7. Stress Corrosion Cracking Resistance of AISI 304 SS Subjected to Laser Shock Processing

verfasst von : Yongkang Zhang, Jinzhong Lu, Kaiyu Luo

Erschienen in: Laser Shock Processing of FCC Metals

Verlag: Springer Berlin Heidelberg

Einloggen

Aktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.

search-config

KI-gestützte Suche

Aus

Abstract

This chapter investigates the effects of massive LSP impacts on the SCC behavior of AISI 304 SS and highlights the distribution of surface residual stress, the SCC initiation and micro-structure on the top surface of three types of U-bend samples. The emphasis is placed on the mechanism of massive LSP impacts on the corrosion resistance of AISI 304 SS.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

über 102.000 Bücher
über 537 Zeitschriften

aus folgenden Fachgebieten:

Automobil + Motoren
Bauwesen + Immobilien
Business IT + Informatik
Elektrotechnik + Elektronik
Energie + Nachhaltigkeit
Finance + Banking
Management + Führung
Marketing + Vertrieb
Maschinenbau + Werkstoffe
Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Jetzt informieren

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

über 67.000 Bücher
über 390 Zeitschriften

aus folgenden Fachgebieten:

Automobil + Motoren
Bauwesen + Immobilien
Business IT + Informatik
Elektrotechnik + Elektronik
Energie + Nachhaltigkeit
Maschinenbau + Werkstoffe

Jetzt Wissensvorsprung sichern!

Jetzt informieren

Vorheriges Kapitel Mechanical Properties of AISI 304 SS and its Welded Joint Subjected to Laser Shock Processing

Nächstes Kapitel Grain Refinement of AISI 304 SS Induced by Multiple Laser Shock Processing Impacts

Montross, C. S., Ye, L., Wei, T., Clark, G., & Mai, Y. W. (2002). Laser shock processing and its effects on microstructure and properties of metal alloys: a review. International Journal of Fatigue, 24, 1021–1036.CrossRef

Ye, C., Suslov, S., Fei, X. L., & Cheng, G. J. (2011). Bimodal nano crystallization of NiTi shape memory alloy by laser shock peening and post-deformation annealing. Acta Materialia, 59, 7219–7227.CrossRef

Lu, J. Z., Luo, K. Y., Zhang, Y. K., Cui, C. Y., Sun, G. F., Zhou, J. Z., et al. (2010). Grain refinement of LY2 aluminum alloy induced by ultra-high plastic strain during multiple laser shock processing impacts. Acta Materialia, 58(11), 3984–3994.CrossRef

Ye, C., Suslov, S., Kim, B. J., Stach, E. A., & Cheng, G. J. (2011). Fatigue performance improvement in AISI 4140 steel by dynamic strain aging and dynamic precipitation during warm laser shock peening. Acta Materialia, 59, 1014–1025.CrossRef

Child, D. J., West, G. D., & Thomson, R. C. (2011). Assessment of surface hardening effects from shot peening on a Ni-based alloy using electron backscatter diffraction techniques. Acta Materialia, 59, 4825–4834.CrossRef

Tan, L., Ren, X., Sridharan, K., & Allen, T. R. (2008). Effect of shot-peening on the oxidation of alloy 800 H exposed to supercritical water and cyclic oxidation. Corrosion Science, 53, 2040–2046.CrossRef

Wen, L., Wang, Y. M., Zhou, Y., Guo, L. X., & Ouyang, J. H. (2011). Microstructure and corrosion resistance of modified 2,024 Al alloy using surface mechanical attrition treatment combined with microarc oxidation process. Corrosion Science, 53, 473–480.CrossRef

Chan, H. L., Ruan, H. H., Chen, A. Y., & Lu, J. (2010). Optimization of the strain rate to achieve exceptional mechanical properties of 304 stainless steel using high speed ultrasonic surface mechanical attrition treatment. Acta Materialia, 58, 5086–5096.CrossRef

Song, D., Ma, A. B., Jiang, J. H., Lin, P. H., Yang, D. H., & Fan, J. F. (2011). Corrosion behaviour of bulk ultra-fine grained AZ91D magnesium alloy fabricated by equal-channel angular pressing. Corrosion Science, 53, 362–373.CrossRef

10.

Xue, Q., Beyerlein, I. J., Alexander, D. J., & Gray, G. T. (2007). Mechanisms for initial grain refinement in OFHC copper during equal channel angular pressing. Acta Materialia, 55, 655–668.CrossRef

11.

Lu, Z. P., Shoji, T., Meng, F. J., Xue, H., Qiu, Y. B., Takeda, Y., et al. (2011). Characterization of microstructure and local deformation in 316 NG weld heat-affected zone and stress corrosion cracking in high temperature water. Corrosion Science, 53, 1916–1932.CrossRef

12.

Ghosh, S., Preet, V., Rana, S., Kain, V., Mittal, V., & Baveja, S. K. (2011). Role of residual stresses induced by industrial fabrication on stress corrosion cracking susceptibility of austenitic stainless steel. Materials and Design, 32, 3823–3831.CrossRef

13.

Mochizuki, M. (2007). Control of welding residual stress for ensuring integrity against fatigue and stress–corrosion cracking. Nuclear Engineering and Design, 237, 107–123.CrossRef

14.

Sano, Y. J., Obata, M., Kubo, T., Mukai, N., Yoda, M., Masaki, K., et al. (2006). Retardation of crack initiation and growth in austenitic stainless steels by laser peening without protective coating. Materials Science and Engineering A, 417(1–2), 334–340.CrossRef

15.

Peyre, P., Scherpereel, X., Berthe, L., Carboni, C., Fabbro, R., Béranger, G., et al. (2000). Surface modifications induced in 316L steel by laser peening and shot-peening. Influence on pitting corrosion resistance. Materials Science and Engineering A, 280(2), 294–302.CrossRef

16.

Peyre, P., Braham, C., Ledion, J., Berthe, L., & Fabbro, R. (2000). Corrosion reactivity of laser-peened steel surface. Journal of Materials Engineering and Performance, 9, 656–662.CrossRef

17.

Amar, H., Vignal, V., Krawiec, H., Josse, C., Peyre, P., Silva, S. N., et al. (2011). Influence of the microstructure and laser shock processing (LSP) on the corrosion behaviour of the AA2050-T8 aluminium alloy. Corrosion Science, 53, 3215–3221.CrossRef

18.

Marchi, C. S., Zaleski, T., Lee, S., Yang, N. Y. C., & Stuart, B. (2008). Effect of laser peening on the hydrogen compatibility of corrosion-resistant nickel alloy. Scripta Materialia, 58, 782–785.CrossRef

19.

Warren, A. W., Guo, Y. B., & Chen, S. C. (2008). Massive parallel laser shock peening: simulation, analysis, and validation. International Journal of Fatigue, 30, 188–197.CrossRef

20.

Hu, Y. X., & Yao, Z. Q. (2008). Overlapping rate effect on laser shock processing of 1045 steel by small spots with Nd:YAG pulsed laser. Surface & Coatings Technology, 202, 1517–1525.CrossRef

21.

ASTM Standard G 36-94 (2000) Standard practice for evaluating stress corrosion cracking resistance of metals and alloys in a boiling magnesium chloride solution. American Society for Testing and Materials, West Consohocken, 134–139.

22.

Luo, K. Y., Lu, J. Z., Zhang, Y. K., Zhou, J. Z., Zhang, L. F., Dai, F. Z., et al. (2011). Effects of laser shock processing on mechanical properties and micro-structure of ANSI 304 stainless steel. Materials Science and Engineering A, 528, 4783–4788.CrossRef

23.

Harold, L., & Michael, R. H. (2008). The effects of laser peening on high-cycle fatigue in 7085–T7651 aluminum alloy. Materials Science and Engineering A, 477, 208–216.CrossRef

24.

Al-Obaid, Y. F. (1995). The effect of shot peening on stress corrosion cracking behaviour of 2205-duplex stainless steel. Engineering Fracture Mechanics, 51(1), 19–25.CrossRef

25.

Lu, J. Z., Luo, K. Y., Zhang, Y. K., Sun, G. F., Gu, Y. Y., Zhou, J. Z., et al. (2010). Grain refinement mechanism of multiple laser shock processing impacts on ANSI 304 SS. Acta Materialia, 58(16), 5354–5362.CrossRef

26.

Kumar, S. R., Gudimetla, K., Venkatachalam, P., & Ravisankar, B. (2010). Stress corrosion cracking of Al7075 alloy processed by equal channel angular pressing. International Journal Engineering Science and Technology, 2, 53–61.

27.

Cheung, C., & Erb, U. (1994). Application of grain boundary engineering concepts to alleviate intergranular cracking in Alloys 600 and 690. Materials Science and Engineering A, 185, 39–43.CrossRef

28.

Schino, A. D., & Kenny, J. M. (2003). Grain size dependence of the fatigue behavior of a ultrafine-grained AISI 304 stainless steel. Materials Letters, 57(21), 3182–3185.CrossRef

Titel: Stress Corrosion Cracking Resistance of AISI 304 SS Subjected to Laser Shock Processing
verfasst von: Yongkang Zhang
Jinzhong Lu
Kaiyu Luo
Verlag: Springer Berlin Heidelberg
Buch: Laser Shock Processing of FCC Metals
Print ISBN: 978-3-642-35673-5

Electronic ISBN: 978-3-642-35674-2

Copyright-Jahr: 2013
DOI: https://doi.org/10.1007/978-3-642-35674-2_7

Premium Partner

Marktübersichten

Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen.

Zur Marktübersicht