Sr₃GdLi(PO₄)₃F: Sm³⁺ phosphor: preparation and luminescence properties evaluation

A series of Sr₃Gd_1−xLi(PO₄)₃F: xSm³⁺ (x = 0.02, 0.04, 0.06, 0.08) phosphors were synthesized by a high-temperature solid state method. The Sm³⁺ activated Sr₃GdLi(PO₄)₃F phosphors can be efficiently excited by the wavelengths in the range from 350 to 450 nm, which matches perfectly with that of the commercial near-UV LED chips. The optimal doping concentration of Sr₃Gd_1−xLi(PO₄)₃F: xSm³⁺ phosphors was determined to be x = 0.04, corresponding to the quantum efficiency of 2.23%, and the CIE chromaticity coordinates (x = 0.5172, y = 0.4641). The concentration quenching mechanism of Sm³⁺ in Sr₃GdLi(PO₄)₃F host is mainly attributed to the dipole–dipole interaction, which was confirmed by the fluorescent lifetimes. The effect of temperature on the photoluminescence property of Sr₃GdLi(PO₄)₃F: Sm³⁺ was investigated. 90% of the intensity is preserved at 150 °C. In addition, a white light emitting diode (WLED) lamp was fabricated by a 405 nm n-UV LED chip coated with Sr₃Gd_0.96Li(PO₄)₃F:0.04Sm³⁺ phosphor and commercial yellow phosphor (YAG: Ce³⁺) of a certain mass ratio. The present work indicates that the Sr₃GdLi(PO₄)₃F: Sm³⁺ orange–red-emitting phosphors tend to be potential application in n-UV WLED.