01.04.2013 | Original Paper | Ausgabe 4/2013

Journal of Polymer Research 4/2013

Solid and melt-state 1H NMR studies of relaxation processes in isotactic polypropylenes

Zeitschrift:
Journal of Polymer Research > Ausgabe 4/2013
Autoren:
Dušan Olčák, Viktor Hronský, Oľga Fričová, Mária Kovaľaková, Peter Duranka, Ivan Chodák

Abstract

Relaxation processes in metallocene and Ziegler–Natta isotactic polypropylenes were studied using 1H MAS NMR spectroscopy. 1H MAS NMR spectra and laboratory-frame spin-lattice relaxation times T 1(1H) were measured within the temperature range 30–190 °C, which covers the glass transition relaxation and melting processes of both polymers. Splitting of the peak related to protons in amorphous regions of the studied samples into three sharp peaks at elevated temperatures made it possible to determine the spin-lattice relaxation times T 1(1H) for particular iPP proton groups. The melt-state NMR spectra of ZN-iPP display three sharp peaks with three additional weak peaks positioned on the less shielded side. Entanglements of ZN-iPP chains are suggested as a possible source of these additional peaks. The spectra of m-iPP indicate substantially fewer entanglements due to its lower molecular weight compared with that of ZN-iPP. The temperature dependences of the relaxation times T 1(1H) relating to specific groups of ZN-iPP were shown to reach minima associated with the motions of amorphous chain segments (glass transition relaxation), which are very close to the melting temperature and minima associated with the melting process. Each of the T 1(1H) temperature dependences for m-iPP shows only one minimum associated with the melting process. When the particular relaxation times T 1, min relating to the minima that occur above the melting temperatures were considered, and these relaxation times were compared for the same proton groups in different samples, significant differences in the relaxation times were observed between samples. Polymer chain motion was more restricted in melted ZN-iPP than in m-iPP, as inferred from the T 1, min values.

Bitte loggen Sie sich ein, um Zugang zu diesem Inhalt zu erhalten

Sie möchten Zugang zu diesem Inhalt erhalten? Dann informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 69.000 Bücher
  • über 500 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Umwelt
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Testen Sie jetzt 30 Tage kostenlos.

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 50.000 Bücher
  • über 380 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Umwelt
  • Maschinenbau + Werkstoffe




Testen Sie jetzt 30 Tage kostenlos.

Literatur
Über diesen Artikel

Weitere Artikel der Ausgabe 4/2013

Journal of Polymer Research 4/2013 Zur Ausgabe

Premium Partner

    Marktübersichten

    Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen. 

    Bildnachweise