01.04.2014 | Ausgabe 2/2014

Metallurgical and Materials Transactions B 2/2014

Transient Asymmetric Flow and Bubble Transport Inside a Slab Continuous-Casting Mold

Zeitschrift:
Metallurgical and Materials Transactions B > Ausgabe 2/2014
Autoren:
Zhongqiu Liu, Baokuan Li, Maofa Jiang
Wichtige Hinweise
Manuscript submitted May 23, 2013.

Abstract

A one third scale water model experiment was conducted to observe the asymmetric flow and vortexing flow inside a slab continuous-casting mold. Dye-injection experiment was used to show the evolution of the transient flow pattern in the liquid pool without and with gas injection. The spread of the dye was not symmetric about the central plane. The flow pattern inside the mold was not stationary. The black sesames were injected into water to visualize the vortexing flow pattern on the top surface. The changes of shape and location of single vortex and two vortices with time had been observed during experiments. Plant ultrasonic testing (UT) of slabs was used to analyze the slab defects distribution, which indicated that the defects are intermittent and asymmetric. A mathematical model has been developed to analyze the time-dependent flow using the realistic geometries, which includes the submerged entry nozzle (SEN), actual mold, and part of the secondary cooling zone. The transient turbulent flow of molten steel inside the mold has been simulated using the large eddy simulation computational approach. Simulation results agree acceptably well with the water model experimentally observed and plant UT results. The oscillating motions of jet and the turbulence naturally promote the asymmetric flow even without the effects of slide gate nozzle or the existence of clogs inside the SEN. The periodic behavior of transient fluid flow in the mold is identified and characterized. The vortexing flow is resulted from asymmetric flow in the liquid pool. The vortices are located at the low-velocity side adjacent to the SEN, and the positions and sizes are different. Finally, the model is applied to investigate the influence of bubble size and casting speed on the time-dependent bubble distribution and removal fraction from the top surface inside the mold.

Bitte loggen Sie sich ein, um Zugang zu diesem Inhalt zu erhalten

Sie möchten Zugang zu diesem Inhalt erhalten? Dann informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 69.000 Bücher
  • über 500 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Umwelt
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe

Testen Sie jetzt 30 Tage kostenlos.

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 50.000 Bücher
  • über 380 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Umwelt
  • Maschinenbau + Werkstoffe​​​​​​​




Testen Sie jetzt 30 Tage kostenlos.

Literatur
Über diesen Artikel

Weitere Artikel der Ausgabe 2/2014

Metallurgical and Materials Transactions B 2/2014 Zur Ausgabe

Premium Partner

    Marktübersichten

    Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen. 

    Bildnachweise