14.06.2016

Transient Liquid Phase Diffusion Bonding of 6061Al-15 wt.% SiC p Composite Using Mixed Cu-Ag Powder Interlayer

verfasst von: Pallab Roy, Tapan Kumar Pal, Joydeep Maity

Erschienen in: Journal of Materials Engineering and Performance | Ausgabe 8/2016

Einloggen

Aktivieren Sie unsere intelligente Suche um passende Fachinhalte oder Patente zu finden.

search-config
loading …

Abstract

Microstructure and shear strength of transient liquid phase diffusion bonded (560 °C, 0.2 MPa) 6061Al-15 wt.% SiCp extruded composite using a 50-µm-thick mixed Cu-Ag powder interlayer have been investigated. During isothermal solidification that took 2 h for completion, a ternary liquid phase formed due to diffusion of Cu and Ag in Al. Subsequent cooling formed a ternary phase mixture (α-Al + CuAl2 + Ag2Al) upon eutectic solidification. With mixed Cu-Ag powder interlayer, isothermal solidification was faster than for pure Al joints made using a 50-µm-thick Cu foil interlayer and for the composite joints made using a 50-µm-thick Cu foil/powder interlayer under similar conditions. The presence of brittle eutectic phase mixture (CuAl2 + Ag2Al) led to poor joint strength at short TLP bonding times. The mixture disappeared upon isothermal solidification with a 2-h hold yielding improved joint strength even with solidification shrinkage in the joint. Increased holding time (6 h) erased shrinkage via solid state diffusion and yielded the highest joint strength (87 MPa) and fair joint efficiency (83%).

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Literatur
1.
Zurück zum Zitat D. Huda, MAEl Baradie, and M.S.J. Hashmi, Metal-Matrix Compsites: Materials Aspects, Part II, J. Mater. Process. Technol., 1993, 37, p 529–541CrossRef D. Huda, MAEl Baradie, and M.S.J. Hashmi, Metal-Matrix Compsites: Materials Aspects, Part II, J. Mater. Process. Technol., 1993, 37, p 529–541CrossRef
2.
Zurück zum Zitat T.J. Lienert, W.A. Baeslack, J. Ringnalda, and H.L. Fraser, Inertia-Friction Welding of SiC-Reinforced 8009-Aluminium, J. Mater. Sci., 1996, 31, p 2149–2157CrossRef T.J. Lienert, W.A. Baeslack, J. Ringnalda, and H.L. Fraser, Inertia-Friction Welding of SiC-Reinforced 8009-Aluminium, J. Mater. Sci., 1996, 31, p 2149–2157CrossRef
3.
Zurück zum Zitat M.B.D. Ellis, Joining of Metal Matrix Composites-A Review, TWI, J., 1997, 6, p 69–128 M.B.D. Ellis, Joining of Metal Matrix Composites-A Review, TWI, J., 1997, 6, p 69–128
4.
Zurück zum Zitat W.I. Hall and F. Manrique, Surface Treatment of Carbon Fiber for Aluminium Alloy Matrix Composites, Scr. Met., 1995, 33, p 2037–2043CrossRef W.I. Hall and F. Manrique, Surface Treatment of Carbon Fiber for Aluminium Alloy Matrix Composites, Scr. Met., 1995, 33, p 2037–2043CrossRef
5.
Zurück zum Zitat M.F. Gittos and P.L. Threadgill, Preliminary Studies of Joining Particulate Reinforced Aluminium Alloy Metal Matrix Composites, Proc. of Int. Symp. on ‘Metal Matrix Composites III: Exploiting the Investment, Institute of Metals, London, December 10-11, 1991. M.F. Gittos and P.L. Threadgill, Preliminary Studies of Joining Particulate Reinforced Aluminium Alloy Metal Matrix Composites, Proc. of Int. Symp. on ‘Metal Matrix Composites III: Exploiting the Investment, Institute of Metals, London, December 10-11, 1991.
6.
Zurück zum Zitat T.S. Luhman, R.L. Williams, and K.B. Das, Development of Joint and Joining Techniques for Metal Matrix Composites, Fourth Quarterly Progress Report, Army Materials and Mechanics Research Center, 1983, p 1-58. T.S. Luhman, R.L. Williams, and K.B. Das, Development of Joint and Joining Techniques for Metal Matrix Composites, Fourth Quarterly Progress Report, Army Materials and Mechanics Research Center, 1983, p 1-58.
7.
Zurück zum Zitat J.H. Devletian, SiC/Al Metal Matrix Composite Welding by a Capacitor Discharge Process, Weld. J., 1987, 66, p 33–39 J.H. Devletian, SiC/Al Metal Matrix Composite Welding by a Capacitor Discharge Process, Weld. J., 1987, 66, p 33–39
8.
Zurück zum Zitat D.J. Field, Aluminium Alloys-Contemporary Research and Applications, Vol 31, London Academic Press, London, 1989, p 523–537CrossRef D.J. Field, Aluminium Alloys-Contemporary Research and Applications, Vol 31, London Academic Press, London, 1989, p 523–537CrossRef
9.
Zurück zum Zitat A. Urena, J.M. Gomez de Salazar, and M.D. Escalera, Diffusion Bonding of Discontinuously Reinforced SiCp/Al Matrix Composites, Key Eng. Mater., 1995, 104–107, p 523–540CrossRef A. Urena, J.M. Gomez de Salazar, and M.D. Escalera, Diffusion Bonding of Discontinuously Reinforced SiCp/Al Matrix Composites, Key Eng. Mater., 1995, 104–107, p 523–540CrossRef
10.
Zurück zum Zitat A.A. Shirzadi and E.R. Wallach, New Approaches for Transient Liquid Phase Diffusion Bonding of Aluminum Based Metal Matrix Composites, Mater. Sci. Technol., 1997, 13, p 135–142CrossRef A.A. Shirzadi and E.R. Wallach, New Approaches for Transient Liquid Phase Diffusion Bonding of Aluminum Based Metal Matrix Composites, Mater. Sci. Technol., 1997, 13, p 135–142CrossRef
11.
Zurück zum Zitat J. Huang, Y. Dong, Y. Wan, X. Zhao, and H. Zhang, Investigation on Reactive Diffusion Bonding of SiCp/6063 MMC by Using Mixed Powders as Interlayers, J. Mater. Process. Technol., 2007, 190, p 312–316CrossRef J. Huang, Y. Dong, Y. Wan, X. Zhao, and H. Zhang, Investigation on Reactive Diffusion Bonding of SiCp/6063 MMC by Using Mixed Powders as Interlayers, J. Mater. Process. Technol., 2007, 190, p 312–316CrossRef
12.
Zurück zum Zitat T.K. Pal, Joining of Aluminium Metal Matrix Composites, Mater. Manuf. Process., 2005, 20, p 717–726CrossRef T.K. Pal, Joining of Aluminium Metal Matrix Composites, Mater. Manuf. Process., 2005, 20, p 717–726CrossRef
13.
Zurück zum Zitat J. Yan, Z. Xu, G. Wu, and S. Yang, Interface Structure and Mechanical Performance of TLP Bonded Joints of Al2O3p/6061 Al Composites Using Cu/Ni Composite Interlayers, Scr. Mater., 2004, 51, p 147–150CrossRef J. Yan, Z. Xu, G. Wu, and S. Yang, Interface Structure and Mechanical Performance of TLP Bonded Joints of Al2O3p/6061 Al Composites Using Cu/Ni Composite Interlayers, Scr. Mater., 2004, 51, p 147–150CrossRef
14.
Zurück zum Zitat D.S. Duvall, W.A. Owczarski, and D.F. Paulonis, TLP Bonding: A New Method for Joining Heat Resistant Alloys, Weld. J., 1974, 53, p 203–214 D.S. Duvall, W.A. Owczarski, and D.F. Paulonis, TLP Bonding: A New Method for Joining Heat Resistant Alloys, Weld. J., 1974, 53, p 203–214
15.
Zurück zum Zitat I. Tuah-Poku, M. Dollar, and T.B. Massalski, A Study of the Transient Liquid Phase Bonding Process applied to a Ag/Cu/Ag Sandwich Joint, Weld. J., 1988, 19A, p 675–686 I. Tuah-Poku, M. Dollar, and T.B. Massalski, A Study of the Transient Liquid Phase Bonding Process applied to a Ag/Cu/Ag Sandwich Joint, Weld. J., 1988, 19A, p 675–686
16.
Zurück zum Zitat Y. Natsume, K. Ohsasa, Y. Tayu, T. Momono, and T. Narita, Numerical Modeling of Transient Liquid- Phase Diffusion Bonding Process of Al using Cu Filler Metal, ISIJ Int., 2003, 43, p 1976–1982CrossRef Y. Natsume, K. Ohsasa, Y. Tayu, T. Momono, and T. Narita, Numerical Modeling of Transient Liquid- Phase Diffusion Bonding Process of Al using Cu Filler Metal, ISIJ Int., 2003, 43, p 1976–1982CrossRef
17.
Zurück zum Zitat D.F. Paulonis, D.S. Duvall, and W.A. Owczarski, U.S. Patent No. 3,678,570, July 1972. D.F. Paulonis, D.S. Duvall, and W.A. Owczarski, U.S. Patent No. 3,678,570, July 1972.
18.
Zurück zum Zitat A.T. Egbewande, C. Chukwukaeme, and O.A. Ojo, Joining of Superalloy Inconel 600 by Diffusion Induced Isothermal Solidification of a Liquated Insert Metal, Mater. Charact., 2007, 59, p 1051–1058CrossRef A.T. Egbewande, C. Chukwukaeme, and O.A. Ojo, Joining of Superalloy Inconel 600 by Diffusion Induced Isothermal Solidification of a Liquated Insert Metal, Mater. Charact., 2007, 59, p 1051–1058CrossRef
19.
Zurück zum Zitat N.P. Wikstrom, O.A. Ojo, and M.C. Chaturvedi, Influence of Process Parameters on Microstructure of Transient Liquid Phase Bonded Inconel 738LC Superalloy with Amdry DF-3 Interlayer, Mater. Sci. Eng. A, 2006, 417, p 299–306CrossRef N.P. Wikstrom, O.A. Ojo, and M.C. Chaturvedi, Influence of Process Parameters on Microstructure of Transient Liquid Phase Bonded Inconel 738LC Superalloy with Amdry DF-3 Interlayer, Mater. Sci. Eng. A, 2006, 417, p 299–306CrossRef
20.
Zurück zum Zitat D.Q. Sun, W.H. Liu, and X.Y. Gu, Transient Liquid Phase Bonding of Magnesium Alloy (Mg-3Al-1Zn) Using Copper Interlayer, Mater. Sci. Technol., 2004, 20, p 1595–1598CrossRef D.Q. Sun, W.H. Liu, and X.Y. Gu, Transient Liquid Phase Bonding of Magnesium Alloy (Mg-3Al-1Zn) Using Copper Interlayer, Mater. Sci. Technol., 2004, 20, p 1595–1598CrossRef
21.
Zurück zum Zitat T. Padron, T.I. Khan, and M.J. Kabir, Modelling the Transient Liquid Phase Bonding Behaviour of a Duplex Stainless Steel Using Copper Interlayers, Mater. Sci. Eng. A, 2004, 385, p 220–228CrossRef T. Padron, T.I. Khan, and M.J. Kabir, Modelling the Transient Liquid Phase Bonding Behaviour of a Duplex Stainless Steel Using Copper Interlayers, Mater. Sci. Eng. A, 2004, 385, p 220–228CrossRef
22.
Zurück zum Zitat T.I. Khan, M.J. Kabir, and R. Bulpett, Effect of Transient Liquid-Phase Bonding Variables on the Properties of Micro-duplex Stainless Steel, Mater. Sci. Eng. A, 2004, 372, p 290–295CrossRef T.I. Khan, M.J. Kabir, and R. Bulpett, Effect of Transient Liquid-Phase Bonding Variables on the Properties of Micro-duplex Stainless Steel, Mater. Sci. Eng. A, 2004, 372, p 290–295CrossRef
23.
Zurück zum Zitat W.F. Gale, D.A. Butts, M.D. Ruscio, and T. Zhou, Microstructure and Mechanical Properties of Titanium Aluminide Wide-Gap, Transient Liquid-Phase Bonds Prepared Using a Slurry-Deposited Composite Interlayer, Metall. Mater. Trans. A, 2002, 33A, p 3205–3214CrossRef W.F. Gale, D.A. Butts, M.D. Ruscio, and T. Zhou, Microstructure and Mechanical Properties of Titanium Aluminide Wide-Gap, Transient Liquid-Phase Bonds Prepared Using a Slurry-Deposited Composite Interlayer, Metall. Mater. Trans. A, 2002, 33A, p 3205–3214CrossRef
24.
Zurück zum Zitat T.I. Khan and B.N. Roy, Transient Liquid Phase Bonding of an ODS Ferrite Steel to Silicon Nitride, J. Mater. Sci., 2004, 39, p 741–743CrossRef T.I. Khan and B.N. Roy, Transient Liquid Phase Bonding of an ODS Ferrite Steel to Silicon Nitride, J. Mater. Sci., 2004, 39, p 741–743CrossRef
25.
Zurück zum Zitat R.S. Bushby and V.D. Scott, Liquid Phase Bonding of Aluminum and Aluminum/Nicalon Composite Using Copper Interlayers, Mater. Sci. Technol., 1993, 9, p 417–423CrossRef R.S. Bushby and V.D. Scott, Liquid Phase Bonding of Aluminum and Aluminum/Nicalon Composite Using Copper Interlayers, Mater. Sci. Technol., 1993, 9, p 417–423CrossRef
26.
Zurück zum Zitat R.S. Bushby and V.D. Scott, Liquid Phase Bonding of Aluminum and Aluminum/Nicalon Composite Using Interlayers of Cu-Ag Alloy, Mater. Sci. Technol., 1995, 11, p 643–649CrossRef R.S. Bushby and V.D. Scott, Liquid Phase Bonding of Aluminum and Aluminum/Nicalon Composite Using Interlayers of Cu-Ag Alloy, Mater. Sci. Technol., 1995, 11, p 643–649CrossRef
27.
Zurück zum Zitat R. Klen and T.W. Eagar, Joining of 6061 Aluminum Metal-Ceramic Particle Reinforced Composites, WRC Bull., 1993, 385, p 1–26 R. Klen and T.W. Eagar, Joining of 6061 Aluminum Metal-Ceramic Particle Reinforced Composites, WRC Bull., 1993, 385, p 1–26
28.
Zurück zum Zitat W.D. MacDonald and T.W. Eagar, Transient Liquid Phase Bonding, Annu. Rev. Mater. Sci., 1992, 22, p 23–46CrossRef W.D. MacDonald and T.W. Eagar, Transient Liquid Phase Bonding, Annu. Rev. Mater. Sci., 1992, 22, p 23–46CrossRef
29.
Zurück zum Zitat T.H. North, K. Ikeuchi, Y. Zhou, and H. Kokawa, Dissolution and Isothermal Solidification in Transient Liquid Phase Brazing, Proceedings of the Symposium on ‘The Metal Science of Joining’, M.J. Cieslak, J.H. Perepezko, S. Kang, and M.E. Glicksman, Eds., The Minerals, Metals & Materials Society, Pennsylvania, 1992, p 83-100. T.H. North, K. Ikeuchi, Y. Zhou, and H. Kokawa, Dissolution and Isothermal Solidification in Transient Liquid Phase Brazing, Proceedings of the Symposium on ‘The Metal Science of Joining’, M.J. Cieslak, J.H. Perepezko, S. Kang, and M.E. Glicksman, Eds., The Minerals, Metals & Materials Society, Pennsylvania, 1992, p 83-100.
30.
Zurück zum Zitat Y. Zhou, W.F. Gale, and T.H. North, Modelling of Transient Liquid Phase Bonding, Int. Mater. Rev., 1995, 40, p 181–196CrossRef Y. Zhou, W.F. Gale, and T.H. North, Modelling of Transient Liquid Phase Bonding, Int. Mater. Rev., 1995, 40, p 181–196CrossRef
31.
Zurück zum Zitat Z. Li, Y. Zhou, and T.H. North, Counteraction of Particulate Segregation During Transient Liquid-Phase Bonding of Aluminum-Based MMC Material, J. Mater. Sci., 1995, 30, p 1075–1082CrossRef Z. Li, Y. Zhou, and T.H. North, Counteraction of Particulate Segregation During Transient Liquid-Phase Bonding of Aluminum-Based MMC Material, J. Mater. Sci., 1995, 30, p 1075–1082CrossRef
32.
Zurück zum Zitat J. Maity, Joining of Aluminium Based Metal Matrix Composite by Transient Liquid Phase Diffusion Bonding Technique, Ph.D. Thesis, Jadavpur University, Kolkata, 2009, p 97. J. Maity, Joining of Aluminium Based Metal Matrix Composite by Transient Liquid Phase Diffusion Bonding Technique, Ph.D. Thesis, Jadavpur University, Kolkata, 2009, p 97.
33.
Zurück zum Zitat J. Maity, Joining of Aluminium Based Metal Matrix Composites, Engineered Metal Matrix Composites: Forming Methods, Material Properties and Industrial Applications, L. Magagnin, Ed., Nova Science Publishers Inc, New York, 2012, p 329–354 J. Maity, Joining of Aluminium Based Metal Matrix Composites, Engineered Metal Matrix Composites: Forming Methods, Material Properties and Industrial Applications, L. Magagnin, Ed., Nova Science Publishers Inc, New York, 2012, p 329–354
34.
Zurück zum Zitat J. Maity, T.K. Pal, and R. Maiti, Transient Liquid Phase Diffusion Bonding of 6061-15 wt.% SiCp in Argon Environment, J. Mater. Process. Technol., 2009, 209, p 3568–3580CrossRef J. Maity, T.K. Pal, and R. Maiti, Transient Liquid Phase Diffusion Bonding of 6061-15 wt.% SiCp in Argon Environment, J. Mater. Process. Technol., 2009, 209, p 3568–3580CrossRef
35.
Zurück zum Zitat J. Maity, T.K. Pal, and R. Maiti, Transient Liquid Phase Bonding of 6061-15 wt.% SiCp in Argon Environment Using Cu Powder Interlayer, Mater. Sci. Technol., 2009, 25, p 1489–1494CrossRef J. Maity, T.K. Pal, and R. Maiti, Transient Liquid Phase Bonding of 6061-15 wt.% SiCp in Argon Environment Using Cu Powder Interlayer, Mater. Sci. Technol., 2009, 25, p 1489–1494CrossRef
36.
Zurück zum Zitat J. Maity, T.K. Pal, and R. Maiti, Transient Liquid Phase Diffusion Bonding of 6061-13 vol.% SiCp Composite Using Cu Powder Interlayer: Mechanism and Interface Characterization, J. Mater. Sci., 2010, 45, p 3575–3587CrossRef J. Maity, T.K. Pal, and R. Maiti, Transient Liquid Phase Diffusion Bonding of 6061-13 vol.% SiCp Composite Using Cu Powder Interlayer: Mechanism and Interface Characterization, J. Mater. Sci., 2010, 45, p 3575–3587CrossRef
37.
Zurück zum Zitat J. Maity, T.K. Pal, and R. Maiti, Microstructural Evaluation and Ultrasonic Characterization of TLPD bonded 6061-SiCp Composite, ISIJ Int., 2008, 48, p 616–623CrossRef J. Maity, T.K. Pal, and R. Maiti, Microstructural Evaluation and Ultrasonic Characterization of TLPD bonded 6061-SiCp Composite, ISIJ Int., 2008, 48, p 616–623CrossRef
38.
Zurück zum Zitat J. Maity, T.K. Pal, and R. Maiti, Microstructural Characterization of TLPD bonded 6061-SiCp Composite, J. Mater. Eng. Perform. ASM Int., 2008, 17, p 746–754CrossRef J. Maity, T.K. Pal, and R. Maiti, Microstructural Characterization of TLPD bonded 6061-SiCp Composite, J. Mater. Eng. Perform. ASM Int., 2008, 17, p 746–754CrossRef
39.
Zurück zum Zitat Anon, Alloy Phase Diagrams, ASM Handbook, vol. 3, ASM International, Materials Park, 1992, p 2.44-3.10. Anon, Alloy Phase Diagrams, ASM Handbook, vol. 3, ASM International, Materials Park, 1992, p 2.44-3.10.
40.
Zurück zum Zitat V. Raghavan, Ag-Al-Cu (Silver-Aluminium-Copper), J. Phase Equil. Diffusion, 2008, 29, p 256–258CrossRef V. Raghavan, Ag-Al-Cu (Silver-Aluminium-Copper), J. Phase Equil. Diffusion, 2008, 29, p 256–258CrossRef
41.
Zurück zum Zitat M.H. Francombe and R.W. Holfman, Physics of Thin Films: Advances in Research and Development, Academic Press, New York, 1971, p 331 M.H. Francombe and R.W. Holfman, Physics of Thin Films: Advances in Research and Development, Academic Press, New York, 1971, p 331
42.
Zurück zum Zitat J. Huang, Y. Wan, and H. Zhang, TLP Bonding of SiCp/2618Al Composites Using Mixed Al-Ag-Cu System Powders as Interlayers, J. Mater. Sci, 2007, 42, p 9746–9749CrossRef J. Huang, Y. Wan, and H. Zhang, TLP Bonding of SiCp/2618Al Composites Using Mixed Al-Ag-Cu System Powders as Interlayers, J. Mater. Sci, 2007, 42, p 9746–9749CrossRef
43.
Zurück zum Zitat Anon, Properties and Selection: Non Ferrous Alloys and Special Purpose Materials, Metals Handbook, vol. 2, ASM International, Materials Park, OH, 1990, p 102-103. Anon, Properties and Selection: Non Ferrous Alloys and Special Purpose Materials, Metals Handbook, vol. 2, ASM International, Materials Park, OH, 1990, p 102-103.
44.
Zurück zum Zitat X. Xie, G.E. Totten, and M.A.H. Howes, Ed., Steel Heat Treatment Hand Book, Marcel Dekker, New York, 1997, p 995 X. Xie, G.E. Totten, and M.A.H. Howes, Ed., Steel Heat Treatment Hand Book, Marcel Dekker, New York, 1997, p 995
45.
Zurück zum Zitat W. Zhou and Z.M. Xu, Casting of SiC Reinforced Metal Matrix Composites, J. Mater. Process. Technol., 1997, 63, p 358–363CrossRef W. Zhou and Z.M. Xu, Casting of SiC Reinforced Metal Matrix Composites, J. Mater. Process. Technol., 1997, 63, p 358–363CrossRef
46.
Zurück zum Zitat Anon, Ceramics and Glasses, Engineering Materials Handbook, ASM International, Materials Park, OH, 1991. Anon, Ceramics and Glasses, Engineering Materials Handbook, ASM International, Materials Park, OH, 1991.
47.
Zurück zum Zitat J.M. Papazian, Effects of SiC Whiskers and Particles on Precipitation in Aluminium Matrix Composites, Metall. Trans. A., 1988, 19A, p 2945–2953CrossRef J.M. Papazian, Effects of SiC Whiskers and Particles on Precipitation in Aluminium Matrix Composites, Metall. Trans. A., 1988, 19A, p 2945–2953CrossRef
48.
Zurück zum Zitat N.A. Gjostein, ‘Short Circuit Diffusion’ in ‘Diffusion’, Papers Presented at a Seminar of the American Society for Metals, American Society for Metals, Metals Park, OH, October 14-15, 1972, p 241. N.A. Gjostein, ‘Short Circuit Diffusion’ in ‘Diffusion’, Papers Presented at a Seminar of the American Society for Metals, American Society for Metals, Metals Park, OH, October 14-15, 1972, p 241.
49.
Zurück zum Zitat X. Ge and S. Schmauder, Micromechanism of Fracture in Al/SiC Composites, J. Mater. Sci., 1995, 30, p 173–178CrossRef X. Ge and S. Schmauder, Micromechanism of Fracture in Al/SiC Composites, J. Mater. Sci., 1995, 30, p 173–178CrossRef
Metadaten
Titel
Transient Liquid Phase Diffusion Bonding of 6061Al-15 wt.% SiC p Composite Using Mixed Cu-Ag Powder Interlayer
verfasst von
Pallab Roy
Tapan Kumar Pal
Joydeep Maity
Publikationsdatum
14.06.2016
Verlag
Springer US
Erschienen in
Journal of Materials Engineering and Performance / Ausgabe 8/2016
Print ISSN: 1059-9495
Elektronische ISSN: 1544-1024
DOI
https://doi.org/10.1007/s11665-016-2165-6

Weitere Artikel der Ausgabe 8/2016

Journal of Materials Engineering and Performance 8/2016 Zur Ausgabe

    Marktübersichten

    Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen.