Resource-Saving Technology for Preparing Nickel Superalloy VZh175 Using Substandard Waste

verfasst von: P. G. Min, V. E. Vadeev, V. V. Kramer

Erschienen in: Metallurgist | Ausgabe 9-10/2017

Einloggen

Aktivieren Sie unsere intelligente Suche um passende Fachinhalte oder Patente zu finden.

search-config
loading …

Abstract

A resource-saving technology is presented for processing up to 100% waste, including substandard material, of wrought alloy VZh175 for turbine disks. The technology has been developed in the scientific-production complex of VIAM and makes it possible the prepare alloy from waste no worse than that produced from fresh charge materials with respect to alloying content, impurities, structure, and mechanical properties. The cost is lower by 20–30% compared with that of alloy melted by industrial technology using 50% standard waste.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Literatur
1.
Zurück zum Zitat E. N. Kablov (ed.), Cast Gas Turbine Engine Blades: Alloys, Technology, Coatings, Nauka, Moscow (2006), pp. 293–445. E. N. Kablov (ed.), Cast Gas Turbine Engine Blades: Alloys, Technology, Coatings, Nauka, Moscow (2006), pp. 293–445.
2.
Zurück zum Zitat E. N. Kablov, “Innovative developments of FGUP VIAM GNTs RF for implementation of strategic areas for development of materials and technology and processes for the period up to 2030,” Aviats. Mater. Tekhnol., No. 1 (34), 3–33 (2015). E. N. Kablov, “Innovative developments of FGUP VIAM GNTs RF for implementation of strategic areas for development of materials and technology and processes for the period up to 2030,” Aviats. Mater. Tekhnol., No. 1 (34), 3–33 (2015).
3.
Zurück zum Zitat P. G. Min, A. V. Goryunov, and V. E. Vadeev, “Contemporary nickel superalloys and effective resource saving technology for their preparation,” Tekhnol. Metallov, No. 8, 12–23 (2014). P. G. Min, A. V. Goryunov, and V. E. Vadeev, “Contemporary nickel superalloys and effective resource saving technology for their preparation,” Tekhnol. Metallov, No. 8, 12–23 (2014).
4.
Zurück zum Zitat P. G. Min and V. V. Sidorov, “Experience of processing alloy ZhS32-VI casting waste in the FGUP VIAM scientific production complex for preparation of cast bar (charge) workpieces,” Aviats. Mater. Tekhnol., No. 4, 20–25 (2013). P. G. Min and V. V. Sidorov, “Experience of processing alloy ZhS32-VI casting waste in the FGUP VIAM scientific production complex for preparation of cast bar (charge) workpieces,” Aviats. Mater. Tekhnol., No. 4, 20–25 (2013).
5.
Zurück zum Zitat P. G. Min and V. V. Sidorov, “Resource saving technology for processing waste cast nickel superalloys,” Proc. Int. Sci.-Techn. Conf. Casting Production and Metallurgy 2014. Belarus (2014), pp. 118–123. P. G. Min and V. V. Sidorov, “Resource saving technology for processing waste cast nickel superalloys,” Proc. Int. Sci.-Techn. Conf. Casting Production and Metallurgy 2014. Belarus (2014), pp. 118–123.
6.
Zurück zum Zitat P. G. Min, V. E. Vadeev, V. A. Kalitsev, and V. V. Kramer, “Technology for preparing wrought alloy VZh175 for GTE turbine disks from standard waste,” Metallurg, No. 9, 76–80 (2015). P. G. Min, V. E. Vadeev, V. A. Kalitsev, and V. V. Kramer, “Technology for preparing wrought alloy VZh175 for GTE turbine disks from standard waste,” Metallurg, No. 9, 76–80 (2015).
7.
Zurück zum Zitat V. V. Sidorov, V. E. Rigin, O. B. Timofeeva, and P. G. Min, “Effect of silicon and phosphorus on heat-resistance properties and structural-phase transformations in single-crystals of high-strength alloy VZhM4-VI,” Aviats. Mater. Tekhnol., No. 3, 32–38 (2013). V. V. Sidorov, V. E. Rigin, O. B. Timofeeva, and P. G. Min, “Effect of silicon and phosphorus on heat-resistance properties and structural-phase transformations in single-crystals of high-strength alloy VZhM4-VI,” Aviats. Mater. Tekhnol., No. 3, 32–38 (2013).
8.
Zurück zum Zitat V. V. Sidorov, V. E. Rigin, P. G. Min, and Yu. I. Folomeikin, “Effect of phosphorus and silicon on the structure and properties of high-temperature cast alloys and development of effective methods for avoiding their unfavorable influence,” MiTOM, No. 6, 55–60 (2015). V. V. Sidorov, V. E. Rigin, P. G. Min, and Yu. I. Folomeikin, “Effect of phosphorus and silicon on the structure and properties of high-temperature cast alloys and development of effective methods for avoiding their unfavorable influence,” MiTOM, No. 6, 55–60 (2015).
9.
Zurück zum Zitat D. E. Kablov, V. V. Sidorov, and P. G. Min, “Effect of nitrogen impurity on structure of nickel superalloy ZhS30-VI single crystals and development of effective methods for refi nement,” Aviats. Mater. Tekhnol., No. 2, 32–36 (2012). D. E. Kablov, V. V. Sidorov, and P. G. Min, “Effect of nitrogen impurity on structure of nickel superalloy ZhS30-VI single crystals and development of effective methods for refi nement,” Aviats. Mater. Tekhnol., No. 2, 32–36 (2012).
10.
Zurück zum Zitat D. E. Kablov, V. V. Sidorov, S. A. Budinovskii, and P. G. Min, “Effect of sulfur impurity on heat-resistance of high-temperature alloy ZhS36-VI single crystals with a protective coating,” Aviats. Mater. Tekhnol., No. 1, 20–30 (2016). D. E. Kablov, V. V. Sidorov, S. A. Budinovskii, and P. G. Min, “Effect of sulfur impurity on heat-resistance of high-temperature alloy ZhS36-VI single crystals with a protective coating,” Aviats. Mater. Tekhnol., No. 1, 20–30 (2016).
11.
Zurück zum Zitat P. G. Min, V. E. Vadeev, and V. V. Kramer, “Refining of nonstandard waste of wrought nickel alloys in a vacuum-induction furnace,” Tekhnol. Metallov, No. 4, 8–13 (2015). P. G. Min, V. E. Vadeev, and V. V. Kramer, “Refining of nonstandard waste of wrought nickel alloys in a vacuum-induction furnace,” Tekhnol. Metallov, No. 4, 8–13 (2015).
12.
Zurück zum Zitat V. V. Sidorov, P. G. Min, Yu. I. Folomeikin, and V. E. Vadeev, “Effect of filtration rate for complexly alloyed nickel alloy through a ceramic foam filter on sulfur impurity content in metal,” Elektrometallurgiya, No. 5, 12–15 (2015). V. V. Sidorov, P. G. Min, Yu. I. Folomeikin, and V. E. Vadeev, “Effect of filtration rate for complexly alloyed nickel alloy through a ceramic foam filter on sulfur impurity content in metal,” Elektrometallurgiya, No. 5, 12–15 (2015).
13.
Zurück zum Zitat V. V. Sidorov, P. G. Min, V. T. Burtsev, et al., “Computer modeling and experimental study of refining in a vacuum of complexly alloyed rhenium-containing nickel melts from sulfur and silicon impurities,” Vestn. RFFI, No. 1(85), 32–36 (2015). V. V. Sidorov, P. G. Min, V. T. Burtsev, et al., “Computer modeling and experimental study of refining in a vacuum of complexly alloyed rhenium-containing nickel melts from sulfur and silicon impurities,” Vestn. RFFI, No. 1(85), 32–36 (2015).
14.
Zurück zum Zitat P. G. Min and V. V. Sidorov, “Refining nickel superalloy ZhS32-VI waste from silicon impurity under vacuum-induction melting conditions,” Trudy VIAM, No. 9, Art. 01 (2014), www.viam-works.ru, acces. 05.04.2016. P. G. Min and V. V. Sidorov, “Refining nickel superalloy ZhS32-VI waste from silicon impurity under vacuum-induction melting conditions,” Trudy VIAM, No. 9, Art. 01 (2014), www.​viam-works.​ru, acces. 05.04.2016.
15.
Zurück zum Zitat V. V. Sidorov and P. G. Min, “Refining complexly alloyed nickel melt from sulfur impurity with melting in a vacuum-induction furnace. Parts 1 and 2,” Elektrometallurgiya, No. 3, 18–23 (2014); No. 5, 26–30 (2014). V. V. Sidorov and P. G. Min, “Refining complexly alloyed nickel melt from sulfur impurity with melting in a vacuum-induction furnace. Parts 1 and 2,” Elektrometallurgiya, No. 3, 18–23 (2014); No. 5, 26–30 (2014).
16.
Zurück zum Zitat V. V. Sidorov, D. E. Kablov, P. G. Min, and V. E. Vadeev, “Refining complexly-alloyed nickel alloy ZhS32-VI from silicon and phosphorus impurities by melt directional solidification with slow rates of solidification front movement,” Tekhnol. Metallov, No. 3, 2–7 (2016). V. V. Sidorov, D. E. Kablov, P. G. Min, and V. E. Vadeev, “Refining complexly-alloyed nickel alloy ZhS32-VI from silicon and phosphorus impurities by melt directional solidification with slow rates of solidification front movement,” Tekhnol. Metallov, No. 3, 2–7 (2016).
17.
Zurück zum Zitat E. N. Kablov and V. V. Sidorov, “Microalloying with REM – contemporary technology for improving the properties of cast nickel superalloys,” Perspekt. Mater., No. 1, 23–24 (2001). E. N. Kablov and V. V. Sidorov, “Microalloying with REM – contemporary technology for improving the properties of cast nickel superalloys,” Perspekt. Mater., No. 1, 23–24 (2001).
18.
Zurück zum Zitat E. M. Savitskii and V. F. Terekhova, Rare-Earth Metal Metallurgy, Nauka, Moscow (1975). E. M. Savitskii and V. F. Terekhova, Rare-Earth Metal Metallurgy, Nauka, Moscow (1975).
19.
Zurück zum Zitat E. A. Mekhanik, P. G. Min, N. V. Gundobin, and G. Yu. Rastegaeva, “Development of procedures for determining the weight fraction of sulfur in nickel superalloys and steels in the concentration range from 0.0001 to 0.0009%,” Trudy VIAM, No. 9, Art. 12 (2014), www.viam-works.ru, acces. 05.04.2016. E. A. Mekhanik, P. G. Min, N. V. Gundobin, and G. Yu. Rastegaeva, “Development of procedures for determining the weight fraction of sulfur in nickel superalloys and steels in the concentration range from 0.0001 to 0.0009%,” Trudy VIAM, No. 9, Art. 12 (2014), www.​viam-works.​ru, acces. 05.04.2016.
Metadaten
Titel
Resource-Saving Technology for Preparing Nickel Superalloy VZh175 Using Substandard Waste
verfasst von
P. G. Min
V. E. Vadeev
V. V. Kramer
Publikationsdatum
09.02.2017
Verlag
Springer US
Erschienen in
Metallurgist / Ausgabe 9-10/2017
Print ISSN: 0026-0894
Elektronische ISSN: 1573-8892
DOI
https://doi.org/10.1007/s11015-017-0397-9

Weitere Artikel der Ausgabe 9-10/2017

Metallurgist 9-10/2017 Zur Ausgabe

    Marktübersichten

    Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen.