Study of Properties and Structure of Silicon Bronze CuSi3Mn1 (C65500) Wire at Various Stages of Its Production by Continuous Casting and Subsequent Drawing

verfasst von: S. A. Tavolzhanskii, E. D. Vedenkin, I. V. Plisetskaya, V. E. Bazhenov, A. A. Nikitina

Erschienen in: Metallurgist | Ausgabe 7-8/2022

Einloggen

Aktivieren Sie unsere intelligente Suche um passende Fachinhalte oder Patente zu finden.

search-config
loading …

Abstract

The structure and properties of CuSi3Mn1 (C65500) silicon bronze wire at various processing stages, including the upward continuous casting of a rod having a diameter (∅) of 8 mm and its subsequent multi-stage drawing with intermediate softening annealing up to a diameter of 4 mm, are studied. It has been established that during continuous casting, chemical interactions occur, leading to a hard crust sticking to the inner surface of the graphite die due to the presence of manganese in the alloy, which affects the stability of the casting process. An increase in casting stability is achieved by using a casting regime with an additional periodic dwell, which prevents a long-term hanging of the hardening crust from adhering to the surface of the graphite die. Furthermore, it was established that, following drawing and softening annealing, a significant change in the structure occurs, comprising the formation of twin grains instead of dendrites. The dispersion and the number of twin grains increase with a decrease in the wire diameter during the drawing process. The mechanical and bending tests of a wire of ∅4 mm showed that it complies with the standards, there being a significant plasticity margin. The initial cast rod having an increased diameter can be used in order to obtain a wire of a larger diameter that complies with the standards.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Literatur
1.
Zurück zum Zitat O. E. Osintsev and V. N. Fedorov, Copper and Copper Alloys. Domestic and Foreign Brands. Handbook [in Russian], Innovatsionnoe Mashinostroenie, Moscow (2016). O. E. Osintsev and V. N. Fedorov, Copper and Copper Alloys. Domestic and Foreign Brands. Handbook [in Russian], Innovatsionnoe Mashinostroenie, Moscow (2016).
2.
Zurück zum Zitat J. R. Davis et al. (Eds.), “Copper and copper alloys,” ASM Specialty Handbook, ASM Intern., Mater. Park, OH, Second ed. (2008), pp. 361–363. J. R. Davis et al. (Eds.), “Copper and copper alloys,” ASM Specialty Handbook, ASM Intern., Mater. Park, OH, Second ed. (2008), pp. 361–363.
3.
Zurück zum Zitat V. Korzhyk, V. Khaskin, S. Peleshenko, A. Grynyuk, I. Hos, O. Ganushchak, O. Babych, and D. Strogonov, “Overview of some perspective technical solutions on laser brazing with filler wires,” The 3rd Int. Sci. Pract. Conf. “Innovations and Prospects of World Science,” Perfect Publishing, Vancouver, Canada (2021), pp. 242–253. V. Korzhyk, V. Khaskin, S. Peleshenko, A. Grynyuk, I. Hos, O. Ganushchak, O. Babych, and D. Strogonov, “Overview of some perspective technical solutions on laser brazing with filler wires,” The 3rd Int. Sci. Pract. Conf. “Innovations and Prospects of World Science,” Perfect Publishing, Vancouver, Canada (2021), pp. 242–253.
4.
Zurück zum Zitat N. S. Arsent’eva, E. A. Kazantsev, A. V. Sulitsyn, L. M. Zheleznyak, L. N Marushchak, and O. L. Glukhova, “Technology of production of welding wire from various alloys at the Kamensk-Uralsky Non-Ferrous Metal Processing Plant”, Metallurgist, No. 3, 67–69 (2008). N. S. Arsent’eva, E. A. Kazantsev, A. V. Sulitsyn, L. M. Zheleznyak, L. N Marushchak, and O. L. Glukhova, “Technology of production of welding wire from various alloys at the Kamensk-Uralsky Non-Ferrous Metal Processing Plant”, Metallurgist, No. 3, 67–69 (2008).
5.
Zurück zum Zitat N. S. Arsent’eva, L. M. Zheleznyak, A. I. Snigirev, E. A. Kazantsev, and N. A. Taskina, “Advanced production of welding wire at the Kamensk-Uralsky Non-Ferrous Metal Processing Plant”, Tsvet. Met., No. 4, 122–126 (2007). N. S. Arsent’eva, L. M. Zheleznyak, A. I. Snigirev, E. A. Kazantsev, and N. A. Taskina, “Advanced production of welding wire at the Kamensk-Uralsky Non-Ferrous Metal Processing Plant”, Tsvet. Met., No. 4, 122–126 (2007).
6.
Zurück zum Zitat S. A. Tavolzhanskii and I. N. Pashkov, “Features of the continuous casting of small-section billets from copper-based alloys,” Metallurgist, 64, No. 9–10, 1068–1076 (2021).CrossRef S. A. Tavolzhanskii and I. N. Pashkov, “Features of the continuous casting of small-section billets from copper-based alloys,” Metallurgist, 64, No. 9–10, 1068–1076 (2021).CrossRef
7.
Zurück zum Zitat R. Wilson, A Practical Approach to Continuous Casting of Copper-Based Alloys and Precious Metals, Institute of Materials, IOM Communications Ltd. (2000), p. 260. R. Wilson, A Practical Approach to Continuous Casting of Copper-Based Alloys and Precious Metals, Institute of Materials, IOM Communications Ltd. (2000), p. 260.
8.
Zurück zum Zitat E. Bagherian, To Enable the Processing of New Complex High Performance Alloys by Improving the Capacity and Performance of Continuous Casting Equipment, PhD Thesis, School of Science & Engineering, University of Dundee (2017). E. Bagherian, To Enable the Processing of New Complex High Performance Alloys by Improving the Capacity and Performance of Continuous Casting Equipment, PhD Thesis, School of Science & Engineering, University of Dundee (2017).
9.
Zurück zum Zitat S. A. Tavolzhansky and K. F. Koletvinov, “Development and application of a method of upward continuous casting of billets of HMP solders of small assortment”, Tsvet. Met., No. 11, 8588 (2015). S. A. Tavolzhansky and K. F. Koletvinov, “Development and application of a method of upward continuous casting of billets of HMP solders of small assortment”, Tsvet. Met., No. 11, 8588 (2015).
10.
Zurück zum Zitat K. F. Koletvinov, S. A. Tavolzhansky, and V. E. Bazhenov, “Research and development of process of continuous-discrete pulling copper alloy billets from melt. State and prospects of development of foundry technologies and equipment in the digital era”, in: Sb. Tr. Vser. Nauch.-prakt. Konf. [in Russian], Universitet Mashinostroeniya, Moscow (2016), pp. 275–284. K. F. Koletvinov, S. A. Tavolzhansky, and V. E. Bazhenov, “Research and development of process of continuous-discrete pulling copper alloy billets from melt. State and prospects of development of foundry technologies and equipment in the digital era”, in: Sb. Tr. Vser. Nauch.-prakt. Konf. [in Russian], Universitet Mashinostroeniya, Moscow (2016), pp. 275–284.
11.
Zurück zum Zitat E-R. Bagherian, Y. Fan, M. Cooper, B. Frame, and A. Abdolvand, “Effect of melt temperature, cleanout cycle, continuous casting direction (horizontal/vertical) and super-cooler size on tensile strength, elongation percentage and microstructure of continuous cast copper alloys,” Metall. Res. Technol., 113(5), [502] (2016); https://doi.org/10.1051/metal/2016030. E-R. Bagherian, Y. Fan, M. Cooper, B. Frame, and A. Abdolvand, “Effect of melt temperature, cleanout cycle, continuous casting direction (horizontal/vertical) and super-cooler size on tensile strength, elongation percentage and microstructure of continuous cast copper alloys,” Metall. Res. Technol., 113(5), [502] (2016); https://​doi.​org/​10.​1051/​metal/​2016030.
12.
Zurück zum Zitat M. B. Gorlovsky and V. N. Merkachev, Handbook of a Wire Drawer, Metallurgiya, Moscow (1993). M. B. Gorlovsky and V. N. Merkachev, Handbook of a Wire Drawer, Metallurgiya, Moscow (1993).
13.
Zurück zum Zitat M. Kulczyk, S. Przybysz, J. Skiba, and W Pachla, “High strength silicon bronze (C65500) obtained by hydrostatic extrusion,” Arch. Metall. Mater., 57, 859–862 (2012).CrossRef M. Kulczyk, S. Przybysz, J. Skiba, and W Pachla, “High strength silicon bronze (C65500) obtained by hydrostatic extrusion,” Arch. Metall. Mater., 57, 859–862 (2012).CrossRef
Metadaten
Titel
Study of Properties and Structure of Silicon Bronze CuSi3Mn1 (C65500) Wire at Various Stages of Its Production by Continuous Casting and Subsequent Drawing
verfasst von
S. A. Tavolzhanskii
E. D. Vedenkin
I. V. Plisetskaya
V. E. Bazhenov
A. A. Nikitina
Publikationsdatum
30.11.2022
Verlag
Springer US
Erschienen in
Metallurgist / Ausgabe 7-8/2022
Print ISSN: 0026-0894
Elektronische ISSN: 1573-8892
DOI
https://doi.org/10.1007/s11015-022-01408-w

Weitere Artikel der Ausgabe 7-8/2022

Metallurgist 7-8/2022 Zur Ausgabe

    Marktübersichten

    Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen.