Reaction and Diffusion Paths of Water and Hydrogen on Rh Covered Black Titania

verfasst von: Imre Szenti, László Bugyi, Zoltán Kónya

Erschienen in: Topics in Catalysis | Ausgabe 12-13/2018

Einloggen

Aktivieren Sie unsere intelligente Suche um passende Fachinhalte oder Patente zu finden.

search-config
loading …

Abstract

The reactions of H2O, H2 D2 and CO with clean and rhodium covered black titania have been investigated by TDS, AES and sensitive temperature programmed work function (TP-WF) measurements to elucidate the complex interactions with this narrow bandgap material promising for visible light energy harvesting. Water formed molecular and dissociative adsorption states with positive outward dipole moments on the reduced, r–TiO2 (110). Surface hydroxyl groups decomposed to H2 and recombined to H2O in a broad temperature range, characterized by TDS peaks at 300, 355–377 and 470 K, which has been associated with surface inhomogeneity. On a strongly reduced, sr–TiO2 (110), a part of H atoms arising from OHa species dissolved in the titania at 200–500 K, and desorbed as H2O with Tp = 570, 670 and 750 K. Sub-monolayer TiOx films produced by stepwise heating on r–TiO2 (110) supported Rh particles suppressed the adsorption of hydrogen, but allowed its spillover to the support. Co-adsorption experiments with D2, H2, H2O and CO on the Rh covered r–TiO2 (110) were also performed. Saturating the Rh by CO at 330 K blocked the uptake of hydrogen on the metal, eliminating its spillover to the support. At 270 K saturation CO exposure removed the pre-adsorbed hydrogen, while at 200 K replaced a part of it decreasing the adsorption bond energy of the rest remained adsorbed. Co-adsorption data proved that the hydrogen desorption states with Tp = 470 and 570 K belong to the decomposition of hydroxyl groups on the r–TiO2 (110) support and at the Rh–TiOx interface, respectively. It is remarkable that the latter state can evolve in the presence of adsorbed CO, which exhibits reactivity towards the same interface.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Literatur
3.
Zurück zum Zitat Liu X, Zhu G, Wang X, Yuan X, Lin T, Huang F (2016) Adv Energy Mater 1600452 Liu X, Zhu G, Wang X, Yuan X, Lin T, Huang F (2016) Adv Energy Mater 1600452
4.
Zurück zum Zitat Fujiwara K, Deligiannakis Y, Skoutelis CG, Pratsinis SE (2014) Appl Catal B - Environ 154–155 9–15 Fujiwara K, Deligiannakis Y, Skoutelis CG, Pratsinis SE (2014) Appl Catal B - Environ 154–155 9–15
7.
Zurück zum Zitat Mor GK, Varghese OK, Paulose M, Ong KG, Grimes CA (2006) Thin Solid Films 496:42CrossRef Mor GK, Varghese OK, Paulose M, Ong KG, Grimes CA (2006) Thin Solid Films 496:42CrossRef
8.
Zurück zum Zitat Rather S, Mehraj-ud-din Z, Zacharia R, Hwang SW, Kim AR, Nahm KS (2009) Int J Hydrog Energy 34:961–966CrossRef Rather S, Mehraj-ud-din Z, Zacharia R, Hwang SW, Kim AR, Nahm KS (2009) Int J Hydrog Energy 34:961–966CrossRef
10.
Zurück zum Zitat Yin X-L, Calatayud M, Qiu H, Wang Y, Birkner A, Minot C, Wöll Ch (2008) Chem Phys Chem 9:253–256CrossRefPubMed Yin X-L, Calatayud M, Qiu H, Wang Y, Birkner A, Minot C, Wöll Ch (2008) Chem Phys Chem 9:253–256CrossRefPubMed
11.
Zurück zum Zitat Du Y, Petrik NG, Deskins NA, Wang Z, Henderson MA, Kimmelb GA, Lyubinetsky I (2012) Phys Chem Chem Phys 14:3066–3074CrossRefPubMed Du Y, Petrik NG, Deskins NA, Wang Z, Henderson MA, Kimmelb GA, Lyubinetsky I (2012) Phys Chem Chem Phys 14:3066–3074CrossRefPubMed
13.
14.
16.
19.
Zurück zum Zitat Schaub R, Thostrup P, Lopez N, Lægsgaard E, Stensgaard I, Nørskov JK, Besenbacher F (2001) Phys Rev Lett 87:266104CrossRefPubMed Schaub R, Thostrup P, Lopez N, Lægsgaard E, Stensgaard I, Nørskov JK, Besenbacher F (2001) Phys Rev Lett 87:266104CrossRefPubMed
20.
21.
Zurück zum Zitat Ketteler G, Yamamoto S, Bluhm H, Andersson K, Starr DE, Ogletree DF, Nilsson HOgasawara,A, Salmeron M (2007) J Phys Chem C 111:8278–8282CrossRef Ketteler G, Yamamoto S, Bluhm H, Andersson K, Starr DE, Ogletree DF, Nilsson HOgasawara,A, Salmeron M (2007) J Phys Chem C 111:8278–8282CrossRef
23.
Zurück zum Zitat Bugyi L, Berkó A, Óvári L, Kiss AM (2008) J Kiss Surf Sci 602:1650CrossRef Bugyi L, Berkó A, Óvári L, Kiss AM (2008) J Kiss Surf Sci 602:1650CrossRef
24.
Zurück zum Zitat Yang Y, Sushchikh M, Mills G, Metiu H, McFarland E (2004) Appl Surf Sci 229:346–351CrossRef Yang Y, Sushchikh M, Mills G, Metiu H, McFarland E (2004) Appl Surf Sci 229:346–351CrossRef
26.
Zurück zum Zitat Marques HP, Canário AR, Moutinho AMC, Teodoro OMND. (2009) Appl Surf Sci 255:7389–7393CrossRef Marques HP, Canário AR, Moutinho AMC, Teodoro OMND. (2009) Appl Surf Sci 255:7389–7393CrossRef
27.
Zurück zum Zitat Tao J, Cuan Q, Gong X-Q, Batzill M (2012) J Phys Chem C 116:20438–20446CrossRef Tao J, Cuan Q, Gong X-Q, Batzill M (2012) J Phys Chem C 116:20438–20446CrossRef
28.
Zurück zum Zitat Wu Z, Zhang W, Xiong F, Yuan Q, Jin Y, Yang J, Huang W (2014) Phys Chem Chem Phys 16:7051–7057CrossRefPubMed Wu Z, Zhang W, Xiong F, Yuan Q, Jin Y, Yang J, Huang W (2014) Phys Chem Chem Phys 16:7051–7057CrossRefPubMed
29.
31.
Zurück zum Zitat Li J, Lu G, Wu G, Mao D, Guo Y, Wang Y, Guo Y (2014) Catal Sci Technol 4:1268CrossRef Li J, Lu G, Wu G, Mao D, Guo Y, Wang Y, Guo Y (2014) Catal Sci Technol 4:1268CrossRef
32.
35.
36.
Zurück zum Zitat Sterchele S, Bortolus M, Biasi P, Mikkola J-P, Salmi T (2016) CR Chimie 19:1011–1020CrossRef Sterchele S, Bortolus M, Biasi P, Mikkola J-P, Salmi T (2016) CR Chimie 19:1011–1020CrossRef
38.
Zurück zum Zitat Farstad MH, Ragazzon D, Walle LE, Schaefer A, Sandell A, Borg A (2015) J Phys Chem C 119:6660–6669CrossRef Farstad MH, Ragazzon D, Walle LE, Schaefer A, Sandell A, Borg A (2015) J Phys Chem C 119:6660–6669CrossRef
39.
40.
41.
Metadaten
Titel
Reaction and Diffusion Paths of Water and Hydrogen on Rh Covered Black Titania
verfasst von
Imre Szenti
László Bugyi
Zoltán Kónya
Publikationsdatum
15.05.2018
Verlag
Springer US
Erschienen in
Topics in Catalysis / Ausgabe 12-13/2018
Print ISSN: 1022-5528
Elektronische ISSN: 1572-9028
DOI
https://doi.org/10.1007/s11244-018-0990-6

Weitere Artikel der Ausgabe 12-13/2018

Topics in Catalysis 12-13/2018 Zur Ausgabe

    Marktübersichten

    Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen.