Study on Evolution of Inclusions in Tinplate Production During RH Refining—Continuous Casting Process

verfasst von : Xiaoao Li, Nan Wang, Min Chen

Erschienen in: Materials Processing Fundamentals 2021

Verlag: Springer International Publishing

Aktivieren Sie unsere intelligente Suche um passende Fachinhalte oder Patente zu finden.

search-config
loading …

Abstract

The evolution behaviors of the type, amount, and size of inclusions in tinplate were studied by industrial experiments and thermodynamic calculations during RH refining process. The results indicated that Al2O3 inclusions were generated at first after Al addition. With the slag-steel and refractory-steel reactions, inclusions varied with the route as Al2O3 inclusions → CaO–Al2O3 system inclusions → CaO–MgO–Al2O3 system inclusions and Al2O3 inclusions → MgO–Al2O3 spinel inclusions → CaO–MgO–Al2O3 system inclusions. From Al addition to the end of RH refining, the number density of inclusions increased from 9.32 to 4.09 per mm2. The total oxygen content in steel could be decreased from 450 to 37 ppm. The size of inclusions varied mainly less than 10 μm, the proportion of inclusions with size less than 5 μm gradually decreased by 15% and inclusions in the range of 5–10 μm increased by 10%. These inclusions with size less than 10 μm were difficult to be removed from liquid steel through the floatation. The inclusions were Al2O3 and CaO·Al2O3 inclusions with a high melting point at the end of RH refining. In order to obtain inclusions with a low melting point, the reasonable C/A mass ratio of the final RH slag is 1.10 through theoretical calculations.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Springer Professional "Wirtschaft"

Online-Abonnement

Mit Springer Professional "Wirtschaft" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 340 Zeitschriften

aus folgenden Fachgebieten:

  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Versicherung + Risiko




Jetzt Wissensvorsprung sichern!

Literatur
1.
Zurück zum Zitat Kaushik P, Lowry M, Yin H, Pielet H (2012) Inclusion characterisation for clean steelmaking and quality control. Ironmaking Steelmaking 39(4):284–300CrossRef Kaushik P, Lowry M, Yin H, Pielet H (2012) Inclusion characterisation for clean steelmaking and quality control. Ironmaking Steelmaking 39(4):284–300CrossRef
2.
Zurück zum Zitat Deng ZY, Zhu MY (2013) Evolution mechanism of non-metallic inclusions in Al-killed alloyed steel during secondary refining process. ISIJ Int 53(3):450–458CrossRef Deng ZY, Zhu MY (2013) Evolution mechanism of non-metallic inclusions in Al-killed alloyed steel during secondary refining process. ISIJ Int 53(3):450–458CrossRef
3.
Zurück zum Zitat Yang GW, Wang XH, Huang FX, Wang WJ, Yin YQ, Tang C (2014) Influence of reoxidation in tundish on inclusion for Ca-treated Al-killed steel. Steel Res Int 85(5):784–792CrossRef Yang GW, Wang XH, Huang FX, Wang WJ, Yin YQ, Tang C (2014) Influence of reoxidation in tundish on inclusion for Ca-treated Al-killed steel. Steel Res Int 85(5):784–792CrossRef
4.
Zurück zum Zitat Li SJ, Cheng GG, Miao ZQ, Dai WX, Chen L, Liu ZQ (2018) Evolution of oxide inclusions in G20CrNi2Mo carburized bearing steel during industrial electroslag remelting. ISIJ Int 58(10):1781–1790CrossRef Li SJ, Cheng GG, Miao ZQ, Dai WX, Chen L, Liu ZQ (2018) Evolution of oxide inclusions in G20CrNi2Mo carburized bearing steel during industrial electroslag remelting. ISIJ Int 58(10):1781–1790CrossRef
5.
Zurück zum Zitat Park JH, Todoroki H (2010) Control of MgO·Al2O3 spinel inclusions in stainless steels. ISIJ Int 50(10):1333–1346CrossRef Park JH, Todoroki H (2010) Control of MgO·Al2O3 spinel inclusions in stainless steels. ISIJ Int 50(10):1333–1346CrossRef
6.
Zurück zum Zitat Park JH, Lee SB, Gaye HR (2008) Thermodynamics of the formation of MgO–Al2O3–TiOx inclusions in Ti-stabilized 11Cr ferritic stainless steel. Metall Mater Trans B 39(6):853–861CrossRef Park JH, Lee SB, Gaye HR (2008) Thermodynamics of the formation of MgO–Al2O3–TiOx inclusions in Ti-stabilized 11Cr ferritic stainless steel. Metall Mater Trans B 39(6):853–861CrossRef
7.
Zurück zum Zitat Kang YJ, Li F, Morita K, Du SC (2006) Mechanism study on the formation of liquid calcium aluminate inclusion from MgO–Al2O3 spinel. Steel Res Int 77(11):785–792CrossRef Kang YJ, Li F, Morita K, Du SC (2006) Mechanism study on the formation of liquid calcium aluminate inclusion from MgO–Al2O3 spinel. Steel Res Int 77(11):785–792CrossRef
8.
Zurück zum Zitat Jiang M, Wang XH, Chen B, Wang WJ (2008) Formation of MgO·Al2O3 inclusions in high strength alloyed structural steel refined by CaO–SiO2–Al2O3–MgO slag. ISIJ Int 48(7):885–890CrossRef Jiang M, Wang XH, Chen B, Wang WJ (2008) Formation of MgO·Al2O3 inclusions in high strength alloyed structural steel refined by CaO–SiO2–Al2O3–MgO slag. ISIJ Int 48(7):885–890CrossRef
9.
Zurück zum Zitat Jiang M, Wang XH, Chen B, Wang WJ (2010) Laboratory study on evolution mechanisms of non-metallic inclusions in high strength alloyed steel refined by high basicity slag. ISIJ Int 50(1):95–104CrossRef Jiang M, Wang XH, Chen B, Wang WJ (2010) Laboratory study on evolution mechanisms of non-metallic inclusions in high strength alloyed steel refined by high basicity slag. ISIJ Int 50(1):95–104CrossRef
10.
Zurück zum Zitat Jiang M, Wang XH, Chen B, Wang WJ (2012) Study on refining slags targeting high cleanliness and lower melting temperature inclusions in Al killed steel. Ironmaking Steelmaking 39(1):20–25CrossRef Jiang M, Wang XH, Chen B, Wang WJ (2012) Study on refining slags targeting high cleanliness and lower melting temperature inclusions in Al killed steel. Ironmaking Steelmaking 39(1):20–25CrossRef
11.
Zurück zum Zitat Jiang M, Wang XH, Wang WJ (2010) Control of non-metallic inclusions by slag-metal reactions for high strength alloying steels. Steel Res Int 81(9):759–765CrossRef Jiang M, Wang XH, Wang WJ (2010) Control of non-metallic inclusions by slag-metal reactions for high strength alloying steels. Steel Res Int 81(9):759–765CrossRef
12.
Zurück zum Zitat Zhang LF, Thomas BG (2003) State of the art in evaluation and control of steel cleanliness. ISIJ Int 43(3):271–291CrossRef Zhang LF, Thomas BG (2003) State of the art in evaluation and control of steel cleanliness. ISIJ Int 43(3):271–291CrossRef
13.
Zurück zum Zitat Shi CB, Chen XC, Guo HJ, Zhu ZJ, Ren H (2012) Assessment of oxygen control and its effect on inclusion characteristics during electroslag remelting of die steel. Steel Res Int 83(5):472–486CrossRef Shi CB, Chen XC, Guo HJ, Zhu ZJ, Ren H (2012) Assessment of oxygen control and its effect on inclusion characteristics during electroslag remelting of die steel. Steel Res Int 83(5):472–486CrossRef
14.
Zurück zum Zitat Suito H, Inoue R (1996) Thermodynamics on control of inclusions composition in ultraclean steels. ISIJ Int 36(5):528–536CrossRef Suito H, Inoue R (1996) Thermodynamics on control of inclusions composition in ultraclean steels. ISIJ Int 36(5):528–536CrossRef
15.
Zurück zum Zitat Sigworth GK, Elliott JF (1974) The thermodynamics of liquid dilute iron alloys. Metal Sci 8(1):298–310CrossRef Sigworth GK, Elliott JF (1974) The thermodynamics of liquid dilute iron alloys. Metal Sci 8(1):298–310CrossRef
16.
Zurück zum Zitat Ohta H, Suito H (1996) Activities in CaO–MgO–Al2O3 slags and deoxidation equilibria of Al, Mg, and Ca. ISIJ Int 36(8):983–990CrossRef Ohta H, Suito H (1996) Activities in CaO–MgO–Al2O3 slags and deoxidation equilibria of Al, Mg, and Ca. ISIJ Int 36(8):983–990CrossRef
17.
Zurück zum Zitat Itoh H, Hino M, Ban-ya S (1997) Assessment of Al deoxidation equilibrium in liquid iron. Tetsu-To-Hagané 83(12):773–778CrossRef Itoh H, Hino M, Ban-ya S (1997) Assessment of Al deoxidation equilibrium in liquid iron. Tetsu-To-Hagané 83(12):773–778CrossRef
18.
Zurück zum Zitat Kishi M, Inoue R, Suito H (1994) Thermodynamics of oxygen and nitrogen in liquid Fe-20mass%Cr alloy equilibrated with titania-based slags. ISIJ Int 34(11):859–867CrossRef Kishi M, Inoue R, Suito H (1994) Thermodynamics of oxygen and nitrogen in liquid Fe-20mass%Cr alloy equilibrated with titania-based slags. ISIJ Int 34(11):859–867CrossRef
19.
Zurück zum Zitat Zhao DW, Li HB, Bao CL, Yang J (2015) Inclusion evolution during modification of alumina inclusions by calcium in liquid steel and deformation during hot rolling process. ISIJ Int 55(10):2115–2124CrossRef Zhao DW, Li HB, Bao CL, Yang J (2015) Inclusion evolution during modification of alumina inclusions by calcium in liquid steel and deformation during hot rolling process. ISIJ Int 55(10):2115–2124CrossRef
20.
Zurück zum Zitat Ren Y, Zhang LF (2016) Thermodynamic model for prediction of slag-steel-inclusion reactions of 304 stainless steels. ISIJ Int 57(1):68–75CrossRef Ren Y, Zhang LF (2016) Thermodynamic model for prediction of slag-steel-inclusion reactions of 304 stainless steels. ISIJ Int 57(1):68–75CrossRef
Metadaten
Titel
Study on Evolution of Inclusions in Tinplate Production During RH Refining—Continuous Casting Process
verfasst von
Xiaoao Li
Nan Wang
Min Chen
Copyright-Jahr
2021
DOI
https://doi.org/10.1007/978-3-030-65253-1_5

    Marktübersichten

    Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen.