Study of the Viscosity of Mold Flux Based on the Vogel–Fulcher–Tammann (VFT) Model

verfasst von: Lejun Zhou, Wanlin Wang

Erschienen in: Metallurgical and Materials Transactions B | Ausgabe 1/2017

Einloggen

Aktivieren Sie unsere intelligente Suche um passende Fachinhalte oder Patente zu finden.

search-config
loading …

Abstract

Viscosity is one of the most important properties of mold flux and affects the process of continuous casting significantly. In order to describe the variation of viscosity of mold flux accurately in a wide range of temperature occurring in the casting mold, a non-Arrhenius Vogel–Fulcher–Tammann (VFT) model was adopted in this study. The results showed that the adjusted coefficient of determination (Adj. R 2) of non-Arrhenius VFT Model ranges from 0.92 to 0.96, which suggests this model could be well adapted to predict the relationship between viscosity and temperature of mold flux. The temperature at which viscosity becomes infinite, T VFT, increased with the addition of Cr2O3 and improvement of basicity, while it decreased with the addition of B2O3, as it was determined by both the degree of polymerization of the melt structure and crystallization behavior of the melt. Also, the pseudo-activation energy, E VFT, of Samples 1 to 5 was 60.1 ± 3.6, 94.7 ± 14.9, 101.7 ± 19.0, 38.0 ± 4.8, and 32.4 ± 4.0 kJ/mol, respectively; it increased with the addition of Cr2O3 and B2O3, but deceased with the increase of basicity.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Literatur
1.
Zurück zum Zitat T. Kajitani, Y. Kato, K. Harada, K. Saito, K. Harashima, and W. Yamada: ISIJ Int., 2008, vol. 48, pp.1215-1224.CrossRef T. Kajitani, Y. Kato, K. Harada, K. Saito, K. Harashima, and W. Yamada: ISIJ Int., 2008, vol. 48, pp.1215-1224.CrossRef
2.
Zurück zum Zitat E. Takeuchi and J.K. Brimacombe: Metall. Trans. B, 1984, vol. 15, pp.493-509.CrossRef E. Takeuchi and J.K. Brimacombe: Metall. Trans. B, 1984, vol. 15, pp.493-509.CrossRef
3.
Zurück zum Zitat Y. Chung, A. W. Cramb: Metall. Mater. Trans. B, 2000, vol. 31, pp.957-71.CrossRef Y. Chung, A. W. Cramb: Metall. Mater. Trans. B, 2000, vol. 31, pp.957-71.CrossRef
5.
6.
Zurück zum Zitat A. Kondratiev, E. Jak, and P. C. Hayes: JOM, 2002, vol. 54, pp.41-45.CrossRef A. Kondratiev, E. Jak, and P. C. Hayes: JOM, 2002, vol. 54, pp.41-45.CrossRef
7.
Zurück zum Zitat L. Zhou, W. Wang, and K. Zhou: ISIJ Int., 2015, vol. 55, pp. 1961-1924. L. Zhou, W. Wang, and K. Zhou: ISIJ Int., 2015, vol. 55, pp. 1961-1924.
8.
Zurück zum Zitat G. Kim and IL Sohn: Metall. Mater. Trans. B, 2013, vol. 45, pp. 86-95. G. Kim and IL Sohn: Metall. Mater. Trans. B, 2013, vol. 45, pp. 86-95.
9.
Zurück zum Zitat X. Qi, G. Wen, P. Tang: J. Iron Steel Res. Int., 2010, vol. 17, pp. 6-10.CrossRef X. Qi, G. Wen, P. Tang: J. Iron Steel Res. Int., 2010, vol. 17, pp. 6-10.CrossRef
10.
Zurück zum Zitat Z. Zhang, G. Wen, P. Tang, and S. Sridhar: ISIJ Int., 2008, vol. 48, pp.739-46.CrossRef Z. Zhang, G. Wen, P. Tang, and S. Sridhar: ISIJ Int., 2008, vol. 48, pp.739-46.CrossRef
11.
Zurück zum Zitat E. Benavidez, L. Santini, M. Valentini, and E. Brandaleze: 11th International Congress on Metallurgy & Materials SAM/CONAMET 2011, 2012, vol. 1, pp. 389–96. E. Benavidez, L. Santini, M. Valentini, and E. Brandaleze: 11th International Congress on Metallurgy & Materials SAM/CONAMET 2011, 2012, vol. 1, pp. 389–96.
12.
Zurück zum Zitat T. Iida, H. Sakai, Y. Kita, and K. Shigeno: ISIJ Int., 2000, vol. 40, pp.S110-S114.CrossRef T. Iida, H. Sakai, Y. Kita, and K. Shigeno: ISIJ Int., 2000, vol. 40, pp.S110-S114.CrossRef
13.
Zurück zum Zitat K.C. Mills and S. Sridhar: Ironmak Steelmak., 1999, vol. 26, pp.262-268.CrossRef K.C. Mills and S. Sridhar: Ironmak Steelmak., 1999, vol. 26, pp.262-268.CrossRef
14.
15.
Zurück zum Zitat D. H. Vogel: Physikalische Zeitschrift, 1921, vol. 22, pp.645-646. D. H. Vogel: Physikalische Zeitschrift, 1921, vol. 22, pp.645-646.
16.
17.
Zurück zum Zitat G. Tammann and W. Hesse: Z. Anorg. Allg. Chem, 1926, vol. 156, pp.245-257.CrossRef G. Tammann and W. Hesse: Z. Anorg. Allg. Chem, 1926, vol. 156, pp.245-257.CrossRef
18.
Zurück zum Zitat D. Giordano and D. B. Dingwell: Earth Planet. Sci. Lett., 2003, vol. 208, pp.337-349.CrossRef D. Giordano and D. B. Dingwell: Earth Planet. Sci. Lett., 2003, vol. 208, pp.337-349.CrossRef
19.
Zurück zum Zitat D. Giordano, J. K. Russell, and D. B. Dingwell: Earth Planet. Sci. Lett., 2008, vol. 271, pp.123-134.CrossRef D. Giordano, J. K. Russell, and D. B. Dingwell: Earth Planet. Sci. Lett., 2008, vol. 271, pp.123-134.CrossRef
20.
21.
Zurück zum Zitat H. Lu and W. Huang: Smart Mater. Struct. 2013, vol. 22, pp.1-8. H. Lu and W. Huang: Smart Mater. Struct. 2013, vol. 22, pp.1-8.
22.
Zurück zum Zitat B. Mokhtarani, A. Sharifi, H. R. Mortaheb, M. Mirzaei, M. Mafi, and F. Sadeghian: J. Chem. Thermodyn., 2009, vol. 41, pp.323-329.CrossRef B. Mokhtarani, A. Sharifi, H. R. Mortaheb, M. Mirzaei, M. Mafi, and F. Sadeghian: J. Chem. Thermodyn., 2009, vol. 41, pp.323-329.CrossRef
23.
Zurück zum Zitat L. Zhou, W. Wang, B. Lu, and G. Wen: Met. Mater. Int., 2015, vol.21, pp.126-133.CrossRef L. Zhou, W. Wang, B. Lu, and G. Wen: Met. Mater. Int., 2015, vol.21, pp.126-133.CrossRef
24.
Zurück zum Zitat L. Zhou, W. Wang, F. Ma, J. Li, J. Wei, H. Matsuur, and F. Tsukihashi.: Metall. Mater. Trans. B, 2012, vol. 43, pp.354-362.CrossRef L. Zhou, W. Wang, F. Ma, J. Li, J. Wei, H. Matsuur, and F. Tsukihashi.: Metall. Mater. Trans. B, 2012, vol. 43, pp.354-362.CrossRef
25.
Zurück zum Zitat H. Tweer, J. H. Simmons, and P. B. Macedo: J. Chem. Phys., 1971, vol. 54, pp.1952-1959.CrossRef H. Tweer, J. H. Simmons, and P. B. Macedo: J. Chem. Phys., 1971, vol. 54, pp.1952-1959.CrossRef
26.
Zurück zum Zitat L. Zhou and W. Wang: Metall. Mater. Trans. B, 2016, vol. 47, pp.1548-1552.CrossRef L. Zhou and W. Wang: Metall. Mater. Trans. B, 2016, vol. 47, pp.1548-1552.CrossRef
27.
Zurück zum Zitat C. Xu, W. Wang, L. Zhou, S. Xie, and C. Zhang: Metall. Mater. Trans. B, 2015, vol. 46, pp.882-892.CrossRef C. Xu, W. Wang, L. Zhou, S. Xie, and C. Zhang: Metall. Mater. Trans. B, 2015, vol. 46, pp.882-892.CrossRef
28.
Zurück zum Zitat V. De. Eisenhüttenleute: Slag Atlas, 2th Edition, Verlag Stahleisen GmbH, Dusseldorf ,1995, pp. 119. V. De. Eisenhüttenleute: Slag Atlas, 2th Edition, Verlag Stahleisen GmbH, Dusseldorf ,1995, pp. 119.
29.
Zurück zum Zitat L. Zhou, W. Wang, J. Wei, K. Zhou: ISIJ Int., 2015, vol. 55, pp. 821-829.CrossRef L. Zhou, W. Wang, J. Wei, K. Zhou: ISIJ Int., 2015, vol. 55, pp. 821-829.CrossRef
Metadaten
Titel
Study of the Viscosity of Mold Flux Based on the Vogel–Fulcher–Tammann (VFT) Model
verfasst von
Lejun Zhou
Wanlin Wang
Publikationsdatum
17.10.2016
Verlag
Springer US
Erschienen in
Metallurgical and Materials Transactions B / Ausgabe 1/2017
Print ISSN: 1073-5615
Elektronische ISSN: 1543-1916
DOI
https://doi.org/10.1007/s11663-016-0835-2

Weitere Artikel der Ausgabe 1/2017

Metallurgical and Materials Transactions B 1/2017 Zur Ausgabe

    Marktübersichten

    Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen.