19.05.2021 | Original Research Article

Understanding the Role of Short-Range Order in the Nucleation and Transformation of the B′/Q′ Precipitates in Al-Mg-Si(-Cu) Alloys

verfasst von: Lipeng Ding, Yaoyao Weng, Zhihong Jia, Ruojin Zang, Qing Liu

Erschienen in: Metallurgical and Materials Transactions A | Ausgabe 8/2021

Einloggen

Aktivieren Sie unsere intelligente Suche um passende Fachinhalte oder Patente zu finden.

search-config
loading …

Abstract

The understanding of metastable hardening precipitate evolution in Al-Mg-Si(-Cu) is still quite confused and elusive due to the disordered nature of several precipitates and the complex processes involved. Atomic-resolution scanning transmission electron microscopy is used here to study the nucleation and transformation mechanisms of the B′/Q′ precipitates in the Al-Mg-Si(-Cu) alloys. It is emphasized that understanding the formation and evolution of short-range order (SRO) in the precipitates is a core to revealing their transformation mechanisms. Although the B′ and Q′ phases have the same crystal structure, and both originate from the β″ precipitate, the formation mechanisms of these two precipitates are different. For B′, formed in the Al-Mg-Si alloy, the β″ phase initially transforms to the U2 phase by the transition of the “low density cylinder” (LDC) to Mg hexagons. Subsequently, the U2 phase transforms to the B′ phase by the rotation of Al-Si columns, and the formation and ordering of triangle B′ sub-units. For Q′, formed in the Al-Mg-Si-Cu alloy, the Cu atoms incorporate initially the interior of the β″ phase and form the substructure of Cu sub-unit clusters. In most cases, these Cu sub-unit clusters are randomly distributed, and the QM and QP lattices are formed throughout the precipitates. In some precipitates, the arrangement of Cu sub-unit clusters however constitutes a hexagonal lattice and leads to the formation of the QC phase. During subsequent aging, the formation and ordering of the triangle Q′ sub-units can lead to the formation of the Q′ phase. Clarifying the role of the SRO in these processes provides a new insight in the understanding of transformation mechanisms of precipitates in Al-Mg-Si(-Cu) alloys.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Literatur
1.
Zurück zum Zitat 1. W.S. Miller, L. Zhuang, J. Bottema, A.J. Wittebrood, P.D. Smet, A. Haszler, A. Vieregge, Mater. Sci. Eng. A, 2000, vol. 280, pp. 37-49.CrossRef 1. W.S. Miller, L. Zhuang, J. Bottema, A.J. Wittebrood, P.D. Smet, A. Haszler, A. Vieregge, Mater. Sci. Eng. A, 2000, vol. 280, pp. 37-49.CrossRef
2.
Zurück zum Zitat 2. Z. Li, R. Zang, P. Zhao, Z. Jia, Mater. Sci. Eng. A, 2020, vol. 782, pp.139206.CrossRef 2. Z. Li, R. Zang, P. Zhao, Z. Jia, Mater. Sci. Eng. A, 2020, vol. 782, pp.139206.CrossRef
3.
Zurück zum Zitat 3. G.A. Edwards, K. Stille, G.L. Dunlop, M.J. Couper, Acta Mater., 1998, vol. 46, pp. 3893-3904.CrossRef 3. G.A. Edwards, K. Stille, G.L. Dunlop, M.J. Couper, Acta Mater., 1998, vol. 46, pp. 3893-3904.CrossRef
4.
Zurück zum Zitat 4. T. Saito, S. Muraishi, C. Marioara, S. Andersen, J. Røyset, R. Holmestad, Metall. Mater. Trans. A, 2013, vol. 44A, pp. 4124-35.CrossRef 4. T. Saito, S. Muraishi, C. Marioara, S. Andersen, J. Røyset, R. Holmestad, Metall. Mater. Trans. A, 2013, vol. 44A, pp. 4124-35.CrossRef
5.
Zurück zum Zitat 5. H.W. Zandbergen, S.J. Andersen, J.Jansen, Science, 1997, vol. 277, pp. 1221-25.CrossRef 5. H.W. Zandbergen, S.J. Andersen, J.Jansen, Science, 1997, vol. 277, pp. 1221-25.CrossRef
6.
Zurück zum Zitat H.k.S. Hasting, A.G. Fro̸seth, S.J. Andersen, R. Vissers, J.C. Walmsley, C.D. Marioara, F.d.r. Danoix, W. Lefebvre, J Appl. Phys., 2009, vol. 106, pp. 123527. H.k.S. Hasting, A.G. Fro̸seth, S.J. Andersen, R. Vissers, J.C. Walmsley, C.D. Marioara, F.d.r. Danoix, W. Lefebvre, J Appl. Phys., 2009, vol. 106, pp. 123527.
7.
Zurück zum Zitat 7. S. Wenner, L. Jones, C.D. Marioara, R. Holmestad, Micron, 2017, vol.96, pp. 103-11.CrossRef 7. S. Wenner, L. Jones, C.D. Marioara, R. Holmestad, Micron, 2017, vol.96, pp. 103-11.CrossRef
8.
Zurück zum Zitat 8. K. Matsuda, Y. Sakaguchi, Y. Miyata, Y. Uetani, T. Sato, S.I. A. Kamio, J Mater. Sci., 2000, vol. 35, pp. 179-89.CrossRef 8. K. Matsuda, Y. Sakaguchi, Y. Miyata, Y. Uetani, T. Sato, S.I. A. Kamio, J Mater. Sci., 2000, vol. 35, pp. 179-89.CrossRef
9.
Zurück zum Zitat 9. C.D. Marioara, S.J. Andersen, H.W. Zandbergen, R. Holmestad, Metall. Mater. Trans. A, 2005, vol. 36A, pp. 691-702. 9. C.D. Marioara, S.J. Andersen, H.W. Zandbergen, R. Holmestad, Metall. Mater. Trans. A, 2005, vol. 36A, pp. 691-702.
10.
Zurück zum Zitat 10. M.A. van Huis, J.H. Chen, H.W. Zandbergen, M.H.F. Sluiter, Acta Mater., 2006, vol. 54, pp. 2945-55.CrossRef 10. M.A. van Huis, J.H. Chen, H.W. Zandbergen, M.H.F. Sluiter, Acta Mater., 2006, vol. 54, pp. 2945-55.CrossRef
11.
Zurück zum Zitat 11. K. Matsuda, S. Ikeno, Y. Uetani, T. Sato, Metall. Mater. Trans. A, 2001, vol. 32A. pp. 1293-99.CrossRef 11. K. Matsuda, S. Ikeno, Y. Uetani, T. Sato, Metall. Mater. Trans. A, 2001, vol. 32A. pp. 1293-99.CrossRef
12.
Zurück zum Zitat 12. L. Ding, Z. Jia, Z. Zhang, R.E. Sanders, Q. Liu, G. Yang, Mater. Sci. Eng. A, 2015, vol. 627, pp. 119-26.CrossRef 12. L. Ding, Z. Jia, Z. Zhang, R.E. Sanders, Q. Liu, G. Yang, Mater. Sci. Eng. A, 2015, vol. 627, pp. 119-26.CrossRef
13.
Zurück zum Zitat 13. L. Ding, Z. Jia, J.-F. Nie, Y. Weng, L. Cao, H. Chen, X. Wu, Q. Liu, Acta Mater., 2018, vol.145, pp. 437-50.CrossRef 13. L. Ding, Z. Jia, J.-F. Nie, Y. Weng, L. Cao, H. Chen, X. Wu, Q. Liu, Acta Mater., 2018, vol.145, pp. 437-50.CrossRef
14.
Zurück zum Zitat 14. K. Li, A. Béché, M. Song, G. Sha, X. Lu, K. Zhang, Y. Du, S.P. Ringer, D. Schryvers, Scr. Mater., 2013, vol.75, pp. 86-89.CrossRef 14. K. Li, A. Béché, M. Song, G. Sha, X. Lu, K. Zhang, Y. Du, S.P. Ringer, D. Schryvers, Scr. Mater., 2013, vol.75, pp. 86-89.CrossRef
15.
Zurück zum Zitat 15. C. Cayron, L. Sagalowicz, O. Beffort, P.A. Buffat, Philos. Mag. A, 1999, vol. 79A, pp. 2833-51.CrossRef 15. C. Cayron, L. Sagalowicz, O. Beffort, P.A. Buffat, Philos. Mag. A, 1999, vol. 79A, pp. 2833-51.CrossRef
16.
Zurück zum Zitat 16. C.D. Marioara, S.J. Andersen, T.N. Stene, H. Hasting, J. Walmsley, A.T.J. Van Helvoort, R. Holmestad, Philos. Mag., 2007, vol.87, pp. 3385-3413.CrossRef 16. C.D. Marioara, S.J. Andersen, T.N. Stene, H. Hasting, J. Walmsley, A.T.J. Van Helvoort, R. Holmestad, Philos. Mag., 2007, vol.87, pp. 3385-3413.CrossRef
17.
Zurück zum Zitat 17. H. Chen, J. Lu, Y. Kong, K. Li, T. Yang, A. Meingast, M. Yang, Q. Lu, Y. Du, Acta Mater., 2020, vol. 185, pp. 193-203.CrossRef 17. H. Chen, J. Lu, Y. Kong, K. Li, T. Yang, A. Meingast, M. Yang, Q. Lu, Y. Du, Acta Mater., 2020, vol. 185, pp. 193-203.CrossRef
18.
Zurück zum Zitat 18. S.J. Andersen, C.D. Marioara, R. Vissers, A. Frøseth, H.W. Zandbergen, Mater. Sci. Eng. A, 2007, vol. 444, pp. 157-69.CrossRef 18. S.J. Andersen, C.D. Marioara, R. Vissers, A. Frøseth, H.W. Zandbergen, Mater. Sci. Eng. A, 2007, vol. 444, pp. 157-69.CrossRef
19.
Zurück zum Zitat 19. S.J. Andersen, C.D. Marioara, A. Frøseth, R. Vissers, H.W. Zandbergen, Mater. Sci. Eng. A, 2005, vol. 390, pp. 127-38.CrossRef 19. S.J. Andersen, C.D. Marioara, A. Frøseth, R. Vissers, H.W. Zandbergen, Mater. Sci. Eng. A, 2005, vol. 390, pp. 127-38.CrossRef
20.
Zurück zum Zitat 20. E.A. Mørtsell, C.D. Marioara, S.J. Andersen, I.G. Ringdalen, J. Friis, S. Wenner, J. Røyset, O. Reiso, R. Holmestad, J Alloy Compd., 2016, vol.699, pp. 235-42.CrossRef 20. E.A. Mørtsell, C.D. Marioara, S.J. Andersen, I.G. Ringdalen, J. Friis, S. Wenner, J. Røyset, O. Reiso, R. Holmestad, J Alloy Compd., 2016, vol.699, pp. 235-42.CrossRef
21.
Zurück zum Zitat 21. M.A. van Huis, J.H. Chen, M.H.F. Sluiter, H.W. Zandbergen, Acta Mater., 2007, vol. 55, pp. 2183-99.CrossRef 21. M.A. van Huis, J.H. Chen, M.H.F. Sluiter, H.W. Zandbergen, Acta Mater., 2007, vol. 55, pp. 2183-99.CrossRef
22.
Zurück zum Zitat J.H. Chen, E. Costan, M.A.v. Huis, Q. Xu, H.W. Zandbergen, Science, 2006, vol. 312, pp. 416-19. J.H. Chen, E. Costan, M.A.v. Huis, Q. Xu, H.W. Zandbergen, Science, 2006, vol. 312, pp. 416-19.
23.
Zurück zum Zitat 23. L. Ding, H. Hu, Z. Jia, Y. Weng, X. Wu, Q. Liu, Scr. Mater., 2016, vol. 118, pp. 55-59.CrossRef 23. L. Ding, H. Hu, Z. Jia, Y. Weng, X. Wu, Q. Liu, Scr. Mater., 2016, vol. 118, pp. 55-59.CrossRef
24.
Zurück zum Zitat 24. Y.X. Lai, W. Fan, M.J. Yin, C.L. Wu, J.H. Chen, J Mater. Sci.Technol., 2020, vol.41, pp. 127-38. 24. Y.X. Lai, W. Fan, M.J. Yin, C.L. Wu, J.H. Chen, J Mater. Sci.Technol., 2020, vol.41, pp. 127-38.
25.
Zurück zum Zitat 25. S. Ji, W. Yang, F. Gao, D. Watson, Z. Fan, Mater. Sci. Eng. A, 2013, vol. 564, pp. 130-39.CrossRef 25. S. Ji, W. Yang, F. Gao, D. Watson, Z. Fan, Mater. Sci. Eng. A, 2013, vol. 564, pp. 130-39.CrossRef
27.
Zurück zum Zitat 27. C. Cayron, P.A. Buffat, O. Beffort, S. Long, J Mater. Sci., 1999, vol. 34, pp. 905-15.CrossRef 27. C. Cayron, P.A. Buffat, O. Beffort, S. Long, J Mater. Sci., 1999, vol. 34, pp. 905-15.CrossRef
28.
Zurück zum Zitat 28. K.M. Ikeno, Y. Uetani, T. Sato, Metall. Mater. Trans. A, 2001, vol. 32A, pp. 1293-99 28. K.M. Ikeno, Y. Uetani, T. Sato, Metall. Mater. Trans. A, 2001, vol. 32A, pp. 1293-99
29.
Zurück zum Zitat 29. L. Ding, A. Orekhov, Y. Weng, Z. Jia, H. Idrissi, D. Schryvers, S. Muraishi, L. Hao, Q. Liu, J Mater. Sci., 2019, vol.54, pp. 7943–52.CrossRef 29. L. Ding, A. Orekhov, Y. Weng, Z. Jia, H. Idrissi, D. Schryvers, S. Muraishi, L. Hao, Q. Liu, J Mater. Sci., 2019, vol.54, pp. 7943–52.CrossRef
30.
Zurück zum Zitat 30. V. Fallah, B. Langelier, N. Ofori-Opoku, B. Raeisinia, N. Provatas, S. Esmaeili, Acta Mater., 2016, vol. 103, pp. 290-300.CrossRef 30. V. Fallah, B. Langelier, N. Ofori-Opoku, B. Raeisinia, N. Provatas, S. Esmaeili, Acta Mater., 2016, vol. 103, pp. 290-300.CrossRef
31.
Zurück zum Zitat 31. Z. Jia, L. Ding, L. Cao, R. Sanders, S. Li, Q. Liu, Metall. Mater. Trans. A, 2016, vol. 48A, pp 459-73. 31. Z. Jia, L. Ding, L. Cao, R. Sanders, S. Li, Q. Liu, Metall. Mater. Trans. A, 2016, vol. 48A, pp 459-73.
32.
Zurück zum Zitat 32. Y. Weng, L. Ding, Z. Zhang, Z. Jia, B. Wen, Y. Liu, S. Muraishi, Y. Li, Q. Liu, Acta Mater., 2019, vol. 180, pp. 301-16.CrossRef 32. Y. Weng, L. Ding, Z. Zhang, Z. Jia, B. Wen, Y. Liu, S. Muraishi, Y. Li, Q. Liu, Acta Mater., 2019, vol. 180, pp. 301-16.CrossRef
33.
Zurück zum Zitat 33. J.K. Sunde, C.D. Marioara, A.T.J. van Helvoort, R. Holmestad, Mater. Charact., 2018, vol. 142, pp. 458-69.CrossRef 33. J.K. Sunde, C.D. Marioara, A.T.J. van Helvoort, R. Holmestad, Mater. Charact., 2018, vol. 142, pp. 458-69.CrossRef
Metadaten
Titel
Understanding the Role of Short-Range Order in the Nucleation and Transformation of the B′/Q′ Precipitates in Al-Mg-Si(-Cu) Alloys
verfasst von
Lipeng Ding
Yaoyao Weng
Zhihong Jia
Ruojin Zang
Qing Liu
Publikationsdatum
19.05.2021
Verlag
Springer US
Erschienen in
Metallurgical and Materials Transactions A / Ausgabe 8/2021
Print ISSN: 1073-5623
Elektronische ISSN: 1543-1940
DOI
https://doi.org/10.1007/s11661-021-06309-2

Weitere Artikel der Ausgabe 8/2021

Metallurgical and Materials Transactions A 8/2021 Zur Ausgabe

    Marktübersichten

    Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen.