleation site of radiation-induced precipitates at irradiation temperatures 380 and 500 °C. At the temperature 600 °C, the RIS at dislocation network almost vanished and the main nucleation sites became twin boundaries as more energetically favorable intra-granular sinks.