21.07.2017 | Original Paper | Ausgabe 5/2018

Polymer Bulletin 5/2018

Tailoring strategies of polyalkylene glycol ester for varied lube applications

Zeitschrift:
Polymer Bulletin > Ausgabe 5/2018
Autoren:
Aruna Kukrety, Ekta Faujdar, Raj K. Singh, Siddharth S. Ray

Abstract

Three biodegradable/ecofriendly polyalkylene glycol esters 1,4-PTHC3, 1,4-PTHC6 and 1,4-PTHC8 [polyglycol containing 1:4 mol fraction of propylene oxide (PO) and tetrahydrofuran (THF)] esterified with propionic acid (C3 fatty acid), hexanoic acid (C6 fatty acid) and octanoic acid (C8 fatty acid) were synthesized via two-step reaction mechanism. Initially, propylene oxide and tetrahydrofuran were polymerized in 1,2 dichloroethane to obtain a polymer 1,4-PTH (polyglycol containing 1:4 mol fraction of PO and THF) with molecular weight (\(\overline{{M_{n}}}\)) 1070.7. Finally, esterification of 1,4-PTH was done with varied fatty acids, i.e., C3, C6 and C8 fatty acid catalyzed by p-toluenesulfonic acid and toluene as solvent to obtain final products 1,4-PTHC3, 1,4-PTHC6 and 1,4-PTHC8 having the molecular weights (\(\overline{{M_{n}}}\)) 1154.78, (\(\overline{{M_{n}}}\)) 1192.86 and (\(\overline{{M_{n}}}\)) 1220.91, respectively. The molecular structure and crystallinity of the synthesized poly(propyleneoxide-co-tetrahydrofuran) ester was studied by FT-IR, X-ray diffraction and DSC. The physicochemical properties like; pour point (ASTM 97), kinematic viscosity (ASTM 445), viscosity index (ASTM 2270), refractive index, density, thermal stability, autoignition temperature (IS 7895), corrosion stability and oxidation stability (IP 48) were determined. The extreme pressure (IP 239) and antiwear properties (ASTM D 4172) were also evaluated in terms of weld load and average wear scar diameter, respectively. Hence all the properties so determined were compared with the specifications of lube oils and it was revealed that these poly(propyleneoxide-co-tetrahydrofuran) esters, i.e., 1,4-PTHC3, 1,4-PTHC6 and 1,4-PTHC8 had suitable physical and tribological properties to be used as base stock for compressor lubricant, metal working fluid and fire-resistant hydraulic fluid.

Graphical Abstract

Bitte loggen Sie sich ein, um Zugang zu diesem Inhalt zu erhalten

Sie möchten Zugang zu diesem Inhalt erhalten? Dann informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 69.000 Bücher
  • über 500 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Umwelt
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Testen Sie jetzt 30 Tage kostenlos.

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 50.000 Bücher
  • über 380 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Umwelt
  • Maschinenbau + Werkstoffe




Testen Sie jetzt 30 Tage kostenlos.

Literatur
Über diesen Artikel

Weitere Artikel der Ausgabe 5/2018

Polymer Bulletin 5/2018 Zur Ausgabe

Premium Partner

    Marktübersichten

    Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen. 

    Bildnachweise