The preparation of waterborne UV-curable urethane acrylate was studied in this paper. The synthetic urethane acrylate could be used in water-based UV-curable inkjet printing as an ink binder. The waterborne UV-curable anionic polyurethane acrylate was prepared by self-emulsifying process. Isophorone diisocyanate (IPDI), polyethylene glycol, dimethylol propionic acid (DMPA), and pentaerythritol triacrylate (PETA) were selected as main raw materials in the experiment. Some influence factors on the properties of the waterborne polyurethane acrylate emulsion were studied, such as the mole ratio of –NCO/–OH, the mass fractions of DMPA, and the degree of neutralization. The results indicated that when the mole ratio of –NCO/–OH was 2.8:1, the mass fraction of DMPA was 3.5 %, the degree of neutralization was 100 %, and the solids of waterborne polyurethane acrylate emulsion could be obtained up to 45 %. The viscosity was 30 mPa·s, and the average size of the particle was 50 nm.
Bitte loggen Sie sich ein, um Zugang zu diesem Inhalt zu erhalten
Sie möchten Zugang zu diesem Inhalt erhalten? Dann informieren Sie sich jetzt über unsere Produkte:
Lili, L. (2013). Research status of water-based ink. Chemical new materials, 41(1), 9–12.
Rui, M., & Yongmei, M. (2014). Research progress of water based UV curable resin. Adhesive of China, 23(1), 46–49.
Xin, Y., & Ruixia, Z. (2014). UV-curable waterborne polyurethane acrylate resin synthesis and performance research. The Key Reports, 17(6), 5–9.
Tisheng, L. (2006). New progress in overseas inkjet printing ink technology innovation. Imaging Techniques, 1(1), 39–41.
Jiang, S. (2014). Environmentally friendly water-based UV synthesis of polyurethane acrylate resin. Coating Industry, 44(6), 49–53.
Huilu, L., & Kangchen, S. (2014). UV curing coating the synthesis and properties of polyurethane acrylates. Insulation Materials, 47(4), 21–25.
He, S. (1946). A method for the determination of isocyanates. Analyst, 71(849), 557–559. CrossRef
- Study on the Preparation of Waterborne UV-Curable Polyurethane Acrylate
- Springer Singapore
- Chapter 115
Neuer Inhalt/© Filograph | Getty Images | iStock