Understanding the influence of carbon addition on the corrosion behavior and mechanical properties of Al alloy “covetics”

Zeitschrift:
Journal of Materials Science > Ausgabe 3/2019
Autoren:
Jason A. Varnell, Mete Bakir, Angela M. DiAscro, Xinyi Chen, Sabrina Nilufar, Iwona Jasiuk, Andrew A. Gewirth
Wichtige Hinweise

Electronic supplementary material

The online version of this article (https://​doi.​org/​10.​1007/​s10853-018-2998-5) contains supplementary material, which is available to authorized users.

Abstract

The recent invention of a new processing method for metals and alloys involving the addition of carbon has led to several reports demonstrating an enhancement in the mechanical properties of the materials known as “covetics.” In this work the corrosion behavior and mechanical properties of a 6061 aluminum–carbon covetic are investigated and explained. Covetic samples with carbon added were found to exhibit a corrosion potential 40–70 mV higher than samples processed without the addition of carbon. However, the corrosion current density of the covetic with carbon added relative to samples without carbon added was also increased. Surface characterization following the corrosion testing using scanning electron microscopy, energy-dispersive X-ray spectroscopy, and X-ray diffraction revealed significant differences between the covetic with carbon added and the covetic parent material processed without carbon addition. After corrosion, the surface of the covetic with carbon added showed a alloying element rich surface morphology from the parent alloy and exhibited a smaller grain size than the material processed without carbon. Additionally, changes in the mechanical properties of the covetic were observed with both the hardness and the compressive strength of the covetic increasing as a result of carbon addition. The observed change in corrosion behavior and mechanical properties of the covetic with carbon added, along with the physical characterization, are consistent with the formation of a secondary phase in the alloy induced by carbon addition during the process used to make the covetic.

Bitte loggen Sie sich ein, um Zugang zu diesem Inhalt zu erhalten

Sie möchten Zugang zu diesem Inhalt erhalten? Dann informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 69.000 Bücher
  • über 500 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Umwelt
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Testen Sie jetzt 30 Tage kostenlos.

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 50.000 Bücher
  • über 380 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Umwelt
  • Maschinenbau + Werkstoffe




Testen Sie jetzt 30 Tage kostenlos.

Zusatzmaterial
Literatur
Über diesen Artikel

Weitere Artikel der Ausgabe 3/2019

Journal of Materials Science 3/2019 Zur Ausgabe

Premium Partner

    Marktübersichten

    Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen. 

    Bildnachweise