Studies on the Purification of Na3AlF6−K2SiF6−AlF3 Melt

The purity of the electrolyte has an important influence on the content of the impurities in electrodeposited silicon. In this paper, effects of electrolysis temperature, current density and the time on the concentrations of two important impurities: phosphorus and iron in the electrolyte were investigated during the purification of Na₃AlF₆₋10%K₂SiF₆₋AlF₃ melt. It was observed that the concentrations of P and Fe in the electrolyte decreased with the electrolysis temperature, current density and the electrolysis time increasing. X-ray fluorescence (XRF) of the electrolyte shows that the concentrations of P and Fe decrease from 4.2ppmw to 1.3ppmw and 204.0ppmw to 42.6ppmw, respectively. The removal rates of P and Fe are 69.08% and 79.12% when the electrolysis was performed for the duration of 3 hours and at a current density of 20mA•cm−2 while the operating temperature was 1225K.