Skip to main content
Erschienen in: Metallurgical and Materials Transactions A 4/2015

01.04.2015

Role of Preparation Method on the Microstructure and Mechanical Properties of PPy/Ni Organic–Inorganic Hybrid Bilayer Coatings on Carbon Steel

verfasst von: A. M. Torres-Huerta, M. A. Dominguez-Crespo, A. Alanis-Valdelamar, E. Onofre-Bustamante, M. L. Escudero, M. C. García-Alonso, J. A. Lois-Correa

Erschienen in: Metallurgical and Materials Transactions A | Ausgabe 4/2015

Einloggen

Aktivieren Sie unsere intelligente Suche um passende Fachinhalte oder Patente zu finden.

search-config
loading …

Abstract

The efficacy of the conducting polymers as coating on a metallic substrate is strongly dependent on the manner how they are applied. Polypyrrole (PPy)/Ni organic–inorganic hybrid coatings were electropolymerized on commercial carbon steel (AISI 1018) by combining potentiostatic and potentiodynamic techniques. In first instance, it was analyzed the electrodeposition of PPy using a constant potential regime and cyclic voltammetry techniques evaluating different synthesis parameters such as deposition time, applied potential, and potential cycles, respectively. Thereafter, it was used a potentiostatic method to obtain PPy/Ni bilayer films. The morphological, mechanical, and adhesion properties of these films depend on the synthesis parameters. The results revealed that polypyrrole films formed by both methods provide a globular-type structure, although coatings produced by cyclic voltammetry are denser and slightly thicker than those produced potentiostatically. Ni (oxide/hydroxide) particles are capable of sealing the pores of globular PPy coatings, thus increasing the hardness of the carbon steel (CS)/PPy/Ni system. As a result of the study, we have seen that PPy/Ni bilayer films are more uniform, compact and enhanced the hardness when the PPy is obtained by cyclic voltammetry than that observed for potentiostatic approach. Specifically, when four potential cycles are used to electropolymerized pyrrole, the more convenience properties in the CS/PPy/Ni arrangement are obtained.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Literatur
1.
Zurück zum Zitat H Hirakawa, EJ Louis, AG Macdiarmid, CK Chiang, AJ Heeger (1977) Synthesis of electrically conducting organic polymers: Halogen derivates of polyacetylene J Chem Soc Chem Commun 1977:579. H Hirakawa, EJ Louis, AG Macdiarmid, CK Chiang, AJ Heeger (1977) Synthesis of electrically conducting organic polymers: Halogen derivates of polyacetylene J Chem Soc Chem Commun 1977:579.
2.
Zurück zum Zitat CK Chiang, CR Fisher, YW Park, AJ Heeger, H Shirakawa, EJ Louis, SC Gau, AG Macdiarmid (1977) Phys Rev Lett 39:1098.CrossRef CK Chiang, CR Fisher, YW Park, AJ Heeger, H Shirakawa, EJ Louis, SC Gau, AG Macdiarmid (1977) Phys Rev Lett 39:1098.CrossRef
3.
Zurück zum Zitat C.K. Chiang, M. A. Druy, S.C. Gau, AJ Heeger, E.J. Louis, A.G. MacDiarmid, YW Park, H Shirakawa (1978) J Am Chem Soc 100: 1013.CrossRef C.K. Chiang, M. A. Druy, S.C. Gau, AJ Heeger, E.J. Louis, A.G. MacDiarmid, YW Park, H Shirakawa (1978) J Am Chem Soc 100: 1013.CrossRef
4.
Zurück zum Zitat A.G. MacDiarmid: Chem. Comm., 2003, pp. 1–4. A.G. MacDiarmid: Chem. Comm., 2003, pp. 1–4.
5.
Zurück zum Zitat V.M. Schmidt, D. Tegtmeyer, J. Heitbaum, Transport of protons and water through polyaniline membranes studied with on-line mass spectrometry, J. Electroanal. Chem. 385 (1995) 149-155.CrossRef V.M. Schmidt, D. Tegtmeyer, J. Heitbaum, Transport of protons and water through polyaniline membranes studied with on-line mass spectrometry, J. Electroanal. Chem. 385 (1995) 149-155.CrossRef
7.
Zurück zum Zitat J.C. Gustafsson-Carlberg, O. Inganäs, M.R. Andersson, C. Booth, A. Azens, C.G. Granqvist, Electrochim. Acta 40 (1995) 2233–35.CrossRef J.C. Gustafsson-Carlberg, O. Inganäs, M.R. Andersson, C. Booth, A. Azens, C.G. Granqvist, Electrochim. Acta 40 (1995) 2233–35.CrossRef
8.
Zurück zum Zitat T.F. Otero, J. Rodriguez, E. Angulo, C. Santamaría, Artificial muscles from bilayer structures, Synth. Met. 57 (1993) 3713–17.CrossRef T.F. Otero, J. Rodriguez, E. Angulo, C. Santamaría, Artificial muscles from bilayer structures, Synth. Met. 57 (1993) 3713–17.CrossRef
9.
Zurück zum Zitat D.W. DeBerry, Modification of the electrochemical and corrosion behavior of stainless steels with an electroactive coating, J. Electrochem. Soc. 132 (1985) 1022–26.CrossRef D.W. DeBerry, Modification of the electrochemical and corrosion behavior of stainless steels with an electroactive coating, J. Electrochem. Soc. 132 (1985) 1022–26.CrossRef
10.
11.
12.
13.
Zurück zum Zitat H.N.T. Le, B. García, C. Deslouis, Q.L. Xuan: J. Appl. Electrochem. 32 (2002) 105–10.CrossRef H.N.T. Le, B. García, C. Deslouis, Q.L. Xuan: J. Appl. Electrochem. 32 (2002) 105–10.CrossRef
14.
Zurück zum Zitat J. Petitjean, S. Aeiyach, J.C. Lacroix, P.C. Lacaze: J. Electroanal. Chem. 478 (1999) 92–100.CrossRef J. Petitjean, S. Aeiyach, J.C. Lacroix, P.C. Lacaze: J. Electroanal. Chem. 478 (1999) 92–100.CrossRef
16.
Zurück zum Zitat I. A. Kartsonakis, E.P. Koumoulos, A.C. Balaskas, G.S. Pappas, C.A. Charitidis, G.C. Kordas: Corr. Sci. 57 (2012) 56–66.CrossRef I. A. Kartsonakis, E.P. Koumoulos, A.C. Balaskas, G.S. Pappas, C.A. Charitidis, G.C. Kordas: Corr. Sci. 57 (2012) 56–66.CrossRef
17.
Zurück zum Zitat I György: in Monographs in Electrochemistry 2nd ed, F. Scholz, eds. Springer, New York, 2012, pp. 83–133. I György: in Monographs in Electrochemistry 2nd ed, F. Scholz, eds. Springer, New York, 2012, pp. 83–133.
18.
Zurück zum Zitat P.A. Sørensen, S. Kiil, K. Dam-Johansen, C.E. Weinell: J. Coat. Technol. Res. 6 (2009) 135–76.CrossRef P.A. Sørensen, S. Kiil, K. Dam-Johansen, C.E. Weinell: J. Coat. Technol. Res. 6 (2009) 135–76.CrossRef
19.
Zurück zum Zitat E. Armelin, A. Meneguzzi, C.A. Ferreira, C. Alemán: Surf. Coat. Technol. 203 (2009) 3763–69.CrossRef E. Armelin, A. Meneguzzi, C.A. Ferreira, C. Alemán: Surf. Coat. Technol. 203 (2009) 3763–69.CrossRef
20.
Zurück zum Zitat M. Graczyk-Zajac, S.Y Vassiliev, M.A Vorotyntsev, G.A. Tsirlina: J. Solid State Electrochem. 14 (2010) 2039–48.CrossRef M. Graczyk-Zajac, S.Y Vassiliev, M.A Vorotyntsev, G.A. Tsirlina: J. Solid State Electrochem. 14 (2010) 2039–48.CrossRef
21.
22.
23.
Zurück zum Zitat S. Zor, F. Kandemirli, E. Yakar, T. Arslan: Prot. Met. Phys. Chem. Surf. 46 (2010) 110–16.CrossRef S. Zor, F. Kandemirli, E. Yakar, T. Arslan: Prot. Met. Phys. Chem. Surf. 46 (2010) 110–16.CrossRef
24.
Zurück zum Zitat S.U. Rahman, M.A. Abul-Hamayel, B.J.A. Aleem: Surf. Coat. Technol. 200 (2006) 2948–54.CrossRef S.U. Rahman, M.A. Abul-Hamayel, B.J.A. Aleem: Surf. Coat. Technol. 200 (2006) 2948–54.CrossRef
26.
27.
Zurück zum Zitat F.J. Rodriguez, L.A. García de la Rosa, A. Alatorre, J. Ibãnez, L. Godinez, S. Gutierrez, P. Herrasti: Prog. Org. Coat. 60 (2007) 297–302.CrossRef F.J. Rodriguez, L.A. García de la Rosa, A. Alatorre, J. Ibãnez, L. Godinez, S. Gutierrez, P. Herrasti: Prog. Org. Coat. 60 (2007) 297–302.CrossRef
28.
Zurück zum Zitat M. Sabouri, T. Shahrabi, H.R. Faridi, M.G. Hosseini: Prog. Org. Coat. 64 (2009) 429–34.CrossRef M. Sabouri, T. Shahrabi, H.R. Faridi, M.G. Hosseini: Prog. Org. Coat. 64 (2009) 429–34.CrossRef
29.
Zurück zum Zitat L.A. Dobrzanski, M. Drak, J. Trzaska: J. Mater. Proc. Technol. 164-165 (2005) 795–804.CrossRef L.A. Dobrzanski, M. Drak, J. Trzaska: J. Mater. Proc. Technol. 164-165 (2005) 795–804.CrossRef
30.
Zurück zum Zitat P. Montoya, J. Calderón, F. Jaramillo: Scientia et Technica 13 (2007) 19–24. P. Montoya, J. Calderón, F. Jaramillo: Scientia et Technica 13 (2007) 19–24.
31.
Zurück zum Zitat C. A. Ferreira, S.C. Domenech, P.C. Lacaze: J. Appl. Electrochem. 31 (2001) 49–56.CrossRef C. A. Ferreira, S.C. Domenech, P.C. Lacaze: J. Appl. Electrochem. 31 (2001) 49–56.CrossRef
32.
33.
Zurück zum Zitat W.D Callister, Introducción a la Ciencia e Ingeniería de los Materiales 2, Reverté, España, 2007. W.D Callister, Introducción a la Ciencia e Ingeniería de los Materiales 2, Reverté, España, 2007.
34.
Zurück zum Zitat C.P. Poole, F.J. Owens, Introducción a la Nanotecnología, Reverté, Barcelona, 2003. C.P. Poole, F.J. Owens, Introducción a la Nanotecnología, Reverté, Barcelona, 2003.
35.
Zurück zum Zitat E. Bardal, Corrosion and Protection, Springer, London, 2007. E. Bardal, Corrosion and Protection, Springer, London, 2007.
36.
Zurück zum Zitat P. Herrasti, P. Ocon, A. Ibanez, E. Fatas: J. Appl. Electrochem. 33 (2003) 533–40.CrossRef P. Herrasti, P. Ocon, A. Ibanez, E. Fatas: J. Appl. Electrochem. 33 (2003) 533–40.CrossRef
37.
Zurück zum Zitat J. Bonastre, P. Garcés, F. Huerta, C. Quijada, L.G. Andion, F. Cases: Corros. Sci. 48 (2006) 1122–36.CrossRef J. Bonastre, P. Garcés, F. Huerta, C. Quijada, L.G. Andion, F. Cases: Corros. Sci. 48 (2006) 1122–36.CrossRef
38.
Zurück zum Zitat M.G. Hosseini, M. Sabouri, T. Shahrabi: Mater. Corros. 57 (2006) 407–10.CrossRef M.G. Hosseini, M. Sabouri, T. Shahrabi: Mater. Corros. 57 (2006) 407–10.CrossRef
39.
Zurück zum Zitat M. Sabouri, T. Shahrabi, M.G. Hosseini: Russ. J. Electrochem. 43 (2007) 1390–97.CrossRef M. Sabouri, T. Shahrabi, M.G. Hosseini: Russ. J. Electrochem. 43 (2007) 1390–97.CrossRef
40.
Zurück zum Zitat M. Sabouri, T. Shahrabi, M.G. Hosseini: Mater. Corros 59 (2008) 814–18.CrossRef M. Sabouri, T. Shahrabi, M.G. Hosseini: Mater. Corros 59 (2008) 814–18.CrossRef
41.
42.
43.
Zurück zum Zitat M. Nakayama, J. Yano, K. Nakaoka, K. Ogura: J Solid State Electrochem. 18 (2002) 57–62. M. Nakayama, J. Yano, K. Nakaoka, K. Ogura: J Solid State Electrochem. 18 (2002) 57–62.
44.
45.
Zurück zum Zitat J.I. Martins, S.C. Costa, M. Bazzaoui, G. Goncalves, E. Fortunato, R. Martins: Electrochim. Acta 51 (2006) 5802–10.CrossRef J.I. Martins, S.C. Costa, M. Bazzaoui, G. Goncalves, E. Fortunato, R. Martins: Electrochim. Acta 51 (2006) 5802–10.CrossRef
46.
Zurück zum Zitat M. Bazzaoui, E.A. Bazzaoui, L. Martins, J.I. Martins: Synth. Met. 128 (2002) 103–14.CrossRef M. Bazzaoui, E.A. Bazzaoui, L. Martins, J.I. Martins: Synth. Met. 128 (2002) 103–14.CrossRef
47.
Zurück zum Zitat S. Roux, P. Audebert, J. Pagetti, M. Roche: J. Mater. Chem. 11 (2001) 3360–66.CrossRef S. Roux, P. Audebert, J. Pagetti, M. Roche: J. Mater. Chem. 11 (2001) 3360–66.CrossRef
48.
49.
Zurück zum Zitat H. Bhandari, R. Srivastav, V. Choudhary, S.K. Dhawan: Thin solid films 519 (2010) 1031–39.CrossRef H. Bhandari, R. Srivastav, V. Choudhary, S.K. Dhawan: Thin solid films 519 (2010) 1031–39.CrossRef
50.
Zurück zum Zitat E. Machnikova, M. Pazderova, M. Bazzaoui, N. Hackerman. Surf. Coat. Technol. 202 (2008) 1543–50.CrossRef E. Machnikova, M. Pazderova, M. Bazzaoui, N. Hackerman. Surf. Coat. Technol. 202 (2008) 1543–50.CrossRef
51.
52.
Zurück zum Zitat A.C. Balaskas, I.A. Kartsonakis, G. Kordas, A.M. Cabral, P.J. Morais: Prog Org. Coat. 71 (2011) 181–87.CrossRef A.C. Balaskas, I.A. Kartsonakis, G. Kordas, A.M. Cabral, P.J. Morais: Prog Org. Coat. 71 (2011) 181–87.CrossRef
53.
Zurück zum Zitat N.C.T. Martins, T. MouraeSilva, M.F. Montemor, J.C.S. Fernandes, M.G.S. Ferreira (2008) Electrochim. Acta 53:4754–63.CrossRef N.C.T. Martins, T. MouraeSilva, M.F. Montemor, J.C.S. Fernandes, M.G.S. Ferreira (2008) Electrochim. Acta 53:4754–63.CrossRef
54.
Zurück zum Zitat N. Attarzadeh, K. Raeissi, M.A. Golozar: Prog. Org. Coat. 63 (2008) 167–74.CrossRef N. Attarzadeh, K. Raeissi, M.A. Golozar: Prog. Org. Coat. 63 (2008) 167–74.CrossRef
55.
56.
Zurück zum Zitat P. Pawar, M.G. Wankhede, P.P. Patil, S.R. Sainkar: Mater. Sci. Eng. A 347 (2003) 365–73.CrossRef P. Pawar, M.G. Wankhede, P.P. Patil, S.R. Sainkar: Mater. Sci. Eng. A 347 (2003) 365–73.CrossRef
57.
58.
59.
60.
Zurück zum Zitat M. Fukuyama, N. Nanai, T. Kojima, Y. Kudoh, S. Yoshimura: Synth. Met. 58 (1993) 367–71.CrossRef M. Fukuyama, N. Nanai, T. Kojima, Y. Kudoh, S. Yoshimura: Synth. Met. 58 (1993) 367–71.CrossRef
62.
Zurück zum Zitat A.J.G. Zarbin, M.-A. De Paoli, O.L. Alves: Synth. Met. 99 (1999) 227–35.CrossRef A.J.G. Zarbin, M.-A. De Paoli, O.L. Alves: Synth. Met. 99 (1999) 227–35.CrossRef
63.
Zurück zum Zitat F. Chen, G. Shi, M. Fu, L. Qu, X. Hong: Synth. Met. 132 (2003) 125–32.CrossRef F. Chen, G. Shi, M. Fu, L. Qu, X. Hong: Synth. Met. 132 (2003) 125–32.CrossRef
65.
Zurück zum Zitat A. Demoulin, C. Trigance, D. Neff, E. Foy, P. Dillmann, V. L’Hostis: Corros. Sci. 52 (2010) 3168–79.CrossRef A. Demoulin, C. Trigance, D. Neff, E. Foy, P. Dillmann, V. L’Hostis: Corros. Sci. 52 (2010) 3168–79.CrossRef
66.
67.
Zurück zum Zitat G.S. Goncalves, A.F. Baldissera, L.F. Rodrigues Jr., E.M.A. Martini, C.A. Ferreira: Synth. Met. 161 (2011) 313–23.CrossRef G.S. Goncalves, A.F. Baldissera, L.F. Rodrigues Jr., E.M.A. Martini, C.A. Ferreira: Synth. Met. 161 (2011) 313–23.CrossRef
69.
Zurück zum Zitat Z. Deng, W.H. Smyrl, S. White: J. Electrochem. Soc. 136 (1989) 2152–58.CrossRef Z. Deng, W.H. Smyrl, S. White: J. Electrochem. Soc. 136 (1989) 2152–58.CrossRef
70.
72.
Zurück zum Zitat K. Naio, M. Takeda, H. Kanno, M. Sakakura, A. Shimada: Electrochim. Acta 45(2000) 1727–31.CrossRef K. Naio, M. Takeda, H. Kanno, M. Sakakura, A. Shimada: Electrochim. Acta 45(2000) 1727–31.CrossRef
73.
Zurück zum Zitat M. Bazzaoui, J.I. Martins, S.C. Costa, E.A. Bazzaoui, T.C. Reis, L. Martins: Electrochim. Acta 51 (2006) 2417–26.CrossRef M. Bazzaoui, J.I. Martins, S.C. Costa, E.A. Bazzaoui, T.C. Reis, L. Martins: Electrochim. Acta 51 (2006) 2417–26.CrossRef
74.
Zurück zum Zitat S.O Lee, T. Tran, B. H. Jung, S. J. Kim, M. J. Kim (2007) Hydrometallurgy 87:91–99.CrossRef S.O Lee, T. Tran, B. H. Jung, S. J. Kim, M. J. Kim (2007) Hydrometallurgy 87:91–99.CrossRef
75.
Zurück zum Zitat A. Brenner, Electrodeposition of Alloys Vol. II, Nickel Academic Press, New York, 1963. A. Brenner, Electrodeposition of Alloys Vol. II, Nickel Academic Press, New York, 1963.
76.
Zurück zum Zitat W.H. Safranek, The Properties of Electrodeposited Metals and Alloys, second ed., American Electroplaters and Surface Finishers Society, Florida, 1986. W.H. Safranek, The Properties of Electrodeposited Metals and Alloys, second ed., American Electroplaters and Surface Finishers Society, Florida, 1986.
77.
Zurück zum Zitat A.M. Kumar, P. Sudhagar, A. Fujishima, Z.M. Gasem (2014) Polymer 55:5417–24.CrossRef A.M. Kumar, P. Sudhagar, A. Fujishima, Z.M. Gasem (2014) Polymer 55:5417–24.CrossRef
78.
Zurück zum Zitat R.A. Mahesh, R. Jayaganthan, S. Prakash: J. Mater. Proc. Technol. 209 (2009) 3501–10.CrossRef R.A. Mahesh, R. Jayaganthan, S. Prakash: J. Mater. Proc. Technol. 209 (2009) 3501–10.CrossRef
79.
Zurück zum Zitat M.P. Argañaraza, S.B. Ribotta, M.E. Folquer, L.M. Gassa, G. Benitez, M.E. Vela, R.C. Salvarezza (2011) Electrochim. Acta 56:5898–903.CrossRef M.P. Argañaraza, S.B. Ribotta, M.E. Folquer, L.M. Gassa, G. Benitez, M.E. Vela, R.C. Salvarezza (2011) Electrochim. Acta 56:5898–903.CrossRef
80.
Zurück zum Zitat K. Zangeneh-Madar, S.M. Monir Vaghefi: Surf. Coat. Technol. 182 (2004) 65–71.CrossRef K. Zangeneh-Madar, S.M. Monir Vaghefi: Surf. Coat. Technol. 182 (2004) 65–71.CrossRef
81.
Metadaten
Titel
Role of Preparation Method on the Microstructure and Mechanical Properties of PPy/Ni Organic–Inorganic Hybrid Bilayer Coatings on Carbon Steel
verfasst von
A. M. Torres-Huerta
M. A. Dominguez-Crespo
A. Alanis-Valdelamar
E. Onofre-Bustamante
M. L. Escudero
M. C. García-Alonso
J. A. Lois-Correa
Publikationsdatum
01.04.2015
Verlag
Springer US
Erschienen in
Metallurgical and Materials Transactions A / Ausgabe 4/2015
Print ISSN: 1073-5623
Elektronische ISSN: 1543-1940
DOI
https://doi.org/10.1007/s11661-015-2766-y

Weitere Artikel der Ausgabe 4/2015

Metallurgical and Materials Transactions A 4/2015 Zur Ausgabe

    Marktübersichten

    Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen.