Sintering behavior and microwave dielectric properties of V5+ substituted Li3Mg2SbO6 ceramics
Erschienen in: Journal of Materials Science: Materials in Electronics | Ausgabe 15/2019
EinloggenAktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.
Wählen Sie Textabschnitte aus um mit Künstlicher Intelligenz passenden Patente zu finden. powered by
Markieren Sie Textabschnitte, um KI-gestützt weitere passende Inhalte zu finden. powered by
Abstract
The Li3Mg2(Sb1−xVx)O6 (0.01 ≤ x ≤ 0.04) ceramics have been synthesized by the solid-state reaction method. The effects of V5+ ion substitution on the sinterability, phase composition and microwave dielectric properties of Li3Mg2(Sb1−xVx)O6 ceramics were investigated. The dehiscence and secondary phase in Li3Mg2SbO6-based ceramics could be effectively inhibited by partial substitution of V5+ on the Sb5+ sites. The optimum microwave dielectric properties (εr = 11.2, Qxf = 54,700 GHz, τf = − 20 ppm/°C) were obtained for Li3Mg2(Sb1−xVx)O6 (x = 0.03) ceramics sintered at 1250 °C. The εr of Li3Mg2(Sb0.97V0.03)O6 ceramics was mainly depended on ionic polarizability as well as density, whereas its Qxf was strongly dominated by average grain size.