Status of Using, Manufacturing and Testing of Ethylene Pyrolysis Furnace Tubes in China

verfasst von : T. Chen, X. D. Chen, Y. R. Lu, Z. B. Ai, Z. C. Fan

Erschienen in: Engineering Asset Management - Systems, Professional Practices and Certification

Verlag: Springer International Publishing

Aktivieren Sie unsere intelligente Suche um passende Fachinhalte oder Patente zu finden.

search-config
loading …

Abstract

In this paper, the problems of short service life, main failure modes and failure mechanisms of ethylene pyrolysis furnace tubes in China were summed up through service condition survey on ethylene pyrolysis furnace tubes in the domestic nine petrochemical corporations, compared with the situation of two ethylene enterprises in the developed countries. Chemical composition, tensile properties at room temperature and high-temperature stress rupture properties of furnace tubes and fittings were obtained through experiments performed on furnace tubes and fittings from six furnace tube manufacturing enterprises. The revision suggestion of centrifugally cast alloy tubes standard and the relationship between newly manufactured furnace tubes and fittings performance and serviced furnace tube failure modes were also discussed in present article.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Wirtschaft"

Online-Abonnement

Mit Springer Professional "Wirtschaft" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 340 Zeitschriften

aus folgenden Fachgebieten:

  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Versicherung + Risiko




Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Literatur
1.
Zurück zum Zitat Guan KS, Xu H, Wang ZW (2005) Quantitative study of creep cavity area of HP40 furnace tubes. Nucl Eng Des 235:1447–1456CrossRef Guan KS, Xu H, Wang ZW (2005) Quantitative study of creep cavity area of HP40 furnace tubes. Nucl Eng Des 235:1447–1456CrossRef
2.
Zurück zum Zitat Liu CJ, Chen Y (2011) Variations of the microstructure and mechanical properties of HP40Nb hydrogen reformer tube with time at elevated temperature. Mater Des 32:2507–2512CrossRef Liu CJ, Chen Y (2011) Variations of the microstructure and mechanical properties of HP40Nb hydrogen reformer tube with time at elevated temperature. Mater Des 32:2507–2512CrossRef
3.
Zurück zum Zitat Branzaa T, Deschaux-Beaumeb F, Sierrab G, Loursa P (2009) Study and prevention of cracking during weld-repair of heat-resistant cast steels. J Mater Process Technol 209:536–547CrossRef Branzaa T, Deschaux-Beaumeb F, Sierrab G, Loursa P (2009) Study and prevention of cracking during weld-repair of heat-resistant cast steels. J Mater Process Technol 209:536–547CrossRef
4.
Zurück zum Zitat Swaminathan J, Guguloth K, Gunjan MK, Roy P, Ghosh R (2008) Failure analysis and remaining life assessment of service exposed primary reformer heater tubes. Eng Fail Anal 15:311–331CrossRef Swaminathan J, Guguloth K, Gunjan MK, Roy P, Ghosh R (2008) Failure analysis and remaining life assessment of service exposed primary reformer heater tubes. Eng Fail Anal 15:311–331CrossRef
5.
Zurück zum Zitat Chen T, Chen XD, Lu YR, Lian XM, Ye J (2012) Influence of grain shape on rupture life of centrifugal casting 25Cr35Ni-Nb alloy tubes. In: Proceeding of ICPVT-13, London, UK Chen T, Chen XD, Lu YR, Lian XM, Ye J (2012) Influence of grain shape on rupture life of centrifugal casting 25Cr35Ni-Nb alloy tubes. In: Proceeding of ICPVT-13, London, UK
6.
Zurück zum Zitat HG/T 2601-2011 Centrifugal casting alloy tubes service of pressure bearing at high temperature HG/T 2601-2011 Centrifugal casting alloy tubes service of pressure bearing at high temperature
7.
Zurück zum Zitat HG/T 3673-2011 Static cast fittings of furnace for service pressure bearing at high temperature HG/T 3673-2011 Static cast fittings of furnace for service pressure bearing at high temperature
8.
Zurück zum Zitat ASTM A608 Standard specification for centrifugally cast iron-chromium-nickel high-alloy tubing for pressure application at high temperatures ASTM A608 Standard specification for centrifugally cast iron-chromium-nickel high-alloy tubing for pressure application at high temperatures
9.
Zurück zum Zitat George EP, Kennedy RL, Pope DP (1998) Review of trace element effects on high-temperature fracture of Fe- and Ni-base alloys. Phys Stat Sol 167:313–333CrossRef George EP, Kennedy RL, Pope DP (1998) Review of trace element effects on high-temperature fracture of Fe- and Ni-base alloys. Phys Stat Sol 167:313–333CrossRef
10.
Zurück zum Zitat White CL, Schneibel JH, Padgett RA (1983) High temperature embrittlement of Ni and Ni-Cr alloys by trace elements. Metall Trans 14:595–610CrossRef White CL, Schneibel JH, Padgett RA (1983) High temperature embrittlement of Ni and Ni-Cr alloys by trace elements. Metall Trans 14:595–610CrossRef
11.
Zurück zum Zitat George EP, Pope DP, Sklenicka V (1992) Clean steel technology. ASM International, Materials Park, p 17 George EP, Pope DP, Sklenicka V (1992) Clean steel technology. ASM International, Materials Park, p 17
12.
Zurück zum Zitat Thomas GB, Gibbons TB (1984) Creep and fracture of a cast Ni-Cr-base alloy containing trace elements. Mater Sci Eng 67:13–23CrossRef Thomas GB, Gibbons TB (1984) Creep and fracture of a cast Ni-Cr-base alloy containing trace elements. Mater Sci Eng 67:13–23CrossRef
13.
Zurück zum Zitat Osgerby S, Gibbons TB (1984) The effect of trace elements on the creep behaviour of an Ni-Cr-base alloy. Mater Sci Eng A157:63–71 Osgerby S, Gibbons TB (1984) The effect of trace elements on the creep behaviour of an Ni-Cr-base alloy. Mater Sci Eng A157:63–71
Metadaten
Titel
Status of Using, Manufacturing and Testing of Ethylene Pyrolysis Furnace Tubes in China
verfasst von
T. Chen
X. D. Chen
Y. R. Lu
Z. B. Ai
Z. C. Fan
Copyright-Jahr
2015
DOI
https://doi.org/10.1007/978-3-319-09507-3_88