01.05.2021 | Assembly

Study on the balance between FSW parameters and heat treatment for an optimized Al2024-T8 joint: microstructural and tensile evaluations

verfasst von: S. Yousefi Shivyari, A. Hosseini Monazzah

Erschienen in: Production Engineering | Ausgabe 5/2021

Einloggen, um Zugang zu erhalten
share
TEILEN

Abstract

In this study, the effects of different rotational speeds (ω) and T6 post weld heat treatment on the microstructure, micro-hardness distribution, and tensile properties of friction stir welded Al2024-T8 were investigated. Rotational speeds of 700, 900 and 1100 rpm at a constant 100 mm/min transverse rate (υ) were used. To investigate the degree of post weld heat treatment’s (PWHT) effectiveness with respect to rotational speed of FSW, half of the joints were heat treated under T6 condition (Solutionizing at 500 °C for 1 h, quenching, and finally aging at 200 °C for 2 h). Ascending trend of grain size on workpieces without PWHT in thermo-mechanically affected zone (TMAZ) from 700 to 1100 rpm indicates that generated heat played the main role rather than plastic deformation. Close hardness results among all different FSW zones under a PWHT condition confirm the success of T6 treatment in overcoming thermo-mechanical microstructural variations resulted from stir friction. The effect of increasing ω/υ on tensile properties among the joints without PWHT is considerable. Higher ω led to higher strength but lower ductility. Therefore, the highest strength was achieved at ω = 1100 rpm (71.2% of base metal), and the highest elongation was achieved at ω = 700 rpm (13.8% of base metal). The results of T6 treated joints showed a strong dependency of PWHT’s effectiveness to FSW parameters. T6 heat treatment resulted in reduced strength in all cases but the amount of reduction relative to original strength was reduced by increased ω. The same trend was observed in ductility with the exception of 25% improvement over original ductility at highest rotational speed (ω = 1100 rpm).

Sie möchten Zugang zu diesem Inhalt erhalten? Dann informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 69.000 Bücher
  • über 500 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Testen Sie jetzt 15 Tage kostenlos.

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 50.000 Bücher
  • über 380 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




Testen Sie jetzt 15 Tage kostenlos.

Literatur
1.
Zurück zum Zitat Zhou C, Yang X, Luan G (2006) Effect of root flaws on the fatigue property of friction stir welds in 2024–T3 aluminum alloys. Mater Sci Eng A 418(1–2):155–160 CrossRef Zhou C, Yang X, Luan G (2006) Effect of root flaws on the fatigue property of friction stir welds in 2024–T3 aluminum alloys. Mater Sci Eng A 418(1–2):155–160 CrossRef
2.
Zurück zum Zitat Staley JT (1992) Aluminum alloys and composites. Encycl Phys Sci 1:591–598 Staley JT (1992) Aluminum alloys and composites. Encycl Phys Sci 1:591–598
3.
Zurück zum Zitat Squillace A, De Fenzo A, Giorleo G, Bellucci F (2004) A comparison between FSW and TIG welding techniques: modifications of microstructure and pitting corrosion resistance in AA 2024–T3 butt joints. J Mater Process Technol 152(1):97–105 CrossRef Squillace A, De Fenzo A, Giorleo G, Bellucci F (2004) A comparison between FSW and TIG welding techniques: modifications of microstructure and pitting corrosion resistance in AA 2024–T3 butt joints. J Mater Process Technol 152(1):97–105 CrossRef
4.
Zurück zum Zitat Thomas W, Nicholas E, Needham J, Murch M, Templesmith P, Dawes C (1991) International patent application no. PCT/GB92/02203 and GB patent application Thomas W, Nicholas E, Needham J, Murch M, Templesmith P, Dawes C (1991) International patent application no. PCT/GB92/02203 and GB patent application
5.
Zurück zum Zitat Arbegast W, Jin Z, Beaudoin A, Bieler T, Radhakrishnan B (2003) Hot deformation of aluminum alloys III. TMS:313 Arbegast W, Jin Z, Beaudoin A, Bieler T, Radhakrishnan B (2003) Hot deformation of aluminum alloys III. TMS:313
6.
Zurück zum Zitat Srivatsan TS, Vasudevan S, Park L (2007) The tensile deformation and fracture behavior of friction stir welded aluminum alloy 2024. Mater Sci Eng A 466(1–2):235–245 CrossRef Srivatsan TS, Vasudevan S, Park L (2007) The tensile deformation and fracture behavior of friction stir welded aluminum alloy 2024. Mater Sci Eng A 466(1–2):235–245 CrossRef
7.
Zurück zum Zitat Liu H, Fujii H, Maeda M, Nogi K (2003) Tensile properties and fracture locations of friction-stir-welded joints of 2017–T351 aluminum alloy. J Mater Process Technol 142(3):692–696 CrossRef Liu H, Fujii H, Maeda M, Nogi K (2003) Tensile properties and fracture locations of friction-stir-welded joints of 2017–T351 aluminum alloy. J Mater Process Technol 142(3):692–696 CrossRef
8.
Zurück zum Zitat Zhao Y, Liu H, Chen S, Lin Z, Hou J (2014) Effects of sleeve plunge depth on microstructures and mechanical properties of friction spot welded alclad 7B04-T74 aluminum alloy. Mater Des 62:40–46 CrossRef Zhao Y, Liu H, Chen S, Lin Z, Hou J (2014) Effects of sleeve plunge depth on microstructures and mechanical properties of friction spot welded alclad 7B04-T74 aluminum alloy. Mater Des 62:40–46 CrossRef
9.
Zurück zum Zitat Hao H, Ni D, Huang H, Wang D, Xiao B, Nie Z, Ma Z (2013) Effect of welding parameters on microstructure and mechanical properties of friction stir welded Al–Mg–Er alloy. Mater Sci Eng A 559:889–896 CrossRef Hao H, Ni D, Huang H, Wang D, Xiao B, Nie Z, Ma Z (2013) Effect of welding parameters on microstructure and mechanical properties of friction stir welded Al–Mg–Er alloy. Mater Sci Eng A 559:889–896 CrossRef
10.
Zurück zum Zitat Fu R-d, Zhang J-f, Li Y-j, Kang J, Liu H-j, Zhang F-c (2013) Effect of welding heat input and post-welding natural aging on hardness of stir zone for friction stir-welded 2024–T3 aluminum alloy thin-sheet. Mater Sci Eng A 559:319–324 CrossRef Fu R-d, Zhang J-f, Li Y-j, Kang J, Liu H-j, Zhang F-c (2013) Effect of welding heat input and post-welding natural aging on hardness of stir zone for friction stir-welded 2024–T3 aluminum alloy thin-sheet. Mater Sci Eng A 559:319–324 CrossRef
11.
Zurück zum Zitat Yu C, Hua D, Li J-z, Zhao J-w, Fu M-j, Li X-h (2015) Effect of welding heat input and post-welded heat treatment on hardness of stir zone for friction stir-welded 2024–T3 aluminum alloy. Trans Nonferrous Met Soc China 25(8):2524–2532 CrossRef Yu C, Hua D, Li J-z, Zhao J-w, Fu M-j, Li X-h (2015) Effect of welding heat input and post-welded heat treatment on hardness of stir zone for friction stir-welded 2024–T3 aluminum alloy. Trans Nonferrous Met Soc China 25(8):2524–2532 CrossRef
12.
Zurück zum Zitat Radisavljevic I, Zivkovic A, Radovic N, Grabulov V (2013) Influence of FSW parameters on formation quality and mechanical properties of Al 2024–T351 butt welded joints. Trans Nonferrous Met Soc China 23(12):3525–3539 CrossRef Radisavljevic I, Zivkovic A, Radovic N, Grabulov V (2013) Influence of FSW parameters on formation quality and mechanical properties of Al 2024–T351 butt welded joints. Trans Nonferrous Met Soc China 23(12):3525–3539 CrossRef
13.
Zurück zum Zitat Zhang J, Feng X, Gao J, Huang H, Ma Z, Guo L (2018) Effects of welding parameters and post-heat treatment on mechanical properties of friction stir welded AA2195-T8 Al-Li alloy. J Mater Sci Technol 34(1):219–227 CrossRef Zhang J, Feng X, Gao J, Huang H, Ma Z, Guo L (2018) Effects of welding parameters and post-heat treatment on mechanical properties of friction stir welded AA2195-T8 Al-Li alloy. J Mater Sci Technol 34(1):219–227 CrossRef
14.
Zurück zum Zitat Steuwer A, Dumont M, Altenkirch J, Birosca S, Deschamps A, Prangnell P, Withers P (2011) A combined approach to microstructure mapping of an Al–Li AA2199 friction stir weld. Acta Mater 59(8):3002–3011 CrossRef Steuwer A, Dumont M, Altenkirch J, Birosca S, Deschamps A, Prangnell P, Withers P (2011) A combined approach to microstructure mapping of an Al–Li AA2199 friction stir weld. Acta Mater 59(8):3002–3011 CrossRef
15.
Zurück zum Zitat Xu W, Liu J, Luan G, Dong C (2009) Temperature evolution, microstructure and mechanical properties of friction stir welded thick 2219-O aluminum alloy joints. Mater Des 30(6):1886–1893 CrossRef Xu W, Liu J, Luan G, Dong C (2009) Temperature evolution, microstructure and mechanical properties of friction stir welded thick 2219-O aluminum alloy joints. Mater Des 30(6):1886–1893 CrossRef
16.
Zurück zum Zitat Aydın H, Bayram A, Uğuz A, Akay KS (2009) Tensile properties of friction stir welded joints of 2024 aluminum alloys in different heat-treated-state. Mater Des 30(6):2211–2221 CrossRef Aydın H, Bayram A, Uğuz A, Akay KS (2009) Tensile properties of friction stir welded joints of 2024 aluminum alloys in different heat-treated-state. Mater Des 30(6):2211–2221 CrossRef
17.
Zurück zum Zitat Aydın H, Bayram A, Durgun I (2010) The effect of post-weld heat treatment on the mechanical properties of 2024–T4 friction stir-welded joints. Mater Des 31(5):2568–2577 CrossRef Aydın H, Bayram A, Durgun I (2010) The effect of post-weld heat treatment on the mechanical properties of 2024–T4 friction stir-welded joints. Mater Des 31(5):2568–2577 CrossRef
18.
Zurück zum Zitat Krishnan K (2002) The effect of post weld heat treatment on the properties of 6061 friction stir welded joints. J Mater Sci 37(3):473–480 CrossRef Krishnan K (2002) The effect of post weld heat treatment on the properties of 6061 friction stir welded joints. J Mater Sci 37(3):473–480 CrossRef
19.
Zurück zum Zitat Chen Y, Liu H, Feng J (2006) Effect of post-weld heat treatment on the mechanical properties of 2219-O friction stir welded joints. J Mater Sci 41(1):297–299 CrossRef Chen Y, Liu H, Feng J (2006) Effect of post-weld heat treatment on the mechanical properties of 2219-O friction stir welded joints. J Mater Sci 41(1):297–299 CrossRef
20.
Zurück zum Zitat Sullivan A, Robson J (2008) Microstructural properties of friction stir welded and post-weld heat-treated 7449 aluminium alloy thick plate. Mater Sci Eng A 478(1–2):351–360 CrossRef Sullivan A, Robson J (2008) Microstructural properties of friction stir welded and post-weld heat-treated 7449 aluminium alloy thick plate. Mater Sci Eng A 478(1–2):351–360 CrossRef
21.
Zurück zum Zitat Hassan KA, Norman A, Price D, Prangnell P (2003) Stability of nugget zone grain structures in high strength Al-alloy friction stir welds during solution treatment. Acta Mater 51(7):1923–1936 CrossRef Hassan KA, Norman A, Price D, Prangnell P (2003) Stability of nugget zone grain structures in high strength Al-alloy friction stir welds during solution treatment. Acta Mater 51(7):1923–1936 CrossRef
22.
Zurück zum Zitat Hu Z, Yuan S, Wang X, Liu G, Huang Y (2011) Effect of post-weld heat treatment on the microstructure and plastic deformation behavior of friction stir welded 2024. Mater Des 32(10):5055–5060 CrossRef Hu Z, Yuan S, Wang X, Liu G, Huang Y (2011) Effect of post-weld heat treatment on the microstructure and plastic deformation behavior of friction stir welded 2024. Mater Des 32(10):5055–5060 CrossRef
23.
Zurück zum Zitat Charit I, Mishra RS (2003) High strain rate superplasticity in a commercial 2024 Al alloy via friction stir processing. Mater Sci Eng A 359(1–2):290–296 CrossRef Charit I, Mishra RS (2003) High strain rate superplasticity in a commercial 2024 Al alloy via friction stir processing. Mater Sci Eng A 359(1–2):290–296 CrossRef
24.
Zurück zum Zitat Sun Y, Fujii H (2017) Effect of abnormal grain growth on microstructure and mechanical properties of friction stir welded SPCC steel plates. Mater Sci Eng A 694:81–92 CrossRef Sun Y, Fujii H (2017) Effect of abnormal grain growth on microstructure and mechanical properties of friction stir welded SPCC steel plates. Mater Sci Eng A 694:81–92 CrossRef
25.
Zurück zum Zitat Smallman RE (2016) Chapter: 11 Phase Transformations I - Precipitation Hardening Transformation. Modern physical metallurgy, 4th Edition. Elsevier Smallman RE (2016) Chapter: 11 Phase Transformations I - Precipitation Hardening Transformation. Modern physical metallurgy, 4th Edition. Elsevier
Metadaten
Titel
Study on the balance between FSW parameters and heat treatment for an optimized Al2024-T8 joint: microstructural and tensile evaluations
verfasst von
S. Yousefi Shivyari
A. Hosseini Monazzah
Publikationsdatum
01.05.2021
Verlag
Springer Berlin Heidelberg
Erschienen in
Production Engineering / Ausgabe 5/2021
Print ISSN: 0944-6524
Elektronische ISSN: 1863-7353
DOI
https://doi.org/10.1007/s11740-021-01054-2

Weitere Artikel der Ausgabe 5/2021

Production Engineering 5/2021 Zur Ausgabe

Premium Partner

    Marktübersichten

    Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen.