Synthesis of highly porous LaCoO3 catalyst by Nanocasting and its performance for oxygen reduction and evolution reactions in alkaline solution

verfasst von: Jin-Hyun Yang, Ho-Jung Sun, Gyungse Park, Jung-Chul An, Joongpyo Shim

Erschienen in: Journal of Electroceramics | Ausgabe 1-4/2018

Einloggen

Aktivieren Sie unsere intelligente Suche um passende Fachinhalte oder Patente zu finden.

search-config
loading …

Abstract

Highly porous LaCoO3 perovskite was synthesized by a nanocasting method using a mesoporous silica template and subsequently applied as a bifunctional catalyst for the oxygen reduction and evolution reactions in alkaline solution. The La-Co citrate complex was mixed a porous SBA-15 silica template, and then, calcinated at 650 °C to prepare a LaCoO3/SBA-15 composite. Highly porous LaCoO3 was prepared by treating this composite with NaOH to remove the SBA-15 silica template. The obtained LaCoO3 showed a very rough surface, high surface area, and relatively small particle size compared with LaCoO3 prepared by the sol-gel method. The catalytic performance of the highly porous LaCoO3 for the oxygen reduction and evolution reactions was electrochemically measured in alkaline solution. LaCoO3 prepared by the nanocasting exhibited higher cell performance than that prepared by sol-gel method due to its larger surface area.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Literatur
1.
Zurück zum Zitat Y. Li, M. Gong, Y. Liang, J. Feng, J.-E. Kim, H. Wang, G. Hong, B. Zhang, H. Dai, Nature Comm. 4(1), 1805 (2013)CrossRef Y. Li, M. Gong, Y. Liang, J. Feng, J.-E. Kim, H. Wang, G. Hong, B. Zhang, H. Dai, Nature Comm. 4(1), 1805 (2013)CrossRef
2.
Zurück zum Zitat Y. Jin, F. Chen, Y. Lei, X. Wu, Chem. Cat. Chem. 7, 2377 (2015) Y. Jin, F. Chen, Y. Lei, X. Wu, Chem. Cat. Chem. 7, 2377 (2015)
3.
Zurück zum Zitat Y. Wang, X. Cui, Y. Li, Z. Shu, H. Chen, J. Shi, Microporous Mesoporous Mater. 176, 8–15 (2013)CrossRef Y. Wang, X. Cui, Y. Li, Z. Shu, H. Chen, J. Shi, Microporous Mesoporous Mater. 176, 8–15 (2013)CrossRef
4.
Zurück zum Zitat P. Xiao, J. Zhu, H. Li, W. Jiang, T. Wang, Y. Zhu, Y. Zhao, J. Li, ChemCatChem 6(6), 1774–1781 (2014)CrossRef P. Xiao, J. Zhu, H. Li, W. Jiang, T. Wang, Y. Zhu, Y. Zhao, J. Li, ChemCatChem 6(6), 1774–1781 (2014)CrossRef
5.
Zurück zum Zitat Y. Wang, J. Ren, Y. Wang, F. Zhang, X. Liu, Y. Guo, G. Lu, J. Phys. Chem. C 112(39), 15293–15298 (2008)CrossRef Y. Wang, J. Ren, Y. Wang, F. Zhang, X. Liu, Y. Guo, G. Lu, J. Phys. Chem. C 112(39), 15293–15298 (2008)CrossRef
6.
Zurück zum Zitat C.-S. Cheng, L. Zhang, Y.-J. Zhang, S.-P. Jiang, Solid State Ionics 179(7-8), 282–289 (2008)CrossRef C.-S. Cheng, L. Zhang, Y.-J. Zhang, S.-P. Jiang, Solid State Ionics 179(7-8), 282–289 (2008)CrossRef
7.
9.
10.
Zurück zum Zitat S. Lee, Y. Lim, E.-A. Lee, H.-J. Hwang, J.-W. Moon, J. Power Source 157(2), 848–854 (2006)CrossRef S. Lee, Y. Lim, E.-A. Lee, H.-J. Hwang, J.-W. Moon, J. Power Source 157(2), 848–854 (2006)CrossRef
11.
Zurück zum Zitat H.-J. Sun, M.-Y. Cho, J.-C. An, S.-W. Eom, G.-S. Park, J. Shim, Trans. Korean Hydrogen New Energy Soc. 25(4), 436–442 (2014)CrossRef H.-J. Sun, M.-Y. Cho, J.-C. An, S.-W. Eom, G.-S. Park, J. Shim, Trans. Korean Hydrogen New Energy Soc. 25(4), 436–442 (2014)CrossRef
12.
Zurück zum Zitat E.-V. Makshina, N.-S. Nesterenko, S. Siffert, E.-A. Zhilinskaya, A. Aboukais, B.-V. Rommanovsky, Catal. Today 131(1-4), 427–430 (2008)CrossRef E.-V. Makshina, N.-S. Nesterenko, S. Siffert, E.-A. Zhilinskaya, A. Aboukais, B.-V. Rommanovsky, Catal. Today 131(1-4), 427–430 (2008)CrossRef
13.
Zurück zum Zitat S.-W. Eom, C.-W. Lee, M.-S. Yun, Y.-K. Sun, Electrochim. Acta 52(4), 1592–1595 (2006)CrossRef S.-W. Eom, C.-W. Lee, M.-S. Yun, Y.-K. Sun, Electrochim. Acta 52(4), 1592–1595 (2006)CrossRef
14.
Zurück zum Zitat X.Z. Cui, Q.J. He, F.M. Cui, J.J. Zhao, L. Li, H.R. Chen, J.L. Shi, Dalton Trans. 18, 3395 (2009)CrossRef X.Z. Cui, Q.J. He, F.M. Cui, J.J. Zhao, L. Li, H.R. Chen, J.L. Shi, Dalton Trans. 18, 3395 (2009)CrossRef
15.
Zurück zum Zitat Q.J. He, J.L. Shi, F. Chen, M. Zhu, L.X. Zhang, Biomaterials 31(12), 3335–3346 (2010)CrossRef Q.J. He, J.L. Shi, F. Chen, M. Zhu, L.X. Zhang, Biomaterials 31(12), 3335–3346 (2010)CrossRef
16.
Zurück zum Zitat Z.L. Hua, J. Zhou, J.L. Shi, Chem. Commun. 47(38), 10536–10547 (2011)CrossRef Z.L. Hua, J. Zhou, J.L. Shi, Chem. Commun. 47(38), 10536–10547 (2011)CrossRef
17.
Zurück zum Zitat Y.S. Li, Y. Chen, L. Li, J.L. Gu, W.R. Zhao, L. Li, J.L. Shi, Appl. Catal. A: G. E. N. 366, 57 (2009) Y.S. Li, Y. Chen, L. Li, J.L. Gu, W.R. Zhao, L. Li, J.L. Shi, Appl. Catal. A: G. E. N. 366, 57 (2009)
18.
Zurück zum Zitat H.J. Shin, R. Ryoo, M. Kruk, M. Jaroniec, Chem. Commun. 349 (2001) H.J. Shin, R. Ryoo, M. Kruk, M. Jaroniec, Chem. Commun. 349 (2001)
19.
20.
Zurück zum Zitat K. Niu, L. Liang, J. Li, F. Zhang, Microporous Mesoporous Mater. 220, 220–224 (2016)CrossRef K. Niu, L. Liang, J. Li, F. Zhang, Microporous Mesoporous Mater. 220, 220–224 (2016)CrossRef
21.
Zurück zum Zitat M.P. Pechini, US Patent 3, 330,697 (1967) M.P. Pechini, US Patent 3, 330,697 (1967)
22.
Zurück zum Zitat K.-J. Lopez, J.-H. Yang, H.-J. Sun, G.-S. Park, S.-W. Eom, H.-R. Rim, H.-K. Lee, J. Shim, Trans. Korean Hydrogen New Energy Soc. 27(6), 677–684 (2016)CrossRef K.-J. Lopez, J.-H. Yang, H.-J. Sun, G.-S. Park, S.-W. Eom, H.-R. Rim, H.-K. Lee, J. Shim, Trans. Korean Hydrogen New Energy Soc. 27(6), 677–684 (2016)CrossRef
23.
Zurück zum Zitat S.-H. Heo, S.-W. Eom, H.-S. Kim, J. Korean Electrochem, Soc. 12, 342 (2009) S.-H. Heo, S.-W. Eom, H.-S. Kim, J. Korean Electrochem, Soc. 12, 342 (2009)
24.
25.
Zurück zum Zitat J. Mastin, M.-A. Einarsrud, T. Grande, Chem. Mater. 18(6), 1680–1687 (2006)CrossRef J. Mastin, M.-A. Einarsrud, T. Grande, Chem. Mater. 18(6), 1680–1687 (2006)CrossRef
26.
Zurück zum Zitat L. Radev, L. Pavlova, B. Samuneva, E. Kashchieva, I. Mihailova, M. Zaharescu, B. Malic, L. Predoana, Process. Appl. Ceramics 2, 103 (2008) L. Radev, L. Pavlova, B. Samuneva, E. Kashchieva, I. Mihailova, M. Zaharescu, B. Malic, L. Predoana, Process. Appl. Ceramics 2, 103 (2008)
27.
Zurück zum Zitat Y. Liu, J. Deng, S. Xie, Z. Wang, H. Dai, Chin. J. Catal. 37(8), 1193–1205 (2016)CrossRef Y. Liu, J. Deng, S. Xie, Z. Wang, H. Dai, Chin. J. Catal. 37(8), 1193–1205 (2016)CrossRef
28.
Zurück zum Zitat J. Zhao, Y. Liu, X. Li, G. Lu, L. You, X. Liang, F. Liu, T. Zhang, Y. Du, Sensors Actuators B Chem. 181, 802–809 (2013)CrossRef J. Zhao, Y. Liu, X. Li, G. Lu, L. You, X. Liang, F. Liu, T. Zhang, Y. Du, Sensors Actuators B Chem. 181, 802–809 (2013)CrossRef
29.
Zurück zum Zitat J. Sauer, F. Marlow, B. Spliethoff, F. Schuth, Chem. Mater. 14(1), 217–224 (2002)CrossRef J. Sauer, F. Marlow, B. Spliethoff, F. Schuth, Chem. Mater. 14(1), 217–224 (2002)CrossRef
30.
Zurück zum Zitat H. Vidal, S. Bernal, R.T. Baker, D. Finol, J.A. Perez Omil, J.M. Pintado, J.M. Rodriguez-Izquierdo, J. Catal. 183(1), 53–62 (1999)CrossRef H. Vidal, S. Bernal, R.T. Baker, D. Finol, J.A. Perez Omil, J.M. Pintado, J.M. Rodriguez-Izquierdo, J. Catal. 183(1), 53–62 (1999)CrossRef
31.
Zurück zum Zitat Y. Seo, K. Kim, Y. Jung, R. Ryoo, Microporous Mesoporous Mater. 207, 156–162 (2015)CrossRef Y. Seo, K. Kim, Y. Jung, R. Ryoo, Microporous Mesoporous Mater. 207, 156–162 (2015)CrossRef
32.
33.
Zurück zum Zitat N. Tien-Thao, H. Alamdari, S. Kaliaguine, J. Solid State Chem. 181(8), 2006–2019 (2008)CrossRef N. Tien-Thao, H. Alamdari, S. Kaliaguine, J. Solid State Chem. 181(8), 2006–2019 (2008)CrossRef
34.
Zurück zum Zitat V.R. Choudhary, S. Banerjee, B.S. Uphade, Appl. Catal. A: General 197(2), L183–L186 (2000)CrossRef V.R. Choudhary, S. Banerjee, B.S. Uphade, Appl. Catal. A: General 197(2), L183–L186 (2000)CrossRef
35.
Zurück zum Zitat J. Deng, L. Zhang, H. Dai, C.-T. Au, Appl. Catal. A: General 352(1-2), 43–49 (2009)CrossRef J. Deng, L. Zhang, H. Dai, C.-T. Au, Appl. Catal. A: General 352(1-2), 43–49 (2009)CrossRef
36.
Zurück zum Zitat S.-W. Eom, S.-Y. Ahn, I.-J. Kim, Y.-K. Sun, H.-S. Kim, J. Electroceram. 23(2-4), 382–386 (2009)CrossRef S.-W. Eom, S.-Y. Ahn, I.-J. Kim, Y.-K. Sun, H.-S. Kim, J. Electroceram. 23(2-4), 382–386 (2009)CrossRef
Metadaten
Titel
Synthesis of highly porous LaCoO3 catalyst by Nanocasting and its performance for oxygen reduction and evolution reactions in alkaline solution
verfasst von
Jin-Hyun Yang
Ho-Jung Sun
Gyungse Park
Jung-Chul An
Joongpyo Shim
Publikationsdatum
16.11.2018
Verlag
Springer US
Erschienen in
Journal of Electroceramics / Ausgabe 1-4/2018
Print ISSN: 1385-3449
Elektronische ISSN: 1573-8663
DOI
https://doi.org/10.1007/s10832-018-0165-7

Weitere Artikel der Ausgabe 1-4/2018

Journal of Electroceramics 1-4/2018 Zur Ausgabe

Neuer Inhalt