Liquid-phase bonded aluminum–silicon/aluminum nitride interface structure was investigated using high-resolution transmission electron microscopy. A textured layer of aluminum formed a stable orientation relationship with aluminum nitride, which showed Al(111) to be tilted by about 4° with respect to the AlN(0001) interface plane. The unique orientation relationship between Al and AlN was predicted as one of the stable orientation relationships using coincidence of reciprocal lattice point method, which surveys the degree of geometrical coherency between two crystals in three-dimensional space. A stable orientation relationship was found to be (001)[1\( \bar{1} \)0]Al//(2\( \bar{2} \)03)[11\( \bar{2} \)0]AlN.
Bitte loggen Sie sich ein, um Zugang zu diesem Inhalt zu erhalten
Sie möchten Zugang zu diesem Inhalt erhalten? Dann informieren Sie sich jetzt über unsere Produkte:
Springer Professional "Wirtschaft+Technik"
Online-Abonnement
Mit dem Kombi-Abo erhalten Sie vollen Zugriff auf über 1,8 Mio. Dokumente aus mehr als 61.000 Fachbüchern und rund 500 Fachzeitschriften aus folgenden Fachgebieten:
Mit dem Technik-Abo erhalten Sie Zugriff auf über 1 Mio. Dokumente aus mehr als 40.000 Fachbüchern und 300 Fachzeitschriften aus folgenden Fachgebieten:
Die B2B-Firmensuche für Industrie und Wirtschaft: Kostenfrei in Firmenprofilen nach Lieferanten, Herstellern, Dienstleistern und Händlern recherchieren.
Lesen Sie in diesem ausgewählten Buchkapitel alles über den 3D-Druck im Hinblick auf Begriffe, Funktionsweise, Anwendungsbereiche sowie Nutzen und Grenzen additiver Fertigungsverfahren. Eigenschaften eines schlanken Produktionssystems sowie der Aspekt der „Schlankheit“ werden ebenso beleuchtet wie die Prinzipien und Methoden der Lean Production. Jetzt gratis downloaden!
Marktübersichten
Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen.