The Influence of Al Content and Thickness on the Microstructure and Tensile Properties in High-Pressure Die Cast Magnesium Alloys

verfasst von: Erin Deda, Tracy D. Berman, John E. Allison

Erschienen in: Metallurgical and Materials Transactions A | Ausgabe 4/2017

Einloggen

Aktivieren Sie unsere intelligente Suche um passende Fachinhalte oder Patente zu finden.

search-config
loading …

Abstract

The influence of Al content and section thickness on the microstructural features and tensile properties of high-pressure die cast AM series magnesium alloys is quantified in order to better understand the relationship between microstructure and tensile properties. It is found that with increasing aluminum content, the yield strength increases and the ductility decreases. Increasing the plate thickness results in a decrease in both the yield strength and ductility. The grain size, β-Mg17Al12 phase volume fraction, and solute content are all quantified through the thickness of the plates. It is found that the plates have a skin with increased hardness, due to a fine grain structure. The primary factors affecting strengthening in these alloys, including microstructural variations through the thickness, are accounted for using a linear superposition model. We conclude that yield strength is dominated by grain boundary strengthening and solid solution strengthening effects. The through-thickness grain size and solute concentration were quantified and these variations were found to play an important role in controlling the yield strength of these alloys.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Literatur
1.
Zurück zum Zitat B.L. Mordike and T. Ebert: Mater. Sci. Eng. A, 2001, vol. 302, pp. 37–45.CrossRef B.L. Mordike and T. Ebert: Mater. Sci. Eng. A, 2001, vol. 302, pp. 37–45.CrossRef
2.
Zurück zum Zitat A.L. Bowles, Q. Han, and J.A. Horton: Essent. Readings Magnes. Technol., 2014, pp. 197–202. A.L. Bowles, Q. Han, and J.A. Horton: Essent. Readings Magnes. Technol., 2014, pp. 197–202.
3.
4.
Zurück zum Zitat M.M. Avedesian and H. Baker, eds.: ASM Specialty Handbook—Magnesium and Magnesium Alloys, ASM International, Metals Park, OH, 1999. M.M. Avedesian and H. Baker, eds.: ASM Specialty Handbook—Magnesium and Magnesium Alloys, ASM International, Metals Park, OH, 1999.
5.
Zurück zum Zitat K.V. Yang, M.A. Easton, and C.H. Cáceres: Adv. Eng. Mater., 2013, vol. 15, pp. 302–7.CrossRef K.V. Yang, M.A. Easton, and C.H. Cáceres: Adv. Eng. Mater., 2013, vol. 15, pp. 302–7.CrossRef
6.
Zurück zum Zitat M .R. Barone and D. A. Caulk: Int. J. Eng. Sci., 2000, vol. 38, pp. 1279–1302.CrossRef M .R. Barone and D. A. Caulk: Int. J. Eng. Sci., 2000, vol. 38, pp. 1279–1302.CrossRef
7.
Zurück zum Zitat J.H. Forsmark, J.W. Zindel, L. Godlewski, and A. Caliskan: SAE Int., 2012, pp. 2–10. J.H. Forsmark, J.W. Zindel, L. Godlewski, and A. Caliskan: SAE Int., 2012, pp. 2–10.
8.
Zurück zum Zitat C. Dørum, O.S. Hopperstad, M. Langseth, O.-G. Lademo, and S. Sannes: SAE Tech. Pap. Ser., 2005, vol. 2005-01-07, p. 8. C. Dørum, O.S. Hopperstad, M. Langseth, O.-G. Lademo, and S. Sannes: SAE Tech. Pap. Ser., 2005, vol. 2005-01-07, p. 8.
9.
Zurück zum Zitat J.P. Weiler, J.T. Wood, R.J. Klassen, E. Maire, R. Berkmortel, and G. Wang: Mater. Sci. Eng. A, 2005, vol. 395, pp. 315–22.CrossRef J.P. Weiler, J.T. Wood, R.J. Klassen, E. Maire, R. Berkmortel, and G. Wang: Mater. Sci. Eng. A, 2005, vol. 395, pp. 315–22.CrossRef
10.
Zurück zum Zitat C.D. Lee: Mater. Sci. Eng. A, 2007, vol. 454–455, pp. 575–80.CrossRef C.D. Lee: Mater. Sci. Eng. A, 2007, vol. 454–455, pp. 575–80.CrossRef
11.
Zurück zum Zitat K.S. Choi, D. Li, X. Sun, M. Li, and J.E. Allison: SAE Int., 2013, pp. 3–10. K.S. Choi, D. Li, X. Sun, M. Li, and J.E. Allison: SAE Int., 2013, pp. 3–10.
12.
Zurück zum Zitat J.E. Allison, D. Backman, and L. Christodoulou: J. Mater., 2006, vol. 58, pp. 25–27. J.E. Allison, D. Backman, and L. Christodoulou: J. Mater., 2006, vol. 58, pp. 25–27.
13.
Zurück zum Zitat S. Sannes, H. Gjestland, and H. Westengen: SAE Tech. Pap. Ser., 2005, vol. 2005-01-03, p. 7. S. Sannes, H. Gjestland, and H. Westengen: SAE Tech. Pap. Ser., 2005, vol. 2005-01-03, p. 7.
14.
Zurück zum Zitat J.H. Forsmark, J.W. Zindel, L. Godlewski, J. Zheng, J.E. Allison, and M. Li: Integr. Mater. Manuf. Innov., 2015, vol. 4, pp. 1–38. J.H. Forsmark, J.W. Zindel, L. Godlewski, J. Zheng, J.E. Allison, and M. Li: Integr. Mater. Manuf. Innov., 2015, vol. 4, pp. 1–38.
15.
Zurück zum Zitat U. Weiss and A. Bach: La Metall. Ital., 2011, vol. 11–12, pp. 31–39. U. Weiss and A. Bach: La Metall. Ital., 2011, vol. 11–12, pp. 31–39.
16.
Zurück zum Zitat K.V. Yang, C.H. Cáceres, and M.A. Easton: Metall. Mater. Trans. A, 2014, vol. 45, pp. 4117–28.CrossRef K.V. Yang, C.H. Cáceres, and M.A. Easton: Metall. Mater. Trans. A, 2014, vol. 45, pp. 4117–28.CrossRef
17.
Zurück zum Zitat P. Sharifi, Y. Fan, K. Sadayappan, G. Birsan, and J.T. Wood: in Magnes. Technol. 2015, 2015, pp. 351–56. P. Sharifi, Y. Fan, K. Sadayappan, G. Birsan, and J.T. Wood: in Magnes. Technol. 2015, 2015, pp. 351–56.
18.
Zurück zum Zitat I. Toda-Caraballo, E.I. Galindo-Nava, and P.E.J. Rivera-Díaz-del-Castillo: Acta Mater., 2014, vol. 75, pp. 287–96.CrossRef I. Toda-Caraballo, E.I. Galindo-Nava, and P.E.J. Rivera-Díaz-del-Castillo: Acta Mater., 2014, vol. 75, pp. 287–96.CrossRef
19.
Zurück zum Zitat C.H. Cáceres, W.J. Poole, A.L. Bowles, and C.J. Davidson: Mater. Sci. Eng. A, 2005, vol. 402, pp. 269–77.CrossRef C.H. Cáceres, W.J. Poole, A.L. Bowles, and C.J. Davidson: Mater. Sci. Eng. A, 2005, vol. 402, pp. 269–77.CrossRef
20.
Zurück zum Zitat D. Rodrigo, M. T. Murray, and H. Mao: SAE Int. Congr. Magnes. Sess., 1999. D. Rodrigo, M. T. Murray, and H. Mao: SAE Int. Congr. Magnes. Sess., 1999.
21.
Zurück zum Zitat T.K. Aune, H. Westengen, and T. Ruden: SAE Tech., 1993, pp. 51–57. T.K. Aune, H. Westengen, and T. Ruden: SAE Tech., 1993, pp. 51–57.
22.
Zurück zum Zitat C.H. Cáceres and B.I. Selling: Mater. Sci. Eng. A, 1996, vol. 220, pp. 109–16.CrossRef C.H. Cáceres and B.I. Selling: Mater. Sci. Eng. A, 1996, vol. 220, pp. 109–16.CrossRef
23.
Zurück zum Zitat T.D. Berman, T.M. Pollock, and J.W. Jones: Metall. Mater. Trans. A, 2015, vol. 46, pp. 2986–98.CrossRef T.D. Berman, T.M. Pollock, and J.W. Jones: Metall. Mater. Trans. A, 2015, vol. 46, pp. 2986–98.CrossRef
24.
Zurück zum Zitat E.I. Barker, K.S. Choi, X. Sun, E. Deda, J. Allison, M. Li, J. Forsmark, J. Zindel, and L. Godlewski: Comput. Mater. Sci., 2014, vol. 92, pp. 353–61.CrossRef E.I. Barker, K.S. Choi, X. Sun, E. Deda, J. Allison, M. Li, J. Forsmark, J. Zindel, and L. Godlewski: Comput. Mater. Sci., 2014, vol. 92, pp. 353–61.CrossRef
25.
Zurück zum Zitat K.S. Choi, E.I. Barker, G. Cheng, X. Sun, J. Forsmark, and M. Li: SAE Int. J. Mater. Manuf., 2016, vol. 9, pp. 2016-01-0290. K.S. Choi, E.I. Barker, G. Cheng, X. Sun, J. Forsmark, and M. Li: SAE Int. J. Mater. Manuf., 2016, vol. 9, pp. 2016-01-0290.
26.
Zurück zum Zitat K. Vanna Yang, M.A. Easton, and C.H. Cáceres: Mater. Sci. Eng. A, 2013, vol. 580, pp. 191–95.CrossRef K. Vanna Yang, M.A. Easton, and C.H. Cáceres: Mater. Sci. Eng. A, 2013, vol. 580, pp. 191–95.CrossRef
27.
Zurück zum Zitat T.D. Berman: University of Michigan, Ann Arbor, MI, unpublished research, 2016. T.D. Berman: University of Michigan, Ann Arbor, MI, unpublished research, 2016.
29.
Zurück zum Zitat B. Puchala, G. Tarcea, E.A. Marquis, M. Hedstrom, H.V. Jagadish, and J.E. Allison: Jom, 2016, vol. 68, pp. 2035–44.CrossRef B. Puchala, G. Tarcea, E.A. Marquis, M. Hedstrom, H.V. Jagadish, and J.E. Allison: Jom, 2016, vol. 68, pp. 2035–44.CrossRef
30.
Zurück zum Zitat L.-Y. Wei and R. Warren: Mater. Sci. Technol., 2007, vol. 23, pp. 745–52.CrossRef L.-Y. Wei and R. Warren: Mater. Sci. Technol., 2007, vol. 23, pp. 745–52.CrossRef
31.
Zurück zum Zitat V.Y. Gertsman, J. Li, S. Xu, J.P. Thomson, and M. Sahoo: Metall. Mater. Trans. A, 2005, vol. 36, pp. 1989–97.CrossRef V.Y. Gertsman, J. Li, S. Xu, J.P. Thomson, and M. Sahoo: Metall. Mater. Trans. A, 2005, vol. 36, pp. 1989–97.CrossRef
32.
Zurück zum Zitat J.H. Forsmark, Z. Dowling, K. Gibson, C. Mueller, L. Godlewski, J.W. Zindel, and J.M. Boileau: SAE Int. J. Mater. Manuf., 2015, vol. 8. J.H. Forsmark, Z. Dowling, K. Gibson, C. Mueller, L. Godlewski, J.W. Zindel, and J.M. Boileau: SAE Int. J. Mater. Manuf., 2015, vol. 8.
33.
Zurück zum Zitat C.M. Gourlay, H.I. Laukli, and A.K. Dahle: Metall. Mater. Trans. A, 2007, vol. 38, pp. 1833–44.CrossRef C.M. Gourlay, H.I. Laukli, and A.K. Dahle: Metall. Mater. Trans. A, 2007, vol. 38, pp. 1833–44.CrossRef
34.
Zurück zum Zitat N. Tahreen, D.L. Chen, M. Nouri, and D.Y. Li: J. Alloys Compd., 2015, vol. 623, pp. 15–23.CrossRef N. Tahreen, D.L. Chen, M. Nouri, and D.Y. Li: J. Alloys Compd., 2015, vol. 623, pp. 15–23.CrossRef
35.
Zurück zum Zitat A.L. Bowles, K. Nogita, M.S. Dargusch, and C.J. Davidson: Mater. Trans, 2004, vol. 45, pp. 3114–19.CrossRef A.L. Bowles, K. Nogita, M.S. Dargusch, and C.J. Davidson: Mater. Trans, 2004, vol. 45, pp. 3114–19.CrossRef
36.
Zurück zum Zitat A.V. Nagasekhar, M.A. Easton, and C.H. Cáceres: Adv. Eng. Mater., 2009, vol. 11, pp. 912–19.CrossRef A.V. Nagasekhar, M.A. Easton, and C.H. Cáceres: Adv. Eng. Mater., 2009, vol. 11, pp. 912–19.CrossRef
37.
Zurück zum Zitat H.I. Laukli: Norwegian University of Science and Technology, 2004. H.I. Laukli: Norwegian University of Science and Technology, 2004.
38.
Zurück zum Zitat H.I. Laukli, C.M. Gourlay, and A.K. Dahle: Metall. Mater. Trans. A Phys. Metall. Mater. Sci., 2005, vol. 36, pp. 805–18.CrossRef H.I. Laukli, C.M. Gourlay, and A.K. Dahle: Metall. Mater. Trans. A Phys. Metall. Mater. Sci., 2005, vol. 36, pp. 805–18.CrossRef
39.
Zurück zum Zitat A.L. Bowles, J.R. Griffiths, and C.J. Davidson: in Magnes. Technol. 2001, 2001, pp. 161–68. A.L. Bowles, J.R. Griffiths, and C.J. Davidson: in Magnes. Technol. 2001, 2001, pp. 161–68.
40.
Zurück zum Zitat K. Vanna Yang, C.H. Cáceres, and M.A. Easton: Mater. Sci. Eng. A, 2013, vol. 580, pp. 355–61.CrossRef K. Vanna Yang, C.H. Cáceres, and M.A. Easton: Mater. Sci. Eng. A, 2013, vol. 580, pp. 355–61.CrossRef
41.
Zurück zum Zitat J.P. Weiler, J.T. Wood, R.J. Klassen, R. Berkmortel, and G. Wang: Mater. Sci. Eng. A, 2006, vol. 419, pp. 297–305.CrossRef J.P. Weiler, J.T. Wood, R.J. Klassen, R. Berkmortel, and G. Wang: Mater. Sci. Eng. A, 2006, vol. 419, pp. 297–305.CrossRef
42.
Zurück zum Zitat H. Cao and M. Wessén: Metall. Mater. Trans. A, 2004, vol. 35A, pp. 309–19.CrossRef H. Cao and M. Wessén: Metall. Mater. Trans. A, 2004, vol. 35A, pp. 309–19.CrossRef
43.
Zurück zum Zitat M.S. Dargusch, M. Nave, S.D. McDonald, and D.H. StJohn: J. Alloys Compd., 2010, vol. 492, pp. L64–68.CrossRef M.S. Dargusch, M. Nave, S.D. McDonald, and D.H. StJohn: J. Alloys Compd., 2010, vol. 492, pp. L64–68.CrossRef
44.
Zurück zum Zitat S. Barbagallo, H.I. Laukli, O. Lohne, and E. Cerri: J. Alloys Compd., 2004, vol. 378, pp. 226–32.CrossRef S. Barbagallo, H.I. Laukli, O. Lohne, and E. Cerri: J. Alloys Compd., 2004, vol. 378, pp. 226–32.CrossRef
45.
Zurück zum Zitat W.P. Sequeira, G.L. Dunlop, and M.T. Murray: in Proc. Third Int. Magnes. Conf., 1996, pp. 63–73. W.P. Sequeira, G.L. Dunlop, and M.T. Murray: in Proc. Third Int. Magnes. Conf., 1996, pp. 63–73.
46.
Zurück zum Zitat D.J. Sakkinen: SAE Tech. Pap., 1994, pp. 558–69. D.J. Sakkinen: SAE Tech. Pap., 1994, pp. 558–69.
47.
Zurück zum Zitat D. Mirković and R. Schmid-Fetzer: Metall. Mater. Trans. A Phys. Metall. Mater. Sci., 2009, vol. 40, pp. 974–81.CrossRef D. Mirković and R. Schmid-Fetzer: Metall. Mater. Trans. A Phys. Metall. Mater. Sci., 2009, vol. 40, pp. 974–81.CrossRef
48.
Zurück zum Zitat X.J. Wang, S.M. Zhu, M.A. Easton, M.A. Gibson, and G. Savage: Int. J. Cast Met. Res., 2014, vol. 27, pp. 161–66.CrossRef X.J. Wang, S.M. Zhu, M.A. Easton, M.A. Gibson, and G. Savage: Int. J. Cast Met. Res., 2014, vol. 27, pp. 161–66.CrossRef
49.
Zurück zum Zitat K. Sadayappan, W. Kasprzak, Z. Brown, L. Ouimet, and A.A. Luo: Mater. Sci. Forum, 2009, vol. 618–619, pp. 381–86.CrossRef K. Sadayappan, W. Kasprzak, Z. Brown, L. Ouimet, and A.A. Luo: Mater. Sci. Forum, 2009, vol. 618–619, pp. 381–86.CrossRef
50.
Zurück zum Zitat M. Zhou, A. Yu, N. Li, H. Hu, and R. Bowers: in Magnes. Technol. 2006, 2006, pp. 121–27. M. Zhou, A. Yu, N. Li, H. Hu, and R. Bowers: in Magnes. Technol. 2006, 2006, pp. 121–27.
51.
Zurück zum Zitat X. Li, S.M. Xiong, and Z. Guo: Mater. Sci. Eng. A, 2015, vol. 633, pp. 35–41.CrossRef X. Li, S.M. Xiong, and Z. Guo: Mater. Sci. Eng. A, 2015, vol. 633, pp. 35–41.CrossRef
52.
Zurück zum Zitat S. Otarawanna, C.M. Gourlay, H.I. Laukli, and A.K. Dahle: Mater. Charact., 2009, vol. 60, pp. 1432–41.CrossRef S. Otarawanna, C.M. Gourlay, H.I. Laukli, and A.K. Dahle: Mater. Charact., 2009, vol. 60, pp. 1432–41.CrossRef
53.
Zurück zum Zitat S.G. Lee, G.R. Patel, and A.M Gokhale: Scr. Mater., 2005, vol. 52, pp. 1063–68. S.G. Lee, G.R. Patel, and A.M Gokhale: Scr. Mater., 2005, vol. 52, pp. 1063–68.
54.
Zurück zum Zitat M.S. Dargusch, K. Pettersen, K. Nogita, M.D. Nave, and G.L. Dunlop: Mater. Trans., 2006, vol. 47, pp. 977–82.CrossRef M.S. Dargusch, K. Pettersen, K. Nogita, M.D. Nave, and G.L. Dunlop: Mater. Trans., 2006, vol. 47, pp. 977–82.CrossRef
55.
Zurück zum Zitat P. Bakke, K. Pettersen, and H. Westengen: in Magnes. Technol. 2003, 2003, pp. 171–76. P. Bakke, K. Pettersen, and H. Westengen: in Magnes. Technol. 2003, 2003, pp. 171–76.
56.
Zurück zum Zitat N. Tahreen, D.L. Chen, M. Nouri, and D.Y. Li: Mater. Sci. Eng. A, 2014, vol. 594, pp. 235–45.CrossRef N. Tahreen, D.L. Chen, M. Nouri, and D.Y. Li: Mater. Sci. Eng. A, 2014, vol. 594, pp. 235–45.CrossRef
57.
Zurück zum Zitat G. Cheng, E.I. Barker, E.V. Stephens, K.S. Choi, and X. Sun: MRS Adv., 2016, pp. 1–12. G. Cheng, E.I. Barker, E.V. Stephens, K.S. Choi, and X. Sun: MRS Adv., 2016, pp. 1–12.
58.
Zurück zum Zitat E. Aghion, N. Moscovitch, and A. Arnon: Mater. Sci. Eng. A, 2007, vol. 447, pp. 341–46.CrossRef E. Aghion, N. Moscovitch, and A. Arnon: Mater. Sci. Eng. A, 2007, vol. 447, pp. 341–46.CrossRef
59.
Zurück zum Zitat W.P. Sequeira, G.L. Dunlop, and M.T. Murray: in Proc. 3 rd Magnes. Conf. 1996, pp. 63–73. W.P. Sequeira, G.L. Dunlop, and M.T. Murray: in Proc. 3 rd Magnes. Conf. 1996, pp. 63–73.
60.
Zurück zum Zitat [60] D.G. Leo Prakash and D. Regener: J. Alloys Compd., 2008, vol. 464, pp. 133–37.CrossRef [60] D.G. Leo Prakash and D. Regener: J. Alloys Compd., 2008, vol. 464, pp. 133–37.CrossRef
61.
Zurück zum Zitat T.N. Baker: in Yield, Flow Fract. Polycrystals, 1982, pp. 235–73. T.N. Baker: in Yield, Flow Fract. Polycrystals, 1982, pp. 235–73.
62.
63.
Zurück zum Zitat S. C. Weakley-Bollin, W. Donlon, W. Donlon, C. Wolverton, J. E. Allison, and J. W. Jones: Metall. Mater. Trans. A, 2004, vol. 35, pp. 2407–18.CrossRef S. C. Weakley-Bollin, W. Donlon, W. Donlon, C. Wolverton, J. E. Allison, and J. W. Jones: Metall. Mater. Trans. A, 2004, vol. 35, pp. 2407–18.CrossRef
64.
Zurück zum Zitat C.H. Cáceres, C.J. Davidson, J.R. Griffiths, and C.L. Newton: Mater. Sci. Eng. A, 2002, vol. 325, pp. 344–55.CrossRef C.H. Cáceres, C.J. Davidson, J.R. Griffiths, and C.L. Newton: Mater. Sci. Eng. A, 2002, vol. 325, pp. 344–55.CrossRef
65.
Zurück zum Zitat T.N. Baker, ed.: Yield, Flow, and Fracture of Polycrystals, 1983. T.N. Baker, ed.: Yield, Flow, and Fracture of Polycrystals, 1983.
66.
Zurück zum Zitat P. Sharifi, Y. Fan, H.B. Anaraki, A. Banerjee, K. Sadayappan, and J.T. Wood: Metall. Mater. Trans. A, 2016, vol. 47, pp. 5159–5168. P. Sharifi, Y. Fan, H.B. Anaraki, A. Banerjee, K. Sadayappan, and J.T. Wood: Metall. Mater. Trans. A, 2016, vol. 47, pp. 5159–5168.
67.
Zurück zum Zitat J.A. Yasi, L.G. Hector, and D.R. Trinkle: Acta Mater., 2010, vol. 58, pp. 5704–13.CrossRef J.A. Yasi, L.G. Hector, and D.R. Trinkle: Acta Mater., 2010, vol. 58, pp. 5704–13.CrossRef
68.
Zurück zum Zitat R.L. Fleischer: in Strength. Met., D. Peckner, ed., 1964, pp. 93–140. R.L. Fleischer: in Strength. Met., D. Peckner, ed., 1964, pp. 93–140.
69.
Zurück zum Zitat C. H. Caceres and P. Lukac: Philos. Mag., 2008, vol. 88, pp. 977–89.CrossRef C. H. Caceres and P. Lukac: Philos. Mag., 2008, vol. 88, pp. 977–89.CrossRef
70.
Zurück zum Zitat J. H. Shen, Y. L. Li, and Q. Wei: Mater. Sci. Eng. A, 2013, vol. 582, pp. 270–75.CrossRef J. H. Shen, Y. L. Li, and Q. Wei: Mater. Sci. Eng. A, 2013, vol. 582, pp. 270–75.CrossRef
71.
Zurück zum Zitat C.H. Cáceres and D.M. Rovera: J. Light Met., 2001, vol. 1, pp. 151–56.CrossRef C.H. Cáceres and D.M. Rovera: J. Light Met., 2001, vol. 1, pp. 151–56.CrossRef
72.
73.
Zurück zum Zitat N.J. Petch: J. Iron Steel Inst., 1953, vol. 174, pp. 25–28. N.J. Petch: J. Iron Steel Inst., 1953, vol. 174, pp. 25–28.
74.
Zurück zum Zitat A. Akhtar and E. Teghtsoonian: Acta Metall., 1969, vol. 17, pp. 1339–49.CrossRef A. Akhtar and E. Teghtsoonian: Acta Metall., 1969, vol. 17, pp. 1339–49.CrossRef
75.
Zurück zum Zitat W. B. Hutchinson and M. R. Barnett: Scr. Mater., 2010, vol. 63, pp. 737–40.CrossRef W. B. Hutchinson and M. R. Barnett: Scr. Mater., 2010, vol. 63, pp. 737–40.CrossRef
76.
Zurück zum Zitat K. Fukuda, Y. Koyanagi, M. Tsushida, H. Kitahara, T. Mayama, and S. Ando: in 9th Pacific Rim Int. Conf. Adv. Mater. Process., 2016, pp. 794–96. K. Fukuda, Y. Koyanagi, M. Tsushida, H. Kitahara, T. Mayama, and S. Ando: in 9th Pacific Rim Int. Conf. Adv. Mater. Process., 2016, pp. 794–96.
77.
Zurück zum Zitat J. Zhang and S.P. Joshi: J. Mech. Phys. Solids, 2012, vol. 60, pp. 945–72.CrossRef J. Zhang and S.P. Joshi: J. Mech. Phys. Solids, 2012, vol. 60, pp. 945–72.CrossRef
78.
Zurück zum Zitat F.E. Hauser, P.R. Landon, and J.E. Dorn: Trans. Am. Inst. Mining, Metall. Pet. Eng. Inc., 1956, vol. 206, pp. 589–93. F.E. Hauser, P.R. Landon, and J.E. Dorn: Trans. Am. Inst. Mining, Metall. Pet. Eng. Inc., 1956, vol. 206, pp. 589–93.
79.
Zurück zum Zitat C.H. Cáceres, G.E. Mann, and J.R. Griffiths: Metall. Mater. Trans. A, 2011, vol. 42, pp. 1950–59.CrossRef C.H. Cáceres, G.E. Mann, and J.R. Griffiths: Metall. Mater. Trans. A, 2011, vol. 42, pp. 1950–59.CrossRef
80.
Zurück zum Zitat P. Sharifi, Y. Fan, J.P. Weiler, and J.T. Wood: J. Alloys Compd., 2014, vol. 605, pp. 237–43.CrossRef P. Sharifi, Y. Fan, J.P. Weiler, and J.T. Wood: J. Alloys Compd., 2014, vol. 605, pp. 237–43.CrossRef
81.
Zurück zum Zitat K.J. Kurzydlowski and J.J. Bucki: Acta Metall. Mater., 1993, vol. 41, pp. 3141–46.CrossRef K.J. Kurzydlowski and J.J. Bucki: Acta Metall. Mater., 1993, vol. 41, pp. 3141–46.CrossRef
82.
Zurück zum Zitat K. Vanna Yang, C.H. Cáceres, A.V. Nagasekhar, and M.A. Easton: Mater. Sci. Eng. A, 2012, vol. 542, pp. 49–55.CrossRef K. Vanna Yang, C.H. Cáceres, A.V. Nagasekhar, and M.A. Easton: Mater. Sci. Eng. A, 2012, vol. 542, pp. 49–55.CrossRef
83.
Zurück zum Zitat A. Akhtar and E. Teghtsoonian: Acta Metall., 1969, vol. 17, pp. 1351–56.CrossRef A. Akhtar and E. Teghtsoonian: Acta Metall., 1969, vol. 17, pp. 1351–56.CrossRef
Metadaten
Titel
The Influence of Al Content and Thickness on the Microstructure and Tensile Properties in High-Pressure Die Cast Magnesium Alloys
verfasst von
Erin Deda
Tracy D. Berman
John E. Allison
Publikationsdatum
20.01.2017
Verlag
Springer US
Erschienen in
Metallurgical and Materials Transactions A / Ausgabe 4/2017
Print ISSN: 1073-5623
Elektronische ISSN: 1543-1940
DOI
https://doi.org/10.1007/s11661-017-3958-4

Weitere Artikel der Ausgabe 4/2017

Metallurgical and Materials Transactions A 4/2017 Zur Ausgabe

    Marktübersichten

    Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen.