Excellent microwave absorption of PANI/SrM/HGMs composite was prepared via sol–gel method and in situ polymerization reaction. The obtained composites were characterized by SEM, XRD, TGA, VSM and a vector network analyzer. The results indicated that HGMs was completely coated by SrM and PANI/SrM/HGMs composite with core–shell structure was successfully synthesized. The composite exhibits perfect magnetic performance and microwave absorption capacity. Measurement of VSM suggests that the Ms of PANI/SrM/HGMs is 38.5 emu/g. Its RL value can reach up to −19 dB when the thickness is 2.0 mm and −22 dB when the thickness is 1.7 mm.
Bitte loggen Sie sich ein, um Zugang zu diesem Inhalt zu erhalten
Die B2B-Firmensuche für Industrie und Wirtschaft: Kostenfrei in Firmenprofilen nach Lieferanten, Herstellern, Dienstleistern und Händlern recherchieren.
Bedingt durch die Altersstruktur vieler Kabelverteilnetze mit der damit verbundenen verminderten Isolationsfestigkeit oder durch fortschreitenden Kabelausbau ist es immer häufiger erforderlich, anstelle der Resonanz-Sternpunktserdung alternative Konzepte für die Sternpunktsbehandlung umzusetzen. Die damit verbundenen Fehlerortungskonzepte bzw. die Erhöhung der Restströme im Erdschlussfall führen jedoch aufgrund der hohen Fehlerströme zu neuen Anforderungen an die Erdungs- und Fehlerstromrückleitungs-Systeme. Lesen Sie hier über die Auswirkung von leitfähigen Strukturen auf die Stromaufteilung sowie die Potentialverhältnisse in urbanen Kabelnetzen bei stromstarken Erdschlüssen. Jetzt gratis downloaden!