Synthesis and characterization of sulfonated polymers containing triazoles as low-humidity proton exchange membranes

verfasst von: Li Ma, Jingmei Xu, Shu Han, Min Yang, Zhe Wang, Hongzhe Ni, Yu Gui

Erschienen in: Journal of Polymer Research | Ausgabe 8/2014

Einloggen

Aktivieren Sie unsere intelligente Suche um passende Fachinhalte oder Patente zu finden.

search-config
loading …

Abstract

A series of copolymers, sulfonated poly (aryl ether ketone sulfones) containing triazoles (SPAEKST), were synthesized by direct polycondensation reactions. The content of sulfonic acid and triazole groups was controlled by adjusting the molar ratio of feeding. The structures of triazole monomer and SPAEKST copolymers were confirmed by their 1H NMR and FTIR spectral analyses. The performance of membranes such as thermal and oxidative stabilities was clearly improved with increasing content of triazole groups. The morphology of SPAEKST membranes was investigated by TEM analyses, and the results indicate that the sulfonic acid groups were dispersed evenly. No clear phase separation was observed. The contact angle tests showed that the presence of triazoles clearly improved the hydrophilicity of membranes. The water desorption curves showed that the water retention of membranes increased with increasing content of triazole groups. The proton conduction of membranes exhibited a low dependence on relative humidity. At 80 °C, the proton conductivity of SPAEKST-30 % reached to 1.1 mScm−1 under 20 % RH.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Literatur
1.
Zurück zum Zitat Park CH, Lee CH, Guiver MD, Lee MY (2011) Prog Polym Sci 36:1443–1498CrossRef Park CH, Lee CH, Guiver MD, Lee MY (2011) Prog Polym Sci 36:1443–1498CrossRef
2.
Zurück zum Zitat Pu ZJ, Chen L, Long Y, Tong LF, Huang X, Liu XB (2013) J Polym Res 20:182CrossRef Pu ZJ, Chen L, Long Y, Tong LF, Huang X, Liu XB (2013) J Polym Res 20:182CrossRef
3.
Zurück zum Zitat Zhang Y, Fei X, Zhang G, Li HT, Shao K, Zhu J, Zhao CJ, Liu ZG, Han MM, Na H (2010) Int J Hydrogen Energy 35:6409–6417CrossRef Zhang Y, Fei X, Zhang G, Li HT, Shao K, Zhu J, Zhao CJ, Liu ZG, Han MM, Na H (2010) Int J Hydrogen Energy 35:6409–6417CrossRef
4.
Zurück zum Zitat Ianniello R, Schmidt VM, Stimming U, Stumper J, Wallau A (1994) Electrochim Acta 39:1863–1869CrossRef Ianniello R, Schmidt VM, Stimming U, Stumper J, Wallau A (1994) Electrochim Acta 39:1863–1869CrossRef
5.
Zurück zum Zitat Alberti G, Casciola M, Massinelli L, Bauer B (2001) J Membr Sci 185:73–81CrossRef Alberti G, Casciola M, Massinelli L, Bauer B (2001) J Membr Sci 185:73–81CrossRef
6.
Zurück zum Zitat Wang CY, Li NW, Shin DW, Lee SY, Kang NR, Lee YM, Guiver MD (2011) Macromolecules 44:7296–7306CrossRef Wang CY, Li NW, Shin DW, Lee SY, Kang NR, Lee YM, Guiver MD (2011) Macromolecules 44:7296–7306CrossRef
7.
Zurück zum Zitat Abu-Saied MA, Fontananova E, Drioli E, Eldin MSM (2013) J Polym Res 20:187CrossRef Abu-Saied MA, Fontananova E, Drioli E, Eldin MSM (2013) J Polym Res 20:187CrossRef
8.
Zurück zum Zitat Zawodzinski TA, Davey J, Valerio J, Gottesfeld S (1995) Electrochim Acta 40:297–302CrossRef Zawodzinski TA, Davey J, Valerio J, Gottesfeld S (1995) Electrochim Acta 40:297–302CrossRef
11.
Zurück zum Zitat Xu JM, Cheng HL, Ma L, Han HL, Huang YS, Wang Z (2014) J Polym Res 21:423CrossRef Xu JM, Cheng HL, Ma L, Han HL, Huang YS, Wang Z (2014) J Polym Res 21:423CrossRef
13.
Zurück zum Zitat Sen U, Acar O, Celik SU, Bozkurt A, Ata A, Tokumasu T, Miyamoto A (2013) J Polym Res 20:217CrossRef Sen U, Acar O, Celik SU, Bozkurt A, Ata A, Tokumasu T, Miyamoto A (2013) J Polym Res 20:217CrossRef
14.
Zurück zum Zitat Wang JT, Yue XJ, Zhang ZZ, Yang Z, Li YF, Zhang H, Yang XL, Wu H, Jiang ZY (2012) Adv Funct Mater 22:4539–4546CrossRef Wang JT, Yue XJ, Zhang ZZ, Yang Z, Li YF, Zhang H, Yang XL, Wu H, Jiang ZY (2012) Adv Funct Mater 22:4539–4546CrossRef
15.
Zurück zum Zitat Balog S, Gasser U, Mortensen K, Gubler L, Scherer GG, Ben H (2010) Macromol Chem Phys 211:635–643CrossRef Balog S, Gasser U, Mortensen K, Gubler L, Scherer GG, Ben H (2010) Macromol Chem Phys 211:635–643CrossRef
17.
Zurück zum Zitat Hu H, Liu W, Yang L, Xiao M, Wang S, Han DM, Meng YZ (2012) Int J Hydrogen Energy 37:4553–4562CrossRef Hu H, Liu W, Yang L, Xiao M, Wang S, Han DM, Meng YZ (2012) Int J Hydrogen Energy 37:4553–4562CrossRef
18.
Zurück zum Zitat Mahajan CV, Ganesan V (2013) J Phys Chem B 117:5315–5329 Mahajan CV, Ganesan V (2013) J Phys Chem B 117:5315–5329
20.
Zurück zum Zitat Majedi FS, Hasani-Sadrabadi MM, Emami SH, Taghipoor M, Dashtimoghadam E, Bertsch A, Moaddel H, Renaud P (2012) Chem Commun 48:7744–7746CrossRef Majedi FS, Hasani-Sadrabadi MM, Emami SH, Taghipoor M, Dashtimoghadam E, Bertsch A, Moaddel H, Renaud P (2012) Chem Commun 48:7744–7746CrossRef
21.
22.
Zurück zum Zitat Hacıvelioğlu F, Özden S, Çelik SU, Yeşilot S, Kılıç A, Bozkurt A (2011) J Mater Chem 21:1020–1027 Hacıvelioğlu F, Özden S, Çelik SU, Yeşilot S, Kılıç A, Bozkurt A (2011) J Mater Chem 21:1020–1027
23.
Zurück zum Zitat Özden Ş, Çelik SÜ, Bozkurt A (2010) Electrochim Acta 55:88498–8503CrossRef Özden Ş, Çelik SÜ, Bozkurt A (2010) Electrochim Acta 55:88498–8503CrossRef
24.
25.
Zurück zum Zitat Wang Z, Li XF, Zhao CJ, Na H (2005) Chem J Chinese Universities 26:2149–2152 Wang Z, Li XF, Zhao CJ, Na H (2005) Chem J Chinese Universities 26:2149–2152
26.
Zurück zum Zitat Liu BJ, Robertson GP, Kim D, Guiver MD, Hu W, Jiang ZH (2007) Macromolecules 40:1934–1944CrossRef Liu BJ, Robertson GP, Kim D, Guiver MD, Hu W, Jiang ZH (2007) Macromolecules 40:1934–1944CrossRef
27.
Zurück zum Zitat Pang JH, Zhang HB, Li XF, Ren DF, Jiang ZH (2007) Macromol Rapid Commun 28:2332–38CrossRef Pang JH, Zhang HB, Li XF, Ren DF, Jiang ZH (2007) Macromol Rapid Commun 28:2332–38CrossRef
28.
Zurück zum Zitat Asano N, Asano M, Suzuki S, Miyatake K, Uchida H, Watanabe M (2006) J Am Chem Soc 128:1762–1769CrossRef Asano N, Asano M, Suzuki S, Miyatake K, Uchida H, Watanabe M (2006) J Am Chem Soc 128:1762–1769CrossRef
29.
Zurück zum Zitat Gui LY, Zhang CJ, Kang S, Tan N, Xiao GY, Yan DY (2010) Int J Hydrogen Energy 35:2436–2445CrossRef Gui LY, Zhang CJ, Kang S, Tan N, Xiao GY, Yan DY (2010) Int J Hydrogen Energy 35:2436–2445CrossRef
30.
Zurück zum Zitat Gomes D, Roeder J, Ponce ML, Nunes SP (2007) J Membr Sci 295:121–129CrossRef Gomes D, Roeder J, Ponce ML, Nunes SP (2007) J Membr Sci 295:121–129CrossRef
32.
Zurück zum Zitat Zhao XJ, Cheng J, Chen SJ, Zhang J, Wang XL (2010) Colloid Polym Sci 288:1327–1332CrossRef Zhao XJ, Cheng J, Chen SJ, Zhang J, Wang XL (2010) Colloid Polym Sci 288:1327–1332CrossRef
33.
Zurück zum Zitat Wainright JS, Wang JT, Weng D, Savinell RF, Litt M (1995) J Electrochem Soc 142:121–123CrossRef Wainright JS, Wang JT, Weng D, Savinell RF, Litt M (1995) J Electrochem Soc 142:121–123CrossRef
34.
35.
Zurück zum Zitat Einsla ML, Kim YS, Hawley M, Lee H, McGrath JE, Liu BJ, Guiver MD, Pivovar BS (2008) Chem Mater 20:5636–5642CrossRef Einsla ML, Kim YS, Hawley M, Lee H, McGrath JE, Liu BJ, Guiver MD, Pivovar BS (2008) Chem Mater 20:5636–5642CrossRef
36.
Zurück zum Zitat Wu L, Huang CH, Woo J, Wu D, Yun S, Seo S, Xu TW, Moon SH (2010) J Phys Chem B 114:13121–13127 Wu L, Huang CH, Woo J, Wu D, Yun S, Seo S, Xu TW, Moon SH (2010) J Phys Chem B 114:13121–13127
37.
38.
39.
Zurück zum Zitat Jiang Z, Zhao X, Fu Y, Manthiram A (2012) J Mater Chen 22:24862 Jiang Z, Zhao X, Fu Y, Manthiram A (2012) J Mater Chen 22:24862
Metadaten
Titel
Synthesis and characterization of sulfonated polymers containing triazoles as low-humidity proton exchange membranes
verfasst von
Li Ma
Jingmei Xu
Shu Han
Min Yang
Zhe Wang
Hongzhe Ni
Yu Gui
Publikationsdatum
01.08.2014
Verlag
Springer Netherlands
Erschienen in
Journal of Polymer Research / Ausgabe 8/2014
Print ISSN: 1022-9760
Elektronische ISSN: 1572-8935
DOI
https://doi.org/10.1007/s10965-014-0551-z

Weitere Artikel der Ausgabe 8/2014

Journal of Polymer Research 8/2014 Zur Ausgabe

    Marktübersichten

    Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen.