Studying the Wear Resistance of the Mandrels of a Two-High Screw Rolling Mill

verfasst von: A. S. Aleshchenko, Nguyen Quang

Erschienen in: Metallurgist | Ausgabe 5-6/2022

Einloggen

Aktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.

search-config
loading …

Abstract

The surface wear of a cylindrical mandrel during elongation rolling of 20Kh13 steel pipe in a MISiS-130D screw-rolling mill is studied. The dimensions of the mandrel were determined before and after the rolling. It is shown that after rolling five 72 × 9 mm hollow shells of 700 mm length, the diameter of the mandrel in the deformation zone decreased by 0.04 mm maximum. The material durability of the mandrel used was 28.5 ton/kg. The finite-element method was used to simulate the elongation rolling of shells into tubes on a short cylindrical mandrel. It was found out that the maximum wear is in the gorge zone, where the diameter dimensions of the mandrel decreased by 0.01 mm after each pass. The material durability of the mandrel decreased by 78.9% after five passes.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Literatur
1.
Zurück zum Zitat A. V. Vydrin, “Developing the technologies of hot rolling of seamless tubes,” Chern. Metally, No. 9, 16–20 (2012). A. V. Vydrin, “Developing the technologies of hot rolling of seamless tubes,” Chern. Metally, No. 9, 16–20 (2012).
2.
Zurück zum Zitat S. V. Samusev, et al., “Shaping of pipe blanks on specialized bending equipment,” Steel in Transl., 46, No. 3, 169–172 (2016).CrossRef S. V. Samusev, et al., “Shaping of pipe blanks on specialized bending equipment,” Steel in Transl., 46, No. 3, 169–172 (2016).CrossRef
3.
Zurück zum Zitat S. V. Samusev, et al., “Research of technological parameters of billet stepwise forming in production of large diameter tubes at tube electric pipe welded line TESA 1420,” Chern. Metally, No. 9, 73–77 (2017). S. V. Samusev, et al., “Research of technological parameters of billet stepwise forming in production of large diameter tubes at tube electric pipe welded line TESA 1420,” Chern. Metally, No. 9, 73–77 (2017).
4.
Zurück zum Zitat B. A. Romantsev, et al., “Development of multipass skew rolling technology for stainless steel and alloy pipes’ production,” Int. J. Adv. Manufact. Technol., 97, No. 9-12, 3223–3230 (2018).CrossRef B. A. Romantsev, et al., “Development of multipass skew rolling technology for stainless steel and alloy pipes’ production,” Int. J. Adv. Manufact. Technol., 97, No. 9-12, 3223–3230 (2018).CrossRef
5.
Zurück zum Zitat B. A. Romantsev, et al., “Producing hot-rolled tubes from Kh18N10T steel in screw-rolling mills,” Proizv. Prokata, No. 8, 14–17 (2014). B. A. Romantsev, et al., “Producing hot-rolled tubes from Kh18N10T steel in screw-rolling mills,” Proizv. Prokata, No. 8, 14–17 (2014).
6.
Zurück zum Zitat A. V. Goncharuk, V. A. Fadeev, and M. V. Kadach, “Seamless pipes manufacturing process improvement using mandreling,” Solid State Phenomena, 316, 402–407 (2021).CrossRef A. V. Goncharuk, V. A. Fadeev, and M. V. Kadach, “Seamless pipes manufacturing process improvement using mandreling,” Solid State Phenomena, 316, 402–407 (2021).CrossRef
7.
Zurück zum Zitat B. A. Romantsev, et al., “Mini tube-production unit 40–80 with a three-high reeling mill,” Metallurgist, 55, No. 11–12, 918–924 (2012).CrossRef B. A. Romantsev, et al., “Mini tube-production unit 40–80 with a three-high reeling mill,” Metallurgist, 55, No. 11–12, 918–924 (2012).CrossRef
8.
Zurück zum Zitat A. S. Aleshchenko, et al., “Wear features of working tools during piercing of high-temperature alloys,” Chern. Metally, 8, No. 8, 63–70 (2018). A. S. Aleshchenko, et al., “Wear features of working tools during piercing of high-temperature alloys,” Chern. Metally, 8, No. 8, 63–70 (2018).
9.
Zurück zum Zitat D. A. Orlov, et al., “Development and investigation of piercing process using cooled guide shoes,” Metallurgist, 65, No. 3–4, 389–399 (2021).CrossRef D. A. Orlov, et al., “Development and investigation of piercing process using cooled guide shoes,” Metallurgist, 65, No. 3–4, 389–399 (2021).CrossRef
10.
Zurück zum Zitat A. A. Korsakov, et al., “Analysis of technology solutions intended to increase the durability of piercing mandrels,” Proizv. Prokata, No. 5, 27–35 (2012). A. A. Korsakov, et al., “Analysis of technology solutions intended to increase the durability of piercing mandrels,” Proizv. Prokata, No. 5, 27–35 (2012).
11.
Zurück zum Zitat I. O. Sazonenko, et al., “Revisiting the issue of increasing the durability of piercing mandrels,” Lit’e Metallurg., No. 4 (68), 135–138 (2012). I. O. Sazonenko, et al., “Revisiting the issue of increasing the durability of piercing mandrels,” Lit’e Metallurg., No. 4 (68), 135–138 (2012).
12.
Zurück zum Zitat B. A. Romantsev, et al., “Features of piercing mill TPA 50-200 working roll wear during rolling continuously-cast and hot-rolled billets,” Metallurgist, 60, No. 9–10, 1062–1069 (2017).CrossRef B. A. Romantsev, et al., “Features of piercing mill TPA 50-200 working roll wear during rolling continuously-cast and hot-rolled billets,” Metallurgist, 60, No. 9–10, 1062–1069 (2017).CrossRef
13.
Zurück zum Zitat B. A. Romantsev, et al., “Features in the wear of the working rolls of TPA 159-426 piercing mill during rolling of continuously-cast billets of large diameter,” Proizv. Prokata, No. 6, 20–27 (2016). B. A. Romantsev, et al., “Features in the wear of the working rolls of TPA 159-426 piercing mill during rolling of continuously-cast billets of large diameter,” Proizv. Prokata, No. 6, 20–27 (2016).
14.
Zurück zum Zitat K. Serin and H. J. Pehle, “Improved service life of hot working tools in seamless tube plants,” Stahl und Eisen, 134, No. 11, 161–174 (2014). K. Serin and H. J. Pehle, “Improved service life of hot working tools in seamless tube plants,” Stahl und Eisen, 134, No. 11, 161–174 (2014).
15.
Zurück zum Zitat N. M. Vavilkin, et al., “Features of the wear of water-cooled mandrels when piercing alloyed steels,” Izv. VUZov: Chern. Metallurg., No. 7, 37–40 (2009). N. M. Vavilkin, et al., “Features of the wear of water-cooled mandrels when piercing alloyed steels,” Izv. VUZov: Chern. Metallurg., No. 7, 37–40 (2009).
16.
Zurück zum Zitat N. M. Vavilkin, et al., “Studying the thermostressed state of water-cooled piercing mandrels,” Izv. VUZov: Chern. Metallurg., No. 9, 35–38 (2010). N. M. Vavilkin, et al., “Studying the thermostressed state of water-cooled piercing mandrels,” Izv. VUZov: Chern. Metallurg., No. 9, 35–38 (2010).
17.
Zurück zum Zitat A. Ramalho, M. Esteves, and P. Marta, “Friction, and wear behaviour of rolling-sliding steel contacts,” Wear, 302, No. 1–2, 1468–1480 (2013).CrossRef A. Ramalho, M. Esteves, and P. Marta, “Friction, and wear behaviour of rolling-sliding steel contacts,” Wear, 302, No. 1–2, 1468–1480 (2013).CrossRef
18.
Zurück zum Zitat K. Min, et al., “Effects of oxide layers on surface defects during hot rolling processes,” Metals Mater. Int., 18, No. 2, 341–348 (2012).CrossRef K. Min, et al., “Effects of oxide layers on surface defects during hot rolling processes,” Metals Mater. Int., 18, No. 2, 341–348 (2012).CrossRef
19.
Zurück zum Zitat M. Yu. Chubukov, et al., “Studying the influence of the technology of producing piercing mandrels on the structure of surface and internal oxide layers,” Chern. Metally, No. 1, 28–33 (2016). M. Yu. Chubukov, et al., “Studying the influence of the technology of producing piercing mandrels on the structure of surface and internal oxide layers,” Chern. Metally, No. 1, 28–33 (2016).
20.
Zurück zum Zitat M. S. Konovalov, “Selecting material, design, and manufacturing technique of mandrels for piercing corrosion-resistant steel billets,” Innovats. Nauka, No. 12-2, 70–73 (2015). M. S. Konovalov, “Selecting material, design, and manufacturing technique of mandrels for piercing corrosion-resistant steel billets,” Innovats. Nauka, No. 12-2, 70–73 (2015).
21.
Zurück zum Zitat B. A. Romantsev, et al., “Improving the wear resistance of piercing-mill mandrels,” Steel in Transl., 38, No. 11, 897–899 (2008).CrossRef B. A. Romantsev, et al., “Improving the wear resistance of piercing-mill mandrels,” Steel in Transl., 38, No. 11, 897–899 (2008).CrossRef
22.
Zurück zum Zitat Yu. L. Gerasimov, S. V. Avdeev, and Yu. L. Bobarikin, “Studying the influence of features of the oxidized coating of piercing mandrels on their durability,” Chern. Metally, No. 7, 46–49 (2017). Yu. L. Gerasimov, S. V. Avdeev, and Yu. L. Bobarikin, “Studying the influence of features of the oxidized coating of piercing mandrels on their durability,” Chern. Metally, No. 7, 46–49 (2017).
23.
Zurück zum Zitat G. Gevorgyan, et al., “Heat treatment of mandrel steel for pipes’ piercing,” J. Physics: Conf. Series, 1926, No. 1, 012039 (2021). G. Gevorgyan, et al., “Heat treatment of mandrel steel for pipes’ piercing,” J. Physics: Conf. Series, 1926, No. 1, 012039 (2021).
24.
Zurück zum Zitat I. I. Lube, et al., “Increase of resistance of piercing mill mandrels at seamless pipes production of 13Cr grade martensite class stainless steel at line ТПА 159-426 of JSC VTZ,” Ferrous Metallurgy: Bul. Sci., Techn. Econom. Inform., 76, No. 12, 1259–1264 (2020). I. I. Lube, et al., “Increase of resistance of piercing mill mandrels at seamless pipes production of 13Cr grade martensite class stainless steel at line ТПА 159-426 of JSC VTZ,” Ferrous Metallurgy: Bul. Sci., Techn. Econom. Inform., 76, No. 12, 1259–1264 (2020).
25.
Zurück zum Zitat M. Yu. Chubukov, et al., “Change in the surface oxide layer of piercing-mill mandrels over time,” Steel in Transl., 46, No. 11, 818–822 (2016).CrossRef M. Yu. Chubukov, et al., “Change in the surface oxide layer of piercing-mill mandrels over time,” Steel in Transl., 46, No. 11, 818–822 (2016).CrossRef
26.
Zurück zum Zitat A. V. Goncharuk et al., “Piercing of a billet in a mill with guide disks,” Russian Metallurgy (Metally), 2020, No. 13, 1637–1642 (2020).CrossRef A. V. Goncharuk et al., “Piercing of a billet in a mill with guide disks,” Russian Metallurgy (Metally), 2020, No. 13, 1637–1642 (2020).CrossRef
27.
Zurück zum Zitat Yu. V. Gamin, et al., “Prediction of billet fracture at two-high screw rolling piercing,” Metallurgist, 64, No. 9–10, 1020–1028 (2021).CrossRef Yu. V. Gamin, et al., “Prediction of billet fracture at two-high screw rolling piercing,” Metallurgist, 64, No. 9–10, 1020–1028 (2021).CrossRef
28.
Zurück zum Zitat A. S. Budnikov, et al., “Effect of plugless deformation in screw rolling three-roll mill on the change of tube wall thickness,” Chern. Metally, No. 12, 41–45 (2019). A. S. Budnikov, et al., “Effect of plugless deformation in screw rolling three-roll mill on the change of tube wall thickness,” Chern. Metally, No. 12, 41–45 (2019).
29.
Zurück zum Zitat A. Alimov, D. Evdokimov, and S. Evsyukov, “Temperature, and strain rate dependent friction model for hot forming of Ti-6Al-4V titanium alloy,” Mater. Today: Proc., No. 19, 1994–1997 (2019). A. Alimov, D. Evdokimov, and S. Evsyukov, “Temperature, and strain rate dependent friction model for hot forming of Ti-6Al-4V titanium alloy,” Mater. Today: Proc., No. 19, 1994–1997 (2019).
Metadaten
Titel
Studying the Wear Resistance of the Mandrels of a Two-High Screw Rolling Mill
verfasst von
A. S. Aleshchenko
Nguyen Quang
Publikationsdatum
29.09.2022
Verlag
Springer US
Erschienen in
Metallurgist / Ausgabe 5-6/2022
Print ISSN: 0026-0894
Elektronische ISSN: 1573-8892
DOI
https://doi.org/10.1007/s11015-022-01372-5

Weitere Artikel der Ausgabe 5-6/2022

Metallurgist 5-6/2022 Zur Ausgabe

    Marktübersichten

    Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen.