In this work, a cast magnesium alloy AZ91D was friction stir processed. Detailed microstructural studies and Gleeble hot ductility tests were conducted on the as-cast and the FSPed samples to comparatively assess their heat-affected zone liquation cracking behavior. The results show that the use of FSP as a pretreatment to fusion welding can strikingly improve the heat-affected zone liquation cracking resistance of alloy AZ91D by reducing the amount and size of the low-melting eutectic β (Mg17Al12) as well as by refining the matrix grain size.
Bitte loggen Sie sich ein, um Zugang zu diesem Inhalt zu erhalten
P.B. Prangnell and C.P. Heason: Acta Mater., 2005, 53, pp. 3179-3192.
CrossRef
2.
T.R. McNelley, S. Swaminathan, J.Q. Su: Scripta Mater., 2008, 58, pp. 349-354.
CrossRef
3.
[3] R.S. Mishra, and M.W. Mahoney:
Friction stir processing. in
Friction stir welding and processing, R.S. Mishra, and M.W. Mahoney, eds., ASM International, USA, 2007, pp. 309-350.
4.
[4] Z.Y. MA, Friction stir processing technology: A review, Metall. Mater. Trans. A, 2008, 39A, pp. 642-658.
CrossRef
5.
[5] S.M. Mousavizade, F.M. Ghaini, M.J. Torkamany, J. Sabbaghzadeh, A. Abdollah-Zadeh: Scripta Mater., 2009, 60, 244-247.
CrossRef
[7] Z.M. Beiranvand, F.M. Ghaini, M. Sheikhi, A. Abdollah-Zadeh: Sci. Technol. Weld. Joi., 2013, 18, pp. 473-477.
CrossRef
8.
[8] G.M. Karthik, G.D. Janaki Ram, R.S. Kottada: Metall. Mater. Trans. B, 2017, 48, pp. 1158-1173.
CrossRef
9.
Siederslebnen M, Honsel AG (2003) Meschede. In: Kainer KU (eds.) Magnesium – Alloys and Technology, Wiley, Weinheim pp. 45–55.
10.
A.K. Dahle, Y.C. Lee, M.D. Nave, P.L. Schaffer, D.H. StJohn: J. Light Met., 2001, 1, pp. 61-72.
CrossRef
11.
Chandler H (Ed.) (1996) Heat Treater’s Guide: Practices and Procedures for Nonferrous Alloys. ASM International, Materials Park pp. 415-438.
12.
[12] S. Celotto: Acta Mater., 2000, 48, pp. 1775-1787.
CrossRef
13.
[13] X. Chai, T. Yuan, S. Kou: Weld. J., 2016, 95, pp. 57s-67s.
14.
[14] T. Zhu, Z.W. Chen, W. Gao: Mater. Charact., 2008, 59, pp. 1550-1558.
CrossRef
15.
[15] W. Zhou, T. Z. Long, C. K. Mark: Mater. Sci. Technol., 2007, 23, pp. 1294-1299.
CrossRef
16.
[16] W. Lin, J.C. Lippold, W.A. Baeslack III: Weld. J., 1993, 71, pp. 135s-153s.
17.
Mandziej ST (2005) Physical simulation of metallurgical processes. In: Bollinghaus T, Herold H (eds) Hot Cracking Phenomena in Welds. Springer, Germany pp. 347-376.
CrossRef
18.
[18] P. Asadi, R.A. Mahdavinejad, S. Tutunchilar: Mat. Sci. Eng. A, 2011, 528, pp. 6469- 6477.
CrossRef
19.
[19] A.H. Feng and Z.Y. Ma: Scripta Mater., 2007, 56, pp. 397-400.
CrossRef
20.
[20] F. Chai, D. Zhang, Y. Li: Materials, 2014, 7, pp. 1573-1589.
CrossRef
21.
[21] C.I. Chang, X.H. Du, J.C. Huang: Scripta Mater., 2008, 59, pp. 356-359.
CrossRef
22.
[22] A.H. Feng and Z.Y. Ma: Acta Mater., 2009, 57, pp. 4248-4260.
CrossRef
Über diesen Artikel
Titel
Use of Friction Stir Processing for Improving Heat-Affected Zone Liquation Cracking Resistance of a Cast Magnesium Alloy AZ91D
Autoren:
G. M. Karthik G. D. Janaki Ram Ravi Sankar Kottada
Die B2B-Firmensuche für Industrie und Wirtschaft: Kostenfrei in Firmenprofilen nach Lieferanten, Herstellern, Dienstleistern und Händlern recherchieren.
Lesen Sie in diesem ausgewählten Buchkapitel alles über den 3D-Druck im Hinblick auf Begriffe, Funktionsweise, Anwendungsbereiche sowie Nutzen und Grenzen additiver Fertigungsverfahren. Eigenschaften eines schlanken Produktionssystems sowie der Aspekt der „Schlankheit“ werden ebenso beleuchtet wie die Prinzipien und Methoden der Lean Production. Jetzt gratis downloaden!
Marktübersichten
Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen.