Synthesis of anisotropic NaNbO₃ seed crystals and fabrication of textured (K_0.5Na_0.5)NbO₃-based ceramics

High aspect ratio patelike NaNbO₃ particles with pure perovskite structure have been successfully synthesized by topochemical microcrystal conversion (TMC) from plate-like precursor particles of the layer-structured Bi_2.5Na_3.5Nb₅O₁₈. By changing the Bi_2.5Na_3.5Nb₅O₁₈/Na₂CO₃ ratio, large and thin NaNbO₃ particles with a thickness of approximately 0.5 μm and a width of approximately 20 μm were obtained. The obtained NaNbO₃ particles is quite suitable for fabricating textured (K_0.5Na_0.5)NbO₃-based ceramics. Using the fine platelike NaNbO₃ particles as templates, dense <001> -oriented (K_0.5Na_0.5)NbO₃-0.5 mol %MnO₂ ceramics with high texture quality (Lotgering factor F ₀₀₁ = 87 %) and excellent piezoelectric properties were produced by templated grain growth. Compared with randomly oriented ceramics, textured samples show greatly enhanced properties. The room-temperature strain S, the piezoelectric coefficient d ₃₃ ^* and d ₃₃ reach up to 0.093 %, 233 pm/V and 195pC/N, respectively, which are all about 1.5 times larger than those of non-textured ceramics.