Ultra-low-carbon steel spheroidization and torsion

Zeitschrift:
Journal of Iron and Steel Research International > Ausgabe 9/2018
Autoren:
Yan-jun Yin, Ji-quan Sun, Ai-min Zhao, Jin Gou

Abstract

Spheroidizing annealing and torsion testing of 0.027 wt% carbon steel rod were conducted to evaluate spheroidization kinetic behavior at 943 K (670 °C) under deformed and non-deformed states. Kinetic curves were also predicted using the Johnson–Mehl–Avrami–Kolmogorov equation, and the results agree well with the experimental ones. After spheroidization was performed twice, the spherical cementite and precipitated carbides became smaller and the distribution was more uniform. Comparison of materials subjected to single and double spheroidizing annealing indicated a difference in grain size. Torsion performance was considerably improved under double spheroidization, especially the maximum torque with slight variations.

Bitte loggen Sie sich ein, um Zugang zu diesem Inhalt zu erhalten

Literatur
Über diesen Artikel

Weitere Artikel der Ausgabe 9/2018

Journal of Iron and Steel Research International 9/2018 Zur Ausgabe

Premium Partner

    Marktübersichten

    Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen. 

    Bildnachweise