The effects of using cathode ray tube (CRT) glass as coarse aggregates in high-strength concrete subjected to high temperature

verfasst von: N. N. M. Pauzi, M. Jamil, R. Hamid, A. Z. Abdin, M. F. M. Zain

Erschienen in: Journal of Material Cycles and Waste Management | Ausgabe 6/2019

Einloggen

Aktivieren Sie unsere intelligente Suche um passende Fachinhalte oder Patente zu finden.

search-config
loading …

Abstract

Waste cathode ray tube glass has been formed into two different products which are spherical glass (GS) and crushed glass (GC). Since it is a new material that acts as a coarse aggregate in concrete production, the architectural and civil structures built with such concretes may face a risk of fire situations. Thus, it is important to analyze the behavior of concrete containing GS and GC after exposure to high temperatures. A series of experimental programs were conducted on mixtures of concrete containing GS and GC as coarse aggregates, which were subjected to high temperatures ranging from ambient temperature to 800 °C at exposure time of 1 and 2 h. Compressive strength, splitting tensile strength, mass loss, and X-ray diffraction were analyzed. Results show better compressive strength in concrete containing GS at temperature 200–600 °C. However, the use of GS affects the splitting tensile strength more negatively, compared to GC. But, at a temperature beyond 600 °C, the use of GC causing bubbles of glass appeared on the surface of concrete and toxic Pb was found in the crushed concrete paste.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Literatur
1.
Zurück zum Zitat Lairaksa N, Moon AR, Makul N (2013) Utilization of cathode ray tube waste: encapsulation of PbO-containing funnel glass in Portland cement clinker. J Environ Manag 117:180–186CrossRef Lairaksa N, Moon AR, Makul N (2013) Utilization of cathode ray tube waste: encapsulation of PbO-containing funnel glass in Portland cement clinker. J Environ Manag 117:180–186CrossRef
2.
Zurück zum Zitat Xu Q, Li G, He W et al (2012) Cathode ray tube (CRT) recycling: current capabilities in China and research progress. Waste Manag 32:1566–1574CrossRef Xu Q, Li G, He W et al (2012) Cathode ray tube (CRT) recycling: current capabilities in China and research progress. Waste Manag 32:1566–1574CrossRef
3.
Zurück zum Zitat Shaw Environmental Inc. (Shaw) (2013) An analysis of the demand for CRT glass processing in the US. CB&I company, Kuusakoski Recycling, USA Shaw Environmental Inc. (Shaw) (2013) An analysis of the demand for CRT glass processing in the US. CB&I company, Kuusakoski Recycling, USA
5.
Zurück zum Zitat Meng W, Wang X, Yuan W et al (2016) The recycling of leaded glass in cathode ray tube (CRT). Procedia Environ Sci 31:954–960CrossRef Meng W, Wang X, Yuan W et al (2016) The recycling of leaded glass in cathode ray tube (CRT). Procedia Environ Sci 31:954–960CrossRef
7.
Zurück zum Zitat Ling TC, Poon CS (2013) Effects of particle size of treated CRT funnel glass on properties of cement mortar. Mater Struct 46:25–34CrossRef Ling TC, Poon CS (2013) Effects of particle size of treated CRT funnel glass on properties of cement mortar. Mater Struct 46:25–34CrossRef
8.
Zurück zum Zitat Ling TC, Poon CS (2014) Use of CRT funnel glass in concrete blocks prepared with different aggregate-to-cement ratios. Green Mater 2:43–51CrossRef Ling TC, Poon CS (2014) Use of CRT funnel glass in concrete blocks prepared with different aggregate-to-cement ratios. Green Mater 2:43–51CrossRef
10.
Zurück zum Zitat Romero D, James J, Mora R, Hays CD (2013) Study on the mechanical and environmental properties of concrete containing cathode ray tube glass aggregate. Waste Manag 33:1659–1666CrossRef Romero D, James J, Mora R, Hays CD (2013) Study on the mechanical and environmental properties of concrete containing cathode ray tube glass aggregate. Waste Manag 33:1659–1666CrossRef
11.
Zurück zum Zitat Zhao H, Poon CS (2017) A comparative study on the properties of the mortar with the cathode ray tube funnel glass sand at different treatment methods. Constr Build Mater 148:900–909CrossRef Zhao H, Poon CS (2017) A comparative study on the properties of the mortar with the cathode ray tube funnel glass sand at different treatment methods. Constr Build Mater 148:900–909CrossRef
12.
Zurück zum Zitat Walczak P, Małolepszy J, Reben M, Rzepa K (2015) Mechanical properties of concrete mortar based on mixture of CRT glass cullet and fluidized fly ash. Procedia Eng 108:453–458CrossRef Walczak P, Małolepszy J, Reben M, Rzepa K (2015) Mechanical properties of concrete mortar based on mixture of CRT glass cullet and fluidized fly ash. Procedia Eng 108:453–458CrossRef
13.
Zurück zum Zitat National Research Council (2010) Prudent practices in the laboratory: handling and disposal of chemicals: nitric acid. In: Laboratory sheet. National Academy of Sciences, USA National Research Council (2010) Prudent practices in the laboratory: handling and disposal of chemicals: nitric acid. In: Laboratory sheet. National Academy of Sciences, USA
14.
Zurück zum Zitat Iniaghe PO, Adie GU (2015) Management practices for end-of-life cathode ray tube glass: review of advances in recycling and best available technologies. Waste Manag Res 33:947–961CrossRef Iniaghe PO, Adie GU (2015) Management practices for end-of-life cathode ray tube glass: review of advances in recycling and best available technologies. Waste Manag Res 33:947–961CrossRef
15.
Zurück zum Zitat Pauzi NNM, Jamil M, Hamid R et al (2019) Influence of spherical and crushed waste cathode-ray tube (CRT) glass on lead (Pb) leaching and mechanical properties of concrete. J Build Eng 21:421–428CrossRef Pauzi NNM, Jamil M, Hamid R et al (2019) Influence of spherical and crushed waste cathode-ray tube (CRT) glass on lead (Pb) leaching and mechanical properties of concrete. J Build Eng 21:421–428CrossRef
16.
Zurück zum Zitat Zhao H, Poon CS, Ling TC (2013) Properties of mortar prepared with recycled cathode ray tube funnel glass sand at different mineral admixture. Constr Build Mater 40:951–960CrossRef Zhao H, Poon CS, Ling TC (2013) Properties of mortar prepared with recycled cathode ray tube funnel glass sand at different mineral admixture. Constr Build Mater 40:951–960CrossRef
17.
Zurück zum Zitat Rajabipour F, Maraghechi H, Fischer G (2010) Investigating the alkali-silica reaction of recycled glass aggregates in concrete materials. J Mater Civ Eng 22:1201–1208CrossRef Rajabipour F, Maraghechi H, Fischer G (2010) Investigating the alkali-silica reaction of recycled glass aggregates in concrete materials. J Mater Civ Eng 22:1201–1208CrossRef
18.
Zurück zum Zitat Maschio S, Tonello G, Furlani E (2013) Recycling glass cullet from waste CRTs for the production of high strength mortars. J Waste Manag 2013:1–8CrossRef Maschio S, Tonello G, Furlani E (2013) Recycling glass cullet from waste CRTs for the production of high strength mortars. J Waste Manag 2013:1–8CrossRef
19.
Zurück zum Zitat IS 456 (2000) Plain and reinforced concrete. Indian Standards, New Delhi IS 456 (2000) Plain and reinforced concrete. Indian Standards, New Delhi
20.
Zurück zum Zitat Kumar R, Singh S, Singh LP (2017) Studies on enhanced thermally stable high strength concrete incorporating silica nanoparticles. Constr Build Mater 153:506–513CrossRef Kumar R, Singh S, Singh LP (2017) Studies on enhanced thermally stable high strength concrete incorporating silica nanoparticles. Constr Build Mater 153:506–513CrossRef
21.
Zurück zum Zitat Laneyrie C, Beaucour AL, Green MF et al (2016) Influence of recycled coarse aggregates on normal and high performance concrete subjected to elevated temperatures. Constr Build Mater 111:368–378CrossRef Laneyrie C, Beaucour AL, Green MF et al (2016) Influence of recycled coarse aggregates on normal and high performance concrete subjected to elevated temperatures. Constr Build Mater 111:368–378CrossRef
22.
Zurück zum Zitat Arioz O (2007) Effects of elevated temperatures on properties of concrete. Fire Saf J 42:516–522CrossRef Arioz O (2007) Effects of elevated temperatures on properties of concrete. Fire Saf J 42:516–522CrossRef
23.
Zurück zum Zitat Ali MH, Dinkha YZ, Haido JH (2017) Mechanical properties and spalling at elevated temperature of high performance concrete made with reactive and waste inert powders. Eng Sci Technol Int J 20:536–541CrossRef Ali MH, Dinkha YZ, Haido JH (2017) Mechanical properties and spalling at elevated temperature of high performance concrete made with reactive and waste inert powders. Eng Sci Technol Int J 20:536–541CrossRef
25.
Zurück zum Zitat Khaliq W, Waheed F (2017) Mechanical response and spalling sensitivity of air entrained high-strength concrete at elevated temperatures. Constr Build Mater 150:747–757CrossRef Khaliq W, Waheed F (2017) Mechanical response and spalling sensitivity of air entrained high-strength concrete at elevated temperatures. Constr Build Mater 150:747–757CrossRef
26.
Zurück zum Zitat Siddique R, Noumowe AN (2010) An overview of the properties of high-strength concrete subjected to elevated temperatures. Indoor Built Environ 19:612–622CrossRef Siddique R, Noumowe AN (2010) An overview of the properties of high-strength concrete subjected to elevated temperatures. Indoor Built Environ 19:612–622CrossRef
27.
Zurück zum Zitat Bosnjak J, Ozbolt J, Hahn R (2013) Permeability measurement on high strength concrete without and with polypropylene fibers at elevated temperatures using a new test setup. Cem Concr Res 53:104–111CrossRef Bosnjak J, Ozbolt J, Hahn R (2013) Permeability measurement on high strength concrete without and with polypropylene fibers at elevated temperatures using a new test setup. Cem Concr Res 53:104–111CrossRef
28.
Zurück zum Zitat Ling TC, Poon CS, Kou SC (2012) Influence of recycled glass content and curing conditions on the properties of self-compacting concrete after exposure to elevated temperatures. Cem Concr Compos 34:265–272CrossRef Ling TC, Poon CS, Kou SC (2012) Influence of recycled glass content and curing conditions on the properties of self-compacting concrete after exposure to elevated temperatures. Cem Concr Compos 34:265–272CrossRef
29.
Zurück zum Zitat Guo MZ, Chen Z, Ling TC, Poon CS (2015) Effects of recycled glass on properties of architectural mortar before and after exposure to elevated temperatures. J Clean Prod 101:1–7CrossRef Guo MZ, Chen Z, Ling TC, Poon CS (2015) Effects of recycled glass on properties of architectural mortar before and after exposure to elevated temperatures. J Clean Prod 101:1–7CrossRef
30.
Zurück zum Zitat AC1 211.4R-08 (2008) Guide for selecting proportions for high-strength concrete using Portland cement and other cementitious material. American Concrete Institute, Michigan AC1 211.4R-08 (2008) Guide for selecting proportions for high-strength concrete using Portland cement and other cementitious material. American Concrete Institute, Michigan
31.
Zurück zum Zitat BS 882:1992 (1992) Specification for aggregates from natural sources for concrete. British Standard, Brussels BS 882:1992 (1992) Specification for aggregates from natural sources for concrete. British Standard, Brussels
32.
Zurück zum Zitat ASTM C192, C (2006) Standard practice for making and curing concrete test specimens in the laboratory. ASTM International, West Conshohocken ASTM C192, C (2006) Standard practice for making and curing concrete test specimens in the laboratory. ASTM International, West Conshohocken
33.
Zurück zum Zitat ASTM E119 (2008) Standard test methods for fire tests of building construction and materials. ASTM International, West Conshohocken ASTM E119 (2008) Standard test methods for fire tests of building construction and materials. ASTM International, West Conshohocken
34.
Zurück zum Zitat ISO 834 (1999) Fire resistance test: elements of building construction. International organization for standardization, Geneva ISO 834 (1999) Fire resistance test: elements of building construction. International organization for standardization, Geneva
35.
Zurück zum Zitat BS EN 12390-3 (2001) Testing hardened concrete, part 3: compressive strength of test specimens. British Standard, Brussels BS EN 12390-3 (2001) Testing hardened concrete, part 3: compressive strength of test specimens. British Standard, Brussels
36.
Zurück zum Zitat ASTM C496 (2004) Standard test method for splitting tensile strength of cylindrical concrete. ASTM International, West Conshohocken ASTM C496 (2004) Standard test method for splitting tensile strength of cylindrical concrete. ASTM International, West Conshohocken
37.
Zurück zum Zitat Jameran A, Ibrahim IS, Yazan SHS, Rahim SNAA (2015) Mechanical properties of steel-polypropylene fibre reinforced concrete under elevated temperature. Procedia Eng 125:818–824CrossRef Jameran A, Ibrahim IS, Yazan SHS, Rahim SNAA (2015) Mechanical properties of steel-polypropylene fibre reinforced concrete under elevated temperature. Procedia Eng 125:818–824CrossRef
38.
Zurück zum Zitat Xiao J, Li Z, Xie Q, Shen L (2016) Effect of strain rate on compressive behaviour of high-strength concrete after exposure to elevated temperatures. Fire Saf J 83:25–37CrossRef Xiao J, Li Z, Xie Q, Shen L (2016) Effect of strain rate on compressive behaviour of high-strength concrete after exposure to elevated temperatures. Fire Saf J 83:25–37CrossRef
39.
Zurück zum Zitat Mousa MI (2015) Effect of elevated temperature on the properties of silica fume and recycled rubber-filled high strength concretes (RHSC). HBRC J 13:1–7CrossRef Mousa MI (2015) Effect of elevated temperature on the properties of silica fume and recycled rubber-filled high strength concretes (RHSC). HBRC J 13:1–7CrossRef
41.
Zurück zum Zitat Sancak E, Sari YD, Simsek O (2008) Effects of elevated temperature on compressive strength and weight loss of the light-weight concrete with silica fume and superplasticizer. Cem Concr Compos 30:715–721CrossRef Sancak E, Sari YD, Simsek O (2008) Effects of elevated temperature on compressive strength and weight loss of the light-weight concrete with silica fume and superplasticizer. Cem Concr Compos 30:715–721CrossRef
42.
Zurück zum Zitat Ling TC, Poon CS (2013) High temperatures properties of barite concrete with CRT funnel glass. Fire Mater 38:279–289CrossRef Ling TC, Poon CS (2013) High temperatures properties of barite concrete with CRT funnel glass. Fire Mater 38:279–289CrossRef
43.
Zurück zum Zitat Ling TC, Poon CS (2014) Use of recycled CRT funnel glass as fine aggregate in dry-mixed concrete paving blocks. J Clean Prod 68:209–215CrossRef Ling TC, Poon CS (2014) Use of recycled CRT funnel glass as fine aggregate in dry-mixed concrete paving blocks. J Clean Prod 68:209–215CrossRef
44.
Zurück zum Zitat Sua-iam G, Makul N (2013) Use of limestone powder during incorporation of Pb-containing cathode ray tube waste in self-compacting concrete. J Environ Manag 128:931–940CrossRef Sua-iam G, Makul N (2013) Use of limestone powder during incorporation of Pb-containing cathode ray tube waste in self-compacting concrete. J Environ Manag 128:931–940CrossRef
45.
Zurück zum Zitat Tan KH, Du H (2013) Use of waste glass as sand in mortar: part I—fresh, mechanical and durability properties. Cem Concr Compos 35:118–126CrossRef Tan KH, Du H (2013) Use of waste glass as sand in mortar: part I—fresh, mechanical and durability properties. Cem Concr Compos 35:118–126CrossRef
47.
Zurück zum Zitat Musa A, Duna S, Mohammed AG (2017) The effect of elevated temperature on compressive strength of waste glass powder and metakaolin concrete. Am J Eng Res 6:63–69 Musa A, Duna S, Mohammed AG (2017) The effect of elevated temperature on compressive strength of waste glass powder and metakaolin concrete. Am J Eng Res 6:63–69
48.
Zurück zum Zitat Terro MJ (2006) Properties of concrete made with recycled crushed glass at elevated temperatures. Build Environ 41:633–639CrossRef Terro MJ (2006) Properties of concrete made with recycled crushed glass at elevated temperatures. Build Environ 41:633–639CrossRef
49.
Zurück zum Zitat Zhao H, Poon CS, Ling TC (2013) Utilizing recycled cathode ray tube funnel glass sand as river sand replacement in the high-density concrete. J Clean Prod 51:184–190CrossRef Zhao H, Poon CS, Ling TC (2013) Utilizing recycled cathode ray tube funnel glass sand as river sand replacement in the high-density concrete. J Clean Prod 51:184–190CrossRef
50.
Zurück zum Zitat Berenjian A, Whittleston G (2017) History and manufacturing of glass. Am J Mater Sci 7:18–24 Berenjian A, Whittleston G (2017) History and manufacturing of glass. Am J Mater Sci 7:18–24
51.
Zurück zum Zitat Lee J, Yee AF (2001) Fracture behavior of glass bead filled epoxies: cleaning process of glass beads. J Appl Polym Sci 79:1371–1383CrossRef Lee J, Yee AF (2001) Fracture behavior of glass bead filled epoxies: cleaning process of glass beads. J Appl Polym Sci 79:1371–1383CrossRef
52.
Zurück zum Zitat Phonphuak N, Kanyakam S, Chindaprasirt P (2016) Utilization of waste glass to enhance physical–mechanical properties of fired clay brick. J Clean Prod 112:3057–3062CrossRef Phonphuak N, Kanyakam S, Chindaprasirt P (2016) Utilization of waste glass to enhance physical–mechanical properties of fired clay brick. J Clean Prod 112:3057–3062CrossRef
53.
Zurück zum Zitat Rashad AM (2015) An exploratory study on high-volume fly ash concrete incorporating silica fume subjected to thermal loads. J Clean Prod 87:735–744CrossRef Rashad AM (2015) An exploratory study on high-volume fly ash concrete incorporating silica fume subjected to thermal loads. J Clean Prod 87:735–744CrossRef
54.
Zurück zum Zitat Vaitkevicius V, Serelis E, Hilbig H (2014) The effect of glass powder on the microstructure of ultra-high performance concrete. Constr Build Mater 68:102–109CrossRef Vaitkevicius V, Serelis E, Hilbig H (2014) The effect of glass powder on the microstructure of ultra-high performance concrete. Constr Build Mater 68:102–109CrossRef
55.
Zurück zum Zitat Ibrahim RK, Hamid R, Taha MR (2012) Fire resistance of high-volume fly ash mortars with nanosilica addition. Constr Build Mater 36:779–786CrossRef Ibrahim RK, Hamid R, Taha MR (2012) Fire resistance of high-volume fly ash mortars with nanosilica addition. Constr Build Mater 36:779–786CrossRef
56.
Zurück zum Zitat Saridemir M, Severcan MH, Ciflikli M et al (2016) The influence of elevated temperature on strength and microstructure of high strength concrete containing ground pumice and metakaolin. Constr Build Mater 124:244–257CrossRef Saridemir M, Severcan MH, Ciflikli M et al (2016) The influence of elevated temperature on strength and microstructure of high strength concrete containing ground pumice and metakaolin. Constr Build Mater 124:244–257CrossRef
Metadaten
Titel
The effects of using cathode ray tube (CRT) glass as coarse aggregates in high-strength concrete subjected to high temperature
verfasst von
N. N. M. Pauzi
M. Jamil
R. Hamid
A. Z. Abdin
M. F. M. Zain
Publikationsdatum
11.07.2019
Verlag
Springer Japan
Erschienen in
Journal of Material Cycles and Waste Management / Ausgabe 6/2019
Print ISSN: 1438-4957
Elektronische ISSN: 1611-8227
DOI
https://doi.org/10.1007/s10163-019-00893-7

Weitere Artikel der Ausgabe 6/2019

Journal of Material Cycles and Waste Management 6/2019 Zur Ausgabe