Structural and electrical transport properties of Pr-doped SrTi0.93Co0.07O3-δ a novel SOEC fuel electrode materials

Zeitschrift:
Journal of Electroceramics > Ausgabe 1-2/2019
Autoren:
B. Kamecki, T. Miruszewski, J. Karczewski

Abstract

Solid Oxide Electrolyzer Cells (SOECs) are very promising electrochemical devices for the production of syngas (H2/CO) by H2O and CO2 co-electrolysis. The structure, microstructure and electrical properties of the fuel electrode material play a crucial role in the performance of the whole cell and efficiency of electrocatalytic reduction of steam into hydrogen. In the present work, a novel Co and Pr co-doped SrTiO3-δ material attracted attention as a potential fuel electrode for SOFC/SOEC. Materials with different praseodymium content were prepared by a solid-state reaction process. XRD confirmed cubic perovskite structure in all obtained samples. SEM results showed porosity in doped materials and EDX proved ABO3 stoichiometry. TEC values were about 1.17–1.26•10−5 K−1 very close to the YSZ electrolyte value. XPS studies turn out that a praseodymium can be multivalent and exist on mixed +3 and + 4 oxidation state. Electrical conductivity of samples was measured by DC 4-wire method in range of 100-800 °C. Highest value of total conductivity was achieved for Sr0.7Pr0.3Ti0.93Co0.07O3-δ and reached 23.7 S∙cm−1. The obtained results were discussed and analyzed in term of defect chemistry.

Unsere Produktempfehlungen

Premium-Abo der Gesellschaft für Informatik

Sie erhalten uneingeschränkten Vollzugriff auf alle acht Fachgebiete von Springer Professional und damit auf über 45.000 Fachbücher und ca. 300 Fachzeitschriften.

Literatur
Über diesen Artikel

Weitere Artikel der Ausgabe 1-2/2019

Journal of Electroceramics 1-2/2019 Zur Ausgabe